The Structural, Photocatalytic Property Characterization and Enhanced Photocatalytic Activities of Novel Photocatalysts Bi₂GaSbO₇ and Bi₂InSbO₇ during Visible Light Irradiation.

ABSTRACT: In order to develop original and efficient visible light response photocatalysts for degrading organic pollutants in wastewater, new photocatalysts Bi₂GaSbO₇ and Bi₂InSbO₇ were firstly synthesized by a solid-state reaction method and their chemical, physical and structural properties were characterized. Bi₂GaSbO₇ and Bi₂InSbO₇ were crystallized with a pyrochlore-type structure and the lattice parameter of Bi₂GaSbO₇ or Bi₂InSbO₇ was 10.356497 Å or 10.666031 Å. The band gap of Bi₂GaSbO₇ or Bi₂InSbO₇ was estimated to be 2.59 eV or 2.54 eV. Compared with nitrogen doped TiO₂, Bi₂GaSbO₇ and Bi₂InSbO₇, both showed excellent photocatalytic activities for degrading methylene blue during visible light irradiation due to their narrower band gaps and higher crystallization perfection. Bi₂GaSbO₇ showed higher catalytic activity compared with Bi₂InSbO₇. The photocatalytic degradation of methylene blue followed by the first-order reaction kinetics and the first-order rate constant was 0.01470 min-1, 0.00967 min-1 or 0.00259 min-1 with Bi₂GaSbO₇, Bi₂InSbO₇ or nitrogen doped TiO₂ as a catalyst. The evolution of CO₂ and the removal of total organic carbon were successfully measured and these results indicated continuous mineralization of methylene blue during the photocatalytic process. The possible degradation scheme and pathway of methylene blue was also analyzed. Bi₂GaSbO₇ and Bi₂InSbO₇ photocatalysts both had great potential to purify textile industry wastewater.

SUBMITTER: Luan J

PROVIDER: S-EPMC5456611 | biostudies-other | 2016 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Biofabricated BiOI with enhanced photocatalytic activity under visible light irradiation.

Project description:In the recent past, there has been a large-scale utilization of plant extracts for the synthesis of various photocatalysts. The biofabrication technology eliminates the usage of harmful chemicals and serves as an eco-friendly approach for environmental remediation. Herein, a comparative analysis between bismuth oxyiodide synthesized via Azadirachta indica (neem) leaf extract (BiOI-G) and without leaf extract (BiOI-C) has been envisaged. The BiOI-G and BiOI-C samples were characterized by spectral and microscopic techniques, which revealed that the Azadirachta indica assisted BiOI-G attained enhanced features over BiOI-C such as narrower band gap, large surface area, porosity, increased absorption range of visible light and effectual splitting of the photogenerated e--h+ pairs. Benefiting from these enhanced features, BiOI-G degraded methyl orange (MO), rhodamine B (RhB), and benzotriazole (BT) at a significantly higher rate in comparison to BiOI-C. The degradation rate of MO, RhB and BT by BiOI-G was observed to be 1.3, 1.25 and 1.29 times higher in comparison to BiOI-C. Moreover, BiOI-G displayed high stability upto five cycles of the photocatalytic activity, which endow its effectiveness as a highly-efficient green photocatalyst.

| S-EPMC9084558 | biostudies-literature

In Situ Synthesis of All-Solid-State Z-Scheme BiOBr0.3I0.7/Ag/AgI Photocatalysts with Enhanced Photocatalytic Activity Under Visible Light Irradiation.

Project description:A series of novel visible light driven all-solid-state Z-scheme BiOBr0.3I0.7/Ag/AgI photocatalysts were synthesized by facile in situ precipitation and photo-reduction methods. Under visible light irradiation, the BiOBr0.3I0.7/Ag/AgI samples exhibited enhanced photocatalytic activity compared to BiOBr0.3I0.7 and AgI in the degradation of methyl orange (MO). The optimal ratio of added elemental Ag was 15%, which degraded 89% of MO within 20 min. The enhanced photocatalytic activity of BiOBr0.3I0.7/Ag/AgI can be ascribed to the efficient separation of photo-generated electron-hole pairs through a Z-scheme charge-carrier migration pathway, in which Ag nanoparticles act as electron mediators. The mechanism study indicated that ·O2- and h+ are active radicals for photocatalytic degradation and that a small amount of ·OH also participates in the photocatalytic degradation process.

| S-EPMC6246750 | biostudies-other

Enhanced Photocatalytic Fuel Denitrification over TiO2/?-Fe2O3 Nanocomposites under Visible Light Irradiation.

Project description:With increasingly stringent environmental regulations, the removal of nitrogen-containing compounds (NCCs) from gasoline fuel has become a more and more important research subject. In this work, we have successfully synthesized TiO2/?-Fe2O3 heterogeneous photocatalysts with different mass ratios of TiO2 vs. ?-Fe2O3. Taking photocatalytic denitrification of typical alkali NCCs, pyridine, in gasoline fuel under visible light irradiation (????420?nm) as the model reaction, the TiO2/?-Fe2O3 hybrids have exhibited enhanced photocatalytic activity compared with pure TiO2 and ?-Fe2O3, giving a pyridine removal ratio of ?100% after irradiation for 240?min. The improved photocatalytic performance can be attributed to the integrative effect of the enhanced light absorption intensity and more efficient separation of photogenerated electron-hole pairs. Importantly, this type of heterogeneous photocatalysts can be easily separate in the reaction medium by an external magnetic field that is very important for industrial purpose. In addition, major reaction intermediates have been identified by the liquid chromatograph-mass spectrometer (HPLC-MS) and a tentative photocatalytic denitrification mechanism has been proposed.

| S-EPMC5552819 | biostudies-other

Enhanced photocatalytic activity of Se-doped TiO2 under visible light irradiation.

Project description:Anatase TiO2 is a typical photocatalyst, and its excellent performance is limited in ultraviolet light range due to its wide band gap of 3.2?eV. A series of Se-doped TiO2 nanoparticles in anatase structure with various Se concentrations up to 17.1?at.% were prepared using sol-gel method. The doped Se ions are confirmed to be mainly in the valence state of?+?4, which provides extra electronic states in the band gap of TiO2. The band gap is effectively narrowed with the smallest gap energy of 2.17?eV, and the photocatalytic activity is effectively improved due to the extended absorption range. The photocatalytic activity was evaluated by the degradation of Rhodamine B (RhB) in aqueous solution under visible light irradiation. The results show that Se doping significantly improves the photocatalytic activity of TiO2 and 13.63?at.% Se-doped TiO2 has the best performance.

| S-EPMC5993730 | biostudies-literature

A new Bi-based visible-light-sensitive photocatalyst BiLa1.4Ca0.6O4.2: crystal structure, optical property and photocatalytic activity.

Project description:A new compound of BiLa1.4Ca0.6O4.2 is synthesized through solid state reaction, where the Ca substitutes, in part, the La site in a stable BiLa2O4.5 phase. The structure of the BiLa1.4Ca0.6O4.2 crystallizes in space group R3mH with a hexagonal lattice constants of a = 3.893(1) Å, c = 9.891(1) Å. Its optical absorption edge is about 2.05 eV, which just spans the visible light region. The photocatalytic activity of the BiLa1.4Ca0.6O4.2 powder to degradation of RhB under visible light irradiation is measured and improved more than 7 times by annealing in nitrogen ambient, indicating that annealing in nitrogen can effectively improve the photocatalytic activity by producing oxygen vacancy. Although the absolute photocatalytic activity obtained is low, there is great potential for enhancing the activity such as nanoscaling, doping, and coupling with other compounds.

| S-EPMC4794645 | biostudies-other

Highly efficient In2S3/WO3 photocatalysts: Z-scheme photocatalytic mechanism for enhanced photocatalytic water pollutant degradation under visible light irradiation.

Project description:A Z-scheme system In2S3/WO3 heterojunction was fabricated via a mild hydrothermal method and further applied for photocatalytic degradation of tetracycline (TCH) and Rhodamine B (Rh B) under visible light irradiation. The morphological structure, chemical composition and optical properties were studied by XRD, SEM, HRTEM and UV-visible absorption spectra. The results revealed that In2S3/WO3 hierarchical structures were successfully constructed, and the prepared In2S3/WO3 photocatalysts exhibited enhanced visible-light absorption compared to pure WO3 nanorods, which are essential to improve the photocatalytic performance. The degradation rate of TCH using the In2S3(40 wt%)/WO3 heterostructure (WI40) photocatalyst was about 212 times and 22 times as high as that for pure WO3 and pure In2S3, respectively. The degradation rate of Rh B with the WI40 photocatalyst was about 56 times the efficiency of pure WO3 and 7.6 times that of pure In2S3. The results of the surface photovoltage (SPV), transient photovoltage (TPV) and reactive oxidation species (ROS) scavenger experiments indicated that the Z-scheme system of In2S3/WO3 is favorable for photoexcited charge transfer at the contact interface of In2S3 and WO3, which benefits the charge separation efficiency and depresses the recombination of photoexcited charge, resulting in favorable photocatalytic pollutant degradation efficiency under visible light irradiation.

| S-EPMC8694021 | biostudies-literature

Photocatalytic Water Splitting for Hydrogen Production with Gd₂MSbO₇ (M = Fe, In, Y) Photocatalysts under Visible Light Irradiation.

Project description:Novel photocatalysts Gd₂FeSbO₇, Gd₂InSbO₇ and Gd₂YSbO₇ were synthesized by the solid state reaction method for the first time. A comparative study about the structural and photocatalytic properties of Gd₂MSbO₇ (M = Fe, In, Y) was reported. The results showed that Gd₂FeSbO₇, Gd₂InSbO₇ and Gd₂YSbO₇ crystallized with the pyrochlore-type structure, cubic crystal system and space group Fd3m. The lattice parameter a for Gd₂FeSbO₇, Gd₂InSbO₇ or Gd₂YSbO₇ was 10.276026 Å, 10.449546 Å or 10.653651 Å. The band gap of Gd₂FeSbO₇, Gd₂InSbO₇ or Gd₂YSbO₇ was estimated to be 2.151 eV, 2.897 eV or 2.396 eV. For the photocatalytic water-splitting reaction, H₂ or O₂ evolution was observed from pure water with Gd₂FeSbO₇, Gd₂InSbO₇ or Gd₂YSbO₇ as catalyst under visible light irradiation (wavelength > 420 nm). Moreover, H₂ or O₂ also spilt by using Gd₂FeSbO₇, Gd₂InSbO₇ or Gd₂YSbO₇ as catalyst from CH₃OH/H₂O or AgNO₃/H₂O solutions under visible light irradiation (λ > 420 nm). Gd₂FeSbO₇ showed the highest activity compared with Gd₂InSbO₇ or Gd₂YSbO₇. At the same time, Gd₂InSbO₇ showed higher activity compared with Gd₂YSbO₇. The photocatalytic activities were further improved under visible light irradiation with Gd₂FeSbO₇, Gd₂InSbO₇ or Gd₂YSbO₇ being loaded by Pt, NiO or RuO₂. The effect of Pt was better than that of NiO or RuO₂ for improving the photocatalytic activity of Gd₂FeSbO₇, Gd₂InSbO₇ or Gd₂YSbO₇.

| S-EPMC5455222 | biostudies-other

Enhanced photocatalytic degradation of tetracycline hydrochloride over Au-doped BiOBr nanosheets under visible light irradiation.

Project description:Bismuth(III) oxybromide (BiOBr) is a typical photocatalyst with a unique layered structure. However, the response of BiOBr to visible light is not strong enough for practical application. Moreover, the charge separation efficiency of BiOBr still needs to be improved. In this study, series of Au-doped BiOBr photocatalysts was prepared through a facile one-step hydrothermal method. The as-prepared Au0.3-BiOBr nanosheets exhibited an excellent electrochemical performance. The charge separation efficiency of Au0.3-BiOBr nanosheets was enhanced by 18.5 times compared with that of BiOBr. The intrinsic photocatalytic activity of Au0.3-BiOBr nanosheets in the degradation of tetracycline hydrochloride was approximately twice higher than that of BiOBr under visible light irradiation. In addition, three pathways were identified for the photocatalytic degradation and mineralization of tetracycline hydrochloride, which involve four reactions: hydroxylation, demethylation, ring opening and mineralization. Accordingly, this study proposes a feasible and effective Au-doped BiOBr photocatalyst, and describes a promising strategy for the design and synthesis of high-performance photocatalysts.

| S-EPMC9417003 | biostudies-literature

Preparation of Pt/?-Bi2MoO6 Photocatalysts and Their Performance in ?-Alkylation Reaction under Visible Light Irradiation.

Project description:Bi(NO3)3·5H2O and (NH4)6Mo7O24·4H2O were used as precursors to synthesize flaky ?-Bi2MoO6 samples by a hydrothermal method, and Pt/?-Bi2MoO6 samples with different mass fractions were prepared by an NaBH4 reduction method. Alpha alkylation of benzyl alcohol and acetophenone with photocatalysts under visible light irradiation was performed, and the activity of 4 wt % Pt/?-Bi2MoO6 (?-Bi2MoO6 was prepared by a nitric acid method, pH = 9, and reaction temperature 180 °C) was the best. The photocatalytic reaction conditions were optimized by changing various kinds of variables, such as the type of catalyst, solvent, and base, and the amount of base, catalyst, and reactant. The optimal conditions for the organic reaction were 75 mg 4 wt % Pt/?-Bi2MoO6, 6 mL n-heptane, 1.2 mmol NaOH, 1 mmol acetophenone, and 3 mmol benzyl alcohol. Under the optimal reaction conditions, the effects of different light wavelengths and light intensities on the reaction were measured, and the cycling ability of the photocatalyst was tested. After five cycles, the photochemical properties of the catalyst were relatively stable. Finally, the active substances were identified (such as electrons (e-), holes (h+), hydroxyl radicals (•OH), and superoxide radicals (•O2-).

| S-EPMC7221669 | biostudies-literature

Magnetic ZnO Crystal Nanoparticle Growth on Reduced Graphene Oxide for Enhanced Photocatalytic Performance under Visible Light Irradiation.

Project description:Magnetite zinc oxide (MZ) (Fe3O4/ZnO) with different ratios of reduced graphene oxide (rGO) was synthesized using the solid-state method. The structural and optical properties of the nanocomposites were analyzed using transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy, Fourier-transform infrared spectroscopy (FTIR), ultraviolet-visible diffuse reflectance spectroscopy (UV-Vis/DRS), and photoluminescence (PL) spectrophotometry. In particular, the analyses show higher photocatalytic movement for crystalline nanocomposite (MZG) than MZ and ZnO nanoparticles. The photocatalytic degradation of methylene blue (MB) with crystalline ZnO for 1.5 h under visible light was 12%. By contrast, the photocatalytic activity for MZG was more than 98.5%. The superior photocatalytic activity of the crystalline nanocomposite was detected to be due to the synergistic effect between magnetite and zinc oxide in the presence of reduced graphene oxide. Moreover, the fabricated nanocomposite had high electron-hole stability. The crystalline nanocomposite was stable when the material was used several times.

| S-EPMC8070817 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data