Structural and Mechanical Characterization of Sustainable Composites Based on Recycled and Stabilized Fly Ash.

ABSTRACT: This paper reports the results on the use of an innovative inert, based on stabilized fly ash from municipal solid waste incineration as a filler for polypropylene. The starting material, which contains large quantities of leachable Pb and Zn, was stabilized by means of an innovative process using rice husk ash as a waste silica source, together with other fly ashes, such as coal fly ash and flue gas desulfurization residues. The use of all waste materials to obtain a new filler makes the proposed technology extremely sustainable and competitive. The new composites, obtained by using the stabilized material as a filler for polypropylene, were characterized and their mechanical properties were also investigated. A comparison with a traditional polypropylene and calcium carbonate based compound was also done. This research activity was realized in the frame of the COSMOS-RICE project, financed by the EU Commission.

SUBMITTER: Besco S

PROVIDER: S-EPMC5456193 | biostudies-other | 2014 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Innovative Fly Ash Geopolymer-Epoxy Composites: Preparation, Microstructure and Mechanical Properties.

Project description:The preparation and characterization of composite materials based on geopolymers obtained from fly ash and epoxy resins are reported for the first time. These materials have been prepared through a synthetic method based on the concurrent reticulation of the organic and inorganic components that allows the formation of hydrogen bonding between the phases, ensuring a very high compatibility between them. These new composites show significantly improved mechanical properties if compared to neat geopolymers with the same composition and comparable performances in respect to analogous geopolymer-based composites obtained starting from more expensive raw material such as metakaolin. The positive combination of an easy synthetic approach with the use of industrial by-products has allowed producing novel low cost aluminosilicate binders that, thanks to their thixotropicity and good adhesion against materials commonly used in building constructions, could be used within the field of sustainable building.

| S-EPMC5456760 | biostudies-other

Data for the physical and mechanical properties of high volume fly ash cement paste composites.

Project description:The data presented herein are compiled of the research summary of "Characterization of High-Volume Fly-Ash Cement Paste for Sustainable Construction Application" (Aydin and Arel, 2017) [1]. This data article provides general information about the ASTM Class C and Class F fly ash cement paste composites composed of silica fume, lime, water reducing admixtures in three different level of workability (0 mm, 100 mm and 200 mm). The dataset here also helps the readers to understand the links with the basic properties of the ingredients, for example, how can porosity be predicted based on the mixture design? how can the strength of the material be linked with the basic strengths of the constituent ingredients?.

| S-EPMC5711659 | biostudies-literature

In Situ Elevated Temperature Testing of Fly Ash Based Geopolymer Composites.

Project description:In situ elevated temperature investigations using fly ash based geopolymers filled with alumina aggregate were undertaken. Compressive strength and short term creep tests were carried out to determine the onset temperature of viscous flow. Fire testing using the standard cellulose curve was performed. Applying a load to the specimen as the temperature increased reduced the temperature at which viscous flow occurred (compared to test methods with no applied stress). Compressive strength increased at the elevated temperature and is attributed to viscous flow and sintering forming a more compact microstructure. The addition of alumina aggregate and reduction of water content reduced the thermal conductivity. This led to the earlier onset and shorter dehydration plateau duration times. However, crack formation was reduced and is attributed to smaller thermal gradients across the fire test specimen.

| S-EPMC5456829 | biostudies-other

Influence of Waste Glass Particle Size on the Physico-Mechanical Properties and Porosity of Foamed Geopolymer Composites Based on Coal Fly Ash.

Project description:In order to protect the environment and counteract climate change, it is necessary to take any actions that enable a reduction in CO2 emissions. One of the key areas is research focused on developing alternative sustainable materials for construction to reduce the global demand for cement. This work presents the properties of foamed geopolymers with the addition of waste glass as well as determined the optimal size and amount of waste glass for improving the mechanical and physical features of the produced composites. Several geopolymer mixtures were fabricated by replacing coal fly ash with 0%, 10%, 20%, and 30% of waste glass by weight. Moreover, the effect of using different particle size ranges of the addition (0.1-1200 µm; 200-1200 µm; 100-250 µm; 63-120 µm; 40-63 µm; 0.1-40 µm) in the geopolymer matrix was examined. Based on the results, it was found that the application of 20-30% of waste glass with a particle size range of 0.1-1200 µm and a mean diameter of 550 µm resulted in approximately 80% higher compressive strength in comparison to unmodified material. Moreover, the samples produced using the smallest fraction (0.1-40 µm) of waste glass in the amount of 30% reached the highest specific surface area (43.711 m2/g), maximum porosity (69%), and density of 0.6 g/cm3.

| S-EPMC10004531 | biostudies-literature

Fly ash/Kaolin based geopolymer green concretes and their mechanical properties.

Project description:Geopolymer concrete mixes were cast using fly ash, kaolin, sodium hydroxide, potassium hydroxide, sodium silicate and aggregates. Portland cement concrete (M30) was used as a reference sample. The effect of silica fume, temperature (40 °C, 60 °C, 80 °C, 100 °C and 120 °C), sodium and potassium hydroxides and different superplasticizers on the compressive strength are reported [1]. Maximum strength was found at 100 °C and 14 M alkali solution [1].

| S-EPMC4659805 | biostudies-other

Influence of Activators on Mechanical Properties of Modified Fly Ash Based Geopolymer Mortars.

Project description:The aim of this work was to study the influence of the type of activator on the formulation of modified fly ash based geopolymer mortars. Geopolymer and alkali-activated materials (AAM) were made from fly ashes derived from coal and biomass combustion in thermal power plants. Basic activators (NaOH, CaO, and Na2SiO3) were mixed with fly ashes in order to develop binding properties other than those resulting from the use of Portland cement. The results showed that the mortars with 5 mol/dm3 of NaOH and 100 g of Na2SiO3 (N5-S22) gave a greater compressive strength than other mixes. The compressive strengths of analyzed fly ash mortars with activators N5-S22 and N5-C10 (5 mol/dm3 NaOH and 10% CaO) varied from 14.3 MPa to 5.9 MPa. The better properties of alkali-activated mortars with regular fly ash were influenced by a larger amount of amorphous silica and alumina phases. Scanning electron microscopy and calorimetry analysis provided a better understanding of the observed mechanisms.

| S-EPMC7084247 | biostudies-literature

Sustainable Cellulose-Aluminum-Plastic Composites from Beverage Cartons Scraps and Recycled Polyethylene.

Project description:The sustainable management of multilayer paper/plastic waste is a technological challenge due to its composite nature. In this paper, a mechanical recycling approach for multilayer cartons (MC) is reported, illustrating the realization of thermoplastic composites based on recycled polyethylene and an amount of milled MC ranging from 20 to 90 wt%. The effect of composition of the composites on the morphology and on thermal, mechanical, and water absorption behavior was investigated and rationalized, demonstrating that above 80 wt% of MC, the fibrous nature of the filler dominates the overall properties of the materials. A maleated polyethylene was also used as a coupling agent and its effectiveness in improving mechanical parameters of composites up to 60 wt% of MC was highlighted.

| S-EPMC8963112 | biostudies-literature

Data on the mechanical properties of recycled wind turbine blade composites.

Project description:Wind turbine blades that face end-of-life recycled mechanically. The recycled material was first comminuted via a hammer-mill through a range of varying screen sizes, resonated (polymeric Methylene diphenyl isocyanate (pMDI)) and then hand-formed and hot pressed. The hot press temperature and time were set as 138 °C and 5 min accordingly, typical for pMDI composite processing. Mechanical properties (Modulus of rupture (MOR), Module of elasticity (MOE) and Internal bond(IB)) dataset of composites made from recycled wind turbine blades(rWTBs) presented. Dataset also presented the influence of resin level, moisture content, mill screen size and density on the mechanical properties of composites [1], [2].

| S-EPMC5992999 | biostudies-literature

Carbon Fiber Reinforced Recycled Polypropylene/Polyolefin Elastomer Composites with High Mechanical Properties.

Project description:The treatment of waste plastics has gradually become a hot topic in the current scientific community. In response to the needs for high-impact performance R-PP-based composites, carbon fiber (CF)-reinforced polyolefin elastomer (POE)/recycled polypropylene (R-PP) composite (CF/POE/R-PP) was prepared by the mechanical blending method, and its mechanical and thermal properties were systematically studied. It was found that the CF could effectively improve the bending and notch impact strength as well as enhance the thermal stability of POE/R-PP. Furthermore, a stable and dispersed composite interface formed by the combination of maleic anhydride-grafted polypropylene (PP-g-MAH) with the surface of CF and the fusion alkyl chains in R-PP and POE further enhanced the CF's reinforcing effect. As a result, the addition of 9 wt.% CF successfully improved the heat resistance of the composite material, and the residual carbon content increased by 97.84% after sintering. The composite toughening of POE and CF effectively improved the impact strength of the composite material, with a maximum increase of over 1000%. This study ultimately resulted in a high-impact-resistant composite material.

| S-EPMC11013364 | biostudies-literature

Mechanical Properties and Microstructure of Class C Fly Ash-Based Geopolymer Paste and Mortar.

Project description:This paper presents workability, compressive strength and microstructure for geopolymer pastes and mortars made of class C fly ash at mass ratios of water-to-fly ash from 0.30 to 0.35. Fluidity was in the range of 145-173 mm for pastes and 131-136 mm for mortars. The highest strengths of paste and mortar were 58 MPa and 85 MPa when they were cured at 70 °C for 24 h. In XRD patterns, unreacted quartz and some reacted product were observed. SEM examination indicated that reacted product has formed and covered the unreacted particles in the paste and mortar that were consistent with their high strength.

| S-EPMC5452326 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data