Operation of Thin-Film Electrolyte Metal-Supported Solid Oxide Fuel Cells in Lightweight and Stationary Stacks: Material and Microstructural Aspects.
Ontology highlight
ABSTRACT:
SUBMITTER: Roehrens D
PROVIDER: S-EPMC5457052 | biostudies-other | 2016 Sep
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Graphitic carbon nitrides are investigated for developing highly durable Pt electrocatalyst supports for polymer electrolyte fuel cells (PEFCs). Three different graphitic carbon nitride materials were synthesized with the aim to address the effect of crystallinity, porosity, and composition on the catalyst support properties: polymeric carbon nitride (gCNM), poly(triazine) imide carbon nitride (PTI/Li(+)Cl(-)), and boron-doped graphitic carbon nitride (B-gCNM). Following accelerated corrosion testing, all graphitic carbon nitride materials are found to be more electrochemically stable compared to conventional carbon black (Vulcan XC-72R) with B-gCNM support showing the best stability. For the supported catalysts, Pt/PTI-Li(+)Cl(-) catalyst exhibits better durability with only 19% electrochemical surface area (ECSA) loss versus 36% for Pt/Vulcan after 2000 scans. Superior methanol oxidation activity is observed for all graphitic carbon nitride supported Pt catalysts on the basis of the catalyst ECSA.
| S-EPMC3985936 | biostudies-other
Project description:Ni-doped chromite anodes were integrated into electrolyte-supported cells (ESC) with 5×5 cm2 size and investigated in fuel cell mode with H2 /H2 O fuel gas. Both a stoichiometric and a nominally A-site deficient chromite anode material showed promising performance at 860 °C approaching the ones of state-of-the-art Ni/Gd-doped ceria (CGO) anodes. While the difference in polarization resistance was small, an increased ohmic resistance of the perovskite anodes was observed, which is related to their limited electronic conductivity. Increasing the chromite electrode thickness was shown to enhance performance and stability considerably. Degradation increased with current density, suggesting its dependency on the electrode potential, and could be reversed by redox cycling. Sulfur poisoning with 20 ppm hydrogen sulfide led to rapid voltage drops for the chromite anodes. It is discussed that Ni nanoparticle exsolution facilitates hydrogen dissociation to the extent that it is not rate-limiting at the investigated temperature unless an insufficiently thick electrode thickness is employed or sulfur impurities are present in the feed gas.
| S-EPMC8252760 | biostudies-literature
Project description:The advent of the arterial switch operation for the treatment of transposition of great arteries (TGA) made the atrial switch operation largely redundant and its use in the developed world is now confined to the atrial component of the double-switch operation for congenitally corrected TGA. In resource-limited countries, however, it remains relevant as a treatment option for patients presenting late with transposition and a regressed left ventricle. The operation is intricate with many potential pitfalls, and this "how I do it" article describes the operative steps in detail to enable surgeons to learn this procedure and make it a part of their surgical armamentarium.
| S-EPMC8457269 | biostudies-literature
Project description:In this paper we present a study on stable radicals and short-lived species generated in anion-exchange membrane (AEM) fuel cells (AEMFCs) during operation. The in situ measurements are performed with a micro-AEMFC inserted into a resonator of an electron paramagnetic resonance (EPR) spectrometer, which enables separate monitoring of radicals formed on the anode and cathode sides. The creation of radicals is monitored by the EPR spin trapping technique. For the first time, we clearly show the formation and presence of stable radicals in AEMs during and after long-term AEMFC operation. The main detected adducts during the operation of the micro-AEMFC are DMPO-OOH and DMPO-OH on the cathode side, and DMPO-H on the anode side. These results indicate that oxidative degradation involving radical reactions has to be taken into account when stability of AEMFCs is investigated.
| S-EPMC7503863 | biostudies-literature
Project description:1.2 Previous studies have confirmed that air and light pollution can cause damage to a number of systems throughout the body, including the ocular surface and retina. However, the exact effect of air pollution and light pollution on tear film function is not clear. This study explored the different operation room environmental exposures on tear film function before and after operation. Sixty medical staff in the operating room were selected and divided into 4 groups according to different surgical methods to evaluate the tear film function before and after operation: Da Vinci surgery group (DVSS), Laparoscopic surgery group (LS), Traditional surgery group (TS), and Ophthalmic microsurgery group (OM). The results showed that the levels of light and air pollution were elevated in operating rooms during the operation and the changes of tear film function in the other three groups were statistically significant except for DVSS group. In TS group, particulate matter (pm) 1 (R = 0.61, p < 0.01), pm2.5 (R = 0.63, p < 0.01), and pm10 (R = 0.67, p < 0.01) were positively correlated with eye redness index, and first and average noninvasive tear film break-up times were positively correlated with illuminance (R = 0.54, p < 0.05; R = 0.97, p < 0.01). In OM group, there was a positive correlation between the operation time and the first (R = 0.69, p < 0.01) and average (R = 0.89, p < 0.01) noninvasive tear film break-up times. Our research found that exposure to different operating room environment will lead to damage of tear film function, but also provide a theoretical basis for the improvement of surgical environment.
| S-EPMC10835182 | biostudies-literature
Project description:Elevation of operational temperatures of polymer electrolyte membrane fuel cells (PEMFCs) has been demonstrated with phosphoric acid-doped polybenzimidazole (PA/PBI) membranes. The technical perspective of the technology is simplified construction and operation with possible integration with, e.g., methanol reformers. Toward this target, significant efforts have been made to develop acid-base polymer membranes, inorganic proton conductors, and organic-inorganic composite materials. This report is devoted to updating the recent progress of the development particularly of acid-doped PBI, phosphate-based solid inorganic proton conductors, and their composite electrolytes. Long-term stability of PBI membranes has been well documented, however, at typical temperatures of 160°C. Inorganic proton-conducting materials, e.g., alkali metal dihydrogen phosphates, heteropolyacids, tetravalent metal pyrophosphates, and phosphosilicates, exhibit significant proton conductivity at temperatures of up to 300°C but have so far found limited applications in the form of thin films. Composite membranes of PBI and phosphates, particularly in situ formed phosphosilicates in the polymer matrix, showed exceptionally stable conductivity at temperatures well above 200°C. Fuel cell tests at up to 260°C are reported operational with good tolerance of up to 16% CO in hydrogen, fast kinetics for direct methanol oxidation, and feasibility of nonprecious metal catalysts. The prospect and future exploration of new proton conductors based on phosphate immobilization and fuel cell technologies at temperatures above 200°C are discussed.
| S-EPMC7298353 | biostudies-literature
Project description:Herein, we demonstrated that carbon-supported platinum (Pt/C) is a low-cost and high-performance electrocatalyst for polymer electrolyte fuel cells (PEFCs). The ethanol reduction method was used to prepare the Pt/C catalyst, which was realized by an effective matching of the carbon support and optimization of the Pt content for preparing a membrane electrode assembly (MEA). For this, the synthesis of Pt/C catalysts with different Pt loadings was performed on two different carbons (KB1600 and KB800) as new support materials. Analysis of the XRD pattern and TEM images showed that the Pt nanoparticles (NPs) with an average diameter of ca. 1.5 nm were uniformly dispersed on the carbon surface. To further confirm the size of the NPs, the coordination numbers of Pt derived from X-ray absorption fine structure (XAFS) data were used. These results suggest that the NP size is almost identical, irrespective of Pt loading. Nitrogen adsorption-desorption analysis indicated the presence of mesopores in each carbon. The BET surface area was found to increase with increasing Pt loading, and the value of the BET surface area was as high as 1286 m2 gcarbon -1. However, after 40 wt% Pt loading on both carbons, the BET surface area was decreased due to pore blockage by Pt NPs. The oxidation reduction reaction (ORR) activity for Pt/KB1600, Pt/KB800 and commercial Pt/C was evaluated by Koutecky-Levich (K-L) analysis, and the results showed first-order kinetics with ORR. The favourable surface properties of carbon produced Pt NPs with increased density, uniformity and small size, which led to a higher electrochemical surface area (ECSA). The ECSA value of the 35 wt% Pt/KB1600 catalyst was 155.0 m2 gpt -1 higher than that of the Pt/KB800 and commercial Pt/C (36.7 wt%) catalysts. A Higher ECSA indicates more available active sites for catalyst particles. The single cell test with MEA revealed that the cell voltage in the high current density regions depends on the BET surface area, and the durability of the 35 wt% Pt/KB1600 catalyst was superior to that of the 30 wt% Pt/KB800 and commercial Pt/C (46.2 wt%) catalysts. This suggests that an optimal ratio of Pt to Pt/KB1600 catalyst provides adequate reaction sites and mass transport, which is crucial to the PEFC's high performance.
| S-EPMC9033965 | biostudies-literature
Project description:The microbial fuel cell (MFC) technology relies on energy storage and harvesting circuitry to deliver stable power outputs. This increases costs, and for wider deployment into society, these should be kept minimal. The present study reports how a MFC system was developed to continuously power public toilet lighting, with for the first time no energy storage nor harvesting circuitry. Two different stacks, one consisting of 15 and the other 18 membrane-less MFC modules, were operated for 6 days and fuelled by the urine of festival goers at the 2019 Glastonbury Music Festival. The 15-module stack was directly connected to 2 spotlights each comprising 6 LEDs. The 18-module stack was connected to 2 identical LED spotlights but going through 2 LED electronic controller/drivers. Twenty hours after inoculation the stacks were able to directly power the bespoke lighting system. The electrical energy produced by the 15-module stack evolved with usage from ≈280 mW (≈2.650 V at ≈105 mA) at the beginning to ≈860 mW (≈2.750 V at ≈300 mA) by the end of the festival. The electrical energy produced by the LED-driven 18-module stack increased from ≈490 mW at the beginning to ≈680 mW toward the end of the festival. During this period, illumination was above the legal standards for outdoor public areas, with the 15-module stack reaching a maximum of ≈89 Lx at 220 cm. These results demonstrate for the first time that the MFC technology can be deployed as a direct energy source in decentralised area (e.g. refugee camps).
| S-EPMC7567022 | biostudies-literature
Project description:In recent decades, fuel cell technology has been undergoing revolutionary developments, with fundamental progress being the replacement of electrolyte solutions with polymer electrolytes, making the device more compact in size and higher in power density. Nowadays, acidic polymer electrolytes, typically Nafion, are widely used. Despite great success, fuel cells based on acidic polyelectrolyte still depend heavily on noble metal catalysts, predominantly platinum (Pt), thus increasing the cost and hampering the widespread application of fuel cells. Here, we report a type of polymer electrolyte fuel cells (PEFC) employing a hydroxide ion-conductive polymer, quaternary ammonium polysulphone, as alkaline electrolyte and nonprecious metals, chromium-decorated nickel and silver, as the catalyst for the negative and positive electrodes, respectively. In addition to the development of a high-performance alkaline polymer electrolyte particularly suitable for fuel cells, key progress has been achieved in catalyst tailoring: The surface electronic structure of nickel has been tuned to suppress selectively the surface oxidative passivation with retained activity toward hydrogen oxidation. This report of a H2–O2 PEFC completely free from noble metal catalysts in both the positive and negative electrodes represents an important advancement in the research and development of fuel cells.
| S-EPMC2634878 | biostudies-literature
Project description:In recent years, considerable research and development efforts are devoted to improving the performance of polymer electrolyte fuel cells. However, the power density and catalytic activities of these energy conversion devices are still far from being satisfactory for large-scale operation. Here we report performance enhancement via incorporation, in the cathode catalyst layers, of a ring-structured backbone matrix into ionomers. Electrochemical characterizations of single cells and microelectrodes reveal that high power density is obtained using an ionomer with high oxygen solubility. The high solubility allows oxygen to permeate the ionomer/catalyst interface and react with protons and electrons on the catalyst surfaces. Furthermore, characterizations of single cells and single-crystal surfaces reveal that the oxygen reduction reaction activity is enhanced owing to the mitigation of catalyst poisoning by sulfonate anion groups. Molecular dynamics simulations indicate that both the high permeation and poisoning mitigation are due to the suppression of densely layered folding of polymer backbones near the catalyst surfaces by the incorporated ring-structured matrix. These experimental and theoretical observations demonstrate that ionomer's tailored molecular design promotes local oxygen transport and catalytic reactions.
| S-EPMC8368003 | biostudies-literature