Tribological Performance of Green Lubricant Enhanced by Sulfidation IF-MoS₂.

ABSTRACT: Biopolymers reinforced with nanoparticle (NP) additives are widely used in tribological applications. In this study, the effect of NP additives on the tribological properties of a green lubricant hydroxypropyl methylcellulose (HPMC) composite was investigated. The IF-MoS₂ NPs were prepared using the newly developed gas phase sulfidation method to form a multilayered, polyhedral structure. The number of layers and crystallinity of IF-MoS₂ increased with sulfidation time and temperature. The dispersity of NPs in the HPMC was investigated using Raman and EDS mapping and showed great uniformity. The use of NPs with HPMC enhanced the tribological performance of the composites as expected. The analysis of the worn surface shows that the friction behavior of the HPMC composite with added NPs is very sensitive to the NP structure. The wear mechanisms vary with NP structure and depend on their lubricating behaviors.

SUBMITTER: Shi SC

PROVIDER: S-EPMC5456592 | biostudies-other | 2016 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Biopolymer Green Lubricant for Sustainable Manufacturing.

Project description:We report on the preparation of a biopolymer thin film by hydroxypropyl methylcellulose (HPMC), which can be used as a dry green lubricant in sustainable manufacturing. The thin films were characterized through scanning electron microscopy, energy-dispersive spectroscopy, and Raman spectroscopy; the films showed desirable levels of thickness, controllability, and uniformity. Tribology tests also showed desirable tribological and antiwear behaviors, caused by the formation of transfer layers. Zebrafish embryo toxicity studies showed that HPMC has excellent solubility and biocompatibility, which may show outstanding potential for applications as a green lubricant. The results of the present study show that these techniques for biopolymer HPMC provide an ecologically responsible and convenient method for preparing functional thin films, which is particularly applicable to sustainable manufacturing.

| S-EPMC5503078 | biostudies-other

Tribological properties of black phosphorus nanosheets as oil-based lubricant additives for titanium alloy-steel contacts.

Project description:The black phosphorus (BP) powders were prepared by high-energy ball milling with red phosphorus as the raw material, and then the BP nanosheets were obtained by liquid-phase exfoliation. The tribological properties of the BP nanosheets as oil-based lubricant additives were investigated by the ball-on-disc tribometer. Results show that compared with the base oil of liquid paraffin (LP), the coefficient of friction and wear rate of the BP nanosheets as the additives in liquid paraffin (BP-LP) are lower for the same loads. BP-LP lubricants could significantly improve the load-bearing capacity of the base oil for titanium alloy-steel contacts and show excellent friction-reducing and anti-wear properties. The surface morphologies and elemental compositions of the friction pairs were further analysed using an optional microscope, scanning electron microscope and X-ray photoelectron spectroscopy. The lubrication mechanism of BP-LP can be attributed to the synergistic effects between lamellar adsorption and interlayer shear of BP nanosheets.

| S-EPMC7540757 | biostudies-literature

Growing and Etching MoS? on Carbon Nanotube Film for Enhanced Electrochemical Performance.

Project description:In this work we directly synthesized molybdenum disulfide (MoS?) nanosheets on carbon nanotube film (MoS?@CNT) via a two-step chemical vapor deposition method (CVD). By etching the obtained MoS?@CNT into 10% wt HNO?, the morphology of MoS? decorated on CNT bundles was modulated, resulting in more catalytic active MoS? edges being exposed for significantly enhanced electrochemical performance. Our results revealed that an 8 h acid etching sample exhibited the best performance for the oxygen evolution reaction, i.e., the current density reached 10 mA/cm² under 375 mV over-potential, and the tafel slope was as low as 94 mV/dec. The enhanced behavior was mainly originated from the more catalytic sites in MoS? induced by the acid etching treatment and the higher conductivity from the supporting CNT films. Our study provides a new route to produce two-dimensional layers on CNT films with tunable morphology, and thus may open a window for exploring its promising applications in the fields of catalytic-, electronic-, and electrochemical-related fields.

| S-EPMC6274235 | biostudies-literature

Layered Double Hydroxide Nanoplatelets with Excellent Tribological Properties under High Contact Pressure as Water-Based Lubricant Additives.

Project description:High efficient and sustainable utilization of water-based lubricant is essential for saving energy. In this paper, a kind of layered double hydroxide (LDH) nanoplatelets is synthesized and well dispersed in water due to the surface modification with oleylamine. The excellent tribological properties of the oleylamine-modified Ni-Al LDH (NiAl-LDH/OAm) nanoplatelets as water-based lubricant additives are evaluated by the tribological tests in an aqueous environment. The modified LDH nanoplatelets are found to not only reduce the friction but also enhance the wear resistance, compared with the water-based cutting fluid and lubricants containing other particle additives. By adding 0.5 wt% LDH nanoplatelets, under 1.5 GPa initial contact pressure, the friction coefficient, scar diameter, depth and width of the wear track dramatically decrease by 83.1%, 43.2%, 88.5% and 59.5%, respectively. It is considered that the sufficiently small size and the excellent dispersion of NiAl-LDH/OAm nanoplatelets in water are the key factors, so as to make them enter the contact area, form a lubricating film and prevent direct collision of asperity peaks. Our investigations demonstrate that the LDH nanoplatelet as a water-based lubricant additive has a great potential value in industrial application.

| S-EPMC4782130 | biostudies-literature

Tribological Properties of Water-lubricated Rubber Materials after Modification by MoS<sub>2</sub> Nanoparticles.

Project description:Frictional vibration and noise caused by water-lubricated rubber stern tube bearings, which are generated under extreme conditions, severely threaten underwater vehicles' survivability and concealment performance. This study investigates the effect of flaky and spherical MoS2 nanoparticles on tribological properties and damping capacity of water-lubricated rubber materials, with the aim of decreasing frictional noise. A CBZ-1 tribo-tester was used to conduct the sliding tests between rubber ring-discs and ZCuSn10Zn2 ring-discs with water lubrication. These materials' typical mechanical properties were analysed and compared. Coefficients of friction (COFs), wear rates, and surface morphologies were evaluated. Frictional noise and critical velocities of generating friction vibration were examined to corroborate above analysis. Results showed that spherical MoS2 nanoparticles enhanced rubber material's mechanical and tribological properties and, in turn, reduced the friction noise and critical velocity. Flaky MoS2 nanoparticles reduced COF but did not enhance their mechanical properties, i.e., the damping capacity, wear resistance property; thus, these nanoparticles did not reduce the critical velocity obviously, even though increased the frictional noise at high load. The knowledge gained in the present work will be useful for optimizing friction pairs under extreme conditions to decrease frictional noise of water-lubricated rubber stern tube bearings.

| S-EPMC5054368 | biostudies-literature

Growth and characteristics of self-assembled MoS2/Mo-S-C nanoperiod multilayers for enhanced tribological performance.

Project description:Highly ordered MoS2/Mo-S-C nanoperiod multilayers are synthesized by a novel self-assembling mechanism in simultaneous sputtering of MoS2 and graphite targets. The sequential formation of MoS2-riched domain layers and Mo-S-C compositional mixed capping layers reveals no correspondence to the sample stage rotation but is caused by the low energy ion bombardment enhanced interdiffusion. The HRTEM observation shows that the phase segregation normal to the film surface is initiated from substrate-film interlayer with clear contrasts in the first few bi-layers, and then diffuses mutually in a quasiperiodic pattern between two altered sub-layers. Compared with sputtered MoS2 film, the bulk film of multilayers exhibit largely improved toughness under a normal load, and the preferential orientation of sputtered MoS2 in (002) basal planes is significantly enhanced, both of which render the film excellent loads-bearing capacity and lubricant properties. The nano-scratching tests performed on a nanoindentation system suggest that the nano-tribological performance of multilayers is directly determined by the altered structure and properties of neighboring sub-layers until stable tribofilms are formed. Meanwhile, the pin-on-disk tribotests in ambient air, low vacuum and high vacuum provide comparably low friction coefficient yet distinct wear lives in different atmospheres due to the partially restricted humid-sensitivity of sputtered MoS2 phase.

| S-EPMC4853724 | biostudies-other

Bifunctional hairy silica nanoparticles as high-performance additives for lubricant.

Project description:Bifunctional hairy silica nanoparticles (BHSNs), which are silica nanoparticles covered with alkyl and amino organic chains, were prepared as high-performance additives for lubricants. Compared with hairy silica nanoparticles covered by a single type of organic chain, binary hairy silica nanoparticles exhibit the advantages of both types of organic chains, which exhibit excellent compatibility with lubricants and adsorbability to metal surfaces. Nanoparticles with different ratios of amino and alkyl ligands were investigated. In comparison to an untreated lubricant, BHSNs reduce the friction coefficient and wear scar diameter by 40% and 60%, respectively. The wear mechanism of BHSNs was investigated, and the protective and filling effect of the nanoparticles improved because of collaboration of amino and alkyl ligands.

| S-EPMC4776138 | biostudies-literature

Sulfur-Doped Alkylated Graphene Oxide as High-Performance Lubricant Additive.

Project description:Sulfur-doped graphene oxide (SA-GO) prepared by sulfuration and alkylation of graphene oxide is applied as an efficient green anti-wear additive for harsh operation conditions of engines. X-ray photoelectron spectroscopy analysis reveals the sulfur content of octadecylamine-modified SA-GO (sulfuration follows alkylation) is increased by 79 times compared with the reverse process that alkylation follows sulfuration, suggesting the preparation route is a key factor of the sulfuration process. The higher sulfur content and -C-S-C- sulfur bonding constitution result better lubrication effect, while the investigation of chain length of alkylation modification and concentration of the alkylated sulfur-doped graphene oxide indicates the octylamine-modified SA-GO shows smaller diameter of wear scar within the concentration range between 1?×?10-4 and 2.5?×?10-4?wt%. The decrement percent of wear scar diameter is 43.2% in 928 lubrication oil and 17.2% in PAO4 oil while the SA-GO modified by octylamine is applied with the concentrations 2.5?×?10-4?wt% in PAO4 and 1?×?10-4?wt% in 928 oil, respectively. The sulfur content in oil samples is only 0.006~0.001?wt%, which is much lower than the sulfur content standard recommended by ILSAC that is 0.5?wt%. The research work indicates the SA-GO additive is more feasible for the pollution treatment which focuses the substantial reduction of sulfur content in lubrication oil on the premise of improving lubrication capability.

| S-EPMC6990272 | biostudies-literature

Enhanced Electrochemical Performance of Self-Assembled Nanoflowers of MoS<sub>2</sub> Nanosheets as Supercapacitor Electrode Materials.

Project description:As supercapacitor electrode materials, their structures, including specific surface area, instability, and interconnection, determine the electrochemical performances (specific capacitance, cycle stability, and rate performance). In this study, 1T-MoS2 nanosheets were self-assembled into nanoflowers via a one-pot facile hydrothermal reaction. The nanoflowers retain the excellent electrical conductive performance and the feature of inherent high specific surface area of the nanosheets. For the sheets are interconnected to each other in flower structure, the structure is more stable and the charges are more easily transferred. Thus, compared to the nanosheet electrode, the nanoflower electrode shows the remarkable advantage when used as the electrode of the energy-storage device, whether it is 1T phase or 2H phase in KCl or in KOH. When measured at 0.5 A g-1 in KOH electrolyte, the MoS2 nanoflower electrode exhibits a high specific capacitance of 1120 F g-1. At the same time, when cycling 2000 times at a current density of 10 A g-1, the capacitance retention ratio can reach up to 96%.

| S-EPMC6776964 | biostudies-literature

Non-halogenated Ionic Liquid Dramatically Enhances Tribological Performance of Biodegradable Oils.

Project description:It is demonstrated that a phosphonium orthoborate ionic liquid may serve as a wear reducing additive in biodegradable oils at steel-steel surfaces in the boundary lubrication regime. Tribological tests were performed in a ball-on-three plate configuration. A set of surface characterization techniques-SEM/EDS, FIB and white light interferometry were used to characterize surfaces following the tribotests and to observe the formation of any tribofilms. 11B NMR was used to follow changes in the composition of the ionic-liquid-oil blends and to identify boron-containing decomposition products after the tribotests. The ionic liquid reduces the wear of steel surfaces by up to 92% compared to the neat oil at 90°C; it is shown that the reduction in wear can be correlated with the formation of boron enriched patches in the boundary films.

| S-EPMC6413702 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data