Evolution Law of Helium Bubbles in Hastelloy N Alloy on Post-Irradiation Annealing Conditions.
Ontology highlight
ABSTRACT:
SUBMITTER: Gao J
PROVIDER: S-EPMC5456587 | biostudies-other | 2016 Oct
REPOSITORIES: biostudies-other
Similar Datasets
Project description:The single crystal 6H-SiC with [0001] crystal direction irradiated by 400 keV He⁺ ions with 1 × 1017 ions/cm² fluence at 400 °C were annealed at 600, 900, 1200 and 1400 °C for different durations. The evolution of helium bubbles and discs was investigated by transmission electron microscopy. An irradiated layer distributed with fine helium bubbles was formed with a width of ~170 nm after helium ion irradiation. The size of gas bubbles increased with increasing annealing time and temperature and finally reached stable values at a given annealing temperature. According to the relationship between the bubble radii and annealing time, an empirical formula for calculating the bubble radii at the annealing temperature ranged from 600 to 1400 °C was given by fitting the experiment data. Planar bubble clusters (discs) were found to form on (0001) crystal plane at both sides of the bubble layer when the annealing temperature was at the range of 800-1200 °C. The mechanism of bubble growth during post-implantation annealing and the formation of bubble discs were also analyzed and discussed.
| S-EPMC5459187 | biostudies-other
Project description:A wet-chemical method combined with spark plasma sintering was used to prepare a W-Y2O3 alloy. High-temperature tensile tests and nano-indentation microhardness tests were used to characterize the mechanical properties of the alloy. After He-ion irradiation, fuzz and He bubbles were observed on the irradiated surface. The irradiation embrittlement was reflected by the crack indentations formed during the microhardness tests. A phase transformation from α-W to γ-W was investigated by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Polycrystallization and amorphization were also observed in the irradiation damage layer. The W materials tended to exhibit lattice distortion, amorphization, polycrystallization and phase transformation under He-ion irradiation. The transformation mechanism predicted by the atomic lattice model was consistent with the available experimental observations. These findings clarify the mechanism of the structural transition of W under ion irradiation and provide a clue for identifying materials with greater irradiation resistance.
| S-EPMC4521205 | biostudies-other
Project description:Helium is insoluble in most metals and precipitates out to form nanoscale bubbles when the concentration is greater than 1 at.%, which can alter the material properties. Introducing controlled defects such as multilayer interfaces may offer some level of helium bubble management. This study investigates the effects of multilayered composites on helium behavior in ion-implanted, multilayered ErD2/Mo thin film composites. Following in-situ and ex-situ helium implantation, scanning and transmission electron microscopy showed the development of spherical helium bubbles within the matrix, but primarily at the layer interfaces. Bubble linkage and surface blistering is observed after high fluence ex-situ helium implantation. These results show the ability of metallic multilayers to alter helium bubble distributions even in the presence of a hydride layer, increasing the lifetime of materials in helium environments.
| S-EPMC8471048 | biostudies-literature
Project description:We investigate the mechanistic nature of the Snf2 family protein HARP, mutations of which are responsible for Schimke immuno-osseous dysplasia. Using a single-molecule magnetic tweezers assay, we construct RPA-stabilized DNA bubbles within torsionally constrained DNA to investigate the annealing action of HARP on a physiologically relevant substrate. We find that HARP closes RPA-stabilized bubbles in a slow reaction, taking on the order of tens of minutes for ∼600 bp of DNA to be re-annealed. The data indicate that DNA re-anneals through the removal of RPA, which is observed as clear steps in the bubble-closing traces. The dependence of the closing rate on both ionic strength and HARP concentration indicates that removal of RPA occurs via an association-dissociation mechanism where HARP does not remain associated with the DNA. The enzyme exhibits classical Michaelis-Menten kinetics and acts cooperatively with a Hill coefficient of 3 ± 1. Our work also allows the determination of some important features of RPA-bubble structures at low supercoiling, including the existence of multiple bubbles and that RPA molecules are mis-registered on the two strands.
| S-EPMC5416776 | biostudies-literature
Project description:We develop a strong diagnostic for bubbles and crashes in Bitcoin, by analysing the coincidence (and its absence) of fundamental and technical indicators. Using a generalized Metcalfe's Law based on network properties, a fundamental value is quantified and shown to be heavily exceeded, on at least four occasions, by bubbles that grow and burst. In these bubbles, we detect a universal super-exponential unsustainable growth. We model this universal pattern with the Log-Periodic Power Law Singularity (LPPLS) model, which parsimoniously captures diverse positive feedback phenomena, such as herding and imitation. The LPPLS model is shown to provide an ex ante warning of market instabilities, quantifying a high crash hazard and probabilistic bracket of the crash time consistent with the actual corrections; although, as always, the precise time and trigger (which straw breaks the camel's back) is exogenous and unpredictable. Looking forward, our analysis identifies a substantial but not unprecedented overvaluation in the price of Bitcoin, suggesting many months of volatile sideways Bitcoin prices ahead (from the time of writing, March 2018).
| S-EPMC6599809 | biostudies-literature
Project description:High- (and medium-) entropy alloys have emerged as potentially suitable structural materials for nuclear applications, particularly as they appear to show promising irradiation resistance. Recent studies have provided evidence of the presence of local chemical order (LCO) as a salient feature of these complex concentrated solid-solution alloys. However, the influence of such LCO on their irradiation response has remained uncertain thus far. In this work, we combine ion irradiation experiments with large-scale atomistic simulations to reveal that the presence of chemical short-range order, developed as an early stage of LCO, slows down the formation and evolution of point defects in the equiatomic medium-entropy alloy CrCoNi during irradiation. In particular, the irradiation-induced vacancies and interstitials exhibit a smaller difference in their mobility, arising from a stronger effect of LCO in localizing interstitial diffusion. This effect promotes their recombination as the LCO serves to tune the migration energy barriers of these point defects, thereby delaying the initiation of damage. These findings imply that local chemical ordering may provide a variable in the design space to enhance the resistance of multi-principal element alloys to irradiation damage.
| S-EPMC10104586 | biostudies-literature
Project description:BACKGROUND:Cosmic radiation exposures have been found to elicit cognitive impairments involving a wide-range of underlying neuropathology including elevated oxidative stress, neural stem cell loss, and compromised neuronal architecture. Cognitive impairments have also been associated with sustained microglia activation following low dose exposure to helium ions. Space-relevant charged particles elicit neuroinflammation that persists long-term post-irradiation. Here, we investigated the potential neurocognitive benefits of microglia depletion following low dose whole body exposure to helium ions. METHODS:Adult mice were administered a dietary inhibitor (PLX5622) of colony stimulating factor-1 receptor (CSF1R) to deplete microglia 2 weeks after whole body helium irradiation (4He, 30 cGy, 400 MeV/n). Cohorts of mice maintained on a normal and PLX5622 diet were tested for cognitive function using seven independent behavioral tasks, microglial activation, hippocampal neuronal morphology, spine density, and electrophysiology properties 4-6 weeks later. RESULTS:PLX5622 treatment caused a rapid and near complete elimination of microglia in the brain within 3 days of treatment. Irradiated animals on normal diet exhibited a range of behavioral deficits involving the medial pre-frontal cortex and hippocampus and increased microglial activation. Animals on PLX5622 diet exhibited no radiation-induced cognitive deficits, and expression of resting and activated microglia were almost completely abolished, without any effects on the oligodendrocyte progenitors, throughout the brain. While PLX5622 treatment was found to attenuate radiation-induced increases in post-synaptic density protein 95 (PSD-95) puncta and to preserve mushroom type spine densities, other morphologic features of neurons and electrophysiologic measures of intrinsic excitability were relatively unaffected. CONCLUSIONS:Our data suggest that microglia play a critical role in cosmic radiation-induced cognitive deficits in mice and, that approaches targeting microglial function are poised to provide considerable benefit to the brain exposed to charged particles.
| S-EPMC7236926 | biostudies-literature
Project description:Coupling electron microscopy techniques with in situ heating ability allows us to study phase transformations on the single-nanoparticle level. We exploit this setup to study disorder-to-order transformation of Pt-Fe alloy nanoparticles, a material that is of great interest to fuel-cell electrocatalysis and ultrahigh density information storage. In contrast to earlier reports, we show that Fe (instead of Pt) segregates towards the particle surface during annealing and forms a Fe-rich FeO x outer shell over the alloy core. By combining both ex situ and in situ approaches to probe the interplay between ordering and surface-segregation phenomena, we illustrate that the surface segregation of Fe precedes the ordering process and affects the ordered phase evolution dramatically. We show that the ordering initiates preferably at the pre-existent Fe-rich shell than the particle core. While the material-specific findings from this study open interesting perspectives towards a controlled phase evolution of Pt-Fe nanoalloys, the characterization methodologies described are general and should prove useful to probing a wide-range of nanomaterials.
| S-EPMC4648033 | biostudies-literature
Project description:In this work, γ-ray irradiation effects on pentacene thin films are investigated in terms of the change in the crystallinity, and electronic structure as well as chemical states of the film. The pentacene films are γ-irradiated up to 3 kGy and then characterized using synchrotron X-ray diffraction, near edge X-ray absorption fine structure (NEXAFS) and X-ray photoelectron spectroscopy. We found that γ-ray irradiation creates defects, resulting in a decrease of X-ray diffraction intensity both in the plane normal and in-plane directions. From angle dependent NEXAFS; the transition of C 1s to π* orbital for irradiated samples increases; suggesting that the unoccupied π* states enhance due to defects or radical formation in pentacene thin films. Additionally, the in-plane resistivity shows a decreasing trend of resistance after irradiation. This trend of increase in conductivity is also consistent with C 1s to π transition, which manifests the increase in carrier concentration. Hall effect measurements further confirmed the increase in carrier concentration as a function of dose; however, the mobility of the sample decreases as the dose rate increases due to the defects created. By post-irradiation annealing, the thin film phase diffraction intensity can be recovered. Altogether, the anisotropic studies on pentacene films disclosed that the irradiation leads to defect formation along in-plane and plane normal directions. Overall, these results suggest that pentacene is one of the robust organic electronic materials; whose structure remains mostly intact even after irradiation up to a dose of 3 kGy.
| S-EPMC9054396 | biostudies-literature
Project description:Many COVID-19 survivors have post-COVID-19 conditions, and females are at a higher risk. We sought to determine (1) how protein levels change from acute to post-COVID-19 conditions, (2) whether females have a plasma protein signature different from that of males, and (3) which biological pathways are associated with COVID-19 when compared to restrictive lung disease. We measured protein levels in 74 patients on the day of admission and at 3 and 6 months after diagnosis. We determined protein concentrations by multiple reaction monitoring (MRM) using a panel of 269 heavy-labeled peptides. The predicted forced vital capacity (FVC) and diffusing capacity of the lungs for carbon monoxide (DLCO) were measured by routine pulmonary function testing. Proteins associated with six key lipid-related pathways increased from admission to 3 and 6 months; conversely, proteins related to innate immune responses and vasoconstriction-related proteins decreased. Multiple biological functions were regulated differentially between females and males. Concentrations of eight proteins were associated with FVC, %, and they together had c-statistics of 0.751 (CI:0.732-0.779); similarly, concentrations of five proteins had c-statistics of 0.707 (CI:0.676-0.737) for DLCO, %. Lipid biology may drive evolution from acute to post-COVID-19 conditions, while activation of innate immunity and vascular regulation pathways decreased over that period. (ProteomeXchange identifiers: PXD041762, PXD029437).
| S-EPMC10775146 | biostudies-literature