Ceramic Ti-B Composites Synthesized by Combustion Followed by High-Temperature Deformation.
Ontology highlight
ABSTRACT:
SUBMITTER: Bazhin PM
PROVIDER: S-EPMC5456993 | biostudies-other | 2016 Dec
REPOSITORIES: biostudies-other
Similar Datasets
Project description:This work reports on the spark plasma sintering (SPS) of self-propagating high-temperature-synthesis (SHS)-derived Ni-W and Ni-W-2wt%hBN (4:1 molar ratio of metals) powders. The synthesis was carried out from a mixture of NiO and WO3 using Mg + C combined reducers through a thermo-kinetic coupling approach. Experiments performed in the thermodynamically optimal area demonstrated the high sensitivity of combustion parameters and product phase composition to the amount of reducers and hBN powder. The powder precursors with and without the addition of hBN were consolidated using SPS at a temperature and pressure of 1300 °C and 50 MPa, respectively, followed by a thorough phase and microstructural characterization of the obtained specimens. SHS-derived powders comprised the nano-sized agglomerates and were characterized by a high sinterability. The specimens of >95% density were subjected to ball-on-plate dry sliding wear tests at a sliding speed of 0.1 ms-1 and a distance of 1000 m utilizing an alumina ball of 10 mm in diameter under a 15 N normal load. The tests were performed at a temperature of 800 °C. A significant improvement in wear behavior was demonstrated for SHS-processed composites in comparison with their counterparts produced via conventional high-energy ball milling technique owing to the phenomena of 'micro-polishing', cyclic 'self-healing' and fatigue. However, the decisive effect of hBN addition in imparting lubrication during an HT wear test was not confirmed.
| S-EPMC8839063 | biostudies-literature
Project description:High-entropy ceramics and their composites display high mechanical strength and attractive high-temperature stabilities. However, properties like strong covalent bond character and low self-diffusion coefficients make them difficult to get sintered, limiting their mass popularity. Here, we present a rapid liquid phase-assisted ultrahigh-temperature sintering strategy and use high-entropy metal diboride/boron carbide composite as a proof of concept. We use a carbon-based heater to fast-heat the composite to around 3000 K, and a small fraction of eutectic liquid was formed at the interface between high-entropy metal diborides and boron carbide. A crystalline dodecaboride intergranular phase was generated upon cooling to ameliorate the adhesion between the components. The as-sintered composite presents a high hardness of 36.4 GPa at a load of 0.49 N and 24.4 GPa at a load of 9.8 N. This liquid phase-assisted rapid ultrahigh-temperature strategy can be widely applicable for other ultrahigh-temperature ceramics as well.
| S-EPMC9258815 | biostudies-literature
Project description:The thermal conductivity of epoxy resin composites filled with combustion-synthesized hexagonal boron nitride (h-BN) particles was investigated. The mixing of the composite constituents was carried out by either a dry method (involving no use of solvent) for low filler loadings or a solvent method (using acetone as solvent) for higher filler loadings. It was found that surface treatment of the h-BN particles using the silane 3-glycidoxypropyltrimethoxysilane (GPTMS) increases the thermal conductivity of the resultant composites in a lesser amount compared to the values reported by other studies. This was explained by the fact that the combustion synthesized h-BN particles contain less -OH or active sites on the surface, thus adsorbing less amounts of GPTMS. However, the thermal conductivity of the composites filled with the combustion synthesized h-BN was found to be comparable to that with commercially available h-BN reported in other studies. The thermal conductivity of the composites was found to be higher when larger h-BN particles were used. The thermal conductivity was also found to increase with increasing filler content to a maximum and then begin to decrease with further increases in this content. In addition to the effect of higher porosity at higher filler contents, more horizontally oriented h-BN particles formed at higher filler loadings (perhaps due to pressing during formation of the composites) were suggested to be a factor causing this decrease of the thermal conductivity. The measured thermal conductivities were compared to theoretical predictions based on the Nielsen and Lewis theory. The theoretical predictions were found to be lower than the experimental values at low filler contents (< 60 vol %) and became increasing higher than the experimental values at high filler contents (> 60 vol %).
| S-EPMC6273151 | biostudies-literature
Project description:To enhance the strength-to-weight ratio of a material, one may try to either improve the strength or lower the density, or both. The lightest solid materials have a density in the range of 1,000 kg/m(3); only cellular materials, such as technical foams, can reach considerably lower values. However, compared with corresponding bulk materials, their specific strength generally is significantly lower. Cellular topologies may be divided into bending- and stretching-dominated ones. Technical foams are structured randomly and behave in a bending-dominated way, which is less weight efficient, with respect to strength, than stretching-dominated behavior, such as in regular braced frameworks. Cancellous bone and other natural cellular solids have an optimized architecture. Their basic material is structured hierarchically and consists of nanometer-size elements, providing a benefit from size effects in the material strength. Designing cellular materials with a specific microarchitecture would allow one to exploit the structural advantages of stretching-dominated constructions as well as size-dependent strengthening effects. In this paper, we demonstrate that such materials may be fabricated. Applying 3D laser lithography, we produced and characterized micro-truss and -shell structures made from alumina-polymer composite. Size-dependent strengthening of alumina shells has been observed, particularly when applied with a characteristic thickness below 100 nm. The presented artificial cellular materials reach compressive strengths up to 280 MPa with densities well below 1,000 kg/m(3).
| S-EPMC3932926 | biostudies-literature
Project description:Bulk B-C-N materials were synthesized under static high thermobaric conditions (20 GPa and 2,000 °C) in a multianvil apparatus from a polymer derived t-BC1.97N ceramic. The bulk samples were characterised using X-ray synchrotron radiation and analytical transmission electron microscopy in combination with electron energy loss spectroscopy. Polycrystalline B-C-N materials with a cubic type structure were formed under the applied reaction conditions, but the formation of a ternary cubic diamond-like c-BC₂N compound, could not be unambiguously confirmed.
| S-EPMC5448883 | biostudies-other
Project description:Natural structural materials like bone and shell have complex, hierarchical architectures designed to control crack propagation and fracture. In modern composites there is a critical trade-off between strength and toughness. Natural structures provide blueprints to overcome this, however this approach introduces another trade-off between fine structural manipulation and manufacturing complex shapes in practical sizes and times. Here we show that robocasting can be used to build ceramic-based composite parts with a range of geometries, possessing microstructures unattainable by other production technologies. This is achieved by manipulating the rheology of ceramic pastes and the shear forces they experience during printing. To demonstrate the versatility of the approach we have fabricated highly mineralized composites with microscopic Bouligand structures that guide crack propagation and twisting in three dimensions, which we have followed using an original in-situ crack opening technique. In this way we can retain strength while enhancing toughness by using strategies taken from crustacean shells.
| S-EPMC5653810 | biostudies-literature
Project description:Transitional metal carbides and nitrides (MXenes) have promise for incorporation into multifunctional composites due to their high electrical conductivity and excellent mechanical and tribological properties. It is unclear, however, to what extent MXenes are also able to improve the mechanical properties of the composites and, if so, what would be the optimal flake size and morphology. Herein, Ti3C2Tx MXene is demonstrated to be indeed a good candidate for mechanical reinforcement in polymer matrices. In the present work, the strain-induced Raman band shifts of mono-/few-/multilayer MXenes flakes have been used to study the mechanical properties of MXene and the interlayer/interfacial stress transfer on a polymer substrate. The mechanical performance of MXene was found to be less dependent upon flake thickness compared to that of graphene. This enables Ti3C2Tx MXene to offer an efficient mechanical reinforcement to a polymer matrix with a flake length of >10 μm and a thickness of 10s of nanometers. Therefore, the degree of exfoliation of MXenes is not as demanding as other two-dimensional (2D) materials for the purpose of mechanical enhancement in polymers. In addition, the active surface chemistry of MXene facilitates possible functionalization to enable a stronger interface with polymers for applications, such as strain engineering and mechanical enhancement, and in materials including membranes, coatings, and textiles.
| S-EPMC9171720 | biostudies-literature
Project description:Polymer derived ceramic (PDC) composite coatings were deposited on AISI 304 substrates using siloxane based preceramic polymer polymethlysilsquioxane (PMS) and ZrSi2 as active filler or Ag as passive filler. The tribological performance of the composite coatings was evaluated at room temperature and moderately high temperatures (150?°C, 200?°C, 300?°C and 400?°C). The composite coatings showed low coefficient of friction (COF), µ, from 0.08 to 0.2 for SiOC-ZrSi2 composite coatings, and from 0.02 to 0.3 for SiOC-Ag composite coatings, at room temperature with increasing normal load from 1 to 5?N. High temperature tribology tests showed high COF values from 0.4 to 1 but low wear for SiOC-ZrSi2 coating, and low COF from 0.2 to 0.3 for SiOC-Ag coatings at lower temperature ranges. Low load friction tests at room temperature showed negligible wear in SiOC-ZrSi2 coatings, suggesting good wear resistant and lubricating properties due to formation of t-ZrO2 and carbon. Low COF and high amount of wear was observed in SiOC-Ag composite coatings at room temperature due to high ductility of Ag and smearing of wear debris in the wear track. The coatings and wear tracks were characterized to evaluate the lubrication and wear behavior.
| S-EPMC6180137 | biostudies-literature
Project description:Ultralight and resilient porous nanostructures have been fabricated in various material forms, including carbon, polymers, and metals. However, the development of ultralight and high-temperature resilient structures still remains extremely challenging. Ceramics exhibit good mechanical and chemical stability at high temperatures, but their brittleness and sensitivity to flaws significantly complicate the fabrication of resilient porous ceramic nanostructures. We report the manufacturing of large-scale, lightweight, high-temperature resilient, three-dimensional sponges based on a variety of oxide ceramic (for example, TiO2, ZrO2, yttria-stabilized ZrO2, and BaTiO3) nanofibers through an efficient solution blow-spinning process. The ceramic sponges consist of numerous tangled ceramic nanofibers, with densities varying from 8 to 40 mg/cm3. In situ uniaxial compression in a scanning electron microscope showed that the TiO2 nanofiber sponge exhibits high energy absorption (for example, dissipation of up to 29.6 mJ/cm3 in energy density at 50% strain) and recovers rapidly after compression in excess of 20% strain at both room temperature and 400°C. The sponge exhibits excellent resilience with residual strains of only ~1% at 800°C after 10 cycles of 10% compression strain and maintains good recoverability after compression at ~1300°C. We show that ceramic nanofiber sponges can serve multiple functions, such as elasticity-dependent electrical resistance, photocatalytic activity, and thermal insulation.
| S-EPMC5457032 | biostudies-literature
Project description:Architected metals and ceramics with nanoscale cellular designs, e.g., nanolattices, are currently subject of extensive investigation. By harnessing extreme material size effects, nanolattices demonstrated classically inaccessible properties at low density, with exceptional potential for superior lightweight materials. This study expands the concept of nanoarchitecture to dense metal/ceramic composites, presenting co-continuous architectures of three-dimensional printed pyrolytic carbon shell reinforcements and electrodeposited nickel matrices. We demonstrate ductile compressive deformability with elongated ultrahigh strength plateaus, resulting in an extremely high combination of compressive strength and strain energy absorption. Simultaneously, property-to-weight ratios outperform those of lightweight nanolattices. Superior to cellular nanoarchitectures, interpenetrating nanocomposites may combine multiple size-dependent characteristics, whether mechanical or functional, which are radically antagonistic in existing materials. This provides a pathway toward previously unobtainable multifunctionality, extending far beyond lightweight structure applications.
| S-EPMC9385151 | biostudies-literature