Polyamide Fiber Reinforced Shotcrete for Tunnel Application.
Ontology highlight
ABSTRACT:
SUBMITTER: Jeon JK
PROVIDER: S-EPMC5456736 | biostudies-other | 2016 Mar
REPOSITORIES: biostudies-other
Similar Datasets
Project description:This study developed a macro-sized polyamide (PA) fiber for concrete reinforcement and investigated the influence of the PA fiber on flexural responses in accordance with ASTM standards. PA fibers are advantageous compared to steel fibers that are corrosive and gravitated. The macro-sized PA fiber significantly improved concrete ductility and toughness. Unlike steel fibers, the PA fibers produced two peak bending strengths. The first-peaks occurred near 0.005 mm of deflection and decreased up to 0.5 mm of deflection. Then the bending strength increased up to second-peaks until the deflections reached between 1.0 and 1.5 mm. The averaged flexural responses revealed that PA fiber content did not significantly influence flexural responses before L/600, but had significant influence thereafter. Toughness performance levels were also determined, and the results indicated more than Level II at L/600 and Level IV at others.
| S-EPMC5456437 | biostudies-other
Project description:Plastic worm wheel is widely used in the vehicle manufacturing field because it is favorable for weight lightening, vibration and noise reduction, as well as corrosion resistance. However, it is very difficult for general plastics to secure the mechanical properties that are required for vehicle gears. If the plastic resin is reinforced by glass fiber in the fabrication process of plastic worm wheel, it is possible to achieve the mechanical properties of metallic material levels. In this study, the mechanical characteristic analysis of the glass-reinforced plastic worm wheel, according to the contents of glass fiber, is performed by analytic and experimental methods. In the case of the glass fiber-reinforced resin, the orientation and contents of glass fibers can influence the mechanical properties. For the characteristic prediction of plastic worm wheel, computer-aided engineering (CAE) analysis processes such as structural and injection molding analysis were executed with the polyamide resin reinforcement glass fiber (25 wt %, 50 wt %). The injection mold for fabricating the prototype plastic worm wheel was designed and made to reflect the CAE analysis results. Finally, the durability of prototype plastic worm wheel fabricated by the injection molding process was evaluated by the experimental method and the characteristics according to the glass fiber contents.
| S-EPMC5452519 | biostudies-other
Project description:Melt-spun surface structured fiber could be a large-scale versatile platform for materials with advanced surface function and local properties. Fibers with distinct surface and bulk structures are developed by tailoring the viscosity ratio and blend ratio of polymer component using the melt-spinning method. Spherical bulge and fibril groove structured fibers are obtained in different viscosity ratio and blend ratio systems. The interfacial bonding between fiber and matrix is improved due to the mechanical interlocking between the structured surface and matrix. The low-viscosity second phase stays as a spherical droplet even in high content. The second phase in matched- and high-viscosity ratio cases is deformed into fibril like droplet which causes an in-situ fibration of the second phase in polymer blend fiber with an enhanced mechanical property. This method provides a simple route to developing polymer materials with surface structure and appropriate mechanical properties to apply in textile and polymer fiber-reinforced composite materials.
| S-EPMC7579542 | biostudies-literature
Project description:Fiber structures play a major role for the function of fiber-reinforced materials such as biological tissue. An objective classification of the fiber orientations into fiber families is crucial to understand its mechanical properties. We introduce the Fiber Image Network Evaluation Algorithm (FINE algorithm) to classify and quantify the number of fiber families in scientific images. Each fiber family is characterized by an amplitude, a mean orientation, and a dispersion. A new alignment index giving the averaged fraction of aligned fibers is defined. The FINE algorithm is validated by realistic grayscale Monte-Carlo fiber images. We apply the algorithm to an in-vivo depth scan of second harmonic generation images of dermal collagen in human skin. The derived alignment index exhibits a crossover at a critical depth where two fiber families with a perpendicular orientation around the main tension line arise. This strongly suggests the presence of a transition from the papillary to the reticular dermis. Hence, the FINE algorithm provides a valuable tool for a reliable classification and a meaningful interpretation of in-vivo collagen fiber networks and general fiber reinforced materials.
| S-EPMC7331592 | biostudies-literature
Project description:In this study, an experimental investigation was conducted on the mechanical properties of lightweight aggregate concrete (LWAC) with different chopped fibers, including basalt fiber (BF) and polyacrylonitrile fiber (PANF). The LWAC performance was studied in regard to compressive strength, splitting tensile strength and shear strength at age of 28 days. In addition, the oven-dried density and water absorption were measured as well to confirm whether the specimens match the requirement of standard. In total, seven different mixture groups were designed and approximately 104 LWAC samples were tested. The test results showed that the oven-dried densities of the LWAC mixtures were in range of 1.819-1.844 t/m3 which satisfied the definition of LWAC by Chinese Standard. Additionally, water absorption decreased with the increasing of fiber content. The development tendency of the specific strength of LWAC was the same as that of the cube compressive strength. The addition of fibers had a significant effect on reducing water absorption. Adding BF and PANF into concrete had a relatively slight impact on the compressive strength but had an obvious effect on splitting tensile strength, flexural strength and shear strength enhancement, respectively. In that regard, a 1.5% fiber volume fraction of BF and PANF showed the maximum increase in strength. The use of BF and PANF could change the failure morphologies of splitting tensile and flexural destruction but almost had slight impact on the shear failure morphology. The strength enhancement parameter ? was proposed to quantify the improvement effect of fibers on cube compressive strength, splitting tensile strength, flexural strength and shear strength, respectively. And the calculation results showed good agreement with test value.
| S-EPMC7178649 | biostudies-literature
Project description:The tensile performance of fiber-reinforced cementitious composite (FRCC) after first matrix cracking is characterized by a tensile stress-crack width relationship called the bridging law. The bridging law can be obtained by an integral calculus of forces carried by individual bridging fibers considering the effect of the fiber inclination angle. The main objective of this study is to investigate experimentally and evaluate the pullout behavior of a single aramid fiber, which is made with a bundling of original yarns of aramid fiber. The bundled aramid fiber has a nonsmooth surface, and it is expected to have good bond performance with the matrix. The test variables in the pullout test are the thickness of the matrix and the inclined angle of the fiber. From the test results, the pullout load-slip curves showed that the load increases lineally until maximum load, after which it decreases gradually. The maximum pullout load and slip at the maximum load increase as the embedded length of the fiber becomes larger. The pullout load-crack width relationship is modeled by a bilinear model, and the bridging law is calculated. The calculated result shows good agreement with the experimental curves obtained by the uniaxial tension test of aramid-FRCC.
| S-EPMC7179034 | biostudies-literature
Project description:BackgroundNano-hydroxyapatite/polyamide 66 (nHA/PA66) is a composite used widely in the repair of bone defects. However, this material is insufficient bioactivity. In contrast, D-RADA16-RGD self-assembling peptide (D-RADA16-RGD sequence containing all D-amino acids is Ac-RADARADARADARADARGDS-CONH2) shows admirable bioactivity for both cell culture and bone regeneration. Here, we describe the fabrication of a favorable biomaterial material (nHA/PA66/D-RADA16-RGD).MethodsProteinase K and circular dichroism spectroscopy were employed to test the stability and secondary structural properties of peptide D-RADA16-RGD respectively. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the surface of these materials. Confocal laser scanning (CLS), cell counting kit-8 tests (CCK-8), alizarin red S staining, cell immunofluorescence analysis and Western blotting were involved in vitro. Also biosafety and bioactivity of them have been evaluated in vivo.ResultsProteinase K and circular dichroism spectroscopy demonstrated that D-RADA16-RGD in nHA/PA66 was able to form stable-sheet secondary structure. SEM and TEM showed that the D-RADA16-RGD material was 7-33 nm in width and 130-600 nm in length, and the interwoven pore size ranged from 40 to 200 nm. CLS suggests that cells in nHA/PA66/D-RADA16-RGD group were linked to adjacent cells with more actin filaments. CCK-8 analysis showed that nHA/PA66/D-RADA16-RGD revealed good biocompatibility. The results of Alizarin-red S staining and Western blotting as well as vivo osteogenesis suggest nHA/PA66/D-RADA16-RGD exhibits better bioactivity.ConclusionThis study demonstrates that our nHA/PA66/D-RADA16-RGD composite exhibits reasonable mechanical properties, biocompatibility and bioactivity with promotion of bone formation.
| S-EPMC6439056 | biostudies-literature
Project description:Metal oxide nanoparticle -reinforced polymers have received considerable attention due to their favorable mechanical properties compared to neat materials. However, the effect of nanoscale reinforcements of the interface on the composites' mechanical properties has not been investigated in-depth to reach their optimal performance in structural applications. Aiming at revealing the effect of synergistic interfacial interactions on the mechanical properties of polymer composites, using a nanoscale reinforcement, herein, a series of zinc oxide nanorod-reinforced polyamide-imide (PAI)/ZnO) composites were fabricated and their mechanical properties and viscoelastic responses were investigated. The composite prepared by reinforcing them with 5 wt % ZnO nanorods resulted in improved elastic modulus, stiffness, and hardness values by 32%, 14% and 35%, respectively, compared to neat polymer thin films. The viscoelastic dynamics of the composites revealed that there was an 11% increase in elastic wave speed in the composite, containing 5 wt % ZnO nanorods, indicating better response to high impacts. Delayed viscoelastic response decreased by 67% spatially and 51% temporally, with a corresponding decrease in the creep rate, for the 5 wt % ZnO nanorod- containing composite, evidencing its potential applicability in high strength lightweight structures. The improved mechanical properties with respect to the filler concentration evidence strong particle-polymer interfacial interactions, creating "chain-bound" clusters, providing clear reinforcement and polymer chain mobility retardation. However, hypervelocity impact testing revealed that all the composites' films were vulnerable to hypervelocity impact, but the spallation region of the composite films reinforced with 2.5 wt % and 5 wt % ZnO nanorods exhibited a cellular-like matrix with shock-induced voids compared to a rather hardened spallation region with cracks in the neat film.
| S-EPMC10055968 | biostudies-literature
Project description:In this paper, shear strength of fiber reinforced recycled concrete was investigated. A Self Consolidated Concrete (SCC) matrix with 100% coarse recycled aggregate and different types of fibers were used in the study. Steel (3D and 5D), synthetic and hybrid fibers with a volume fraction of 0.75% were added to the concrete matrix to prepare eight beams. In addition, two beams were cast without fibers as control specimens. All beams were prepared without shear reinforcement and were tested to evaluate concrete contribution to the shear capacity. In addition, optical images were captured to allow for full-field displacement measurements using Digital Image Correlation (DIC). The results showed about 23.44-64.48% improvement in the average concrete shear capacity for fiber-reinforced beams when compared to that of the control specimens. The percentage improvement was affected by fiber type and the steel fiber beams achieved the best performance. The addition of the fiber delayed the crack initiation and improved the post-cracking and ductile behavior of all beams. Moreover, the experimental results were compared to those predicted by codes and proposed equations found in the literature for concrete strength with and without fibers.
| S-EPMC7560474 | biostudies-literature
Project description:Silkworm silk, which is obtained from domesticated Bombyx mori (B. mori), can be produced in a large scale. However, the mechanical properties of silkworm silk are inferior to its counterpart, spider dragline silk. Therefore, researchers are continuously exploring approaches to reinforce silkworm silk. Herein, we report a facile and scalable hot stretching process to reinforce natural silk fibers obtained from silkworm cocoons. Experimental results show that the obtained hot-stretched silk fibers (HSSFs) retain the chemical components of the original silk fibers while being endowed with increased β-sheet nanocrystal content and crystalline orientation, leading to enhanced mechanical properties. Significantly, the average modulus of the HSSFs reaches 21.6 ± 2.8 GPa, which is about twice that of pristine silkworm silk fibers (11.0 ± 1.7 GPa). Besides, the tensile strength of the HSSFs reaches 0.77 ± 0.13 GPa, which is also obviously higher than that of the pristine silk (0.56 ± 0.08 GPa). The results show that the hot stretching treatment is effective and efficient for producing superstiff, strong, and tough silkworm silk fibers. We anticipate this approach may be also effective for reinforcing other natural or artificial polymer fibers or films containing abundant hydrogen bonds.
| S-EPMC8992573 | biostudies-literature