Investigation of Fumed Silica/Aqueous NaCl Superdielectric Material.

ABSTRACT: A constant current charge/discharge protocol which showed fumed silica filled to the point of incipient wetness with aqueous NaCl solution to have dielectric constants >10⁸ over the full range of dielectric thicknesses of 0.38-3.9 mm and discharge times of 0.25->100 s was studied, making this material another example of a superdielectric. The dielectric constant was impacted by both frequency and thickness. For time to discharge greater than 10 s the dielectric constant for all thicknesses needed to be fairly constant, always >10⁸, although trending higher with increasing thickness. At shorter discharge times the dielectric constant consistently decreased, with decreasing time to discharge. Hence, it is reasonable to suggest that for time to discharge >10 s the dielectric constant at all thicknesses will be greater than 10⁸. This in turn implies an energy density for a 5 micron thick dielectric layer in the order of 350 J/cm³ for discharge times greater than 10 s.

SUBMITTER: Jenkins N

PROVIDER: S-EPMC5456494 | biostudies-other | 2016 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Phase Changes of Monosulfoaluminate in NaCl Aqueous Solution.

Project description:Monosulfoaluminate (Ca?Al?(SO?)(OH)12?6H?O) plays an important role in anion binding in Portland cement by exchanging its original interlayer ions (SO?2- and OH-) with chloride ions. In this study, scanning transmission X-ray microscope (STXM), X-ray absorption near edge structure (XANES) spectroscopy, and X-ray diffraction (XRD) were used to investigate the phase change of monosulfoaluminate due to its interaction with chloride ions. Pure monosulfoaluminate was synthesized and its powder samples were suspended in 0, 0.1, 1, 3, and 5 M NaCl solutions for seven days. At low chloride concentrations, a partial dissolution of monosulfoaluminate formed ettringite, while, with increasing chloride content, the dissolution process was suppressed. As the NaCl concentration increased, the dominant mechanism of the phase change became ion exchange, resulting in direct phase transformation from monosulfoaluminate to Kuzel's salt or Friedel's salt. The phase assemblages of the NaCl-reacted samples were explored using thermodynamic calculations and least-square linear combination (LC) fitting of measured XANES spectra. A comprehensive description of the phase change and its dominant mechanism are discussed.

| S-EPMC5503050 | biostudies-other

Molecular Insights into Aqueous NaCl Electrolytes Confined within Vertically-oriented Graphenes.

Project description:Vertically-oriented graphenes (VGs) are promising active materials for electric double layer capacitors (EDLCs) due to their unique morphological and structural features. This study, for the first time, reports the molecular dynamics (MD) simulations on aqueous NaCl electrolytes confined within VG channels with different surface charge densities and channel widths. Simulation results show that the accessibility of ions and the structure of EDLCs are determined by the ion type/size, surface charging, and VG channel width. For relatively narrow VG channels with the same width, the threshold charge density (to compensate the energy penalty for shedding hydration shell) and the dehydration rate of Cl(-) ions are larger than those of Na(+) ions. To achieve the highest ion concentration coefficient, the effective VG channel width should be between the crystal and hydration diameters of the ions. The results are further quantified and elucidated by calculating the electrolyte density profiles. The molecular insights obtained in the current work are useful in guiding the design and fabrication of VGs for advancing their EDLC applications.

| S-EPMC4589769 | biostudies-literature

Functions of MnO<sub>x</sub> in NaCl Aqueous Solution for Artificial Photosynthesis.

Project description:Photoelectrochemical water splitting has been intensively investigated as artificial photosynthesis technology to convert solar energy into chemical energy. The use of seawater and salted water has advantages for minimum environmental burden; however, the oxidation of Cl- ion to hypochlorous acid (HClO), which has toxicity and heavy corrosiveness, should occur at the anode, along with the oxygen evolution. Here, O2 and HClO production in aqueous solution containing Cl- on photoanodes modified with various metal oxides was investigated. The modification of MnOx resulted in the promotion of the O2 evolution reaction (OER) specifically without HClO production over a wide range of conditions. The results will contribute not only to the practical application of artificial photosynthesis using salted water but also to the elucidation of substantial function of manganese as the element for OER center in natural photosynthesis.

| S-EPMC7584672 | biostudies-literature

Effects of a protic ionic liquid on the reaction pathway during non-aqueous sol-gel synthesis of silica: a Raman spectroscopic investigation.

Project description:The reaction pathway during the formation of silica via a two-component "non-aqueou" sol-gel synthesis is studied by in situ time-resolved Raman spectroscopy. This synthetic route is followed with and without the addition of the protic ionic liquid 1-ethylimidazolium bis(trifluoromethanesulfonyl)imide (C2HImTFSI) in order to investigate its effect on the reaction pathway. We demonstrate that Raman spectroscopy is suitable to discriminate between different silica intermediates, which are produced and consumed at different rates with respect to the point of gelation. We find that half-way to gelation monomers and shorter chains are the most abundant silica species, while the formation of silica rings strongly correlates to the sol-to-gel transition. Thus, curling up of linear chains is here proposed as a plausible mechanism for the formation of small rings. These in turn act as nucleation sites for the condensation of larger rings and thus the formation of the open and polymeric silica network. We find that the protic ionic liquid does not change the reaction pathway per se, but accelerates the cyclization process, intermediated by the faster inclusion of monomeric species.

| S-EPMC4013642 | biostudies-literature

Dissolution of Mesoporous Silica Supports in Aqueous Solutions: Implications for Mesoporous Silica-based Water Treatment Processes.

Project description:Under pH 7 - 10 conditions, the mesoporous silica supports proposed for use in water treatment are relatively unstable. In batch experiments conducted in pH 7 solutions, the commonly used support SBA-15 dissolved quickly, releasing approximately 30 mg/L of dissolved silica after 2 hours. In column experiments, more than 45% of an initial mass of 0.25 g SBA-15 dissolved within 2 days when a pH 8.5 solution flowed through the column. In a mixed iron oxide/SBA-15 system, the dissolution of SBA-15 changed the iron oxide reactivity toward H(2)O(2) decomposition, because dissolved silica deposited on iron oxide surface and changed its catalytic active sites. As with SBA-15, other mesoporous silica materials including HMS, MCM-41, four types of functionalized SBA-15, and two types of metal oxide-containing SBA-15 also dissolved under circumneutral pH solutions. The dissolution of mesoporous silica materials raises questions about their use under neutral and alkaline pH in aqueous solutions, because silica dissolution might compromise the behavior of the material.

| S-EPMC3465675 | biostudies-literature

Chromium removal from aqueous solution by a PEI-silica nanocomposite.

Project description:It is essential and important to determine the adsorption mechanism as well as removal efficiency when using an adsorption technique to remove toxic heavy metals from wastewater. In this research, the removal efficiency and mechanism of chromium removal by a silica-based nanoparticle were investigated. A PEI-silica nanoparticle was synthesized by a one-pot technique and exhibited uniformly well-dispersed PEI polymers in silica particles. The adsorption capacity of chromium ions was determined by a batch adsorption test, with the PEI-silica nanoparticle having a value of 183.7 mg/g and monolayer sorption. Adsorption of chromium ions was affected by the solution pH and altered the nanoparticle surface chemically. First principles calculations of the adsorption energies for the relevant adsorption configurations and XPS peaks of Cr and N showed that Cr(VI), [HCrO4]- is reduced to two species, Cr(III), CrOH2+ and Cr3+, by an amine group and that Cr(III) and Cr(VI) ions are adsorbed on different functional groups, oxidized N and NH3+.

| S-EPMC5780388 | biostudies-literature

An investigation of the kinetics and thermodynamics of NaCl nucleation through composite clusters.

Project description:Having a good understanding of nucleation is critical for the control of many important processes, such as polymorph selection during crystallization. However, a complete picture of the molecular-level mechanisms of nucleation remains elusive. In this work, we take an in-depth look at the NaCl homogeneous nucleation mechanism through thermodynamics. Distinguished from the classical nucleation theory, we calculate the free energy of nucleation as a function of two nucleus size coordinates: crystalline and amorphous cluster sizes. The free energy surface reveals a thermodynamic preference for a nonclassical mechanism of nucleation through a composite cluster, where the crystalline nucleus is surrounded by an amorphous layer. The thickness of the amorphous layer increases with an increase in supersaturation. The computed free energy landscape agrees well with the composite cluster-free energy model, through which phase specific thermodynamic properties are evaluated. As the supersaturation increases, there is a change in stability of the amorphous phase relative to the solution phase, resulting in a change from one-step to two-step mechanism, seen clearly from the free energy profile along the minimum free energy path crossing the transition curve. By obtaining phase-specific diffusion coefficients, we construct the full mesoscopic model and present a clear roadmap for NaCl nucleation.

| S-EPMC9802385 | biostudies-literature

New Mussel Inspired Polydopamine-Like Silica-Based Material for Dye Adsorption.

Project description:A straightforward and economic procedure has been developed for the synthesis of a new polydopamine-like silica-based material that has been obtained by oxidation of catechol with KIO4 followed by reaction with 3-aminopropyltrimethoxysilane. All techniques adopted for characterization showed that the obtained material is rich in different functional groups and the morphological analyses revealed dimensions in the nanometric range. The hybrid material has been characterized by several techniques showing its polydopamine-like nature, and preliminary observations for dye adsorption have been reported.

| S-EPMC7408388 | biostudies-literature

Dielectric Decrement for Aqueous NaCl Solutions: Effect of Ionic Charge Scaling in Nonpolarizable Water Force Fields.

Project description:We investigate the dielectric constant and the dielectric decrement of aqueous NaCl solutions by means of molecular dynamic simulations. We thereby compare the performance of four different force fields and focus on disentangling the origin of the dielectric decrement and the influence of scaled ionic charges, as often used in nonpolarizable force fields to account for the missing dynamic polarizability in the shielding of electrostatic ion interactions. Three of the force fields showed excessive contact ion pair formation, which correlates with a reduced dielectric decrement. In spite of the fact that the scaling of charges only weakly influenced the average polarization of water molecules around an ion, the rescaling of ionic charges did influence the dielectric decrement, and a close-to-linear relation of the slope of the dielectric constant as a function of concentration with the ionic charge was found.

| S-EPMC6875873 | biostudies-literature

Bifunctional acid-base mesoporous silica@aqueous miscible organic-layered double hydroxides.

Project description:A facile method for the synthesis of a series of mesoporous silica nanoporous (MSN) aqueous miscible organic layered double hydroxide core@shell nanocomposites using MCM-41, Al-MCM-41, SBA-15, and MCM-48 as the core is reported. These materials exhibit hierarchical morphologies with high surface areas and good porosity. Chemically, these materials offer controllable bifunctional basicity and acidity.

| S-EPMC9060557 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data