Preparation and Properties of Alkali Activated Metakaolin-Based Geopolymer.

ABSTRACT: The effective activation and utilization of metakaolin as an alkali activated geopolymer precursor and its use in concrete surface protection is of great interest. In this paper, the formula of alkali activated metakaolin-based geopolymers was studied using an orthogonal experimental design. It was found that the optimal geopolymer was prepared with metakaolin, sodium hydroxide, sodium silicate and water, with the molar ratio of SiO₂:Al₂O₃:Na₂O:NaOH:H₂O being 3.4:1.1:0.5:1.0:11.8. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) were adopted to investigate the influence of curing conditions on the mechanical properties and microstructures of the geopolymers. The best curing condition was 60 °C for 168 h, and this alkali activated metakaolin-based geopolymer showed the highest compression strength at 52.26 MPa. In addition, hollow micro-sphere glass beads were mixed with metakaolin particles to improve the thermal insulation properties of the alkali activated metakaolin-based geopolymer. These results suggest that a suitable volume ratio of metakaolin to hollow micro-sphere glass beads in alkali activated metakaolin-based geopolymers was 6:1, which achieved a thermal conductivity of 0.37 W/mK and compressive strength of 50 MPa. By adjusting to a milder curing condition, as-prepared alkali activated metakaolin-based geopolymers could find widespread applications in concrete thermal protection.

SUBMITTER: Chen L

PROVIDER: S-EPMC5457102 | biostudies-other | 2016 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Geopolymer Based on Mechanically Activated Air-cooled Blast Furnace Slag.

Project description:An efficient solution to increase the sustainability of building materials is to replace Portland cement with alkali-activated materials (AAM). Precursors for those systems are often based on water-cooled ground granulated blast furnace slags (GGBFS). Quenching of blast furnace slag can be done also by air but in that case, the final product is crystalline and with a very low reactivity. The present study aimed to evaluate the cementitious properties of a mechanically activated (MCA) air-cooled blast furnace slag (ACBFS) used as a precursor in sodium silicate alkali-activated systems. The unreactive ACBFS was processed in a planetary ball mill and its cementing performances were compared with an alkali-activated water-cooled GGBFS. Mixes based on mechanically activated ACBFS reached the 7-days compressive strength of 35 MPa and the 28-days compressive strength 45 MPa. The GGBFS-based samples showed generally higher compressive strength values.

| S-EPMC7085006 | biostudies-literature

Innovative Fly Ash Geopolymer-Epoxy Composites: Preparation, Microstructure and Mechanical Properties.

Project description:The preparation and characterization of composite materials based on geopolymers obtained from fly ash and epoxy resins are reported for the first time. These materials have been prepared through a synthetic method based on the concurrent reticulation of the organic and inorganic components that allows the formation of hydrogen bonding between the phases, ensuring a very high compatibility between them. These new composites show significantly improved mechanical properties if compared to neat geopolymers with the same composition and comparable performances in respect to analogous geopolymer-based composites obtained starting from more expensive raw material such as metakaolin. The positive combination of an easy synthetic approach with the use of industrial by-products has allowed producing novel low cost aluminosilicate binders that, thanks to their thixotropicity and good adhesion against materials commonly used in building constructions, could be used within the field of sustainable building.

| S-EPMC5456760 | biostudies-other

Preparation of a Composite Calcium Silicate Board with Carbide Slag and Coal-Based Solid Waste Activated by Different Alkali Activators.

Project description:Overall performance of composite calcium silicate boards (CCSBs) was investigated to further promote their application. The alkali activators were used to fully hydrate the calcium and silicon raw materials, which further improved the comprehensive performance of the CCSBs made of four pure industrial solid wastes. Within the range of dosage in this study, single doping of different proportions of the alkali activator improved the flexural strength of the CCSB. Based on this, the mechanical properties of the CCSB were further improved as the compounded alkali activator was optimized. Flexural strength is improved when the average pore diameter was refined. The freeze-thaw cycle test shows that a compound-doped alkali activator can effectively reduce the mass loss and strength loss, thereby improving the frost resistance of this material. This research discussed an economically affordable approach to prepare the CCSB material made of industrial solid waste.

| S-EPMC7178769 | biostudies-literature

Influence of Activators on Mechanical Properties of Modified Fly Ash Based Geopolymer Mortars.

Project description:The aim of this work was to study the influence of the type of activator on the formulation of modified fly ash based geopolymer mortars. Geopolymer and alkali-activated materials (AAM) were made from fly ashes derived from coal and biomass combustion in thermal power plants. Basic activators (NaOH, CaO, and Na2SiO3) were mixed with fly ashes in order to develop binding properties other than those resulting from the use of Portland cement. The results showed that the mortars with 5 mol/dm3 of NaOH and 100 g of Na2SiO3 (N5-S22) gave a greater compressive strength than other mixes. The compressive strengths of analyzed fly ash mortars with activators N5-S22 and N5-C10 (5 mol/dm3 NaOH and 10% CaO) varied from 14.3 MPa to 5.9 MPa. The better properties of alkali-activated mortars with regular fly ash were influenced by a larger amount of amorphous silica and alumina phases. Scanning electron microscopy and calorimetry analysis provided a better understanding of the observed mechanisms.

| S-EPMC7084247 | biostudies-literature

Concreting a sustainable future: A dataset of alkali-activated concrete and its properties.

Project description:This data article introduces a dataset comprising 1630 alkali-activated concrete (AAC) mixes, compiled from 106 literature sources. The dataset underwent extensive curation to address feature redundancy, transcription errors, and duplicate data, yielding refined data ready for further data-driven science in the field of AAC, where this effort constitutes a novelty. The carbon footprint associated with each material used in the AAC mixes, as well as the corresponding CO2 footprint of every mix, were approximated using two published articles. Serving as a foundation for future expansions and rigorous data applications, this dataset enables the characterization of AAC properties through machine learning algorithms or as a benchmark for performance comparison among different formulations. In summary, the dataset provides a resource for researchers focusing on AAC and related materials and offers insights into the environmental benefits of substituting traditional Portland concrete with AAC.

| S-EPMC10493887 | biostudies-literature

Preparation of acid aluminum phosphate solutions for metakaolin phosphate geopolymer binder.

Project description:This work assessed the potential of synthetic acid aluminum phosphate solutions for the enhancement of the characteristics of metakaolin phosphate geopolymer binders obtained at room temperature. The main parameters dealt with are the concentration of the initial phosphoric acid solution (40 wt%, 50 wt%, and 60 wt%) and the molar ratio Al/P (1/3 and 1.4/3) of the synthesized acid aluminum phosphate solutions. The prepared solutions have different contents and types of mono aluminum phosphate compounds (MAP) and their reactivity is pH-dependent. This is because of the continuous neutralization of the protons due to the dissolution of aluminum hydroxide, which raises the pH and decreases the conductivity. Thus the acid aluminum phosphate solutions with molar ratio Al/P of 1/3 are the most reactive. They have significantly enhanced the compressive strength of the resulting phosphate geopolymer binders. But, when compared to phosphate geopolymer obtained with pure phosphoric acid of the same concentration, the highest rate of compressive strength improvement is recorded for acid aluminum phosphate solutions having an initial concentration of phosphoric acid of 40 wt%. Thus, the modification of the composition of the phosphoric acid with the addition of the appropriate amount of aluminum is beneficial for enhancing the characteristics of phosphate geopolymer binder at any age.

| S-EPMC9041915 | biostudies-literature

Microstructural and Mechanical Properties of Alkali Activated Colombian Raw Materials.

Project description:Microstructural and mechanical properties of alkali activated binders based on blends of Colombian granulated blast furnace slag (GBFS) and fly ash (FA) were investigated. The synthesis of alkali activated binders was conducted at 85 °C for 24 h with different slag/fly ash ratios (100:0, 80:20, 60:40, 40:60, 20:80, and 0:100). Mineralogical and microstructural characterization was carried out by means of X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM/EDX) and Nuclear magnetic resonance (NMR). Mechanical properties were evaluated through the compressive strength, modulus of elasticity and Poisson's ratio. The results show that two different reaction products were detected in the slag/fly ash mixtures, a calcium silicate hydrate with Al in its structure (C-A-S-H gel) and a sodium aluminosilicate hydrate (N-A-S-H gel) with higher number of polymerized species and low content in Ca. It was found that with the increase of the amount of added slag, the amount of C-A-S-H gel increased and the amount of N-A-S-H gel decreased. The matrix was more dense and compact with almost absence of pores. The predominance of slag affected positively the compressive strength, Young's modulus and Poisson's ratio, with 80% slag and 20% fly ash concrete being the best mechanical performance blend.

| S-EPMC5456669 | biostudies-other

Preparation, characterization, electrical conductivity, and life cycle assessment of carbon nanofibers-reinforced Ecuadorian natural zeolite-based geopolymer composites.

Project description:Geopolymers are inorganic crosslinked polymers with much less carbon footprint than ordinary Portland cement. Geopolymers and geopolymer-based materials have superior mechanical and durability properties with extreme thermal and chemical resistance. Carbon nano- or microfibers-reinforced geopolymers show potential properties such as electric conductivity, enhanced mechanical and thermal stability, and multi-functionality. This study evaluated the effect of incorporating carbon nanofibers in natural zeolite-based geopolymers and their impact on the mechanical, thermal, and electric conductivity of yielded geopolymer composites. Additionally, a life cycle assessment for 1 m3 geopolymer and its carbon fiber reinforced geopolymers' production has been conducted to evaluate the environmental impact of the processes.

| S-EPMC10957430 | biostudies-literature

Orthogonal Experimental Study on the Factors Affecting the Mechanical Properties of Alkali-Activated Slag Materials.

Project description:Blast furnace slag is one of the largest solid wastes in the world. The slag-based geopolymer obtained by alkali activation has many advantages, such as a high strength, a good corrosion resistance, low carbon and environmental protection. Existing studies have shown that the mechanical properties of slag-based geopolymers are related to the combined effects of many factors, but there is still a lack of reliable conclusions on the primary and secondary influence degree of each factor, which greatly affects the scientific preparation and application of slag-based geopolymers. In order to solve this problem, we choose to proceed from the two perspectives of the mix ratio of the alkali activator and the elemental composition of raw materials. Through the orthogonal analysis method, this paper studies the influence of the modulus of the alkali activator, the solid-to-liquid ratio of the activator, the water-cement ratio and the metakaolin replacement rate on the uniaxial compressive strength of a slag-based geopolymer. The results show that when the solid-liquid ratio is about 0.25, the modulus of the alkali activator is 1.3~1.5, the water-cement ratio is about 0.4 and the samples with higher strength can be prepared. With the addition of metakaolin, a new gel phase NASH was formed in the system, which significantly promoted the late strength and toughness growth of the sample. The research results comprehensively analyze the influence of different factors on the mechanical properties of the slag-based geopolymer, which can provide a valuable reference for the engineering application of alkali-activated slag materials.

| S-EPMC9782184 | biostudies-literature

Resistance to Chemical Attack of Hybrid Fly Ash-Based Alkali-Activated Concretes.

Project description:The environmental impacts related to Portland cement production in terms of energy consumption, the massive use of natural resources and CO2 emissions have led to the search for alternative cementitious materials. Among these materials, alkali-activated cements based on fly ash (FA) have been considered for concrete production with greater sustainability. In the present article, the chemical durability properties (resistance to sulphates, chloride permeability, and resistance to carbonation) of a hybrid alkali-activated concrete based on fly ash-ordinary Portland cement (FA/OPC) with proportions of 80%/20% were evaluated. It is noted that the FA was a low-quality pozzolan with a high unburned carbon content (20.67%). The results indicated that FA/OPC concrete had good durability with respect to the OPC concrete, with 95% less expansion in the presence of sodium sulphate and a 2% strength loss at 1100 days, compared with the 56% strength loss of the OPC concrete. In addition, FA/OPC showed lower chloride permeability. On the contrary, the FA/OPC was more susceptible to carbonation. However, the residual compressive strength was 23 MPa at 360 days of CO2 exposure. Based on the results, FA/OPC, using this type of FA, can be used as a replacement for OPC in the presence of these aggressive agents in the service environment.

| S-EPMC7435788 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data