Building Energy Storage Panel Based on Paraffin/Expanded Perlite: Preparation and Thermal Performance Study.

ABSTRACT: This study is focused on the preparation and performance of a building energy storage panel (BESP). The BESP was fabricated through a mold pressing method based on phase change material particle (PCMP), which was prepared in two steps: vacuum absorption and surface film coating. Firstly, phase change material (PCM) was incorporated into expanded perlite (EP) through a vacuum absorption method to obtain composite PCM; secondly, the composite PCM was immersed into the mixture of colloidal silica and organic acrylate, and then it was taken out and dried naturally. A series of experiments, including differential scanning calorimeter (DSC), scanning electron microscope (SEM), best matching test, and durability test, have been conducted to characterize and analyze the thermophysical property and reliability of PCMP. Additionally, the thermal performance of BESP was studied through a dynamic thermal property test. The results have showed that: (1) the surface film coating procedure can effectively solve the leakage problem of composite phase change material prepared by vacuum impregnation; (2) the optimum adsorption ratio for paraffin and EP was 52.5:47.5 in mass fraction, and the PCMP has good thermal properties, stability, and durability; and (3) in the process of dynamic thermal performance test, BESP have low temperature variation, significant temperature lagging, and large heat storage ability, which indicated the potential of BESP in the application of building energy efficiency.

SUBMITTER: Kong X

PROVIDER: S-EPMC5456498 | biostudies-other | 2016 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

A Study on a Novel Phase Change Material Panel Based on Tetradecanol/Lauric Acid/Expanded Perlite/Aluminium Powder for Building Heat Storage.

Project description:Phase change material (PCM) used in buildings can reduce the building energy consumption and indoor temperature fluctuation. A composite PCM has been fabricated by the binary eutectic mixture of tetradecanol (TD) and lauric acid (LA) absorbed into the expanded perlite (EP) using vacuum impregnation method, and its thermal conductivity was promoted by aluminium powder (AP) additive. Besides, the styrene-acrylic emulsion has been mixed with the composite PCM particles to form the protective film, so as to solve the problem of leakage. Thus, a novel PCM panel (PCMP) has been prepared using compression moulding forming method. The thermal property, microstructure characteristic, mechanical property, thermal conductivity, thermal reliability and leakage of the composite PCM have been investigated and analysed. Meanwhile, the thermal performance of the prepared PCMP was tested through PCMPs installed on the inside wall of a cell under outdoor climatic conditions. The composite PCM has a melting temperature of 24.9 °C, a freezing temperature of 25.2 °C, a melting latent heat of 78.2 J/g and a freezing latent heat of 81.3 J/g. The thermal conductivity test exposed that the thermal conductivity has been enhanced with the addition of AP and the latent heat has been decreased, but it still remains in a high level. The leakage test result has proven that liquid PCM leaking has been avoided by the surface film method. The thermal performance experiment has shown the significant function of PCMP about adjusting the indoor temperature and reducing the heats transferring between the wall inside and outside. In view of the thermal performance, mechanical property and thermal reliability results, it can be concluded that the prepared PCMP has a promising building application potential.

| S-EPMC5457220 | biostudies-other

Accelerated Thermal Cycling Test of Microencapsulated Paraffin Wax/Polyaniline Made by Simple Preparation Method for Solar Thermal Energy Storage.

Project description:Microencapsulated paraffin wax/polyaniline was prepared using a simple in situ polymerization technique, and its performance characteristics were investigated. Weight losses of samples were determined by Thermal Gravimetry Analysis (TGA). The microencapsulated samples with 23% and 49% paraffin showed less decomposition after 330 °C than with higher percentage of paraffin. These samples were then subjected to a thermal cycling test. Thermal properties of microencapsulated paraffin wax were evaluated by Differential Scanning Calorimeter (DSC). Structure stability and compatibility of core and coating materials were also tested by Fourier transform infrared spectrophotometer (FTIR), and the surface morphology of the samples are shown by Field Emission Scanning Electron Microscopy (FESEM). It has been found that the microencapsulated paraffin waxes show little change in the latent heat of fusion and melting temperature after one thousand thermal recycles. Besides, the chemical characteristics and structural profile remained constant after one thousand thermal cycling tests. Therefore, microencapsulated paraffin wax/polyaniline is a stable material that can be used for thermal energy storage systems.

| S-EPMC5452494 | biostudies-other

Preparation, Mechanical and Thermal Properties of Cement Board with Expanded Perlite Based Composite Phase Change Material for Improving Buildings Thermal Behavior.

Project description:Here we demonstrate the mechanical properties, thermal conductivity, and thermal energy storage performance of construction elements made of cement and form-stable PCM-Rubitherm® RT 28 HC (RT28)/expanded perlite (EP) composite phase change materials (PCMs). The composite PCMs were prepared by adsorbing RT28 into the pores of EP, in which the mass fraction of RT28 should be limited to be no more than 40 wt %. The adsorbed RT28 is observed to be uniformly confined into the pores of EP. The phase change temperatures of the RT28/EP composite PCMs are very close to that of the pure RT28. The apparent density and compression strength of the composite cubes increase linearly with the mass fraction of RT28. Compared with the thermal conductivity of the boards composed of cement and EP, the thermal conductivities of the composite boards containing RT28 increase by 15%-35% with the mass fraction increasing of RT28. The cubic test rooms that consist of six boards were built to evaluate the thermal energy storage performance, it is found that the maximum temperature different between the outside surface of the top board with the indoor temperature using the composite boards is 13.3 °C higher than that of the boards containing no RT28. The thermal mass increase of the built environment due to the application of composite boards can contribute to improving the indoor thermal comfort and reducing the energy consumption in the buildings.

| S-EPMC5458928 | biostudies-other

Preparation and Thermal Properties of Propyl Palmitate-Based Phase Change Composites with Enhanced Thermal Conductivity for Thermal Energy Storage.

Project description:Phase change materials (PCMs), which can absorb and release large amounts of latent heat during phase change, have been extensively studied for heat storage and thermal management. However, technical bottlenecks regarding low thermal conductivity and leakage have hindered practical applications of PCMs. In this paper, a simple, economical, and scalable absorption polymerization technique is proposed to prepare the polymethyl methacrylate/propyl palmitate/expanded graphite (MPCM/EG) phase change composites by constructing the microencapsulated phase change materials (polymethyl methacrylate/propyl palmitate, MPCM) with core-shell structures in the three-dimensional (3D) EG networks, taking propyl palmitate as the PCM core, polymethyl methacrylate (PMMA) as the shell, and long-chain "worm-like" EG as the thermally conductive networks. This technique proved to be a more appropriate combinatorial pathway than direct absorption of MPCM via EG. The MPCM/EG composites with high thermal conductivity, high enthalpy, excellent thermal stability, low leakage, and good thermal cycle reliability were prepared. The results showed that the MPCM-80/EG-10 composite demonstrated a high thermal conductivity of 3.38 W/(m·K), a phase change enthalpy up to 152.0 J/g, an encapsulation ratio of 90.3%, outstanding thermal stability performance, and long-term thermal cycle reliability when the EG loading is 10% and propyl palmitate is 80%. This research offers an easy and efficient approach for designing and fabricating phase change composites with promising applications in diverse energy-saving fields, such as renewable energy collection, building energy conservation, and microelectronic devices thermal protection.

| S-EPMC10421114 | biostudies-literature

Bi-Functional Paraffin@Polyaniline/TiO2/PCN-222(Fe) Microcapsules for Solar Thermal Energy Storage and CO2 Photoreduction.

Project description:A novel type of bi-functional microencapsulated phase change material (MEPCM) microcapsules with thermal energy storage (TES) and carbon dioxide (CO2) photoreduction was designed and fabricated. The polyaniline (PANI)/titanium dioxide (TiO2)/PCN-222(Fe) hybrid shell encloses phase change material (PCM) paraffin by the facile and environment-friendly Pickering emulsion polymerization, in which TiO2 and PCN-222(Fe) nanoparticles (NPs) were used as Pickering stabilizer. Furthermore, a ternary heterojunction of PANI/(TiO2)/PCN-222(Fe) was constructed due to the tight contact of the three components on the hybrid shell. The results indicate that the maximum enthalpy of MEPCMs is 174.7 J·g-1 with encapsulation efficiency of 77.2%, and the thermal properties, chemical composition, and morphological structure were well maintained after 500 high-low temperature cycles test. Besides, the MEPCM was employed to reduce CO2 into carbon monoxide (CO) and methane (CH4) under natural light irradiation. The CO evolution rate reached up to 45.16 μmol g-1 h-1 because of the suitable band gap and efficient charge migration efficiency, which is 5.4, 11, and 62 times higher than pure PCN-222(Fe), PANI, and TiO2, respectively. Moreover, the CO evolution rate decayed inapparently after five CO2 photoreduction cycles. The as-prepared bi-functional MEPCM as the temperature regulating building materials and air purification medium will stimulate a potential application.

| S-EPMC8746944 | biostudies-literature

Form-Stable Phase Change Materials Based on Eutectic Mixture of Tetradecanol and Fatty Acids for Building Energy Storage: Preparation and Performance Analysis.

Project description:This paper is focused on preparation and performance analysis of a series of form-stable phase change materials (FSPCMs), based on eutectic mixtures as phase change materials (PCMs) for thermal energy storage and high-density polyethylene (HDPE)-ethylene-vinyl acetate (EVA) polymer as supporting materials. The PCMs were eutectic mixtures of tetradecanol (TD)-capric acid (CA), TD-lauric acid (LA), and TD-myristic acid (MA), which were rarely explored before. Thermal properties of eutectic mixtures and FSPCMs were measured by differential scanning calorimeter (DSC). The onset melting/solidification temperatures of form-stable PCMs were 19.13 °C/13.32 °C (FS TD-CA PCM), 24.53 °C/24.92 °C (FS TD-LA PCM), and 33.15 °C/30.72 °C (FS TD-MA PCM), respectively, and latent heats were almost greater than 90 J/g. The surface morphologies and chemical stability of form-stable PCM were surveyed by scanning electron microscopy (SEM) and Fourier-transform infrared (FT-IR) spectroscopy, respectively. The thermal cycling test revealed that the thermal reliability of these three form-stable PCMs was good. Thermal storage/release experiment indicated melting/solidification time was shortened by introducing 10 wt % aluminum powder (AP). It is concluded that these FSPCMs can act as potential building thermal storage materials in terms of their satisfactory thermal properties.

| S-EPMC5452832 | biostudies-other

Influence of Granulometry on Thermal and Mechanical Properties of Cement Mortars Containing Expanded Perlite as a Lightweight Aggregate.

Project description:This research aims at clarifying the influence of the granulometry of expanded perlite, on the thermal conductivity, structural strength, density, and water absorption of lightweight mortars. Three original perlite gradations have been obtained and three pairs of twin test mortars have been tested with those gradations. SEM tests have also been run to clarify the interaction, at a microscopic level, between the expanded perlite and the cement grouting. The results indicate that the mere manipulation of the granulometry may have a considerable and very beneficial effect on the mixture's properties, such as thermal conductivity and water absorption.

| S-EPMC6926826 | biostudies-literature

Molecular solar thermal energy storage in photoswitch oligomers increases energy densities and storage times.

Project description:Molecular photoswitches can be used for solar thermal energy storage by photoisomerization into high-energy, meta-stable isomers; we present a molecular design strategy leading to photoswitches with high energy densities and long storage times. High measured energy densities of up to 559 kJ kg-1 (155 Wh kg-1), long storage lifetimes up to 48.5 days, and high quantum yields of conversion of up to 94% per subunit are demonstrated in norbornadiene/quadricyclane (NBD/QC) photo-/thermoswitch couples incorporated into dimeric and trimeric structures. By changing the linker unit between the NBD units, we can at the same time fine-tune light-harvesting and energy densities of the dimers and trimers so that they exceed those of their monomeric analogs. These new oligomers thereby meet several of the criteria to be met for an optimum molecule to ultimately enter actual devices being able to undergo closed cycles of solar light-harvesting, energy storage, and heat release.

| S-EPMC5956078 | biostudies-literature

A Low-Temperature Heat Output Photoactive Material-Based High-Performance Thermal Energy Storage Closed System.

Project description:Designing and synthesizing photothermal conversion materials with better storage capacity, long-term stability as well as low temperature energy output capability is still a huge challenge in the area of photothermal storage. In this work, we report a brand new photothermal conversion material obtained by attaching trifluoromethylated azobenzene (AzoF) to reduced graphene oxide (rGO). AzoF-rGO exhibits outstanding heat storage density and power density up to 386.1 kJ·kg-1 and 890.6 W·kg-1, respectively, with a long half-life (87.7 h) because of the H-bonds based on high attachment density. AzoF-rGO also exhibits excellent cycling stability and is equipped with low-temperature energy output capability, which achieves the reversible cycle of photothermal conversion within a closed system. This novel AzoF-rGO complex, which on the one hand exhibits remarkable energy storage performance as well as excellent storage life span, and on the other hand is equipped with the ability to release heat at low temperatures, shows broad prospects in the practical application of actual photothermal storage.

| S-EPMC8000957 | biostudies-literature

Preparation of NaF Microcapsules for High-Temperature Thermal Storage

Project description:A novel NaF phase change microcapsule with a carbon shell

| S-EPMC9301709 | biostudies-literature