Experimental Study on Reaction Characteristics of PTFE/Ti/W Energetic Materials under Explosive Loading.

ABSTRACT: Metal/fluoropolymer composites represent a new category of energetic structural materials that release energy through exothermic chemical reactions initiated under shock loading conditions. This paper describes an experiment designed to study the reaction characteristics of energetic materials with low porosity under explosive loading. Three PTFE (polytetrafluoroethylene)/Ti/W mixtures with different W contents are processed through pressing and sintering. An inert PTFE/W mixture without reactive Ti particles is also prepared to serve as a reference. Shock-induced chemical reactions are recorded by high-speed video through a narrow observation window. Related shock parameters are calculated based on experimental data, and differences in energy release are discussed. The results show that the reaction propagation of PTFE/Ti/W energetic materials with low porosity under explosive loading is not self-sustained. As propagation distance increases, the energy release gradually decreases. In addition, reaction failure distance in PTFE/Ti/W composites is inversely proportional to the W content. Porosity increased the failure distance due to higher shock temperature.

SUBMITTER: Li Y

PROVIDER: S-EPMC5457232 | biostudies-other | 2016 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:The deformation and fracture characteristics of shale in the Changning-Xingwen region were experimentally studied under triaxial cyclic loading with a controlled pore-water pressure. An RLW-2000M microcomputer-controlled coal-rock rheometer was used in the State key Laboratory of coal mine disaster dynamics and control in Chongqing University. These experimental results have indicated the following. (i) The shale softened after being saturated with water, while its failure strength decreased with the increase of axial strain. (ii) A complete cyclic loading-unloading process can be divided into four stages under the coupling action of axial cyclic loading and pore-water pressure; namely the slow or accelerated increasing of strain in the loading stage, and the slow or accelerated decreasing of strain in the unloading stage. (iii) The axial plastic deformation characteristics were similar when pore-water pressures were set to 2, 6 and 10 MPa. Nevertheless, the shale softened ostensibly and fatigue damage occurred during the circulation process when the pore-water pressure was set to 14 MPa. (iv) It has been observed that the mean strain and strain amplitude under axial cyclic are positively correlated with pore-water pressure, while the elastic modulus is negatively correlated with pore-water pressure. As the cycle progresses, the trends in these parameters vary, which indicates that the deformation and elastic characteristics of shale are controlled by pore-water pressure and cyclic loading conditions. (v) Evidenced via triaxial compression tests, it was predominantly shear failure that occurred in the shale specimens. In addition, axial cyclic loading caused the shale to generate complex secondary fractures, resulting in the specimens cracking along the bedding plane due to the effect of pore-water pressure. This study provides valuable insight into the understanding of the deformation and failure mechanisms of shale under complicated stress conditions.

Dataset Information

Experimental Study on Reaction Characteristics of PTFE/Ti/W Energetic Materials under Explosive Loading.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets