Polyols from Microwave Liquefied Bagasse and Its Application to Rigid Polyurethane Foam.

ABSTRACT: Bagasse flour (BF) was liquefied using bi-component polyhydric alcohol (PA) as a solvent and phosphoric acid as a catalyst in a microwave reactor. The effect of BF to solvent ratio and reaction temperatures on the liquefaction extent and characteristics of liquefied products were evaluated. The results revealed that almost 75% of the raw bagasse was converted into liquid products within 9 min at 150 °C with a BF to solvent ratio of 1/4. The hydroxyl and acid values of the liquefied bagasse (LB) varied with the liquefied conditions. High reaction temperature combining with low BF to solvent ratio resulted in a low hydroxyl number for the LB. The molecular weight and polydispersity of the LB from reactions of 150 °C was lower compared to that from 125 °C. Rigid polyurethane (PU) foams were prepared from LB and methylene diphenyl diisocyanate (MDI), and the structural, mechanical and thermal properties of the PU foam were evaluated. The PU foams prepared using the LB from high reaction temperature showed better physical and mechanical performance in comparison to those from low reaction temperature. The amount of PA in the LB has the ability of increasing thermal stability of LB-PU foams. The results in this study may provide fundamental information on integrated utilizations of sugarcane bagasse via microwave liquefaction process.

SUBMITTER: Xie J

PROVIDER: S-EPMC5458812 | biostudies-other | 2015 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Producing Lignin-Based Polyols through Microwave-Assisted Liquefaction for Rigid Polyurethane Foam Production.

Project description:Lignin-based polyols were synthesized through microwave-assisted liquefaction under different microwave heating times (5-30 min). The liquefaction reactions were carried out using polyethylene glycol (PEG-400)/glycerol as liquefying solvents and 97 wt% sulfur acid as a catalyst at 140 °C. The polyols obtained were analyzed for their yield, composition and structural characteristics using gel permeation chromatography (GPC), Fourier transform infrared (FT-IR) and nuclear magnetic resonance (NMR) spectra. FT-IR and NMR spectra showed that the liquefying solvents reacted with the phenol hydroxyl groups of the lignin in the liquefied product. With increasing microwave heating time, the viscosity of polyols was slightly increased and their corresponding molecular weight (MW) was gradually reduced. The optimal condition at the microwave heating time (5 min) ensured a high liquefaction yield (97.47%) and polyol with a suitable hydroxyl number (8.628 mmol/g). Polyurethane (PU) foams were prepared by polyols and methylene diphenylene diisocyanate (MDI) using the one-shot method. With the isocyanate/hydroxyl group ([NCO]/[OH]) ratio increasing from 0.6 to 1.0, their mechanical properties were gradually increased. This study provided some insight into the microwave-assisted liquefied lignin polyols for the production of rigid PU foam.

| S-EPMC5455266 | biostudies-other

Mechanical and Insulation Performance of Rigid Polyurethane Foam Reinforced with Lignin-Containing Nanocellulose Fibrils.

Project description:Isocyanates are critical components that affect the crosslinking density and structure of polyurethane (PU) foams. However, due to the cost and hazardous nature of the precursor for isocyanate synthesis, there is growing interest in reducing their usage in polyurethane foam production-especially in rigid PU foams (RPUF) where isocyanate is used in excess of the stoichiometric ratio. In this study, lignin-containing nanocellulose fibrils (LCNF) were explored as mechanical reinforcements for RPUF with the goal of maintaining the mechanical performance of the foam while using less isocyanate. Different amounts of LCNF (0-0.2 wt.%) were added to the RPUF made using isocyanate indices of 1.1, 1.05, 1.0, and 0.95. Results showed that LCNF served as a nucleating agent, significantly reducing cell size and thermal conductivity. LCNF addition increased the crosslinking density of RPUF, leading to enhanced compressive properties at an optimal loading of 0.1 wt.% compared to unreinforced foams at the same isocyanate index. Furthermore, at the optimal loading, LCNF-reinforced foams made at lower isocyanate indices showed comparable stiffness and strength to unreinforced foams made at higher isocyanate indices. These results highlight the reinforcing potential of LCNF in rigid polyurethane foams to improve insulation and mechanical performance with lower isocyanate usage.

| S-EPMC11313736 | biostudies-literature

Fire Suppression and Thermal Behavior of Biobased Rigid Polyurethane Foam Filled with Biomass Incineration Waste Ash.

Project description:Currently, there is great demand to implement circular economy principles and motivate producers of building materials to integrate into a closed loop supply chain system and improve sustainability of their end-product. Therefore, it is of great interest to replace conventional raw materials with inorganic or organic waste-based and filler-type additives to promote sustainability and the close loop chain. This article investigates the possibility of bottom waste incineration ash (WA) particles to be used as a flame retardant replacement to increase fire safety and thermal stability under higher temperatures. From 10 wt.% to 50 wt.% WA particles do not significantly deteriorate performance characteristics, such as compressive strength, thermal conductivity, and water absorption after 28 days of immersion, and at 32 °C WA particles improve the thermal stability of resultant PU foams. Furthermore, 50 wt.% WA particles reduce average heat release by 69% and CO2 and CO yields during fire by 76% and 77%, respectively. Unfortunately, WA particles do not act as a smoke suppressant and do not reduce smoke release rate.

| S-EPMC7182938 | biostudies-literature

Enhanced Fire Safety of Rigid Polyurethane Foam via Synergistic Effect of Phosphorus/Nitrogen Compounds and Expandable Graphite.

Project description:In order to explore highly efficient flame-retardant rigid polyurethane foam (RPUF), phosphorus/nitrogen compounds and expandable graphite (EG) were successfully incorporated into RPUF by a free one-spot method. The combustion results showed that the fire safety of the RPUF samples was remarkably improved by the addition of phosphoric/nitrogen compounds and EG. With the incorporation of 22.4 wt.% phosphorus/nitrogen compounds and 3.2 wt.% EG, the RPUF composites achieved UL-94 V-0 rating. Besides, the total heat release and total smoke release of RPUF composites were reduced by 29.6% and 32.4% respectively, compared to those of the pure RPUF sample. PO• and PO2• together with nonflammable gaseous products were evolved from phosphoric/nitrogen compounds in the gas phase, which quenched the flammable free radicals in the matrix and diluted the concentration of combustible gaseous products generated from PRUF during combustion. The compact char residues which acted as excellent physical barriers were formed by catalysis of EG and phosphoric/nitrogen compounds in the condense phase. The fire hazard of RPUF was significantly reduced by the synergistic effect of phosphorus-nitrogen compounds and EG. This work provides a promising strategy to enhance the fire safety of RPUF.

| S-EPMC7587603 | biostudies-literature

Liquefaction of Lignin Using Chemical Decomposition and Its Application to Polyurethane Foam.

Project description:To utilize the chemical application of lignin (LN), a decomposition reaction was carried out to cleave chemical bonds. Indeed, a liquefaction process is essential for the chemical use of lignin to achieve a uniform reaction and maximize the chemical utility of lignin. To this end, hydroxyl radicals were adopted as a powerful oxidation agent, and FT-IR results confirmed the cleavage of the ether linkages. Additionally, the water solubility of LN significantly increased after decomposition, and dissolution levels up to 0.5 g·mL-1 were obtained. Using these high solubility properties in water, NMR and DLS analyses were performed. In particular, an average particle diameter of 300 ± 240 nm was found, corresponding to the size of polydisperse l-LN. By controlling size uniformity and using high water-solubility levels, polyurethane foams were manufactured using l-LN.

| S-EPMC8153736 | biostudies-literature

Synthesis of Lightweight Renewable Microwave-Absorbing Bio-Polyurethane/Fe3O4 Composite Foam: Structure Analysis and Absorption Mechanism

Project description:Sustainable renewable polymer foam used as a lightweight porous skeleton for microwave absorption is a novel strategy that can effectively solve the problems of the large surface density, high additive amount, and narrow absorbing band of absorbing materials. In this article, novel renewable microwave-absorbing foams were prepared using Sapiumse biferum kernel oil-based polyurethane foam (BPUF) as porous matrix and Fe3O4-nanoparticles as magnetic absorbents. The microstructure and the microwave absorption performance, the structural effects on the properties, and electromagnetic mechanism of the magnetic BPUF (mBPUF) were systematically characterized and analyzed. The results show that the mBPUF displayed a porous hierarchical structure and was multi-interfacial, which provided a skeleton and matching layer for the Fe3O4 nanoparticles. The effective reflection loss (RL ≤ −10 dB) frequency of the mBPUF was from 4.16 GHz to 18 GHz with only 9 wt% content of Fe3O4 nanoparticles at a thickness of 1.5~5 mm. The surface density of the mBPUF coatings was less than 0.5 kg/cm2 at a thickness of 1.8 mm. The lightweight characteristics and broadband absorption were attributed to the porous hierarchical structures and the dielectric combined with the magnetic loss effect. It indicates that the mBPUF is a prospective broadband-absorbing material in the field of lightweight stealth materials.

| S-EPMC9603621 | biostudies-literature

Development of High-Performance Coconut Oil-Based Rigid Polyurethane-Urea Foam: A Novel Sequential Amidation and Prepolymerization Process.

Project description:The utilization of coconut diethanolamide (p-CDEA) as a substitute polyol for petroleum-based polyol in fully biobased rigid polyurethane-urea foam (RPUAF) faces challenges due to its short chain and limited cross-linking capability. This leads to compromised cell wall resistance during foam expansion, resulting in significant ruptured cells and adverse effects on mechanical and thermal properties. To address this, a novel sequential amidation-prepolymerization route was employed on coconut oil, yielding a hydroxyl-terminated poly(urethane-urea) prepolymer polyol (COPUAP). Compared to p-CDEA, COPUAP exhibited a decreased hydroxyl value (496.3-473.2 mg KOH/g), an increase in amine value (13.464-24.561 mg KOH/g), and an increase in viscosity (472.4-755.8 mPa·s), indicating enhanced functionality of 34.3 mgKOH/g and chain lengthening. Further, COPUAP was utilized as the sole B-side polyol in the production of RPUAF (PU-COPUAP). The improved functionality of COPUAP and its improved cross-linking capability during foaming have significantly improved cell morphology, resulting in a remarkable 4.7-fold increase in compressive strength (132-628 kPa), a 3.5-fold increase in flexural strength (232-828 kPa), and improved insulation properties with a notable decrease in thermal conductivity (48.02-34.52 mW/m·K) compared to PU-CDEA in the literature. Additionally, PU-COPUAP exhibited a 16.5% increase in the water contact angle (114.93° to 133.87°), attributing to the formation of hydrophobic biuret segments and a tightly packed, highly cross-linked structure inhibiting water penetration. This innovative approach sets a new benchmark for fully biobased rigid foam production, delivering high load-bearing capacity, exceptional insulation, and significantly improved hydrophobicity.

| S-EPMC10956093 | biostudies-literature

Biodegradable, Flame-Retardant, and Bio-Based Rigid Polyurethane/Polyisocyanurate Foams for Thermal Insulation Application.

Project description:This article raised the issue of studies on the use of new bio-polyol based on white mustard seed oil and 2,2'-thiodiethanol (3-thiapentane-1,5-diol) for the synthesis of rigid polyurethane/polyisocyanurate (RPU/PIR) foams. For this purpose, new formulations of polyurethane materials were prepared. Formulations contained bio-polyol content from 0 to 0.4 chemical equivalents of hydroxyl groups. An industrial flame retardant, tri(2-chloro-1-methylethyl) phosphate (Antiblaze TCMP), was added to half of the formulations. Basic foaming process parameters and functional properties, such as apparent density, compressive strength, brittleness, absorbability and water absorption, aging resistance, thermal conductivity coefficient λ, structure of materials, and flammability were examined. The susceptibility of the foams to biodegradation in soil was also examined. The increase in the bio-polyol content caused a slight increase in processing times. Also, it was noted that the use of bio-polyol had a positive effect on the functional properties of obtained RPU/PIR foams. Foams modified by bio-polyol based on mustard seed oil showed lower apparent density, brittleness, compressive strength, and absorbability and water absorption, as well as thermal conductivity, compared to the reference (unmodified) foams. Furthermore, the obtained materials were more resistant to aging and more susceptible to biodegradation.

| S-EPMC6918136 | biostudies-literature

Rational Design of a Polyurethane Foam.

Project description:Polyurethane (PU) foams are exceptionally versatile due to the nature of PU bond formation and the large variety of polymeric backbones and formulation components such as catalysts and surfactants. This versatility introduces a challenge, namely a near unlimited number of variables for formulating foams. In addition to this, PU foam development requires expert knowledge, not only in polyurethane chemistry but also in the art of evaluating the resulting foams. In this work, we demonstrate that a rational experimental design framework in conjunction with a design of experiments (DoE) approach reduces both the number of experiments required to understand the formulation space and reduces the need for tacit knowledge from a PU expert. We focus on an in-depth example where a catalyst and two surfactants of a known formulation are set as factors and foam physical properties are set as responses. An iterative DoE approach is used to generate a set of foams with substantially different cell morphology and hydrodynamic behaviour. We demonstrate that with 23 screening formulations and 16 final formulations, foam physical properties can be modelled from catalyst and surfactant loadings. This approach also allows for the exploration of relationships between the cell morphology of PU foam and its hydrodynamic behaviour.

| S-EPMC9736621 | biostudies-literature

Influence of the Characteristics of Expandable Graphite on the Morphology, Thermal Properties, Fire Behaviour and Compression Performance of a Rigid Polyurethane Foam.

Project description:Three types of expandable graphite (EG) differing in particle size and expansion volume, are compared as flame retardant additives to rigid polyurethane foams (RPUFs). In this paper we discuss microstructure, thermal stability, fire behavior, and compression performance. We find that ell size distributions were less homogeneous and cell size was reduced. Furthermore, thermal conductivity increased along with EG loading. Thermogravimetric analysis (TGA) showed that EG only increased residue yield differently. The results indicate that a higher expansion of EG increased the limiting oxygen index (LOI) value, whereas a bigger particle size EG improved the rating of the vertical burning test (UL94). Results from the cone calorimeter test showed that a bigger particle size EG effectively reduced peak of heat release rate (pHRR). Furthermore, a higher expansion, led to a decrease in smoke production (TSP). The combination of both characteristics gives extraordinary results. The physical⁻mechanical characterization of the EG/RPUF foams revealed that their compression performance decreased slightly, mostly due to the effect of a bigger size EG.

| S-EPMC6401788 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data