Synthesis and Characterization of N-Doped Porous TiO₂ Hollow Spheres and Their Photocatalytic and Optical Properties.

ABSTRACT: Three kinds of N-doped mesoporous TiO₂ hollow spheres with different N-doping contents, surface area, and pore size distributions were prepared based on a sol-gel synthesis and combined with a calcination process. Melamine formaldehyde (MF) microspheres have been used as sacrificial template and cetyltrimethyl ammonium bromide (CTAB) or polyvinylpyrrolidone (PVP) was selected as pore-directing agent. Core-shell intermediate spheres of titania-coated MF with diameters of 1.2-1.6 μm were fabricated by varying the volume concentration of TiO₂ precursor from 1 to 3 vol %. By calcining the core-shell composite spheres at 500 °C for 3 h in air, an in situ N-doping process occurred upon the decomposition of the MF template and CTAB or PVP pore-directing surfactant. N-doped mesoporous TiO₂ hollow spheres with sizes in the range of 0.4-1.2 μm and shell thickness from 40 to 110 nm were obtained. The composition and N-doping content, thermal stability, morphology, surface area and pore size distribution, wall thickness, photocatalytic activities, and optical properties of the mesoporous TiO₂ hollow spheres derived from different conditions were investigated and compared based on Fourier-transformation infrared (FTIR), SEM, TEM, thermogravimetric analysis (TGA), nitrogen adsorption-desorption, and UV-vis spectrophotoscopy techniques. The influences of particle size, N-doping, porous, and hollow characteristics of the TiO₂ hollow spheres on their photocatalytic activities and optical properties have been studied and discussed based on the composition analysis, structure characterization, and optical property investigation of these hollow spherical TiO₂ matrices.

SUBMITTER: Li H

PROVIDER: S-EPMC5456619 | biostudies-other | 2016 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Facile fabrication of porous BiVO4 hollow spheres with improved visible-light photocatalytic properties.

Project description:Bismuth vanadate (BiVO4) hollow spheres with porous structure have been successfully fabricated by a one-step wet solution method with no surfactant and template. The structure, morphologies, and composition of the as-prepared products were studied with X-ray powder diffraction (XRD), transmission electron morphology (TEM), Brunauer-Emmett-Teller (BET), X-ray photoelectron spectroscopy (XPS) and UV-vis spectroscopy. Based upon the time-dependent experimental results, BiVO4 nanospheres with hollow and solid structures can be controlled effectively through the reaction time, and a reasonable formation process was suggested in this work. Moreover, the experiment of degrading methyl orange (MO) under visible-light illumination was conducted to evaluate the photocatalytic performance of the obtained BiVO4 samples. The porous BiVO4 hollow spheres exhibit superior visible-light photocatalytic properties for MO degradation than other photocatalysts under irradiation, and could be reused for up to five times without significant reduction in the photocatalytic activity. In addition, based on active group trapping experiments, ˙OH radicals as the main active species from H2O2 molecules play a vital role in the photocatalytic degradation of MO, and a photocatalytic mechanism for the BiVO4 system was proposed. High photocatalytic activity, universality and stability suggest that the porous BiVO4 hollow spheres may have potential applications in wastewater treatment.

| S-EPMC9049651 | biostudies-literature

Self-Templated Synthesis of Ultrathin Nanosheets Constructed TiO2 Hollow Spheres with High Electrochemical Properties.

Project description:TiO2 is well-known nanomaterials and mostly used as solid nanoparticles, and normal hollow spheres for photocatalysts or electrode materials. In this study, a novel self-templated method is presented to successfully fabricate high-surface-area ultrathin nanosheets constructed TiO2 hollow spheres through the solvothermal treatment of the titanate-silicone composite particles combined with calcination. The uniquely structured hollow spheres exhibit excellent rate capability and good cycle stability even at a high current density of ≈10 C for the anode material of Li-ion battery.

| S-EPMC5102664 | biostudies-literature

Synthesis, characterization and photocatalytic properties of nanostructured lanthanide doped β-NaYF4/TiO2 composite films.

Project description:The photocatalytic approach is known to be one of the most promising advanced oxidation processes for the tertiary treatment of polluted water. In this paper, β-NaYF4/TiO2 composite films have been synthetized through a novel sol-gel/spin-coating approach using a mixture of β-diketonate complexes of Na and Y, and Yb3+, Tm3+, Gd3+, Eu3+ as doping ions, together with the TiO2 P25 nanoparticles. The herein pioneering approach represents an easy, straightforward and industrially appealing method for the fabrication of doped β-NaYF4/TiO2 composites. The effect of the doped β-NaYF4 phase on the photocatalytic activity of TiO2 for the degradation of methylene blue (MB) has been deeply investigated. In particular, the upconverting TiO2/β-NaYF4: 20%Yb, 2% Gd, x% Tm (x = 0.5 and 1%) and the downshifting TiO2/β-NaYF4: 10% Eu composite films have been tested on MB degradation both under UV and visible light irradiation. An improvement up to 42.4% in the degradation of MB has been observed for the TiO2/β-NaYF4: 10% Eu system after 240 min of UV irradiation.

| S-EPMC9374679 | biostudies-literature

Hydrothermal Synthesis of Bismuth Ferrite Hollow Spheres with Enhanced Visible-Light Photocatalytic Activity.

Project description:In recent years, semiconductor hollow spheres have gained much attention due to their unique combination of morphological, chemical, and physico-chemical properties. In this work, we report for the first time the synthesis of BiFeO3 hollow spheres by a facile hydrothermal treatment method. The mechanism of formation of pure phase BiFeO3 hollow spheres is investigated systematically by variation of synthetic parameters such as temperature and time, ratio and amount of precursors, pressure, and calcination procedures. The samples were characterized by X-ray powder diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy, and UV-vis diffuse reflectance spectroscopy. We observe that the purity and morphology of the synthesized materials are very sensitive to synthesis parameters. In general, the chemically and morphologically very robust hollow spheres have diameters in the range of 200 nm to 2 μm and a wall thickness of 50-200 nm. The synthesized BiFeO3 hollow spheres were applied as catalysts in the photodegradation of the model pollutant Rhodamine B under visible-light irradiation. Notably, the photocatalyst demonstrated exceptionally high removal efficiencies leading to complete degradation of the dye in less than 150 min at neutral pH. The superior efficiencies of the synthesized material are attributed to the unique features of hollow spheres. The active species in the photocatalytic process have been identified by trapping experiments.

| S-EPMC10343919 | biostudies-literature

Structural, Morphological, Optical and Photocatalytic Properties of Y, N-Doped and Codoped TiO₂ Thin Films.

Project description:Pure TiO₂, Y-N single-doped and codoped TiO₂ powders and thin films deposited on glass beads were successfully prepared using dip-coating and sol-gel methods. The samples were analyzed using grazing angle X-ray diffraction (GXRD), Raman spectroscopy, time resolved luminescence, ground state diffuse reflectance absorption and scanning electron microscopy (SEM). According to the GXRD patterns and micro-Raman spectra, only the anatase form of TiO₂ was made evident. Ground state diffuse reflectance absorption studies showed that doping with N or codoping with N and Y led to an increase of the band gap. Laser induced luminescence analysis revealed a decrease in the recombination rate of the photogenerated holes and electrons. The photocatalytic activity of supported catalysts, toward the degradation of toluidine, revealed a meaningful enhancement upon codoping samples at a level of 2% (atomic ratio). The photocatalytic activity of the material and its reactivity can be attributed to a reduced, but significant, direct photoexcitation of the semiconductor by the halogen lamp, together with a charge-transfer-complex mechanism, or with the formation of surface oxygen vacancies by the N dopant atoms.

| S-EPMC5553417 | biostudies-other

Controllable Fabrication and Optical Properties of Uniform Gadolinium Oxysulfate Hollow Spheres.

Project description:Uniform gadolinium oxysulfate (Gd2O2SO4) hollow spheres were successfully fabricated by calcination of corresponding Gd-organic precursor obtained via a facile hydrothermal process. The Gd2O2SO4 hollow spheres have a mean diameter of approximately 550?nm and shell thickness in the range of 30-70?nm. The sizes and morphologies of as-prepared Gd2O2SO4 hollow spheres could be deliberately controlled by adjusting the experimental parameters. Eu-doped Gd2O2SO4 hollow spheres have also been prepared for the property modification and practical applications. The structure, morphology, and properties of as-prepared products were characterized by XRD, TEM, HRTEM, SEM and fluorescence spectrophotometer. Excited with ultraviolet (UV) pump laser, successful downconversion (DC) could be achieved for Eu-doped Gd2O2SO4 hollow spheres.

| S-EPMC4680860 | biostudies-other

Enhanced electrocatalytic performance for H2O2 generation by boron-doped porous carbon hollow spheres.

Project description:Electrocatalytic generation of H2O2 via the 2-electron pathway of oxygen reduction reaction (2e-ORR) is an attractive technology compared to the anthraquinone process due to convenience and environmental friendliness. However, catalysts with excellent selectivity and high activity for 2e-ORR are necessary for practical applications. Reported here is a catalyst comprising boron-doped porous carbon hollow spheres (B-PCHSs) prepared using the hard template method coupled with borate transesterification. In an alkali electrolyte, the selectivity of B-PCHS for 2e-ORR above 90% in range of 0.4-0.7 VRHE and an onset potential of 0.833 V was obtained. Meanwhile, the generation rate of H2O2 reached 902.48 mmol h-1 gcat-1 at 0.4 VRHE under 59.13 mA cm-2 in batch electrolysis. The excellent catalytic selectivity of B-PCHS for 2e-ORR originates from the boron element, and the catalytic activity of B-PCHS for H2O2 generation is contributed to the morphology of porous hollow spheres, which facilitates mass transfer processes.

| S-EPMC11016794 | biostudies-literature

One-pot preparation of hierarchical Cu2O hollow spheres for improved visible-light photocatalytic properties.

Project description:As visible light photocatalysts, narrow bandgap semiconductors can effectively convert solar energy to chemical energy, exhibiting potential applications in alleviating energy shortage and environmental pollution. Cu2O hollow spheres with a narrow band gap and uniform hierarchical structures have been fabricated in a controlled way. The one-pot solvothermal method without any template is simple and facile. The morphologies, crystal structures, composition, specific surface areas, and optical and photoelectric properties of the products were analyzed by various techniques. The hollow and solid Cu2O spheres could be fabricated by controlling the reaction time, and a possible growth process of the Cu2O hollow spheres was revealed. The degradation of methyl orange (MO) was used to investigate the visible-light catalytic properties of the Cu2O samples. More than 90% of MO is degraded under visible light illumination of 20 min, exhibiting a quick catalytic reaction. The rate constant of the Cu2O hollow spheres was 2.54 times and 46.6 times larger than those of the Cu2O solid spheres and commercial Cu2O powder, respectively. The possible photocatalytic mechanism of MO was revealed over Cu2O hollow spheres through the detection of active species. The as-prepared Cu2O hollow spheres display improved visible-light catalytic activity and stability, indicating their potential application in wastewater treatment.

| S-EPMC9054622 | biostudies-literature

A Gram Scale Soft-Template Synthesis of Heteroatom Doped Nanoporous Hollow Carbon Spheres for Oxygen Reduction Reaction.

Project description:Heteroatom-doped nanoporous carbon materials with unique hierarchical structures have been shown to be promising supports and catalysts for energy conversion; however, hard-template methods are limited by their inflexibility and time-consuming process. Soft-template methods have been suggested as an alternative, but they are limited by their picky requirements for stable reactions and the few known precursors for small-batch synthesis. In this study, a gram-scale soft-template-based silica-assisted method was investigated for producing nitrogen-doped hollow nanoporous carbon spheres (N-HNCS). Nitrogen doping is accomplished during preparation with enhanced electrocatalytic activity without complicating the methodology. To investigate the effect of the unique structural characteristics of N-HNCS (specific surface area: 1250 m2 g-1; pore volume: 1.2 cm3 g-1), cobalt was introduced as an active center for the oxygen reduction reaction. Finely tuned reaction conditions resulted in well-dispersed cobalt particles with minimal agglomeration. This sheds light on the advancement of new experimental procedures for developing more active and promising non-noble catalysts in large and stable batches.

| S-EPMC10534767 | biostudies-literature

Synthesis of Double-Shell Hollow TiO2@ZIF-8 Nanoparticles With Enhanced Photocatalytic Activities.

Project description:Synthesis of semiconductor-MOF heterostructure photocatalysts has attracted considerable attention for their thermal stability, controllable crystallinity, and enhanced photocatalytic activity. In this work, the hollow nanostructure of anatase TiO2 was prepared by etching SiO2 from core-shell SiO2@TiO2 nanoparticles. ZIF-8, one of the metal-organic frameworks (MOFs), was hybrid synthesized on the surface of hollow TiO2 and formed double-shell hollow nanoparticles. The photocatalytic activity of the double-shell hollow TiO2@ZIF-8 nanoparticles toward methylene blue (MB) under UV light irradiation was processed, and the highest photocatalytic efficiency of 99.1% was shown compared with TiO2 and SiO2@TiO2 nanoparticles. This study suggests a promising approach to achieve an advanced photocatalytic performance toward dye degradation using MOFs for the surface engineering of semiconductors.

| S-EPMC7645166 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data