Rolling Contact Fatigue Performances of Carburized and High-C Nanostructured Bainitic Steels.
Ontology highlight
ABSTRACT:
SUBMITTER: Wang Y
PROVIDER: S-EPMC5456959 | biostudies-other | 2016 Nov
REPOSITORIES: biostudies-other
Similar Datasets
Project description:The recently developed nanobainitic steels show high strength as well as high ductility. Although this combination seems to be promising for fatigue design, fatigue properties of nanostructured bainitic steels are often surprisingly low. To improve the fatigue behavior, an understanding of the correlation between the nanobainitic microstructure and the fatigue limit is fundamental. Therefore, our hypothesis to predict the fatigue limit was that the main function of the microstructure is not necessarily totally avoiding the initiation of a fatigue crack, but the microstructure has to increase the ability to decelerate or to stop a growing fatigue crack. Thus, the key to understanding the fatigue behavior of nanostructured bainite is to understand the role of the microstructural features that could act as barriers for growing fatigue cracks. To prove this hypothesis, we carried out fatigue tests, crack growth experiments, and correlated these results to the size of microstructural features gained from microstructural analysis by light optical microscope and EBSD-measurements. Finally, we were able to identify microstructural features that influence the fatigue crack growth and the fatigue limit of nanostructured bainitic steels.
| S-EPMC5456631 | biostudies-other
Project description:The formation of white etching cracks (WECs) in steel rolling element bearings can lead to the premature rolling contact fatigue (RCF) failure mode called white structure flaking. Driving mechanisms are still debated but are proposed to be combinations of mechanical, tribochemical and electrical effects. A number of studies have been conducted to record and map WECs in RCF-tested samples and bearings failed from the field. For the first time, this study uses serial sectioning metallography techniques on non-hydrogen charged test samples over a range of test durations to capture the evolution of WEC formation from their initiation to final flaking. Clear evidence for subsurface initiation at non-metallic inclusions was observed at the early stages of WEC formation, and with increasing test duration the propagation of these cracks from the subsurface region to the contact surface eventually causing flaking. In addition, an increase in the amount of associated microstructural changes adjacent to the cracks is observed, this being indicative of the crack being a prerequisite of the microstructural alteration.
| S-EPMC6951819 | biostudies-literature
Project description:Steels are heavily used in infrastructure and the transportation industry, and enhancing their fatigue resistance is a major challenge in materials engineering. In this study, by introducing a gradient microstructure into 304 austenitic steel, which is one of the most widely used types of stainless steel, we show that a strength gradient substantially enhances the fatigue life of the material. Pre-notched samples with negative strength gradients in front of the notch's tip endure many more fatigue cycles than do samples with positive strength gradients during the crack initiation stage, and samples with either type of gradient perform better than do gradient-free samples with the same average yield strength. However, as a crack grows, samples with positive strength gradients exhibit better resistance to fatigue crack propagation than do samples with negative gradients or no gradient. This study demonstrates a simple and promising strategy for using gradient structures to enhance the fatigue resistance of materials and complements related studies of strength and ductility.
| S-EPMC4764920 | biostudies-literature
Project description:In this paper, analytical results are compared for the newly developed steels, Fe-Mn-Al-C (X105) and Fe-Mn-Al-Nb-Ti-C (X98), after being hot-rolled and also after undergoing thermomechanical treatment in a Gleeble simulator. These steels have a relatively low density (~6.68 g/cm3) and a content of approx. 11% aluminum. The multistage compression of axisymmetric samples constituting a simulation of the real technological process and hot-rolling performed on a semi-industrial line were carried out using three cooling variants: in water, in air, and after isothermal heating and cooling in water. The temperature at the end of the thermomechanical treatment for all variants was 850 °C. On the basis of detailed structural studies, it was found that the main mechanism for removing the effects of the strain hardening that occurred during the four-stage compression involved the dynamic recrystallization occurring in the first and second stages, the hot formability and dynamic recovery in successive stages of deformation, and the static and/or metadynamic recrystallization that occurred at intervals between individual deformations, as well as after the last deformation during isothermal heating. Analysis of the phase composition and structure allowed us to conclude that the tested steels have an austenitic-ferritic structure with carbide precipitates. Research using scanning and transmission electron microscopy identified ?-(Fe, Mn)3AlC and M7C3 carbides in both the analyzed steels. In addition, complex carbides based on Nb and Ti were identified in X98 steel; (Ti, Nb)C carbides occurred in the entire volume of the material. Slow cooling after thermomechanical treatment influenced the formation of larger ?-carbides at the border of the austenite and ferrite grains than in the case of rapid cooling. The size and morphology of the carbides found in the examined steels was varied. Back-scattered electron diffraction studies showed that wide-angle boundaries dominated in these steels.
| S-EPMC7041428 | biostudies-literature
Project description:The tendencies of development within the field of engineering materials show a persistent trend towards the increase of strength and toughness. This pressure is particularly pronounced in the field of steels, since they compete with light alloys and composite materials in many applications. The improvement of steels' mechanical properties is sought to be achieved with the formation of exceptionally fine microstructures ranging well into the nanoscale, which enable a substantial increase in strength without being detrimental to toughness. The preferred route by which such a structure can be produced is not by applying the external plastic deformation, but by controlling the phase transformation from austenite into ferrite at low temperatures. The formation of bainite in steels at temperatures lower than about 200 °C enables the obtainment of the bulk nanostructured materials purely by heat treatment. This offers the advantages of high productivity, as well as few constraints in regard to the shape and size of the workpiece when compared with other methods for the production of nanostructured metals. The development of novel bainitic steels was based on high Si or high Al alloys. These groups of steels distinguish a very fine microstructure, comprised predominantly of bainitic ferrite plates, and a small fraction of retained austenite, as well as carbides. The very fine structure, within which the thickness of individual bainitic ferrite plates can be as thin as 5 nm, is obtained purely by quenching and natural ageing, without the use of isothermal transformation, which is characteristic for most bainitic steels. By virtue of their fine structure and low retained austenite content, this group of steels can develop a very high hardness of up to 65 HRC, while retaining a considerable level of impact toughness. The mechanical properties were evaluated by hardness measurements, impact testing of notched and unnotched specimens, as well as compression and tensile tests. Additionally, the steels' microstructures were characterised using light microscopy, field emission scanning electron microscopy (FESEM) and high-resolution transmission electron microscopy (HRTEM). The obtained results confirmed that the strong refinement of the microstructural elements in the steels results in a combination of extremely high strength and very good toughness.
| S-EPMC7085109 | biostudies-literature
Project description: Not available
| S-EPMC10532896 | biostudies-literature
Project description:Architected materials can achieve impressive shape-changing capabilities according to how their microarchitecture is engineered. Here we introduce an approach for dramatically advancing such capabilities by utilizing wrapped flexure straps to guide the rolling motions of tightly packed micro-cams that constitute the material's microarchitecture. This approach enables high shape-morphing versatility and extreme ranges of deformation without accruing appreciable increases in strain energy or internal stress. Two-dimensional and three-dimensional macroscale prototypes are demonstrated, and the analytical theory necessary to design the proposed materials is provided and packaged as a software tool. An approach that combines two-photon stereolithography and scanning holographic optical tweezers is demonstrated to enable the fabrication of the proposed materials at their intended microscale.
| S-EPMC6214902 | biostudies-literature
Project description:Passive air samplers (PASs) have been used for mapping gaseous mercury concentration in extensive areas. In this work, an easy-to-use and -prepare gold nanoparticle (NP)-based PAS has been investigated. The PAS is constituted of a microfibrous quartz disk filter impregnated of gold NP photo-growth on TiO2 NPs (Au@TiO2) and used as gaseous mercury adsorbing material. The disk was housed in a cylinder glass container and subjected to an axial diffusive sampling. The adsorbed mercury was measured by thermal desorption using a Tekran® instrument. Different amounts of Au@TiO2 (ranging between 4.0 and 4.0 × 10-3 mg) were deposited by drop-casting onto the fibrous substrate and assessed for about 1 year of deployment in outdoor environment with a mercury concentration mean of about 1.24 ± 0.32 ng/m3 in order to optimize the adsorbing layer. PASs showed a linear relation of the adsorbed mercury as a function of time with a rate of 18.5 ± 0.4 pg/day (?1.5% of the gaseous concentration per day). However, only the PAS with 4 mg of Au@TiO2, provided with a surface density of about 3.26 × 10-2 mg/mm2 and 50 ?m thick inside the fibrous quartz, kept stability in working, with a constant sampling rate (SR) (0.0138 ± 0.0005 m3/day) over an outdoor monitoring experimental campaign of about 1 year. On the other hand, higher sampling rates have been found when PASs were deployed for a few days, making these tools also effective for one-day monitoring. Furthermore, these PASs were used and re-used after each thermal desorption to confirm the chance to reuse such structured layers within their samplers, thus supporting the purpose to design inexpensive, compact and portable air pollutant sampling devices, ideal for assessing both personal and environmental exposures. During the whole deployment, PASs were aided by simultaneous Tekran® measurements.
| S-EPMC7660345 | biostudies-literature
Project description:To study the effect of the surface properties on the bending fatigue performance of heavy-duty gear steel, the authors of this paper used the ultrasonic surface rolling process (USRP) to strengthen 20Cr2Ni4A carburized gear steel. USRP is a novel technique in which the ultrasonic technology is incorporated into the concept of conventional deep rolling. In this study, we illustrated how the surface properties and cross-section mechanical property influence the three-point bending fatigue life of the samples before and after USRP treatment. At the same time, the predicted failure probability-stress-number of cycles (P-S-N) curve was drawn, and the fatigue fracture was analysed. The results show that the fatigue limit increased from 651.36 MPa to 918.88 MPa after USRP treatment. The fatigue source is mainly from the sample interior or surface scratches, and the fatigue performance is positively correlated with the results of the material surface roughness, surface residual stress and surface hardness. At the same time, combined with the change in the phase structure, dislocation structure, residual stress and hardness of the cross section of the material, it is found that the USRP process turns the steel into a gradient material with five layers. Finally, the coupling mechanism between the ultrasonic surface strengthening deformation layer and the carburized layer of 20Cr2Ni4A carburized gear steel is presented, and the grain structure distribution diagram of the section of the 20Cr2Ni4A model after surface strengthening treatment was simulated. The mechanism that influenced the fatigue performance after USRP treatment is explained from the perspectives of the surface and cross section of the samples.
| S-EPMC8152014 | biostudies-literature
Project description:The antagonism between strength and resistance to hydrogen embrittlement in metallic materials is an intrinsic obstacle to the design of lightweight yet reliable structural components operated in hydrogen-containing environments. Economical and scalable microstructural solutions to this challenge must be found. Here, we introduce a counterintuitive strategy to exploit the typically undesired chemical heterogeneity within the material's microstructure that enables local enhancement of crack resistance and local hydrogen trapping. We use this approach in a manganese-containing high-strength steel and produce a high dispersion of manganese-rich zones within the microstructure. These solute-rich buffer regions allow for local micro-tuning of the phase stability, arresting hydrogen-induced microcracks and thus interrupting the percolation of hydrogen-assisted damage. This results in a superior hydrogen embrittlement resistance (better by a factor of two) without sacrificing the material's strength and ductility. The strategy of exploiting chemical heterogeneities, rather than avoiding them, broadens the horizon for microstructure engineering via advanced thermomechanical processing.
| S-EPMC8610813 | biostudies-literature