Preparation and Characterization of Modified Soda Lignin with Polyethylene Glycol.

ABSTRACT: Soda lignin does not have thermal flowing characteristics and it is impossible for it to be further thermally molded. To achieve the fusibility of soda lignin for fiber preparation by melt-spinning, an effective method for soda lignin modification was conducted by cooking it with polyethylene glycol (PEG) 400 at various ratios. The higher the ratio of PEG that was used, the more PEG molecular chains were grafted at the alpha carbon of the soda lignin through ether bonds, resulting in lower thermal transition temperatures and more excellent fusibility. The modified soda lignin with a weight ratio of lignin to PEG of 1:4 exhibited a relative thermal stability of molten viscosity at selected temperatures. Thereafter, the resultant fusible soda lignin was successfully melt-spun into filaments with an average diameter of 33 ± 5 μm, which is smaller than that of some industrial lignins. Accordingly, it is possible to utilize soda lignin to produce fibrous carbonaceous materials.

SUBMITTER: Zhang F

PROVIDER: S-EPMC5456608 | biostudies-other | 2016 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Preparation, Characterization and Evaluation of Antibacterial Properties of Polylactide-Polyethylene Glycol-Chitosan Active Composite Films.

Project description:Chitin is a natural biopolymer obtained from the exoskeleton of crustaceans. Chitosan is a derivative of chitin, which has antimicrobial properties and potential applications in several industries. Moreover, the composites of chitosan with other biodegradable polymers, such as polylactide (PLA) as packaging film, have shown promising results. In this study, chitosan was obtained and characterized from shrimp shells. Then, polylactide-chitosan composite films were prepared by a solvent casting technique using various amounts of chitosan (0.5-2% w/w) and polyethylene glycol as plasticizer (10% w/w). Thermal, mechanical properties, Fourier-transform infrared, scanning electron microscopy, as well as antibacterial properties of composite films were determined. It was found that adding chitosan (CH) into PLA films has a significant effect on tensile strength and no effect on thermal properties. The results showed a reduction on average of 1 log of colony-forming units against Staphylococcus aureus, while there is no antibacterial effect against Salmonella typhimurium. The study proved the antibacterial effect of CH in films of PLA against Gram-positive bacteria and appropriate mechanical properties. These films could be used for the development of biodegradable/eco-friendly food packaging prototypes, as a potential solution to replace conventional non-degradable packaging materials.

| S-EPMC9183075 | biostudies-literature

Polyethylene glycol vs sodium picosulfate/magnesium citrate for colonoscopy preparation.

Project description:Background and study aimsPolyethylene glycol-based electrolyte solutions (PEG-ELS) and the combination of sodium picosulfate/magnesium citrate (SPMC) are commonly used bowel preparation agents. The aim of the present study was to compare the two agents with regard to cleansing efficacy and tolerance among individuals scheduled for outpatient colonoscopy.Materials and methodsThe 368 colonoscopy outpatients at three Norwegian hospitals were randomized to bowel lavage with either PEG-ELS or SPMC. Compliance and patient tolerance were evaluated using a patient questionnaire. Bowel cleansing was evaluated using the Ottawa Bowel Preparation Quality Scale (OBPS), a validated scoring system with scores between 0 (best) and 14.ResultsThere was no difference in the cleansing quality between the PEG-ELS and SPMC groups (median OBPS 5.0 in both groups). The group that received SPMC reported better overall patient tolerance than the PEG-ELS group (72.6 % vs 59.0 % reporting no or slight discomfort, P < 0.01). Compliance with the recommended total fluid intake (4 L) was better in the SPMC group than in the PEG-ELS group (94.2 % vs 81.2 % respectively, P < 0.01); moreover, the polyp detection rate was superior (34.3 % vs 23.3 %, P = 0.02).ConclusionPEG-ELS and SPMC are equally effective in cleansing efficacy, but SPMC was better tolerated by patients and resulted in superior patient compliance and polyp detection rate.Clinical trial registrationNCT01624454.

| S-EPMC4423298 | biostudies-literature

Colonoscopy preparation: polyethylene glycol with Gatorade is as safe and efficacious as four liters of polyethylene glycol with balanced electrolytes.

Project description:BackgroundFour liters of polyethylene glycol 3350 (PEG) with balanced electrolytes for colonoscopy preparation has had poor acceptance. Another approach is the use of electrolyte-free PEG combined with 1.9 L of Gatorade. Despite its widespread use, there are no data on metabolic safety and minimal data on efficacy. Our aim was to assess the efficacy and electrolyte safety of these two PEG-based preparations.MethodsThis was a prospective, randomized, single-blind, non-inferiority trial. Patients were randomized to 238 g PEG + 1.9 L Gatorade or 4 L of PEG-ELS containing 236 g PEG. Split dosing was not performed. On procedure day blood was drawn for basic chemistries. The primary outcome was preparation quality from procedure photos using the Boston Bowel Preparation Scale.ResultsWe randomized 136 patients (66 PEG + Gatorade, 70 PEG-ELS). There were no differences in preparation scores between the two agents in the ITT analysis (7.2 ± 1.9 for PEG-ELS and 7.0 ± 2.1 for PEG + Gatorade; p = 0.45). BBPS scores were identical for those who completed the preparation and dietary instructions as directed (7.4 ± 1.7 for PEG-ELS, and 7.4 ± 1.8 for PEG + Gatorade; p = 0.98). There were no statistical differences in serum electrolytes between the two preparations. Patients who received PEG + Gatorade gave higher overall satisfaction scores for the preparation experience (p = 0.001), and had fewer adverse effects.ConclusionsUse of 238 g PEG + 1.9 L Gatorade appears to be safe, better tolerated, and non-inferior to 4 L PEG-ELS. This preparation may be especially useful for patients who previously tolerated PEG-ELS poorly.

| S-EPMC3571759 | biostudies-literature

Bowel preparation using 2-L split-dose polyethylene glycol regimen plus lubiprostone versus 4-L split-dose polyethylene glycol regimen: a randomized controlled trial.

Project description:BackgroundColonoscopy is a standard procedure for evaluating colon diseases and screening for colorectal cancer, and bowel cleanliness prior to colonoscopy is key. The aim of this study was to compare the bowel cleansing efficacy of low-volume (2 L) split-dose polyethylene glycol (PEG) plus single-dose (24 µg) lubiprostone (LB) and high-volume (4 L) split-dose PEG.MethodsPatients scheduled to undergo outpatient colonoscopy between December 2019 and June 2021 at Rajavithi Hospital were enrolled and randomized into two groups: 2 L PEG + LB or 4 L PEG. Colon cleanliness was evaluated using the Boston Bowel Preparation Scale (BBPS) by reviewing images of the colon after completion of colonoscopy. Secondary outcomes comprised cecal intubation rate, procedure time, withdrawal time, polyp detection rate, adenoma detection rate, patient satisfaction, compliance (based on complete ingestion of bowel preparation regimen), willingness to repeat the preparation regimen, and associated adverse events.ResultsOne hundred and forty patients were included, with 70 in each group. The mean total and segment-specific BBPS scores were not significantly different between groups. However, the rate of adequate bowel preparation was significantly higher in the 2 L PEG + LB group than the 4 L PEG group (100% [95% CI 94.6-100] versus 88.4% [95% CI 78.4-94.9], p = 0.004) in the per-protocol analysis. Colonic polyps were the most common finding. The polyp detection rate, adenoma detection rate, and all secondary outcomes were statistically similar in the two groups (p > 0.05).ConclusionsThe combination of 2 L split-dose PEG plus LB improves bowel cleanliness (based on BBPS scores) to a comparable degree to the standard 4 L split-dose PEG, without additional adverse events and with a lower PEG volume.

| S-EPMC9482745 | biostudies-literature

NMR Characterization of Polyethylene Glycol Conjugates for Nanoparticle Functionalization.

Project description:The molecular weight, purity, and functionalization of polyethylene glycols are often characterized by 1H NMR spectroscopy. Oft-forgotten, the typical 1H NMR pulse sequence is not 13C decoupled. Hence, for large polymers, the 13C coupled 1H peaks arising from the repeating units have integrations comparable to that of the 1H of the terminal groups. Ignoring this coupling leads to erroneous assignments. Once correctly assigned, these 13C coupled 1H peaks can be used to determine both the molecular weight of the polymer and the efficacy of conjugation of a terminal moiety more accurately than the uncoupled 1H of the repeating unit.

| S-EPMC9893458 | biostudies-literature

Sugar-Responsive Pseudopolyrotaxane Composed of Phenylboronic Acid-Modified Polyethylene Glycol and ?-Cyclodextrin.

Project description:We have designed a sugar-responsive pseudopolyrotaxane (PPRX) by combining phenylboronic acid-modified polyethylene glycol (PBA-PEG) and ?-cyclodextrin. Phenylboronic acid (PBA) was used as a sugar-recognition motif in the PPRX because PBA reacts with a diol portion of the sugar molecule and forms a cyclic ester. When D-fructose or D-glucose was added to a suspension of PPRX, PPRX disintegrated, depending on the concentration of the sugars. Interestingly, catechol does not show a response although catechol has a high affinity for PBA. We analyzed the response mechanism of PPRX by considering equilibria.

| S-EPMC5455434 | biostudies-literature

Electrophysiological effects of polyethylene glycol modified gold nanoparticles on mouse hippocampal neurons.

Project description:Gold nanoparticles (AuNPs) can cross the blood brain barrier, thus can be used as nanocarriers in brain drug delivery. However, the effect of bare and polyethylene glycol-modified (PEGylated) AuNPs on normal neural function has not been extensively investigated. In this study, bioelectrical properties of neuronal functions of male BALB/c mice were explored ex vivo and in vivo by using 5 nm bare AuNPs and PEGylated AuNPs. Electrophysiological properties of neurons from hippocampal CA1 region sections were recorded by patch clamp method. Ex vivo, firing rate of action and membrane potentials in response to negative current stimuli significantly altered only after bare AuNP exposure compared to control (p < 0.05). After in vivo injections, anxiety levels of animals were similar. Amplitude of action potentials reduced only in bare AuNP group (p < 0.05). In conclusion, excitability of hippocampal neurons is increasing with bare AuNP exposure, and PEGylation might be more biocompatible for medical applications.

| S-EPMC7779771 | biostudies-literature

Mechanical and In Vitro Biocompatibility of Brushite Cement Modified by Polyethylene Glycol.

Project description:Brushite (dicalcium phosphate dihydrate, DCPD) cement, owing to its high solubility in physiological condition and ability to guide new bone formation, is widely used to treat bone defects. In the present study, we have evaluated the effects of poly ethylene glycol (PEG) addition on the setting time, compressive strength and in vitro biocompatibility of brushite cement. The brushite cements were prepared by mixing β-tricalcium phosphate [β-TCP, Ca(3)(PO(4))(2)] and monocalcium phosphate monohydrate [MCPM, Ca(H(2)PO(4))(2). H(2)O]. PEG was introduced at 2.0 and 5.0 wt% with the liquid. Introduction of PEG resulted in marginal increase in both initial and final setting time; however, significantly affected the compressive strength. Effects of PEG incorporation on in vitro biocompatibility of brushite cements were studied by using human fetal osteoblast cells (hFOB) cells. Field emission scanning electron microscope (FESEM) images and immunohistochemical analysis indicated that pure and PEG incorporated brushite cement facilitates cell adhesion, proliferation and differentiation. Fewer cells expressed vinculin protein with increased PEG content in the cement. Cell proliferation was found to decrease with increased PEG concentration while the cell differentiation increased with PEG content. Our results provide a better understanding of in vitro biocompatibility of PEG added brushite cements that can be used to customize the cement compositions based on application need.

| S-EPMC3489179 | biostudies-literature

Preparation and Characterization of Films Extruded of Polyethylene/Chitosan Modified with Poly(lactic acid).

Project description:The use of mixtures of synthetic and natural polymers is a potential option to reduce the pollution by plastic waste. In this work, the method for the chemical modification of chitosan with poly(lactic acid) was developed; then, the preparation of films of blends of polyethylene and chitosan-poly(lactic acid) produced by an extrusion method using polyethylene-graft maleic anhydride as a compatibilizer. It was possible to obtain films with a maximum content of 20 wt% and 30 wt%, chitosan, with and without compatibilizer, respectively. Scanning electron microscope (SEM) analysis showed a homogeneous surface on all films. The addition of the compatibilizer had a significant effect on the mechanical properties of the films, such as an increase in Young's modulus and a decrease in the elongation at break; additionally, the compatibilizer promotes thermal degradation in a single step and gives the film a slight increase in thermal resistance. These results are attributed to an improved interaction in the interface of polyethylene and chitosan-poly(lactic acid), promoted by the compatibilizer.

| S-EPMC5455231 | biostudies-other

Polyethylene-glycol-modified single-walled carbon nanotubes for intra-articular delivery to chondrocytes.

Project description:Osteoarthritis (OA) is a common and debilitating degenerative disease of articular joints for which no disease-modifying medical therapy is currently available. Inefficient delivery of pharmacologic agents into cartilage-resident chondrocytes after systemic administration has been a limitation to the development of anti-OA medications. Direct intra-articular injection enables delivery of high concentrations of agents in close proximity to chondrocytes; however, the efficacy of this approach is limited by the fast clearance of small molecules and biomacromolecules after injection into the synovial cavity. Coupling of pharmacologic agents with drug delivery systems able to enhance their residence time and cartilage penetration can enhance the effectiveness of intra-articularly injected anti-OA medications. Herein we describe an efficient intra-articular delivery nanosystem based on single-walled carbon nanotubes (SWCNTs) modified with polyethylene glycol (PEG) chains (PEG-SWCNTs). We show that PEG-SWCNTs are capable to persist in the joint cavity for a prolonged time, enter the cartilage matrix, and deliver gene inhibitors into chondrocytes of both healthy and OA mice. PEG-SWCNT nanoparticles did not elicit systemic or local side effects. Our data suggest that PEG-SWCNTs represent a biocompatible and effective nanocarrier for intra-articular delivery of agents to chondrocytes.

| S-EPMC4373402 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data