Monitoring Poisson's Ratio Degradation of FRP Composites under Fatigue Loading Using Biaxially Embedded FBG Sensors.

ABSTRACT: The significance of strain measurement is obvious for the analysis of Fiber-Reinforced Polymer (FRP) composites. Conventional strain measurement methods are sufficient for static testing in general. Nevertheless, if the requirements exceed the capabilities of these conventional methods, more sophisticated techniques are necessary to obtain strain data. Fiber Bragg Grating (FBG) sensors have many advantages for strain measurement over conventional ones. Thus, the present paper suggests a novel method for biaxial strain measurement using embedded FBG sensors during the fatigue testing of FRP composites. Poisson's ratio and its reduction were monitored for each cyclic loading by using embedded FBG sensors for a given specimen and correlated with the fatigue stages determined based on the variations of the applied fatigue loading and temperature due to the autogenous heating to predict an oncoming failure of the continuous fiber-reinforced epoxy matrix composite specimens under fatigue loading. The results show that FBG sensor technology has a remarkable potential for monitoring the evolution of Poisson's ratio on a cycle-by-cycle basis, which can reliably be used towards tracking the fatigue stages of composite for structural health monitoring purposes.

SUBMITTER: Akay E

PROVIDER: S-EPMC5457062 | biostudies-other | 2016 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Monitoring the Damage State of Fiber Reinforced Composites Using an FBG Network for Failure Prediction.

Project description:A structural health monitoring (SHM) study of biaxial glass fibre-reinforced epoxy matrix composites under a constant, high strain uniaxial fatigue loading is performed using fibre Bragg grating (FBG) optical sensors embedded in composites at various locations to monitor the evolution of local strains, thereby understanding the damage mechanisms. Concurrently, the temperature changes of the samples during the fatigue test have also been monitored at the same locations. Close to fracture, significant variations in local temperatures and strains are observed, and it is shown that the variations in temperature and strain can be used to predict imminent fracture. It is noted that the latter information cannot be obtained using external strain gages, which underlines the importance of the tracking of local strains internally.

| S-EPMC5344542 | biostudies-other

Microwave Curing Characteristics of CFRP Composite Depending on Thickness Variation Using FBG Temperature Sensors.

Project description:Microwave curing technology, which has seen increased commercialization recently due to its ability to cut the curing time and ensure high quality, requires an understanding of the curing characteristics of composite materials of varying thickness. Therefore, this study aimed to perform cure monitoring to evaluate the effects of variations in thickness on the quality of microwave curing. For this study, a fiber Bragg grating sensor was used to measure temperature changes in specimens during the curing cycle for cure monitoring which is generally used for optimization of the curing cycle; then, the time taken for temperature increase and overshoot of the specimen, and the times at which the specimen thickness varied, were quantitatively evaluated. Testing confirmed that microwave curing reduced the curing time in the sections in which the temperature rose; also, the specimen thickness caused overshoot of up to approximately 40 °C at the side, which can affect the curing quality of the composite materials. Furthermore, voids were observed on the side of all specimens. The results indicated that, in order to improve the quality of microwave curing of composite materials, the curing cycle should be optimized by considering the characteristics of the microwave curing equipment.

| S-EPMC7178681 | biostudies-literature

Fatigue degradation and electric recovery in Silicon solar cells embedded in photovoltaic modules.

Project description:Cracking in Silicon solar cells is an important factor for the electrical power-loss of photovoltaic modules. Simple geometrical criteria identifying the amount of inactive cell areas depending on the position of cracks with respect to the main electric conductors have been proposed in the literature to predict worst case scenarios. Here we present an experimental study based on the electroluminescence (EL) technique showing that crack propagation in monocrystalline Silicon cells embedded in photovoltaic (PV) modules is a much more complex phenomenon. In spite of the very brittle nature of Silicon, due to the action of the encapsulating polymer and residual thermo-elastic stresses, cracked regions can recover the electric conductivity during mechanical unloading due to crack closure. During cyclic bending, fatigue degradation is reported. This pinpoints the importance of reducing cyclic stresses caused by vibrations due to transportation and use, in order to limit the effect of cracking in Silicon cells.

| S-EPMC3968460 | biostudies-other

Fatigue Damage Monitoring of a Composite Step Lap Joint Using Distributed Optical Fibre Sensors.

Project description:Over the past few decades, there has been a considerable interest in the use of distributed optical fibre sensors (DOFS) for structural health monitoring of composite structures. In aerospace-related work, health monitoring of the adhesive joints of composites has become more significant, as they can suffer from cracking and delamination, which can have a significant impact on the integrity of the joint. In this paper, a swept-wavelength interferometry (SWI) based DOFS technique is used to monitor the fatigue in a flush step lap joint composite structure. The presented results will show the potential application of distributed optical fibre sensor for damage detection, as well as monitoring the fatigue crack growth along the bondline of a step lap joint composite structure. The results confirmed that a distributed optical fibre sensor is able to enhance the detection of localised damage in a structure.

| S-EPMC5503041 | biostudies-other

Sensitivity and phase response of FBG based acousto-optic sensors for real-time MRI applications.

Project description:Fiber Bragg grating (FBG) based sensors have recently been introduced to the field of magnetic resonance imaging (MRI). Real-time MRI applications demand highly amplitude and phase sensitive MRI compatible sensors. Thus, a model and detailed analysis of FBG based ultrasound detection are required for designing better performing sensors. A hybrid FBG model incorporating numerical and FEA methods was developed and used for sensitivity and linearity analysis. The transfer matrix method was used for the modeling of optical modulation whereas FEA was used for pressure field calculations within the grating. The model was verified through reflection spectrum and acoustic pressure sensitivity testing of two π-phase shifted FBGs in a side slope read-out configuration. The sensitivity curves with respect to the operation point on the side slope was characterized in terms of amplitude and phase, and nonlinearity of the phase response has been quantified. Lastly, the impact of phase linearity of the FBG based acousto-optic sensor was tested under MRI when the sensor was used as a position marker and an analog phase shifter based solution was demonstrated.

| S-EPMC7250432 | biostudies-literature

A review on strengthening steel beams using FRP under fatigue.

Project description:In recent decades, the application of fibre-reinforced polymer (FRP) composites for strengthening structural elements has become an efficient option to meet the increased cyclic loads or repair due to corrosion or fatigue cracking. Hence, the objective of this study is to explore the existing FRP reinforcing techniques to care for fatigue damaged structural steel elements. This study covers the surface treatment techniques, adhesive curing, and support conditions under cyclic loading including fatigue performance, crack propagation, and failure modes with finite element (FE) simulation of the steel bridge girders and structural elements. FRP strengthening composites delay initial cracking, reduce the crack growth rate, extend the fatigue life, and decrease the stiffness decay with residual deflection. Prestressed carbon fibre-reinforced polymer (CFRP) is the best strengthening option. End anchorage prevents debonding of the CRRP strips at the beam ends by reducing the local interfacial shear and peel stresses. Hybrid-joint, nanoadhesive, and carbon-flex can also be attractive for strengthening systems.

| S-EPMC4163320 | biostudies-other

Laboratory and In-Situ Testing of Integrated FBG Sensors for SHM for Concrete and Timber Structures.

Project description:Long-term structural health monitoring (SHM) plays an important role in the safety of public transport infrastructure such as bridges or tunnels and warns in the event of any emerging problem. This article describes development and testing of system based on fiber Bragg grating (FBG) sensors that can detect changes in strain and temperature. The first phase of the research has been focused on the development of new fiber optic sensors for the monitoring of concrete structures and their investigation in laboratory conditions. The work also shows novel applicability of the same FBG technology for glulam structures. Mechanical loading tests of the concrete beam as well as glulam beam with embedded sensors were carried out. Data measured by developed fiber optic sensors were compared with the readings from reference sensors as well as with the analytically calculated values. The achieved results proved good agreement between the measured data, analytical data and reference methods. In second phase of the research, the pilot installation of the sensors was carried out on the newly constructed prestressed-concrete bridge. The bridge was monitored throughout pre-stressing phase and monitoring continued after the completion of the construction works. Problems with the fragility of the sensors occurred during the measurements, but the obtained results provide a good basis for further improvement of the system.

| S-EPMC7146198 | biostudies-literature

Effect of Temperature Variation and Pre-Sustained Loading on the Bond between Basalt FRP Sheets and Concrete.

Project description:The coupled effects of temperature variation and pre-sustained loading on the bond between basalt fiber reinforced polymer (BFRP) sheets and a concrete substrate were studied. Single lap-shear test specimens were exposed to temperatures of 15, 30, 40, 50, and 60 °C for 3 h with pre-sustained loading at 35% of the ultimate load capacity (Fu). Compared with the case of 15 °C, the interfacial fracture energy of the specimens at 30 and 40 °C increased by 46% and 11%, respectively, whereas those reduced by 73% and 77% at 50 and 60 °C, respectively. The coupled effects of temperature and pre-sustained loading on the effective bond length are insignificant for the specimens at both 15 and 30 °C and the effective bond length increased to 300 mm when the temperature exceeded 40 °C. The failure crack still occurred in the concrete substrate at the temperatures of 15 and 30 °C, and changed to the debonding of the adhesive layer from the concrete substrate at the temperature above 30 °C.

| S-EPMC7177933 | biostudies-literature

Antimicrobial Polymeric Composites with Embedded Nanotextured Magnesium Oxide.

Project description:Nanotextured magnesium oxide (MgO) can exhibit both antibacterial and tissue regeneration activity, which makes it very useful for implant protection. To successfully combine these two properties, MgO needs to be processed within an appropriate carrier system that can keep MgO surface available for interactions with cells, slow down the conversion of MgO to the less active hydroxide and control MgO solubility. Here we present new composites with nanotextured MgO microrods embedded in different biodegradable polymer matrixes: poly-lactide-co-glycolide (PLGA), poly-lactide (PLA) and polycaprolactone (PCL). Relative to their hydrophilicity, polarity and degradability, the matrices were able to affect and control the structural and functional properties of the resulting composites in different manners. We found PLGA matrix the most effective in performing this task. The application of the nanotextured 1D morphology and the appropriate balancing of MgO/PLGA interphase interactions with optimal polymer degradation kinetics resulted in superior bactericidal activity of the composites against either planktonic E. coli or sessile S. epidermidis, S. aureus (multidrug resistant-MRSA) and three clinical strains isolated from implant-associated infections (S. aureus, E. coli and P. aeruginosa), while ensuring controllable release of magnesium ions and showing no harmful effects on red blood cells.

| S-EPMC8271688 | biostudies-literature

Effect of Stress Ratio and Loading Frequency on the Corrosion Fatigue Behavior of Smooth Steel Wire in Different Solutions.

Project description:In this work, the effects of loading condition and corrosion solution on the corrosion fatigue behavior of smooth steel wire were discussed. The results of polarization curves and weight loss curves showed that the corrosion of steel wire in acid solution was more severe than that in neutral and alkaline solutions. With the extension of immersion time in acid solution, the cathodic reaction of steel wire gradually changed from the reduction of hydrogen ion to the reduction of oxygen, but was always the reduction of hydrogen ion in neutral and alkaline solutions. The corrosion kinetic parameters and equivalent circuits of steel wires were also obtained by simulating the Nyquist diagrams. In corrosion fatigue test, the effect of stress ratio and loading frequency on the crack initiation mechanism was emphasized. The strong corrosivity of acid solution could accelerate the nucleation of crack tip. The initiation mechanism of crack under different conditions was summarized according to the side and fracture surface morphologies. For the crack initiation mechanism of anodic dissolution, the stronger the corrosivity of solution was, the more easily the fatigue crack source formed, while, for the crack initiation mechanism of deformation activation, the lower stress ratio and higher frequency would accelerate the generation of corrosion fatigue crack source.

| S-EPMC5457049 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data