The Effect of Bi-Sr and Ca-Sr Interactions on the Microstructure and Tensile Properties of Al-Si-Based Alloys.

ABSTRACT: The effect of bismuth and calcium additions on the microstructural characteristics and the tensile properties of the modified and grain-refined Al-Si based B319 alloys were studied in this paper. Based on the results obtained, it has been concluded that Bi reacts with both Sr and Mg, leading to severe demodification of the eutectic Si at Bi levels of 0.15%-0.6% Bi. Bismuth causes a decrease of the yield and tensile strengths for the as-cast and artificially aged conditions and an increase of yield strength in the solution heat-treated condition. The elongation increases with the Bi in the solution heat-treated condition. Based on this, Bi is found to be an efficient solid-solution strengthening element for these alloys. Thus, solution heat treatment, rather than the artificial aging, may be recommended for alloys containing about 1.0% Bi. Calcium has no significant demodification effect on the Sr-modified Si particles at 100-400 ppm Ca, and has a modifying effect at ~600 ppm Ca. The elongation increases with the Ca level at all conditions (as-cast, solution heat-treated, and artificially aged). A slight increase of the tensile strength in the heat-treated conditions was also observed. The lowest tensile properties either in the as-cast or the heat-treated conditions correspond to the most demodified-Si condition obtained at 408 ppm Ca. Calcium is, therefore, not as detrimental to the tensile properties as Bi.

SUBMITTER: Samuel AM

PROVIDER: S-EPMC5456678 | biostudies-other | 2016 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effects of Si and Sr elements on solidification microstructure and thermal conductivity of Al-Si-based alloys.

Project description:Effects of Si and Sr on solidification microstructure and thermal conductivity of Al-Si binary alloys and Al-9Si-Sr ternary were investigated, respectively, with a special focus on the relationship between solidification microstructure and thermal conductivity. It was found that (i) in Al-Si binary alloys, with increasing Si content, α-Al grain size increases and then decreases when Si content is over 7 wt%, while the percentage of eutectic Si continuously increases, which significantly decreases the thermal conductivity and electrical conductivity, and (ii) in Al-9Si-Sr ternary alloys, the presence of Sr has no significant effect on α-Al grain, but effectively modifies eutectic Si and significantly improves the thermal and electrical conductivity. On this basis, two theoretical calculation models [the Maxwell model and the Hashin-Shtrikman (H-S) model] were used to elucidate the relationship between solidification microstructure and thermal conductivity. Compared with the Maxwell model, the H-S model fits better with the measured values. The obtained results are very helpful to the precise composition control during alloy design and recycling of Al-Si-based alloys with the aim to further improve the thermal conductivity of Al-Si-based alloys.Graphical abstractSupplementary informationThe online version contains supplementary material available at 10.1007/s10853-022-07045-7.

| S-EPMC8933373 | biostudies-literature

Microstructure and properties of additively manufactured Al-Ce-Mg alloys.

Project description:Additive manufacturing of aluminum alloys is largely dominated by a near-eutectic Al-Si compositions, which are highly weldable, but have mechanical properties that are not competitive with conventional wrought Al alloys. In addition, there is a need for new Al alloys with improved high temperature properties and thermal stability for applications in the automotive and aerospace fields. In this work, we considered laser powder bed fusion additive manufacturing of two alloys in the Al-Ce-Mg system, designed as near-eutectic (Al-11Ce-7Mg) and hyper-eutectic (Al-15Ce-9Mg) compositions with respect to the binary L → Al + Al11Ce eutectic reaction. The addition of magnesium is used to promote solid solution strengthening. A custom laser scan pattern was used to reduce the formation of keyhole porosity, which was caused by excessive vaporization due to the high vapor pressure of magnesium. The microstructure and tensile mechanical properties of the alloys were characterized in the as-fabricated condition and following hot isostatic pressing. The two alloys exhibit significant variations in solidification structure morphology. These variations in non-equilibrium solidification structure were rationalized using a combination of thermodynamic and thermal modeling. Both alloys showed higher yield strength than AM Al-10Si-Mg for temperatures up to 350 °C and better strength retention at elevated temperatures than additively manufactured Scalmaloy.

| S-EPMC7998028 | biostudies-literature

Effect of Zr and Ti Addition and Aging Treatment on the Microstructure and Tensile Properties of Al-2%Cu-Based Alloys.

Project description:The present work investigated the effect of aging treatment on the microstructure and tensile properties of an Al-2%Cu base alloy containing various additions of Zr and other alloying elements. Aging was carried out at temperatures of 180-300 °C for different aging times at each temperature. The tensile properties indicated that Zr additions improved the strength of the base alloy, especially at high Zr levels at 180 °C. At the 220 °C aging temperature, however, while Zr addition did not have a beneficial effect on the alloy strength, the ductility was found to improve. Zr-Ti combined additions had a significant effect on the microstructure of the base alloy, as the morphology of the α-Al grains transformed into a non-dendritic morphology, and the grain size decreased sharply. These effects were at their maximum at 180 °C and 0.5 wt% Zr addition. Moreover, the Zr-containing alloys aged at higher temperatures, such as 220 °C and 240 °C, maintained a noticeably higher level of strength over the base alloy aged at the same temperatures. Quality index charts based on the tensile test data also reflected an improvement in alloy quality and strength with Zr-Ti combined additions.

| S-EPMC9267249 | biostudies-literature

On the Microstructure and Properties of Nb-Ti-Cr-Al-B-Si-X (X = Hf, Sn, Ta) Refractory Complex Concentrated Alloys.

Project description:We studied the effect of the addition of Hf, Sn, or Ta on the density, macrosegregation, microstructure, hardness and oxidation of three refractory metal intermetallic composites based on Nb (RM(Nb)ICs) that were also complex concentrated alloys (i.e., RM(Nb)ICs/RCCAs), namely, the alloys TT5, TT6, and TT7, which had the nominal compositions (at.%) Nb-24Ti-18Si-5Al-5B-5Cr-6Ta, Nb-24Ti-18Si-4Al-6B-5Cr-4Sn and Nb-24Ti-17Si-5Al-6B-5Cr-5Hf, respectively. The alloys were compared with B containing and B free RM(Nb)ICs. The macrosegregation of B, Ti, and Si was reduced with the addition, respectively of Hf, Sn or Ta, Sn or Ta, and Hf or Sn. All three alloys had densities less than 7 g/cm3. The alloy TT6 had the highest specific strength in the as cast and heat-treated conditions, which was also higher than that of RCCAs and refractory metal high entropy alloys (RHEAs). The bcc solid solution Nbss and the tetragonal T2 and hexagonal D88 silicides were stable in the alloys TT5 and TT7, whereas in TT6 the stable phases were the A15-Nb3Sn and the T2 and D88 silicides. All three alloys did not pest at 800 °C, where only the scale that was formed on TT5 spalled off. At 1200 °C, the scale of TT5 spalled off, but not the scales of TT6 and TT7. Compared with the B free alloys, the synergy of B with Ta was the least effective regarding oxidation at 800 and 1200 °C. Macrosegregation of solutes, the chemical composition of phases, the hardness of the Nbss and the alloys, and the oxidation of the alloys at 800 and 1200 °C were considered from the perspective of the Niobium Intermetallic Composite Elaboration (NICE) alloy design methodology. Relationships between properties and the parameters VEC, δ, and Δχ of alloy or phase and between parameters were discussed. The trends of parameters and the location of alloys and phases in parameter maps were in agreement with NICE.

| S-EPMC8715753 | biostudies-literature

Properties Comparison of Ti-Al-Si Alloys Produced by Various Metallurgy Methods.

Project description:Melting metallurgy is still the most frequently used and simplest method for the processing of metallic materials. Some of the materials (especially intermetallics) are very difficult to prepare by this method due to the high melting points, poor fluidity, or formation of cracks and pores after casting. This article describes the processing of Ti-Al-Si alloys by arc melting, and shows the microstructure, phase composition, hardness, fracture toughness, and compression tests of these alloys. These results are compared with the same alloys prepared by powder metallurgy by the means of a combination of mechanical alloying and spark plasma sintering. Ti-Al-Si alloys processed by melting metallurgy are characterized by a very coarse structure with central porosity. The phase composition is formed by titanium aluminides and titanium silicides, which are full of cracks. Ti-Al-Si alloys processed by the powder metallurgy route have a relatively homogeneous fine-grained structure with higher hardness. However, these alloys are very brittle. On the other hand, the fracture toughness of arc-melted samples is immeasurable using Palmqvist's method because the crack is stopped by a large area of titanium aluminide matrix.

| S-EPMC6803991 | biostudies-literature

Characterization of Microstructures and Tensile Properties of Recycled Al-Si-Cu-Fe-Mn Alloys with Individual and Combined Addition of Titanium and Cerium.

Project description:Individual and combined addition of Ti and Ce on the recycled Al-Si-Cu-Fe-Mn alloy was conducted. The microstructures and tensile properties of these fabricated alloys were investigated. In the case of Ti or Ce which was individually added, the added amount was ranging from 0.03?wt.% to 0.09?wt.%. The combined addition of Ti and Ce was set at the ratios of 1?:?1, 1?:?3, and 3?:?1 with a total amount of 0.12?wt.%. Microstructures and phases of these alloys were investigated by using an optical microscope, X-ray diffraction testing, and SEM coupled with EDS. The morphologies of these alloys were quantified by analyzing the SDAS value, length of secondary phases, and phases' distribution uniformity. Tensile testing was carried out for understanding the strengthen effect of the modification process. Results show that the addition of Ce was favorable to the strength and % elongation because the coarse needle-like phase and the polyhedral phase were effectively refined. Their SDAS values and distribution factor were remarkably declined with the increase of the Ce level. The Ti addition could also refine the secondary phases and SDAS values. But its effect was not as prominent as the addition of Ce. Combined addition of Ti and Ce elements at the ratio of 1?:?3 resulted in the samples reaching maximum comprehensive tensile properties. In this case, the short needle-like phase was uniformly distributed in the microstructure. Few polyhedral phases could be found in the Al-Si-Cu-Fe-Mn matrix. The strengthening of these fabricated materials was due to the grain refinement for ?-Al and modification for coarse secondary phases. In addition, distribution uniformity of secondary phases was also changed by their modification effects.

| S-EPMC6311731 | biostudies-literature

Microstructure and Tensile Behavior of Laser Arc Hybrid Welded Dissimilar Al and Ti Alloys.

Project description:Fiber laser-cold metal transfer arc hybrid welding was developed to welding-braze dissimilar Al and Ti alloys in butt configuration. Microstructure, interface properties, tensile behavior, and their relationships were investigated in detail. The results show the cross-weld tensile strength of the joints is up to 213 MPa, 95.5% of same Al weld. The optimal range of heat input for accepted joints was obtained as 83-98 J·mm-1. Within this range, the joint is stronger than 200 MPa and fractures in weld metal, or else, it becomes weaker and fractures at the intermetallic compounds (IMCs) layer. The IMCs layer of an accepted joint is usually thin and continuous, which is about 1μm-thick and only consists of TiAl₂ due to fast solidification rate. However, the IMCs layer at the top corner of fusion zone/Ti substrate is easily thickened with increasing heat input. This thickened IMCs layer consists of a wide TiAl₃ layer close to FZ and a thin TiAl₂ layer close to Ti substrate. Furthermore, both bead shape formation and interface growth were discussed by laser-arc interaction and melt flow. Tensile behavior was summarized by interface properties.

| S-EPMC5453262 | biostudies-other

Effect of Rare Earth Metals on the Microstructure of Al-Si Based Alloys.

Project description:The present study was performed on A356 alloy [Al-7 wt %Si 0.0.35 wt %Mg]. To that La and Ce were added individually or combined up to 1.5 wt % each. The results show that these rare earth elements affect only the alloy melting temperature with no marked change in the temperature of Al-Si eutectic precipitation. Additionally, rare earth metals have no modification effect up to 1.5 wt %. In addition, La and Ce tend to react with Sr leading to modification degradation. In order to achieve noticeable modification of eutectic Si particles, the concentration of rare earth metals should exceed 1.5 wt %, which simultaneously results in the precipitation of a fairly large volume fraction of insoluble intermetallics. The precipitation of these complex intermetallics is expected to have a negative effect on the alloy performance.

| S-EPMC5456565 | biostudies-other

Effect of Ni/Si Mass Ratio and Thermomechanical Treatment on the Microstructure and Properties of Cu-Ni-Si Alloys.

Project description:The effect of the Ni/Si mass ratio and combined thermomechanical treatment on the microstructure and properties of ternary Cu-Ni-Si alloys is discussed systematically. The Cu-Ni-Si alloy with a Ni/Si mass ratio of 4-5 showed good comprehensive properties. Precipitates with disc-like shapes were confirmed as the Ni2Si phase with orthorhombic structure through transmission electron microscopy, high-resolution transmission electron microscopy, and 3D atom probe characterization. After the appropriate thermomechanical treatment, the studied alloy with a Ni/Si mass ratio of 4.2 exhibited excellent mechanical properties: a hardness of 290 HV, tensile strength of 855 MPa, yield strength of 782 MPa, and elongation of 4.5%. Compared with other approaches, the thermomechanical treatment increased the hardness and strength without sacrificing electrical conductivity. Theoretical calculations indicated that the high strength was primarily attributed to the Orowan precipitation strengthening and secondarily ascribed to the work hardening, which were highly consistent with the experimental results. The appropriate Ni/Si mass ratio with a low content of Ni and Si atoms shows high strength and excellent electrical conductivity through combined thermomechanical treatment. This work provides a guideline for the design and preparation of multicomponent Cu-Ni-Si-X alloys with ultrahigh strength and excellent electrical conductivity.

| S-EPMC6650849 | biostudies-literature

Effects of Complex Modification by Sr-Sb on the Microstructures and Mechanical Properties of Al-18 wt % Mg₂Si-4.5Cu Alloys.

Project description:This research was carried out to investigate the influence of Sr-Sb on the microstructures and mechanical properties of Al-18 wt % Mg₂Si-4.5Cu alloys. After the addition of 0.2 wt % Sr-Sb, the morphologies of primary Mg₂Si transformed from equiaxed dendrite to cube in as-cast alloys and the average size of primary Mg₂Si decreased from ~50 to ~20 μm. The shape of eutectic Mg₂Si changed from Chinese script to short rod. After extrusion and T6 heat treatment, the ultimate tensile strength of modified alloy at room temperature (RT) and 100 °C increased respectively from 229 to 288 MPa, and from 231 to 272 MPa. The elongation-to-failure only slightly improved from 2.9% to 3.8% and from 3.3% to 3.7% at RT and 100 °C, respectively. The tensile fracture surface revealed a transition from brittle fracture to ductile fracture after modifying by 0.2 wt % Sr-Sb.

| S-EPMC5456687 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data