Effect of Stress Ratio and Loading Frequency on the Corrosion Fatigue Behavior of Smooth Steel Wire in Different Solutions.

ABSTRACT: In this work, the effects of loading condition and corrosion solution on the corrosion fatigue behavior of smooth steel wire were discussed. The results of polarization curves and weight loss curves showed that the corrosion of steel wire in acid solution was more severe than that in neutral and alkaline solutions. With the extension of immersion time in acid solution, the cathodic reaction of steel wire gradually changed from the reduction of hydrogen ion to the reduction of oxygen, but was always the reduction of hydrogen ion in neutral and alkaline solutions. The corrosion kinetic parameters and equivalent circuits of steel wires were also obtained by simulating the Nyquist diagrams. In corrosion fatigue test, the effect of stress ratio and loading frequency on the crack initiation mechanism was emphasized. The strong corrosivity of acid solution could accelerate the nucleation of crack tip. The initiation mechanism of crack under different conditions was summarized according to the side and fracture surface morphologies. For the crack initiation mechanism of anodic dissolution, the stronger the corrosivity of solution was, the more easily the fatigue crack source formed, while, for the crack initiation mechanism of deformation activation, the lower stress ratio and higher frequency would accelerate the generation of corrosion fatigue crack source.

SUBMITTER: Wang S

PROVIDER: S-EPMC5457049 | biostudies-other | 2016 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Notch Corrosion Fatigue Behavior of Ti-6Al-4V.

Project description:The aim of this paper is to map the corrosion fatigue characteristics of Ti-6Al-4V alloy through the evaluation of the corrosion fatigue initiation and failure mechanisms. The study included the effect of the stress concentration factor at very high Kt values and the role of different inert or corrosive environments. This alloy is widely used in naval-structures and aero-engine communities and the outcomes of the work will have direct relevance to industrial service operations. Axial fatigue tests (R = 0.1; 2 × 10⁵ cycles; f = 10 Hz) were carried out on smooth and high notched (Ktmax = 18.65) flat specimens in laboratory air, paraffin oil, laboratory air + beeswax coating, recirculated 3.5% NaCl solution. The step loading procedure was used to perform the fatigue tests and the surface replica method and crack propagation gages were used to check crack nucleation and propagation until failure. Log-Log plots of σmaxvs.Kt showed a bilinear behavior and enabled the demonstration of the presence of a threshold stress intensity factor (Kt = 8-9), after which the environment has no effect on the fatigue damage for all the tested environments.

| S-EPMC5455940 | biostudies-other

Corrosion Behavior of AISI 1045 Steel in Seawater in the Presence of Flavobacterium sp.

Project description:A systematic comparison study was carried out to investigate the effect of Flavobacterium sp. on AISI 1045 steel corrosion by weight loss, fluorescence microscopy (FM), surface analysis, cell count, pH measure, electrochemical impedance spectroscopy (EIS), and polarization curves. The impedances were considerably increased by Flavobacterium sp. between 1 and 7 day exposure and after 30 day exposure but considerably decreased by Flavobacterium sp. after 15 and 21 day exposure, which were supported by the Icorr results and the weight loss data. Furthermore, the biofilm was formed on the coupons. The pH values were considerably decreased by Flavobacterium sp. after 15 and 21 day exposure. The results proved that Flavobacterium sp. decreased the corrosion rates between 1 and 7 day exposure and after 30 day exposure and increased the corrosion rates between 15 and 21 day exposure, which could be ascribed to the protective biofilm and the secreted corrosive acid, respectively. In addition, Flavobacterium sp. considerably increased the pit numbers, the maximum pit depths, and the corresponding widths and considerably decreased the Epit values. Importantly, the coverage and the heterogeneity of the biofilm were positively correlated with the increases in the maximum pit depths and the corresponding widths and the decreases in the Epit values by Flavobacterium sp. The results demonstrated that Flavobacterium sp. increased the pitting corrosion, which could involve the heterogeneous biofilm cover.

| S-EPMC7062711 | biostudies-literature

Corrosion of steel in groundwater

Project description:Microbially-induced corrosion of carbon steel in anoxic groundwater

| PRJEB19087 | ENA

Corrosion Behavior of Titanium in Simulated Body Solutions with the Addition of Biomolecules.

Project description:Titanium is one of the most used biomaterials for different applications. The aim of this study is to investigate the influence of adenine, thymine, and l-histidine as important biomolecules in the human body on the corrosion behavior of titanium in simulated body solutions. Open circuit measurements, potentiodynamic measurements, electrochemical impedance spectroscopy measurements, and quantum chemical calculations were employed during the investigation. All electrochemical methods used revealed that the investigated biomolecules provide better corrosion resistance to titanium in artificial body solutions. The increase in corrosion resistance is a result of the formation of a stable protective film on the metal surface. Also, quantum chemical calculations are in compliance with electrochemical test results and indicate that adenine, thymine, and l-histidine may act as corrosion inhibitors in the investigated solutions.

| S-EPMC7288364 | biostudies-literature

Fatigue and Fracture Behavior of a Cold-Drawn Commercially Pure Aluminum Wire.

Project description:Fatigue properties and cracking behavior of cold-drawn commercially pure aluminum wires (CPAWs) widely used as the overhead transmission conductors were investigated. It was found that the fracture surface of the CPAWs shows an obvious four-stage fracture characteristic, i.e., crack initiation, planar crack propagation, 45°-inclined crack propagation and final rapid fracture. The crack growth mechanisms for the CPAWs were found quite different from those for the conventional coarse-grained materials. The cracks in the CPAWs firstly grow along the grain boundaries (Stage I crack growth), and then grow along the plane of maximum shear stress during the last stage of cycling (Stage II crack growth), leading to the distinctive fracture surfaces, i.e., the granular surface in the planar crack propagation region and the coarse fatigue striations in the 45°-inclined crack propagation region. The grain boundary migration was observed in the fatigued CPAWs. The increase in fatigue load enhances the dislocation recovery, increases the grain boundary migration rate, and thus promotes the occurrence of softening and damage localization up to the final failure.

| S-EPMC5457069 | biostudies-other

Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions.

Project description:This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC) in a nitrite-containing chloride solution. Slow strain rate testing (SSRT) in 30 wt. % MgCl₂ solution established SCC susceptibility, as evidenced by post-SSRT fractography. Addition of nitrite to the chloride solution, which is reported to have inhibitive influence on corrosion of stainless steels, was found to increase SCC susceptibility. The susceptibility was also found to increase with nitrite concentration. This behaviour is explained on the basis of the passivation and pitting characteristics of 316L steel in chloride solution.

| S-EPMC5456438 | biostudies-other

Static and Fatigue Behavior Investigation of Artificial Notched Steel Reinforcement.

Project description:Pitting corrosion is one of the most common forms of localized corrosion. Corrosion pit results in a stress concentration and fatigue cracks usually initiate and propagate from these corrosion pits. Aging structures may fracture when the fatigue crack reaches a critical size. This paper experimentally simulates the effects of pitting morphologies on the static and fatigue behavior of steel bars. Four artificial notch shapes are considered: radial ellipse, axial ellipse, triangle and length-variable triangle. Each shape notch includes six sizes to simulate a variety of pitting corrosion morphologies. The stress-strain curves of steel bars with different notch shape and depth are obtained based on static tensile testing, and the stress concentration coefficients for various conditions are determined. It was determined that the triangular notch has the highest stress concentration coefficient, followed by length-variable triangle, radial ellipse and axial ellipse shaped notches. Subsequently, the effects of notch depth and notch aspect ratios on the fatigue life under three stress levels are investigated by fatigue testing, and the equations for stress range-fatigue life-notch depth are obtained. Several conclusions are drawn based on the proposed study. The established relationships provide an experimental reference for evaluating the fatigue life of concrete bridges.

| S-EPMC5458989 | biostudies-other

Experimental and computational chemical studies on the corrosion inhibitive properties of carbonitrile compounds for carbon steel in aqueous solutions.

Project description:The present work aims to study 6-amino-4-aryl-2-oxo-1-phenyl-1,2-dihydropyridine-3,5-dicarbonitrile derivatives namely: 6-Amino-2-oxo-1,4-diphenyl-1,2-dihydropyridine-3,5-dicarbonitrile (PdC-H), 6-Amino-2-oxo-1-phenyl-4-(p-tolyl)-1,2-dihydropyridine-3,5-dicarbonitrile (PdC-Me) and 6-Amino-4-(4-hydroxyphenyl)-2-oxo-1-phenyl-1,2-dihydropyridine-3,5-dicarbonitrile (PdC-OH) as corrosion inhibitors to provide protection for carbon steel in a molar hydrochloric acid medium. Chemical measurements such as (weight loss) and electrochemical techniques such as (Potentiodynamic polarization, electrochemical impedance spectroscopy, and Electron frequency modulation) were applied to characterize the inhibitory properties of the synthesized derivatives. The adsorption of these derivatives on the carbon steel surface was confirmed by Attenuated Total Refraction Infrared (ATR-IR), Atomic Force Microscope (AFM), and X-ray Photoelectron Spectroscopy (XPS). Our findings revealed that the tested derivatives have corrosion inhibition power, which increased significantly from 75.7 to 91.67% on the addition of KI (PdC-OH:KI = 1:1) to inhibited test solution with PdC-OH derivative at 25 °C. The adsorption process on the metal surface follows the Langmuir adsorption model. XPS analysis showed that the inhibitor layer consists of an iron oxide/hydroxide mixture in which the inhibitor molecules are incorporated. Computational chemical theories such as DFT calculations and Mont Carlo simulation have been performed to correlate the molecular properties of the investigated inhibitors with experimental efficiency. The theoretical speculation by Dmol3 corroborates with the results from the experimental findings.

| S-EPMC8569179 | biostudies-literature

The Corrosion Behavior of X100 Pipeline Steel in a Sodium Chloride Solution Containing Magnesium and Calcium.

Project description:The influences of Mg2+ and Ca2+ on the short-term (1800 s) corrosion behavior of X100 pipeline steel were investigated in a sodium chloride (NaCl) solution saturated with CO2. Either Ca2+ or Mg2+ in the solution inhibited the short-term corrosion of X100 pipeline steel, with the corrosion current density decreasing from 262.4 μA cm-2 to 163.5 μA cm-2 or 80.8 μA cm-2. During longer-term (8-48 h) immersion, the Mg2+ inhibited the formation of the protective scale, whereas the Ca2+ accelerated the formation of the scale. Further, an experimental equation establishing the relationship between the precipitation rate of the corrosion scale and the exposure time was proposed to quantitatively study the effects of Mg2+ and Ca2+ on the precipitation rate of the corrosion scale.

| S-EPMC10420105 | biostudies-literature

Behavior of Hybrid Reinforced Concrete Bridge Decks under Static and Fatigue Loading.

Project description:This paper presents a new bridge deck reinforcement alternative using hybrid reinforced concrete (Hybrid) consisting of Glass Fiber Reinforced Polymer (GFRP) rebar and alkali-resistant fiberglass composite macrofibers added to the concrete mixture. Fiberglass composite macrofibers are a miniaturized GFRP reinforcing bar that is a composite of resin and glass fibers. An experimental testing program and analytical modeling were conducted to evaluate the structural performance at the service and ultimate limit states. Thirteen full-scale bridge deck specimens were constructed and tested under static and fatigue loading. The fatigue loading was applied up to two million cycles at a frequency of 4 Hz. Post-fatigue, the specimens were tested to failure to compare pre-and post-fatigue behavior. Simplified and moment-curvature analytical models were used to predict the specimens' flexural strength at the ultimate level, and both were found to be accurate for predicting pre- and post-fatigue strength. Deflection and crack width were monitored throughout the fatigue loading, and these values were compared to the recommended AASHTO LRFD serviceability limits. Testing and analytical results showed that the Hybrid deck is a viable alternative to steel-reinforced and GFRP-reinforced bridge decks for flexural behavior. The service and ultimate level behavior of each bridge deck type was adequate as compared to the AASHTO LRFD service limits. The exceptional post-peak energy absorption demonstrated by the Hybrid adds ductility to previously elastic GFRP reinforced sections.

| S-EPMC9740706 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data