Influence of Specimen Preparation and Test Methods on the Flexural Strength Results of Monolithic Zirconia Materials.

ABSTRACT: The aim of this work was to evaluate the influence of specimen preparation and test method on the flexural strength results of monolithic zirconia. Different monolithic zirconia materials (Ceramill Zolid (Amann Girrbach, Koblach, Austria), Zenostar ZrTranslucent (Wieland Dental, Pforzheim, Germany), and DD Bio zx² (Dental Direkt, Spenge, Germany)) were tested with three different methods: 3-point, 4-point, and biaxial flexural strength. Additionally, different specimen preparation methods were applied: either dry polishing before sintering or wet polishing after sintering. Each subgroup included 40 specimens. The surface roughness was assessed using scanning electron microscopy (SEM) and a profilometer whereas monoclinic phase transformation was investigated with X-ray diffraction. The data were analyzed using a three-way Analysis of Variance (ANOVA) with respect to the three factors: zirconia, specimen preparation, and test method. One-way ANOVA was conducted for the test method and zirconia factors within the combination of two other factors. A 2-parameter Weibull distribution assumption was applied to analyze the reliability under different testing conditions. In general, values measured using the 4-point test method presented the lowest flexural strength values. The flexural strength findings can be grouped in the following order: 4-point < 3-point < biaxial. Specimens prepared after sintering showed significantly higher flexural strength values than prepared before sintering. The Weibull moduli ranged from 5.1 to 16.5. Specimens polished before sintering showed higher surface roughness values than specimens polished after sintering. In contrast, no strong impact of the polishing procedures on the monoclinic surface layer was observed. No impact of zirconia material on flexural strength was found. The test method and the preparation method significantly influenced the flexural strength values.

SUBMITTER: Schatz C

PROVIDER: S-EPMC5456702 | biostudies-other | 2016 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:One therapeutical alternative in the treatment of functional disorders is the use of printed oral splints. The mechanical properties of these materials are highly essential to their clinical effectiveness, and their performance may vary depending on factors such as cleaning, post-polymerization, or their orientation during construction. The objective of this in vitro investigation is to evaluate the effectiveness of the selected materials in terms of their biaxial flexural strength in relation to the criteria listed above. Splint materials were used in the printing of 720 discs. The printing process was carried out in different orientations in relation to the building platform. Either an automatic or manual cleaning process was performed on the samples. For post-polymerization, either an LED or Xenon light was utilized. A piston-on-three-ball test was used to measure the biaxial flexural strength (BFS) of the materials after they were stored in water for either 24 h or 60 days. The homogeneity of the data was controlled by employing the Levene method, and the differences between the groups were analyzed using the ANOVA and Bonferroni methods. After being stored for twenty-four hours, the mean BFS ranged anywhere from 79 MPa to 157 MPa. Following a period of sixty hours, the BFS exhibited a substantial drop and revealed values that ranged from 72 to 127 MPa. There was no significant difference that could be identified between the materials or between the various cleaning processes. The results of post-polymerization showed that the LED light produced higher means than the Xenon light did. In terms of position, the mean values varied greatly, with 0°'s mean value being 101 MPa, 45°'s mean value being 102 MPa, and 90°'s mean value being 115 MPa. The use of a build orientation of 90° and post-polymerization with LED light resulted in significantly increased biaxial flexural strength. According to this study, this design should be implemented in order to ensure that splint materials have the highest possible strength.

Dataset Information

Influence of Specimen Preparation and Test Methods on the Flexural Strength Results of Monolithic Zirconia Materials.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets