Enhanced Visible Transmittance of Thermochromic VO₂ Thin Films by SiO₂ Passivation Layer and Their Optical Characterization.

ABSTRACT: This paper presents the preparation of high-quality vanadium dioxide (VO₂) thermochromic thin films with enhanced visible transmittance (Tvis) via radio frequency (RF) sputtering and plasma enhanced chemical vapor deposition (PECVD). VO₂ thin films with high Tvis and excellent optical switching efficiency (Eos) were successfully prepared by employing SiO₂ as a passivation layer. After SiO₂ deposition, the roughness of the films was decreased 2-fold and a denser structure was formed. These morphological changes corresponded to the results of optical characterization including the haze, reflectance and absorption spectra. In spite of SiO₂ coating, the phase transition temperature (Tc) of the prepared films was not affected. Compared with pristine VO₂, the total layer thickness after SiO₂ coating was 160 nm, which is an increase of 80 nm. Despite the thickness change, the VO₂ thin films showed a higher Tvis value (λ 650 nm, 58%) compared with the pristine samples (λ 650 nm, 43%). This enhancement of Tvis while maintaining high Eos is meaningful for VO₂-based smart window applications.

SUBMITTER: Yu JH

PROVIDER: S-EPMC5456844 | biostudies-other | 2016 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Fenestration elements that enable spectrally selective dynamic modulation of the near-infrared region of the electromagnetic spectrum are of great interest as a means of decreasing the energy consumption of buildings by adjusting solar heat gain in response to external temperature. The binary vanadium oxide VO2 exhibits a near-room-temperature insulator-metal electronic transition accompanied by a dramatic modulation of the near-infrared transmittance. The low-temperature insulating phase is infrared transparent but blocks infrared transmission upon metallization. There is considerable interest in harnessing the thermochromic modulation afforded by VO2 in nanocomposite thin films. However, to prepare a viable thermochromic film, the visible-light transmittance must be maintained as high as possible while maximizing thermochromic modulation in the near-infrared region of the electromagnetic spectrum, which necessitates the development of high-crystalline-quality VO2 nanocrystals of the optimal particle size embedded within the appropriate host matrix and refractive index matched to the host medium. Here, we demonstrate the preparation of acrylate-based nanocomposite thin films with varying sizes of embedded VO2 nanoparticles. The observed strong size dependence of visible-light transmittance and near-infrared modulation is explicable on the basis of optical simulations. In this article, we elucidate multiple scattering and absorption mechanisms, including Mie scattering, temperature-/phase-variant refractive-index mismatch between VO2 nanocrystals and the encapsulating matrix, and the appearance of a surface plasmon resonance using temperature-variant absorptance and diffuse transmittance spectroscopy measurements performed as a function of particle loading for the different sizes of VO2 nanocrystals. Nanocrystals with dimensions of 44 ± 30 nm show up to >32% near-infrared energy modulation across the near-infrared region of the electromagnetic spectrum while maintaining high visible-light transmission. The results presented here, providing mechanistic elucidation of the size dependence of the different scattering mechanisms, underscore the importance of nanocrystallite dimensions, refractive-index matching, and individualized dispersion of particles within the host matrix for the preparation of viable thermochromic thin films mitigating Mie scattering and differential refractive-index scattering.

Project description:Over the years, vanadium dioxide, (VO2(M1)), has been extensively utilised to fabricate thermochromic thin films with the focus on using external stimuli, such as heat, to modulate the visible through near-infrared transmittance for energy efficiency of buildings and indoor comfort. It is thus valuable to extend the study of thermochromic materials into the mid-infrared (MIR) wavelengths for applications such as smart radiative devices. On top of this, there are numerous challenges with synthesising pure VO2 (M1) thin films, as most fabrication techniques require the post-annealing of a deposited thin film to convert amorphous VO2 into a crystalline phase. Here, we present a direct method to fabricate thicker VO2(M1) thin films onto hot silica substrates (at substrate temperatures of 400 °C and 700 °C) from vanadium pentoxide (V2O5) precursor material. A high repetition rate (10 kHz) femtosecond laser is used to deposit the V2O5 leading to the formation of VO2 (M1) without any post-annealing steps. Surface morphology, structural properties, and UV-visible optical properties, including optical band gap and complex refractive index, as a function of the substrate temperature, were studied and reported below. The transmission electron microscopic (TEM) and X-ray diffraction studies confirm that VO2 (M1) thin films deposited at 700 °C are dominated by a highly texturized polycrystalline monoclinic crystalline structure. The thermochromic characteristics in the mid-infrared (MIR) at a wavelength range of 2.5-5.0 μm are presented using temperature-dependent transmittance measurements. The first-order phase transition from metal-to-semiconductor and the hysteresis bandwidth of the transition were confirmed to be 64.4 °C and 12.6 °C respectively, for a sample fabricated at 700 °C. Thermo-optical emissivity properties indicate that these VO2 (M1) thin films fabricated with femtosecond laser deposition have strong potential for both radiative thermal management or control via active energy-saving windows for buildings, and satellites and spacecraft.

Dataset Information

Enhanced Visible Transmittance of Thermochromic VO₂ Thin Films by SiO₂ Passivation Layer and Their Optical Characterization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets