Chloride Permeability of Damaged High-Performance Fiber-Reinforced Cement Composite by Repeated Compressive Loads.

ABSTRACT: The development of cracking in concrete structures leads to significant permeability and to durability problems as a result. Approaches to controlling crack development and crack width in concrete structures have been widely debated. Recently, it was recognized that a high-performance fiber-reinforced cement composite (HPFRCC) provides a possible solution to this inherent problem of cracking by smearing one or several dominant cracks into many distributed microcracks under tensile loading conditions. However, the chloride permeability of HPFRCC under compressive loading conditions is not yet fully understood. Therefore, the goal of the present study is to explore the chloride diffusion characteristics of HPFRCC damaged by compressive loads. The chloride diffusivity of HPFRCC is measured after being subjected to various repeated loads. The results show that the residual axial strain, lateral strain and specific crack area of HPFRCC specimens increase with an increase in the damage induced by repeated loads. However, the chloride diffusion coefficient increases only up to 1.5-times, whereas the specific crack area increases up to 3-times with an increase in damage. Although HPFRCC shows smeared distributed cracks in tensile loads, a significant reduction in the diffusion coefficient of HPFRCC is not obtained compared to plain concrete when the cyclic compressive load is applied below 85% of the strength.

SUBMITTER: Lee BJ

PROVIDER: S-EPMC5456180 | biostudies-other | 2014 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Improvement of Performances of the Gypsum-Cement Fiber Reinforced Composite (GCFRC).

Project description:The novelty of this paper lies in the identification of the scientific patterns of the influence of thermal power plant waste (TPPW) on the hydration mechanism and the structure of the gypsum-cement binder (GCB). The classification of raw materials for the production of GCB has been developed taking into account the genesis, which contributes to the prediction of the properties of composites. The features of the hydration phase formation and hardening of GCB have been studied taking into account the chemical, structural and morphological features of fly ash and slag. In addition, the microstructural, morphological, and thermal properties of the cured binders at a 28 day cure were determined. For the first time, scientific data on the properties of gypsum-cement fiber-reinforced composite using TPPW and microfiber have been obtained. The results show that the synergistic effect of gypsum-cement binder, TPPW, and polyamide or basalt microfiber improves the physicomechanical properties of a 28 day cured binder: compressive strength of 20 MPa, flexural strength of 8.9 MPa, and softening coefficient 0.87.

| S-EPMC7503270 | biostudies-literature

Fabrication of benzoyl chloride treated tiger-nut fiber reinforced insect repellent hybrid composite.

Project description:An insect repellent composite containing tiger nut particulate fibre, waste low density polyethene (LDPE) and castor oil alkyd resin was fabricated. Canarium schweinfurthii gum was used as insect repellent compound and maleic anhydride as compatibilizer. The tiger nut chaff was subjected to benzoylation using benzoyl chloride to increase the fibre-matrix interaction. The compound and composition was then moulded with LDPE as dual matrices for excellent physico-mechanical properties (pressed for 5 min, 130 °C and 25 bar and cured). The 10 wt.% treated composite exhibited a minimum water absorption of ~ 0.085%, optimal chemical resistance for both acids (HCl and H2SO4) and bases (NaOH and KOH) and no effect on thickness. Density measurement showed the lowest value of ~ 0.0096 g/cm3 for the treated fibre composite. However, the tensile strength, flexural stress, hardness and impact load were improved up to 35.08 Mpa, 456.3 Mpa, 95 and 730 J/m respectively with treated composites. Insect repellent tests against termites and cockroaches show repellent activity with time intervals. FTIR and SEM analysis showed fibre modification achieved.

| S-EPMC9132963 | biostudies-literature

Pullout Behavior of Bundled Aramid Fiber in Fiber-Reinforced Cementitious Composite.

Project description:The tensile performance of fiber-reinforced cementitious composite (FRCC) after first matrix cracking is characterized by a tensile stress-crack width relationship called the bridging law. The bridging law can be obtained by an integral calculus of forces carried by individual bridging fibers considering the effect of the fiber inclination angle. The main objective of this study is to investigate experimentally and evaluate the pullout behavior of a single aramid fiber, which is made with a bundling of original yarns of aramid fiber. The bundled aramid fiber has a nonsmooth surface, and it is expected to have good bond performance with the matrix. The test variables in the pullout test are the thickness of the matrix and the inclined angle of the fiber. From the test results, the pullout load-slip curves showed that the load increases lineally until maximum load, after which it decreases gradually. The maximum pullout load and slip at the maximum load increase as the embedded length of the fiber becomes larger. The pullout load-crack width relationship is modeled by a bilinear model, and the bridging law is calculated. The calculated result shows good agreement with the experimental curves obtained by the uniaxial tension test of aramid-FRCC.

| S-EPMC7179034 | biostudies-literature

Compressive Strength of Steel Fiber-Reinforced Concrete Employing Supervised Machine Learning Techniques.

Project description:Recently, research has centered on developing new approaches, such as supervised machine learning techniques, that can compute the mechanical characteristics of materials without investing much effort, time, or money in experimentation. To predict the 28-day compressive strength of steel fiber-reinforced concrete (SFRC), machine learning techniques, i.e., individual and ensemble models, were considered. For this study, two ensemble approaches (SVR AdaBoost and SVR bagging) and one individual technique (support vector regression (SVR)) were used. Coefficient of determination (R2), statistical assessment, and k-fold cross validation were carried out to scrutinize the efficiency of each approach used. In addition, a sensitivity technique was used to assess the influence of parameters on the prediction results. It was discovered that all of the approaches used performed better in terms of forecasting the outcomes. The SVR AdaBoost method was the most precise, with R2 = 0.96, as opposed to SVR bagging and support vector regression, which had R2 values of 0.87 and 0.81, respectively. Furthermore, based on the lowered error values (MAE = 4.4 MPa, RMSE = 8 MPa), statistical and k-fold cross validation tests verified the optimum performance of SVR AdaBoost. The forecast performance of the SVR bagging models, on the other hand, was equally satisfactory. In order to predict the mechanical characteristics of other construction materials, these ensemble machine learning approaches can be applied.

| S-EPMC9228203 | biostudies-literature

Rheological and Mechanical Properties of High-Performance Fiber-Reinforced Cement Composites with a Low Water-Cement Ratio.

Project description:High-performance fiber-reinforced cement composites (HPFRCCs) have been widely used in structural engineering due to their excellent performance. With the trend of lightweight construction, these materials, which can be used in prefabricated components, are becoming more and more important. This study investigated the influence of the water-cement (w/c) ratio, within the 0.19-0.28 range, on the rheological and mechanical properties of HPFRCCs; the pore structure and microstructure were observed to evaluate its effect. An elastic modulus test showed that a smaller w/c ratio would result in a higher rigidity of the material. Both the yield shear stress and plastic viscosity decreased to significantly different degrees with an increasing w/c ratio; a decrease in the yield shear stress and plastic viscosity was conducive to air discharge from the composite and, hence, reduced the air content. Most of the internal pores had a diameter of 20-100 nm or larger than 200 nm, while the proportion of those with a diameter of 100-200 nm was relatively low. When the w/c ratio was below 0.22, the flexural and compressive strengths barely increased due to an increment in the number of larger pores (i.e., diameter >200 nm). The results showed that the yield shear stress, plastic viscosity, pore uniformity, and the number of pores with a diameter above 200 nm are the dominant factors affecting the HPFRCC performance at a low w/c ratio.

| S-EPMC8945063 | biostudies-literature

Preparation, characterization, and evaluation of compressive strength of polypropylene fiber reinforced geopolymer mortars.

Project description:The study of the fiber-matrix interface represents a crucial topic to determine the mechanical performance of geopolymer-based materials reinforced with polypropylene fibers (PPF). This research proposes the use of natural zeolite in the preparation geopolymers mortars through alkaline activation with NaOH, Ca(OH)2 and Na2SiO3, and with river sand as a fine aggregate. PPF were incorporated into the geopolymer-based mortar matrix in different proportions like 0, 0.5, and 1 wt.%. The mortars were cured for 24 h at 60 °C and then aged for six days more at room temperature. All samples analyzed through compressive strength were also characterized by X-ray diffraction, thermal analysis, Infrared Spectroscopy, and scanning electron microscopy techniques. The results indicated that the best mix design among the ones used: NaOH (10 M), Na2SiO3/NaOH = 3, Ca(OH)2 = 1.5 wt.% and PPF = 0.5 wt.%. The optimum mix design showed a compressive strength of 4.63 MPa on average. Besides, the fibers enhanced the compressive strength of those samples which the PP fibers probably have better dispersion inside the matrix of the geopolymer mortar.

| S-EPMC7168747 | biostudies-literature

Study on the Compressive Properties of Magnesium Phosphate Cement Mixing with Eco-Friendly Coir Fiber Considering Fiber Length.

Project description:Coir fiber (CF), an eco-friendly and renewable natural fiber, was introduced into magnesium phosphate cement (MPC) mortar to improve its crack resistance. A total of 21 specimens were employed to investigate the failure pattern, compressive strength, stress-strain curve, and energy absorption of MPC with varying CF lengths (0, 5, 10, 15, 20, 25, and 30 mm) after a curing period of 28 days through a static compressive test. The results demonstrated that compressive strength, elastic modulus, and secant modulus decreased with the increase in CF length. However, energy absorption presented a convex curve, which increased to the maximum value (77.0% relative to the value of the specimen without CF) with a CF length of 20 mm and then declined. A series of modern micro-tests were then carried out to analyze the microstructure and composition of specimens to explain the properties microscopically.

| S-EPMC7411843 | biostudies-literature

Mechanical Characterization of High-Performance Steel-Fiber Reinforced Cement Composites with Self-Healing Effect.

Project description:The crack self-healing behavior of high-performance steel-fiber reinforced cement composites (HPSFRCs) was investigated. High-strength deformed steel fibers were employed in a high strength mortar with very fine silica sand to decreasing the crack width by generating higher interfacial bond strength. The width of micro-cracks, strongly affected by the type of fiber and sand, clearly produced the effects on the self-healing behavior. The use of fine silica sand in HPSFRCs with high strength deformed steel fibers successfully led to rapid healing owing to very fine cracks with width less than 20 µm. The use of very fine silica sand instead of normal sand produced 17%-19% higher tensile strength and 51%-58% smaller width of micro-cracks.

| S-EPMC5453159 | biostudies-literature

Effect of fiber entanglement in chopped glass fiber reinforced composite manufactured via long fiber spray-up molding.

Project description:Long Fiber Spray-up Molding (LFSM) deviates from the conventional approach in liquid composite molding (LCM) processes by utilizing extremely long chopped strands of fibers as the primary reinforcement material in its fabrication process. In LFSM, chopped fibers are impregnated with resin that is sprayed vertically downwards before reaching the mold surface. The spraying mechanism is mounted on an actuator, which is capable of spraying freely in any specified pattern or direction. Under LFSM, it is extremely difficult to fabricate a composite part with uniformly distributed fiber content throughout its volume. The consequences of the non-uniform fiber volume distribution arise from the fiber entanglement as the length of the fiber reaches up to 100 mm in LFSM. In this study, the effect of fiber entanglement during LFSM was analyzed through various approaches. This included measuring the coefficient of friction between fibers in contact and examining the correlation between fiber lengths and the number of intersections. Furthermore, the viscoelastic properties of the uncured composite part were assessed by experimenting with the influence of viscosity on fiber length during compression molding. The results were then computed, modeled, and visualized in MATLAB, considering variations in viscosity and fiber length, both before and after compression molding.

| S-EPMC10782114 | biostudies-literature

Using Machine Learning Algorithms to Estimate the Compressive Property of High Strength Fiber Reinforced Concrete.

Project description:The low tensile strain capacity and brittle nature of high-strength concrete (HSC) can be improved by incorporating steel fibers into it. Steel fibers' addition in HSC results in bridging behavior which improves its post-cracking behavior, provides cracks arresting and stresses transfer in concrete. Using machine learning (ML) techniques, concrete properties prediction is an effective solution to conserve construction time and cost. Therefore, sophisticated ML approaches are applied in this study to predict the compressive strength of steel fiber reinforced HSC (SFRHSC). To fulfil this purpose, a standalone ML model called Multiple-Layer Perceptron Neural Network (MLPNN) and ensembled ML algorithms named Bagging and Adaptive Boosting (AdaBoost) were employed in this study. The considered parameters were cement content, fly ash content, slag content, silica fume content, nano-silica content, limestone powder content, sand content, coarse aggregate content, maximum aggregate size, water content, super-plasticizer content, steel fiber content, steel fiber diameter, steel fiber length, and curing time. The application of statistical checks, i.e., root mean square error (RMSE), determination coefficient (R2), and mean absolute error (MAE), was also performed for the assessment of algorithms' performance. The study demonstrated the suitability of the Bagging technique in the prediction of SFRHSC compressive strength. Compared to other models, the Bagging approach was more accurate as it produced higher, i.e., 0.94, R2, and lower error values. It was revealed from the SHAP analysis that curing time and super-plasticizer content have the most significant influence on the compressive strength of SFRHSC. The outcomes of this study will be beneficial for researchers in civil engineering for the timely and effective evaluation of SFRHSC compressive strength.

| S-EPMC9267573 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data