High Purity and Yield of Boron Nitride Nanotubes Using Amorphous Boron and a Nozzle-Type Reactor.

ABSTRACT: Enhancement of the production yield of boron nitride nanotubes (BNNTs) with high purity was achieved using an amorphous boron-based precursor and a nozzle-type reactor. Use of a mixture of amorphous boron and Fe decreases the milling time for the preparation of the precursor for BNNTs synthesis, as well as the Fe impurity contained in the B/Fe interdiffused precursor nanoparticles by using a simple purification process. We also explored a nozzle-type reactor that increased the production yield of BNNTs compared to a conventional flow-through reactor. By using a nozzle-type reactor with amorphous boron-based precursor, the weight of the BNNTs sample after annealing was increased as much as 2.5-times with much less impurities compared to the case for the flow-through reactor with the crystalline boron-based precursor. Under the same experimental conditions, the yield and quantity of BNNTs were estimated as much as ~70% and ~1.15 g/batch for the former, while they are ~54% and 0.78 g/batch for the latter.

SUBMITTER: Kim J

PROVIDER: S-EPMC5456191 | biostudies-other | 2014 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Rebar graphene from functionalized boron nitride nanotubes.

Project description:The synthesis of rebar graphene on Cu substrates is described using functionalized boron nitride nanotubes (BNNTs) that were annealed or subjected to chemical vapor deposition (CVD) growth of graphene. Characterization shows that the BNNTs partially unzip and form a reinforcing bar (rebar) network within the graphene layer that enhances the mechanical strength through covalent bonds. The rebar graphene is transferrable to other substrates without polymer assistance. The optical transmittance and conductivity of the hybrid rebar graphene film was tested, and a field effect transistor was fabricated to explore its electrical properties. This method of synthesizing 2D hybrid graphene/BN structures should enable the hybridization of various 1D nanotube and 2D layered structures with enhanced mechanical properties.

| S-EPMC4310641 | biostudies-literature

Achieving Boron-Carbon-Nitrogen Heterostructures by Collision Fusion of Carbon Nanotubes and Boron Nitride Nanotubes.

Project description:Heterostructures may exhibit completely new physical properties that may be otherwise absent in their individual component materials. However, how to precisely grow or assemble desired complex heterostructures is still a significant challenge. In this work, the collision dynamics of a carbon nanotube and a boron nitride nanotube under different collision modes were investigated using the self-consistent-charge density-functional tight-binding molecular dynamics method. The energetic stability and electronic structures of the heterostructure after collision were calculated using the first-principles calculations. Five main collision outcomes are observed, that is, two nanotubes can (1) bounce back, (2) connect, (3) fuse into a defect-free BCN heteronanotube with a larger diameter, (4) form a heteronanoribbon of graphene and hexagonal boron nitride and (5) create serious damage after collision. It was found that both the BCN single-wall nanotube and the heteronanoribbon created by collision are the direct band-gap semiconductors with the band gaps of 0.808 eV and 0.544 eV, respectively. These results indicate that collision fusion is a viable method to create various complex heterostructures with new physical properties.

| S-EPMC10254723 | biostudies-literature

Chemical affinity and dispersibility of boron nitride nanotubes.

Project description:Boron nitride nanotubes (BNNTs) are electrically insulating nanoparticles that display highly competitive elastic modulus and thermal conductivity. Long presented as potential fillers for nanocomposite applications, their poor dispersibility in most commodity polymers has, however, limited their spread. In this work, the chemical affinity of purified BNNTs, measured in terms of Hansen solubility parameters (HSP), were obtained through sedimentation tests in a wide set of organic solvents, taking into account relative sedimentation time. The parameters obtained were {δ d; δ p; δ h} = {16.8; 10.7; 14.7} ± {0.3; 0.9; 0.3} MPa1/2, with a Hildebrand parameter, δ t = 24.7 MPa1/2 and a sphere radius of 5.4 MPa1/2. The solubility parameters were determined considering complete dispersion of the purified nanomaterial, as well as the viscosity and density of the host solvent. These factors, combined with the high purity of the BNNTs, are crucial to minimize the uncertainty of the HSP characterization. Such refined values provide necessary insights both to optimize the solvent casting of unmodified BNNTs, and to orient the surface modification efforts that would be needed to integrate these nanomaterials into a wider range of host matrices.

| S-EPMC9419523 | biostudies-literature

Dual growth mode of boron nitride nanotubes in high temperature pressure laser ablation.

Project description:The morphological analysis of the end of boron nitride nanotubes (BNNTs) using high-resolution transmission electron microscopy (HR-TEM) can provide valuable insight into the growth mechanism in high temperature pressure (HTP) laser ablation where the best quality of BNNT materials can be obtained so far. Two growth modes of BNNT coexisting during the synthesis process have been proposed based on HR-TEM observation and length analysis. One is the root growth mode, in which boron nitride (BN) species formed via the surface interaction between surrounding N2 molecules and boron nanodroplets incorporate into the tubular structure. Another mode called open-end growth mode means the prolongation of tube growth from the exposed BN edge surrounding the surface of boron nanodroplets which is constructed by the heterogeneous nucleation of absorbed BN radicals from the gas plume. The statistical data, the proportions of end structures and the length of BNNTs, could be fitted to two growth modes, and the open-end growth mode is found to be especially effective in producing longer nanotubes with a higher growth rate. The scientific understanding of the growth mechanism is believed to provide the control for optimized production of BNNTs.

| S-EPMC6821736 | biostudies-literature

Tunable and high-purity room temperature single-photon emission from atomic defects in hexagonal boron nitride.

Project description:Two-dimensional van der Waals materials have emerged as promising platforms for solid-state quantum information processing devices with unusual potential for heterogeneous assembly. Recently, bright and photostable single photon emitters were reported from atomic defects in layered hexagonal boron nitride (hBN), but controlling inhomogeneous spectral distribution and reducing multi-photon emission presented open challenges. Here, we demonstrate that strain control allows spectral tunability of hBN single photon emitters over 6 meV, and material processing sharply improves the single photon purity. We observe high single photon count rates exceeding 7 × 106 counts per second at saturation, after correcting for uncorrelated photon background. Furthermore, these emitters are stable to material transfer to other substrates. High-purity and photostable single photon emission at room temperature, together with spectral tunability and transferability, opens the door to scalable integration of high-quality quantum emitters in photonic quantum technologies.Inhomogeneous spectral distribution and multi-photon emission are currently hindering the use of defects in layered hBN as reliable single photon emitters. Here, the authors demonstrate strain-controlled wavelength tuning and increased single photon purity through suitable material processing.

| S-EPMC5615041 | biostudies-literature

Purification of Boron Nitride Nanotubes Enhances Biological Application Properties.

Project description:Commercially available boron nitride nanotubes (BNNTs) and their purified form (pBNNTs) were dispersed in aqueous solutions with various dispersants, and their cytotoxicity and drug encapsulation capacity were monitored. Our data suggest that pBNNTs showed an average increase in dispersibility of 37.3% in aqueous solution in the presence of 10 different dispersants. In addition, 100 ?g of pBNNTs induced an average decrease in cytotoxicity of 27.4% compared to same amount of BNNTs in normal cell lines. The same amount of pBNNTs can encapsulate 10.4-fold more drug (camptothecin) compared to BNNTs. These data suggest that the purification of BNNTs improves several of their properties, which can be applied to biological experiments and are thus essential in the biological application of BNNTs.

| S-EPMC7073224 | biostudies-literature

Surfactant-assisted individualization and dispersion of boron nitride nanotubes.

Project description:Boron nitride nanotubes (BNNTs) belong to a novel class of material with useful thermal, electronic and optical properties. However, the study and the development of applications of this material requires the formation of stable dispersions of individual BNNTs in water. Here we address the dispersion of BNNT material in water using surfactants with varying properties. The surfactants were compared based on the quantity of BNNTs dispersed and the quality of the dispersions, as visualized by AFM and cryo-TEM. All surfactants produce dispersions of individualized or small bundles of BNNTs. Of the surfactants tested, high molecular weight, nonionic surfactants suspend the most BNNTs, while ionic surfactants remove the most h-BN impurities. The surfactant dispersions were further characterized by ensemble measurements, such as UV absorption and photoluminescence, dynamic light scattering (DLS), and zeta potential to investigate dispersion stability and quality. These techniques provide a facile strategy for testing future BNNT dispersions. The results of this study reveal that BNNT dispersions in aqueous solution can be tuned to fit a specific application through surfactant selection.

| S-EPMC9473271 | biostudies-literature

Dynamic thin film mediated slicing of boron nitride nanotubes.

Project description:A method has been developed to slice boron nitride nanotubes BNNTs under continuous flow in a vortex fluidic device (VFD), along with a method to partially purify the as received BNNT containing material. The latter involves heating the BNNTs to 600 °C followed by dispersing in a 1 : 3 isopropyl alcohol (IPA) and water mixture at 100 °C. The VFD mediated slicing of the BNNTs comprises irradiating the rapidly rotating glass tube (20 mm OD) with a pulsed Nd:YAG laser. Systematically exploring the operating parameter space of the VFD established slicing of ca. 200 μm long purified BNNTs down to 340 nm to 400 nm, in ca. 53% yield, in a 1 : 1 mixture of IPA and water, in the absence of reagents/harsh chemicals, at a flow rate of 0.45 mL min-1, a concentration of 0.1 mg mL-1 BNNTs and an 8.5k rpm rotational speed, with the pulsed laser operating at 1064 nm and 250 mJ per pulse.

| S-EPMC9417105 | biostudies-literature

Boron Nitride Nanotubes Versus Carbon Nanotubes: A Thermal Stability and Oxidation Behavior Study.

Project description:Nanotubes made of boron nitride (BN) and carbon have attracted considerable attention within the literature due to their unique mechanical, electrical and thermal properties. In this work, BN and carbon nanotubes, exhibiting high purity (>99%) and similar surface areas (~200 m2/g), were systematically investigated for their thermal stability and oxidation behavior by combining thermal gravimetric analysis and differential scanning calorimetry methods at temperatures of up to ~1300 °C under a synthetic air flow environment. The BN nanotubes showed a good resistance to oxidation up to ~900 °C and fully transformed to boron oxide up to ~1100 °C, while the carbon nanotubes were stable up to ~450 °C and almost completely combusted up to ~800 °C. The different oxidation mechanisms are attributed to the different chemical nature of the two types of nanotubes.

| S-EPMC7762177 | biostudies-literature

Heteroepitaxial growth of single-walled carbon nanotubes from boron nitride.

Project description:The growth of single-walled carbon nanotubes (SWCNTs) with predefined structure is of great importance for both fundamental research and their practical applications. Traditionally, SWCNTs are grown from a metal catalyst with a vapor-liquid-solid mechanism, where the catalyst is in liquid state with fluctuating structures, and it is intrinsically unfavorable for the structure control of SWCNTs. Here we report the heteroepitaxial growth of SWCNTs from a platelet boron nitride nanofiber (BNNF), which is composed of stacked (002) planes and is stable at high temperatures. SWCNTs are found to grow epitaxially from the open (002) edges of the BNNFs, and the diameters of the SWCNTs are multiples of the BN (002) interplanar distance. In situ transmission electron microscopy observations coupled with first principles calculations reveal that the growth of SWCNTs from the BNNFs follows a vapor-solid-solid mechanism. Our work opens opportunities for the control over the structure of SWCNTs by hetero-crystallographic epitaxy.

| S-EPMC3521219 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data