Upscaling of a Batch De-Vulcanization Process for Ground Car Tire Rubber to a Continuous Process in a Twin Screw Extruder.

ABSTRACT: As a means to decrease the amount of waste tires and to re-use tire rubber for new tires, devulcanization of ground passenger car tires is a promising process. Being an established process for NR and EPDM, earlier work has shown that for ground passenger car tire rubber with a relatively high amount of SBR, a devulcanization process can be formulated, as well. This was proven for a laboratory-scale batch process in an internal mixer, using diphenyl disulfide as the devulcanization aid and powder-sized material. In this paper, the devulcanization process for passenger car tire rubber is upscaled from 15 g per batch and transformed into a continuous process in a co-rotating twin screw extruder with a capacity of 2 kg/h. As SBR is rather sensitive to devulcanization process conditions, such as thermal and mechanical energy input, the screw design was based on a low shear concept. A granulate with particle sizes from 1-3.5 mm was chosen for purity, as well as economic reasons. The devulcanization process conditions were fine-tuned in terms of: devulcanization conditions (time/temperature profile, concentration of devulcanization aid), extruder parameters (screw configuration, screw speed, fill factor) and ancillary equipment (pre-treatment, extrudate handling). The influence of these parameters on the devulcanization efficiency and the quality of the final product will be discussed. The ratio of random to crosslink scission as determined by a Horikx plot was taken for the evaluation of the process and material. A best practice for continuous devulcanization will be given.

SUBMITTER: Saiwari S

PROVIDER: S-EPMC5457053 | biostudies-other | 2016 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Continuous twin screw granulation: Impact of microcrystalline cellulose batch-to-batch variability during granulation and drying - A QbD approach.

Project description:Despite significant advances in the research domain of continuous twin screw granulation, limited information is currently available on the impact of raw material properties, especially considering batch-to-batch variability. The importance of raw material variability and subsequent mitigation of the impact of this variability on the manufacturing process and drug product was recently stressed in the Draft Guidance for Industry on Quality Considerations for Continuous Manufacturing by the U.S. Food and Drug Administration (FDA). Therefore, this study assessed the impact of microcrystalline cellulose (MCC) batch-to-batch variability and process settings in a continuous twin screw wet granulation and semi-continuous drying line. Based on extensive raw material characterization and subsequent principal component analysis, raw material variability was quantitatively introduced in the design of experiments approach by means of t1 and t2 scores. L/S ratio had a larger effect on critical granule attributes and processability than screw speed and drying time. A large impact of the t1 and t2 scores was found, indicating the importance of raw material attributes. For the studied formulation, it was concluded that MCC batches with a low water binding capacity, low moisture content and high bulk density generated granules with the most desirable quality attributes. Additionally, an innovative and quantitative approach towards mitigating batch-to-batch variability of raw materials was proposed, which is also applicable for additional excipients and APIs.

| S-EPMC8044642 | biostudies-literature

Continuous and scalable synthesis of a porous organic cage by twin screw extrusion (TSE).

Project description:The continuous and scalable synthesis of a porous organic cage (CC3), obtained through a 10-component imine polycondensation between triformylbenzene and a vicinal diamine, was achieved using twin screw extrusion (TSE). Compared to both batch and flow syntheses, the use of TSE enabled the large scale synthesis of CC3 using minimal solvent and in short reaction times, with liquid-assisted grinding (LAG) also promoting window-to-window crystal packing to form a 3-D diamondoid pore network in the solid state. A new kinetically trapped [3+5] product was also observed alongside the formation of the targeted [4+6] cage species. Post-synthetic purification by Soxhlet extraction of the as-extruded 'technical grade' mixture of CC3 and [3+5] species rendered the material porous.

| S-EPMC7448373 | biostudies-literature

Integrated Batch and Continuous Flow Process for the Synthesis of Goniothalamin.

Project description:An integrated batch and continuous flow process has been developed for the gram-scale synthesis of goniothalamin. The synthetic route hinges upon a telescoped continuous flow Grignard addition followed by an acylation reaction capable of delivering a racemic goniothalamin precursor (16) (20.9 g prepared over 3 h), with a productivity of 7 g·h-1. An asymmetric Brown allylation protocol was also evaluated under continuous flow conditions. This approach employing (-)-Ipc2B(allyl) provided an (S)-goniothalamin intermediate in 98% yield and 91.5% enantiomeric excess (ee) with a productivity of 1.8 g·h-1. For the final step, a ring-closing metathesis reaction was explored under several conditions in both batch and flow regimes. In a batch operation, the Grubbs second-generation was shown to be effective and highly selective for the desired ring closure product over those arising from other modes of reactivity, and the reaction was complete in 1.5 h. In a flow operation, reactivity and selectivity were attenuated relative to the batch mode; however, after further optimization, the residence time could be reduced to 16 min with good selectivity and good yield of the target product. A tube-in-tube reactor was investigated for in-situ ethylene removal to favor ring-closing over cross-metathesis, in this context. These results provide further evidence of the utility of flow chemistry for organometallic processing and reaction telescoping. Using the developed integrated batch and flow methods, a total of 7.75 g of goniothalamin (1) was synthesized.

| S-EPMC7391960 | biostudies-literature

Machine learning assisted optimization of blending process of polyphenylene sulfide with elastomer using high speed twin screw extruder.

Project description:Random forest regression was applied to optimize the melt-blending process of polyphenylene sulfide (PPS) with poly(ethylene-glycidyl methacrylate-methyl acrylate) (E-GMA-MA) elastomer to improve the Charpy impact strength. A training dataset was constructed using four elastomers with different GMA and MA contents by varying the elastomer content up to 20 wt% and the screw rotation speed of the extruder up to 5000 rpm at a fixed barrel temperature of 300 °C. Besides the controlled parameters, the following measured parameters were incorporated into the descriptors for the regression: motor torque, polymer pressure, and polymer temperatures monitored by infrared-ray thermometers installed at four positions (T1 to T4) as well as the melt viscosity and elastomer particle diameter of the product. The regression without prior knowledge revealed that the polymer temperature T1 just after the first kneading block is an important parameter next to the elastomer content. High impact strength required high elastomer content and T1 below 320 °C. The polymer temperature T1 was much higher than the barrel temperature and increased with the screw speed due to the heat of shear. The overheating caused thermal degradation, leading to a decrease in the melt viscosity and an increase in the particle diameter at high screw speed. We thus reduced the barrel temperature to keep T1 around 310 °C. This increased the impact strength from 58.6 kJ m-2 as the maximum in the training dataset to 65.3 and 69.0 kJ m-2 at elastomer contents of 20 and 30 wt%, respectively.

| S-EPMC8674312 | biostudies-literature

Topical Micro-Emulsion of 5-Fluorouracil by a Twin Screw Processor-Based Novel Continuous Manufacturing Process for the Treatment of Skin Cancer: Preparation and In Vitro and In Vivo Evaluations.

Project description:5-Fluorouracil (5-FU), a BCS class III drug, has low oral bioavailability and is cytotoxic in nature causing severe systemic side effects when administered through the intravenous route. Topical drug delivery could potentially mitigate the systemic side-effects. Microemulsions (MEs) would be an apt solution due to enhanced partitioning of the drug to the skin. However, conventional methods for preparing MEs are inefficient since they are not continuous and are very tedious and time-consuming processes hence revealing the need for the development of continuous manufacturing technology. In our study, 5-FU MEs were prepared using a continuous manufacturing Twin Screw Process (TSP) and its efficiency in the treatment of skin cancer was evaluated. Water-in-oil MEs were prepared using isopropyl myristate as the oil phase and Aerosol OT and Tween 80 as the surfactants. The average particle size was observed to be 178 nm. Transmission electron microscopy was employed to confirm the size and shape of the MEs. FTIR study proved no physical or chemical interaction between the excipients and the drug. In vitro drug release using vertical diffusion cells and ex vivo skin permeation studies showed that the drug was released sustainably and permeated across the skin, respectively. In in vitro cytotoxicity studies, 5-FU MEs were accessed in HaCat and A431 cell lines to determine percentage cell viability and IC50. Skin irritation and histopathological examination implied that the 5-FU MEs did not cause any significant irritation to the skin. In vivo pharmacodynamics studies in rats suggested that the optimised formulation was effective in treating squamous cell carcinoma (SCC). Therefore, 5-FU MEs efficiently overcame the various drawbacks faced during oral and intravenous drug delivery. Also, TSP proved to be a technique that overcomes the various problems associated with the conventional methods of preparing MEs.

| S-EPMC10534867 | biostudies-literature

Ground Tire Rubber Modified by Elastomers via Low-Temperature Extrusion Process: Physico-Mechanical Properties and Volatile Organic Emission Assessment.

Project description:In this paper, low-temperature extrusion of ground tire rubber was performed as a pro-ecological waste tires recycling method. During this process, ground tire rubber was modified with constant content of dicumyl peroxide and a variable amount of elastomer (in the range: 2.5-15 phr). During the studies, three types of elastomers were used: styrene-butadiene rubber, styrene-ethylene/butylene-styrene grafted with maleic anhydride and ethylene-octene copolymer. Energy consumption measurements, curing characteristics, physico-mechanical properties and volatile organic compounds emitted from modified reclaimed GTR were determined. The VOCs emission profile was investigated using a passive sampling technique, miniature emission chambers system and static headspace analysis and subsequently quantitative or qualitative analysis by gas chromatography. The VOCs analysis showed that in the studied conditions the most emitted volatile compounds are dicumyl peroxide decomposition by-products, such as: α-methylstyrene, acetophenone, α-cumyl alcohol, methyl cumyl ether, while the detection level of benzothiazole (devulcanization "marker") was very low. Moreover, it was found that the mechanical properties of the obtained materials significantly improved with a higher content of styrene-butadiene rubber and styrene-ethylene/butylene-styrene grafted with maleic anhydride while the opposite trend was observed for ethylene-octene copolymer content.

| S-EPMC8839703 | biostudies-literature

Characterization of microbial communities during a Ground Tire Rubber (GTR) desulfurization process

Project description:Characterization of microbial communities during a Ground Tire Rubber (GTR) desulfurization process

| PRJEB24536 | ENA

Particle-level residence time data in a twin-screw feeder.

Project description:A full discharge process of a twin-screw feeder has been simulated with DEM (discrete element method). The result files are available at the Mendeley Data repository (https://doi.org/10.17632/d76rzzd8r7.1) and contain the following particle data: x,y,z coordinates of the initial position inside the feeder, particle radius, and the discharge time of each particle are available at three different initial feeder fill levels. With this data it is possible to generate residence time distributions (RTDs) of arbitrary spatial regions in the feeder to analyze the material flow inside the feeder, optimize refill strategies, and ultimately improve batch definition in continuous manufacturing. Example RTDs and evaluation scripts are available in the repository.

| S-EPMC6838427 | biostudies-literature

Devulcanization of ground tire rubber: microwave and thermomechanical approaches

Project description:We devulcanized ground tire rubber (GTR) in a laboratory microwave oven and an internal mixer, measured the soluble content and the cross-link density of the samples, and then used Horikx’s analysis. The results showed that microwave treatment caused severe degradation of the polymer chains, while in the case of thermomechanical devulcanization, the selective scission of covalent cross-links is more common. Four devulcanized ground tire rubber (dGTR) samples were chosen for further study and three groups of samples were produced: dGTR samples containing vulcanizing agents and different amounts of paraffin oil (dGTR-based mixtures), natural rubber-based rubber mixtures with different dGTR contents and reference rubber mixtures with dGTR-based mixtures (increased vulcanizing agent contents). Cure characteristics showed a plasticizer-like effect of dGTR. Tensile and tear strength decreased drastically with increasing dGTR content; however, elongation at break values did not follow such a trend. Mechanical properties improved with increased vulcanizing agent contents. The examined properties of the samples improved even further with the use of thermomechanically devulcanized samples. Horikx’s analysis showed that this is attributable to moderate polymer chain scission.

| S-EPMC7538573 | biostudies-literature

Impact of hydrophilic binders on stability of lipid-based sustained release matrices of quetiapine fumarate by the continuous twin screw melt granulation technique.

Project description:Dose dumping is the major drawback of sustained release (SR) matrices. The current research aimed to develop the stable lipid-based SR matrices of quetiapine fumarate (QTF) using Geleol™ (glyceryl monostearate; GMS) as the lipid matrix carrier and Klucel™ EF (HPC EF), Kollidon® VA64, and Kollidon® 12PF as hydrophilic binders. Formulations were developed using advanced twin screw melt granulation (TSMG) approach and the direct compression (DC) technique. Compared with the blends of DC, the granules of TSMG exhibited improved flow properties and tabletability. Solid-state characterization by differential scanning calorimetry of the prepared granules exhibited the crystalline nature of the lipid. Fourier transform infrared spectroscopy demonstrated no interaction between the formulation ingredients. The compressed matrices of TSMG and DC resulted in the sustained release of a drug over 16-24 h. Upon storage under accelerated conditions for 6 months, the matrices of TSMG retained their sustained release characteristics with no dose dumping in alcohol, whereas the matrices of DC resulted in the dose dumping of the drug attributing to the loss of matrix integrity and phase separation of lipid. Thus, it is concluded that the uniform distribution of a softened binder into a molten lipid carrier results in the stable matrices of TSMG.

| S-EPMC8274555 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data