Reactivation of a Retarded Suspension of Ground Granulated Blast-Furnace Slag.

ABSTRACT: An effective retarded suspension of ground granulated blast-furnace slag (GGBFS) needs a strong activator to reactivate the hydration. In this research study, sodium hydroxide (NaOH) as an alkali activator in two different concentrations (30 and 50 wt.%) was used to overcome the retardation and give the hardened GGBFS the reasonable strength. The study was carried out with a mixture of GGBFS, a solution of 1.0 wt.% d-gluconic acid (C₆H12O₇) as a retarder in the mixing water and a methyl cellulose as a stabilizer. The reactivation was executed after seven different periods (up to 28 days) after the system was retarded. The following investigations were performed: slump test, measurement of ultrasonic (US) velocity, compressive strength and gross density, thermogravimetry (TG) and scanning electron microscopy (SEM). The analyses of the hardened samples were carried out seven, 28 and 90 days after the reactivation. The result of the study is an effective reactivation of a retarded suspension. In this case, the activator with 50 wt.% NaOH shows a very high performance. The setting time of the reactivated binders is much longer compared to the reference, but, in the longer term, the compressive strength and the progress of the hydration exceed the performance of the reference.

SUBMITTER: Schneider N

PROVIDER: S-EPMC5456691 | biostudies-other | 2016 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Studying the Hydration of a Retarded Suspension of Ground Granulated Blast-Furnace Slag after Reactivation.

Project description:This article presents a combined use of a retarder (d-gluconic acid) and an alkaline activator (sodium hydroxide) in a binder system based on ground granulated blast-furnace slag. The properties of the retarder are extending the dormant hydration period and suppressing the generation of strength-giving phases. Different retarder concentrations between 0.25 and 1.00 wt.% regulate the intensity and the period of the retardation and also the characteristics of the strength development. The activator concentration of 30 and 50 wt.% regulates the overcoming of the dormant period and thereby the solution of the slag and hence the formation of the hydration products. The research objective is to produce a mineral binder system based on two separate liquid components. The highest concentration of retarder and activator generates the highest compressive strength and mass of hydration products-after 90 days of hydration a compressive strength of more than 50 N/mm². The main phases are calcium silicate hydrate and hydrotalcite. Generally, the combination of retarder and activator shows a high potential in the performance increase of the hydration process.

| S-EPMC5457240 | biostudies-other

Durability of Fibre-Reinforced Calcium Aluminate Cement (CAC)-Ground Granulated Blast Furnace Slag (GGBFS) Blended Mortar after Sulfuric Acid Attack.

Project description:Concrete wastewater infrastructures are important to modern society but are susceptible to sulfuric acid attack when exposed to an aggressive environment. Fibre-reinforced mortar has been adopted as a promising coating and lining material for degraded reinforced concrete structures due to its unique crack control and excellent anti-corrosion ability. This paper aims to evaluate the performance of polyethylene (PE) fibre-reinforced calcium aluminate cement (CAC)-ground granulated blast furnace slag (GGBFS) blended strain-hardening mortar after sulfuric acid immersion, which represented the aggressive sewer environment. Specimens were exposed to 3% sulfuric acid solution for up to 112 days. Visual, physical and mechanical performance such as water absorption ability, sorptivity, compressive and direct tensile strength were evaluated before and after sulfuric acid attack. In addition, micro-structure changes to the samples after sulfuric acid attack were also assessed by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) to further understand the deterioration mechanism. The results show that overall fibre-reinforced calcium aluminate cement (CAC)-based samples performed significantly better than fibre-reinforced ordinary Portland cement (OPC)-based samples as well as mortar samples in sulfuric acid solution in regard to visual observations, penetration depth, direct tensile strength and compressive reduction. Gypsum generation in the cementitious matrix of both CAC and OPC-based systems was the main reason behind the deterioration mechanism after acid attack exposure. Moreover, laboratory sulfuric acid testing has been proven for successfully screening the cementitious material against an acidic environment. This method can be considered to design the service life of concrete wastewater pipes.

| S-EPMC7503559 | biostudies-literature

Predicting compressive strength of high-performance concrete with high volume ground granulated blast-furnace slag replacement using boosting machine learning algorithms.

Project description:Predicting the compressive strength of concrete is a complicated process due to the heterogeneous mixture of concrete and high variable materials. Researchers have predicted the compressive strength of concrete for various mixes using machine learning and deep learning models. In this research, compressive strength of high-performance concrete with high volume ground granulated blast-furnace slag replacement is predicted using boosting machine learning (BML) algorithms, namely, Light Gradient Boosting Machine, CatBoost Regressor, Gradient Boosting Regressor (GBR), Adaboost Regressor, and Extreme Gradient Boosting. In these studies, the BML model's performance is evaluated based on prediction accuracy and prediction error rates, i.e., R2, MSE, RMSE, MAE, RMSLE, and MAPE. Additionally, the BML models were further optimised with Random Search algorithms and compared to BML models with default hyperparameters. Comparing all 5 BML models, the GBR model shows the highest prediction accuracy with R2 of 0.96 and lowest model error with MAE and RMSE of 2.73 and 3.40, respectively for test dataset. In conclusion, the GBR model are the best performing BML for predicting the compressive strength of concrete with the highest prediction accuracy, and lowest modelling error.

| S-EPMC9184605 | biostudies-literature

Properties of Foamed Mortar Prepared with Granulated Blast-Furnace Slag.

Project description:Foamed mortar with a density of 1300 kg/m³ was prepared. In the initial laboratory trials, water-to-cement (w/c) ratios ranging from 0.54 to 0.64 were tested to determine the optimal value for foamed mortar corresponding to the highest compressive strength without compromising its fresh state properties. With the obtained optimal w/c ratio of 0.56, two types of foamed mortar were prepared, namely cement-foamed mortar (CFM) and slag-foamed mortar (SFM, 50% cement was replaced by slag weight). Four different curing conditions were adopted for both types of foamed mortar to assess their compressive strength, ultrasonic pulse velocity (UPV) and thermal insulation performance. The test results indicated that utilizing 50% of slag as cement replacement in the production of foamed mortar improved the compressive strength, UPV and thermal insulation properties. Additionally, the initial water curing of seven days gained higher compressive strength and increased UPV values as compared to the air cured and natural weather curing samples. However, this positive effect was more pronounced in the case of compressive strength than in the UPV and thermal conductivity of foamed mortar.

| S-EPMC5455276 | biostudies-other

Strength Development and Hydration Behavior of Self-Activation of Commercial Ground Granulated Blast-Furnace Slag Mixed with Purified Water.

Project description:In this study, ground granulated blast-furnace slag (GGBFS) samples from Singapore, Korea, and the United Arab Emirates were hydrated with purified water to estimate the cementing capabilities without activators. Raw GGBFS samples and hardened pastes were characterized to provide rational explanations for the strengths and hydration products. The slag characteristics that influenced the best strength of raw GGBFS were identified. Although it is widely recognized that GGBFS alone generally shows little cementing capability when hydrated with water, the GGBFSs examined in this study demonstrated various strength developments and hydration behaviors; one of the GGBFS samples even produced a high strength comparable to that of alkali- or Ca(OH)₂-activated GGBFS. In particular, as the GGBFS exhibited a greater number of favorable slag characteristics for hydraulic reactivity, it produced more C-S-H and ettringite. The results demonstrated a reasonable potential for commercial GGBFS with calcium sulfates to function as an independent cementitious binder without activators.

| S-EPMC5456657 | biostudies-other

Effect of the Formation of Amorphous Networks on the Structure and Hydration Characteristics of Granulated Blast Furnace Slag.

Project description:The slag obtained in the process of pig iron smelting has been widely used, but the variational hydration activity always is a significant factor affecting its quality. In this experiment, the laboratory simulated slag was prepared by adjusting the chemical composition and cooling method. The experiment primary characterized the structure and hydration process with different types of slag by using MAS NMR, XRD, compressive strength, ICP, SEM, and hydration heat, then obtained the influence of the composition of the network former S/A (the mass ratio of SiO2 and Al2O3 in chemical composition) and amorphous phase content on its structure and hydration activity. The result shows that lowering the S/A value can reduce the degree of vitreous polymerization in the slag; reducing the S/A value of the slag can make the slag hydration time advance, and consequently, the cumulative exotherm increases, the liquid phase Ca/Si and Al/Si ionic ratio increases, and the hydration product changes from C-S-H gel to C-A-S-H gel, which ultimately leads to an increase in compressive strength. In the high S/A value slag, the formation of the trace crystal phase of gehlenite is beneficial to reduce the degree of polymerization of the amorphous.

| S-EPMC7143658 | biostudies-literature

Using Experimental Statistical Models for Predicting Strength and Deformability of Self-Compacting Concrete with Ground Blast-Furnace Slag.

Project description:Ground blast-furnace slag is one of the waste products available in Ukraine and other countries. It is obtained at metallurgical enterprises in huge quantities and can be efficiently used for concrete production. The article is devoted to obtaining experimental-statistical models of the influence of technological factors that determine the composition of self-compacting concrete (SCC) based on ground blast-furnace slag and polycarboxylate superplasticizer on compressive strength, tensile strength, prismatic strength, elastic modulus and crack resistance. Analysis of the investigated factors' influence on the specified SCC properties is carried out and positive influence of blast-furnace slag and superplasticizer simultaneous action on durability and deformation characteristics is studied. A design method of SCC composition design using the obtained mathematical models is developed. It allows for the consideration of a set of necessary parameters simultaneously. A numerical example is given.

| S-EPMC9228754 | biostudies-literature

Geopolymer Based on Mechanically Activated Air-cooled Blast Furnace Slag.

Project description:An efficient solution to increase the sustainability of building materials is to replace Portland cement with alkali-activated materials (AAM). Precursors for those systems are often based on water-cooled ground granulated blast furnace slags (GGBFS). Quenching of blast furnace slag can be done also by air but in that case, the final product is crystalline and with a very low reactivity. The present study aimed to evaluate the cementitious properties of a mechanically activated (MCA) air-cooled blast furnace slag (ACBFS) used as a precursor in sodium silicate alkali-activated systems. The unreactive ACBFS was processed in a planetary ball mill and its cementing performances were compared with an alkali-activated water-cooled GGBFS. Mixes based on mechanically activated ACBFS reached the 7-days compressive strength of 35 MPa and the 28-days compressive strength 45 MPa. The GGBFS-based samples showed generally higher compressive strength values.

| S-EPMC7085006 | biostudies-literature

Recovery of scandium and neodymium from blast furnace slag using acid baking-water leaching.

Project description:The current study puts the emphasis on developing a pyro-hydrometallurgical process, called acid baking-water leaching, to recover scandium and neodymium from blast furnace slag produced by the ironmaking industry. In this process, the feed is mixed with concentrated sulfuric acid, digested at 200-400 °C, and leached in water at ambient conditions. This process offers several advantages including less acidic waste generation and rapid kinetics. With fundamental investigations into the digestion mechanism, acid to slag mass ratio and baking temperature are determined to have the most significant positive and negative impacts, respectively. At low acid to slag ratio, the silicate bearing phases in the feed do not digest, resulting in low extraction. At 200 °C baking temperature, a hydrated aluminum sulfate ((Al(H2O)6)2(SO4)3(H2O)4.4) phase with weak hydrogen bonds is formed that leaches in water rapidly (<10 min); while at 400 °C, Al2(SO4)3 with strong ionic bonds is formed that leaches at slower kinetics (>4 h). Fundamental investigations into the water leaching process indicate that the diffusion of water through the firm solid product (ash layer) is the rate determining step. We expect the results of this study would help enable valorization of industrial byproducts, in particular ironmaking slag.

| S-EPMC9056533 | biostudies-literature

Properties of Concrete Using Treated Low-Class Recycled Coarse Aggregate and Blast Furnace Slag Sand.

Project description:Since high quality natural aggregates are becoming scarce, it is important that industrial recycled products and by-products are used as aggregates for concrete. In Japan, the use of recycled aggregate (RG) is encouraged. Since, strength and durability of recycled aggregate concrete is lower than that of normal aggregate concrete, the use of recycled aggregate has not been significant. In order to improve physical properties of concrete using recycled coarse aggregate, blast furnace slag sand has been proposed. Recently, blast furnace slag sand is expected to improve durability, freezing, and thawing damage of concrete in Japan. Properties of fresh and hardened concrete bleeding, compressive strength, and resistance to freezing and thawing which are caused by the rapid freezing and thawing test using liquid nitrogen is a high loader than the JIS A 1148 A method that were investigated. As a result, concrete using treated low-class recycled coarse aggregate and 50% or 30% replacement of crushed sand with blast furnace slag sand showed the best results, in terms of bleeding, resistance to freezing and thawing.

| S-EPMC7078881 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data