The Contact Ageing Effect on Fretting Damage of an Electro-Deposited Coating against an AISI52100 Steel Ball.

ABSTRACT: This article investigates the effect of contact ageing on fretting damage of an epoxy-based cathodic electro-deposited coating for use on automotive seat slide tracks (made of cold-rolled high strength steel). Static normal load was induced at the contact between the coating and an AISI52100 ball for a certain duration. It was identified that plastically deformed contact area increased logarithmically as a function of time when the contact was under static normal load. Fretting tests after various durations of static contact were conducted using a ball-on-flat plate apparatus. All fretting tests were halted when the friction coefficient reached a critical value of 0.5, indicating complete coating failure. The total number of fretting cycles to the critical friction coefficient was found to vary with the duration of static contact before fretting. It was identified that the number of cycles to the critical friction coefficient decreased with the increased duration of static contact. Meanwhile, the friction coefficient at steady-state sliding was not greatly affected by the duration of static contact before fretting. Finally, the relation between coating thickness after indentation creep and the number of cycles to the critical friction coefficient was found to be linear. Obtained results show that the duration of static contact before fretting has an influence on the fretting lifetime of an electro-deposited coating.

SUBMITTER: Kim K

PROVIDER: S-EPMC5457045 | biostudies-other | 2016 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Evaluation and Description of Friction between an Electro-Deposited Coating and a Ceramic Ball under Fretting Condition.

Project description:This article describes fretting behavior of zirconia and silicon nitride balls on an electro-deposited coating. Fretting tests are performed using a ball-on-flat configuration. The evolution of the kinetic friction coefficient is determined, along with slip ratio. Experimental results show that the steady-state friction coefficient between ceramic balls (Si₃N₄ and ZrO₂) and an electro-deposited coating is about 0.06, lower than the value between AISI 52100 ball and the coating. After a steady-state sliding, the transition of the friction coefficient is varied with a ball. The friction coefficient for ZrO₂ balls became a critical value after higher fretting cycles than those for Si₃N₄ and AISI 52100 balls. In addition, it is identified that two parameters can describe the transition of the friction coefficient. Finally, the evolution of the friction coefficient is expressed as an exponential or a power-law form.

| S-EPMC5455471 | biostudies-other

The roles of contact conformity, temperature and displacement amplitude on the lubricated fretting wear of a steel-on-steel contact.

Project description:This paper investigates the effect of contact geometry, temperature and displacement amplitude on the fretting behaviour of an aero-turbo oil lubricated cylinder-on-flat contact. To be effective, the lubricant needed both to penetrate the contact and then offer protection. Lubricant penetration into the fretting contact is found to be controlled by two physical parameters, namely (i) the width of the contact that remains covered throughout the fretting test and (ii) the lubricant viscosity. The protection offered by the lubricant (assuming that it has successfully penetrated the contact) is influenced by four physical parameters, namely (i) lubricant viscosity, (ii) traverse velocity, (iii) nominal contact pressure, and (iv) chemical effects. The relationship between the three experimental parameters which were varied in the programme of work (temperature, fretting displacement and cylinder radius) and physical parameters which influence the protection offered by the lubricant film can be competing, and therefore complex wear behaviour is observed. The roles of the various parameters in controlling the wear behaviour are presented in a coherent physical framework.

| S-EPMC5095370 | biostudies-literature

Evaluation of the corrosion resistance of a Ni-P coating deposited on additive manufacturing steel: A dataset

Project description:This article presents the data set obtained for the research work entitled “Effect of a Ni-P coating on the corrosion resistance of an additive manufacturing carbon steel immersed in a 0.1 M NaCl solution” [1]. Microstructural, mechanical, and electrochemical characterization (using the electrochemical impedance and electrochemical noise spectroscopy technique) is performed on a material obtained by additive manufacturing and the influence of a Ni-P coating on it. The layer sizes and hardness of the substrate are measured, as well as the thickness of the coating and its hardness, values for corrosion resistance, resistance to electrochemical noise and location indices are calculated. The data show an adequate deposition rate for the type of coating, as well as the increase in corrosion resistance when the coating is applied to the steel by additive manufacturing.

| S-EPMC7452479 | biostudies-literature

A contact-electro-catalysis process for producing reactive oxygen species by ball milling of triboelectric materials.

Project description:Ball milling is a representative mechanochemical strategy that uses the mechanical agitation-induced effects, defects, or extreme conditions to activate substrates. Here, we demonstrate that ball grinding could bring about contact-electro-catalysis (CEC) by using inert and conventional triboelectric materials. Exemplified by a liquid-assisted-grinding setup involving polytetrafluoroethylene (PTFE), reactive oxygen species (ROS) are produced, despite PTFE being generally considered as catalytically inert. The formation of ROS occurs with various polymers, such as polydimethylsiloxane (PDMS) and polypropylene (PP), and the amount of generated ROS aligns well with the polymers' contact-electrification abilities. It is suggested that mechanical collision not only maximizes the overlap in electron wave functions across the interface, but also excites phonons that provide the energy for electron transition. We expect the utilization of triboelectric materials and their derived CEC could lead to a field of ball milling-assisted mechanochemistry using any universal triboelectric materials under mild conditions.

| S-EPMC10810876 | biostudies-literature

Tribocorrosion Failure Mechanism of TiN/SiOx Duplex Coating Deposited on AISI304 Stainless Steel.

Project description:TiN/SiOx duplex coatings were synthesized on AISI304 stainless steel by plasma immersion ion implantation and deposition (PIIID) followed by radio frequency magnetron sputtering (RFMS). The microstructure and tribocorrosion failure behaviors of the duplex coatings were investigated by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, atomic force microscopy, reciprocating-sliding tribometer, and electrochemical tests. The as-deposited duplex coating had a two-layered columnar growth structure consisting of face-centered cubic TiN and amorphous SiOx. Sliding tests showed that the TiN interlayer had good adhesion with the substrate, but the SiOx layer suffered from severe delamination failure. Friction force induced a number of micro-cracks in the coating, which provided channels for the diffusion of NaCl solution. The tribocorrosion test showed that the duplex coating exhibited a lower wear-performance in NaCl solution than in ambient atmosphere. Multi-scale chloride ion corrosion occurred simultaneously and substantially degraded the bonding strength of the columnar crystals or neighboring layers. Force-corrosion synergy damage eventually led to multi-degradation failure of the duplex coating. The presented results provide a comprehensive understanding of the tribocorrosion failure mechanism in coatings with duplex architecture.

| S-EPMC5457005 | biostudies-other

Electrochemically Deposited Zinc (Tetraamino)phthalocyanine as a Light-activated Antimicrobial Coating Effective against S. aureus.

Project description:Light-activated antimicrobial coatings are currently considered to be a promising approach for the prevention of nosocomial infections. In this work, we present a straightforward strategy for the deposition of a photoactive biocidal organic layer of zinc (tetraamino)phthalocyanine (ZnPcNH2) in an electrochemical oxidative process. The chemical structure and morphology of the resulting layer are widely characterized by microscopic and spectroscopic techniques, while its ability to photogenerate reactive oxygen species (ROS) is investigated in situ by UV-Vis spectroscopy with α-terpinene or 1,3-diphenylisobenzofuran as a chemical trap. It is shown that the ZnPcNH2 photosensitizer retained its photoactivity after immobilization, and that the reported light-activated coating exhibits promising antimicrobial properties towards Staphyloccocus aureus (S. aureus).

| S-EPMC8838431 | biostudies-literature

Reciprocal Sliding Friction Model for an Electro-Deposited Coating and Its Parameter Estimation Using Markov Chain Monte Carlo Method.

Project description:This paper describes a sliding friction model for an electro-deposited coating. Reciprocating sliding tests using ball-on-flat plate test apparatus are performed to determine an evolution of the kinetic friction coefficient. The evolution of the friction coefficient is classified into the initial running-in period, steady-state sliding, and transition to higher friction. The friction coefficient during the initial running-in period and steady-state sliding is expressed as a simple linear function. The friction coefficient in the transition to higher friction is described with a mathematical model derived from Kachanov-type damage law. The model parameters are then estimated using the Markov Chain Monte Carlo (MCMC) approach. It is identified that estimated friction coefficients obtained by MCMC approach are in good agreement with measured ones.

| S-EPMC5502884 | biostudies-other

Chemical-Vapor-Deposited Graphene as a Thermally Conducting Coating.

Project description:We performed scanning thermal microscopy measurements on single layers of chemical-vapor-deposited (CVD) graphene supported by different substrates, namely, SiO2, Al2O3, and PET using a double-scan technique to remove the contribution to the heat flux through the air and the cantilever. Then, by adopting a simple lumped-elements model, we developed a new method that allows determining, through a multistep numerical analysis, the equivalent thermal properties of thermally conductive coatings of nanometric thickness. In this specific case we found that our CVD graphene is "thermally equivalent", for heat injection perpendicular to the graphene planes, to a coating material of conductivity k eff = 2.5 ± 0.3 W/m K and thickness t eff = 3.5 ± 0.3 nm in perfect contact with the substrate. For the SiO2 substrate, we also measured stacks made of 2- and 4-CVD monolayers, and we found that the effective thermal conductivity increases with increasing number of layers and, with a technologically achievable number of layers, is expected to be comparable to that of 1 order of magnitude-thicker metallic thin films. This study provides a powerful method for characterizing the thermal properties of graphene in view of several thermal management applications.

| S-EPMC6541428 | biostudies-literature

Characterizing fretting damage in different test media for cardiovascular device durability testing.

Project description:In vitro durability tests of cardiovascular devices are often used to evaluate the potential for fretting damage during clinical use. Evaluation of fretting damage is important because severe fretting can concentrate stress and lead to the loss of structural integrity. Most international standards call for the use of phosphate buffered saline (PBS) for such tests although there has been little evidence to date that the use of PBS is appropriate in terms of predicting the amount of fretting damage that would occur in vivo. In order to determine an appropriate test media for in vitro durability tests where fretting damage is being evaluated, we utilized an in vitro test that is relevant to cardiovascular devices both in terms of dimensions and materials (nitinol, cobalt-chromium, and stainless steel) to characterize fretting damage in PBS, deionized water (DIW), and heparinized porcine blood. Overall, tests conducted in blood were found to have increased levels of fretting damage over tests in DIW or PBS, although the magnitude of this difference was smaller than the variability for each test media. Tests conducted in DIW and PBS led to mostly similar amounts of fretting damage with the exception of one material combination where DIW had greatly reduced damage compared to PBS and blood. Differences in fretting damage among materials were also observed with nitinol having less fretting damage than stainless steel or cobalt-chromium. In general, evaluating fretting damage in PBS or DIW may be appropriate although caution should be used when selecting test media and interpreting results given some of the differences observed across different materials.

| S-EPMC6374031 | biostudies-literature

Vapor-Deposited Reactive Coating with Chemically and Topographically Erasable Properties.

Project description:An erasable coating was prepared to modify material surfaces with accessibilities, including specific conjugation, elimination of the conjugated chemistry/function, and the reactivation of a second new chemistry/function. The coating was realized based on a vapor-deposited functional poly-p-xylylene coating composed of an integrated 3-((3-methylamido)-disulfanyl)propanoic acid functional group, resulting in not only chemical reactivity, but also a disulfide interchange mechanism. Mechanically, the coating was robust in terms of the thermal stability and adhesive property on a variety of substrate materials. Chemically, the anchoring site of carboxylic acid was accessible for specific conjugation, and a disulfide bridge moiety was used to disengage already installed functions/properties. In addition, the homogeneous nature of the vapor-phased coating technique is known for its morphology/thickness and distribution of the functional moiety, which allowed precision to address the installation or erasure of functions and properties. Characterization of the precisely confined hydrophilic/hydrophobic wetting property and the alternating reversibility of this wetting property on the same surface was achieved.

| S-EPMC6835693 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data