Very High Cycle Fatigue Failure Analysis and Life Prediction of Cr-Ni-W Gear Steel Based on Crack Initiation and Growth Behaviors.

ABSTRACT: The unexpected failures of structural materials in very high cycle fatigue (VHCF) regime have been a critical issue in modern engineering design. In this study, the VHCF property of a Cr-Ni-W gear steel was experimentally investigated under axial loading with the stress ratio of R = -1, and a life prediction model associated with crack initiation and growth behaviors was proposed. Results show that the Cr-Ni-W gear steel exhibits the constantly decreasing S-N property without traditional fatigue limit, and the fatigue strength corresponding to 10⁸ cycles is around 485 MPa. The inclusion-fine granular area (FGA)-fisheye induced failure becomes the main failure mechanism in the VHCF regime, and the local stress around the inclusion play a key role. By using the finite element analysis of representative volume element, the local stress tends to increase with the increase of elastic modulus difference between inclusion and matrix. The predicted crack initiation life occupies the majority of total fatigue life, while the predicted crack growth life is only accounts for a tiny fraction. In view of the good agreement between the predicted and experimental results, the proposed VHCF life prediction model involving crack initiation and growth can be acceptable for inclusion-FGA-fisheye induced failure.

SUBMITTER: Deng H

PROVIDER: S-EPMC5458838 | biostudies-other | 2015 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Analysis of Fatigue Crack Paths in Cold Drawn Pearlitic Steel.

Project description:In this paper, a fracto-metallographic analysis was performed on the cracked specimens of cold drawn pearlitic steel subjected to fatigue tests. Fatigue cracks are transcollonial and exhibit a preference for fracturing pearlitic lamellae, with non-uniform crack opening displacement values, micro-discontinuities, branchings, bifurcations and frequent local deflections that create microstructural roughness. At the micro-level, the cold drawn pearlitic steel exhibits higher micro-roughness than the hot rolled bar (this is a consequence of the manufacturing process by cold drawing), so that the actual fractured surface in the cold drawn wire is greater than that in the hot rolled bar, due to the fact that the crack deflection events are more frequent and with higher angle in the former (the heavily drawn prestressing steel wire). These findings show the relevant role on the manufacturing process by cold drawing in the fatigue crack propagation in pearlitic steel.

| S-EPMC5458916 | biostudies-other

Antagonistic fatigue crack acceleration/deceleration phenomena in Ni-based superalloy 718 under hydrogen-supply.

Project description:Mechanical properties of structural alloys, including Ni-based superalloy 718 (Alloy718), are degraded when hydrogen (H) is supplied: hydrogen embrittlement (HE). The presence of H notably deteriorates fatigue crack growth (FCG) property, which renders the growth rate much higher and shortens the lifetime of the components operating in the hydrogenating environment. Hence, the mechanisms behind such acceleration phenomenon in FCG should be understood comprehensively toward developing promising alloys resistant to hydrogen occlusion. In particular, Alloy718 has a meager resistance to HE, even regularly displaying superior mechanical and physical performances. Notwithstanding, the present study unveiled that the FCG acceleration by dissolved H in Alloy718 can be negligible. An abnormal deceleration of FCG can instead be pronounced by optimizing the metallurgical state, a hopeful prospect in Ni-based alloys applied to the hydrogenating environment.

| S-EPMC10133311 | biostudies-literature

Role of slip in hydrogen-assisted crack initiation in Ni-based alloy 725.

Project description:We conduct in situ tensile straining experiments to investigate the role of hydrogen and slip in crack initiation in nickel-based alloy 725. Our experiments reveal no tendency for hydrogen to enhance localized slip and no necessity of slip for crack initiation. We use electrochemical charging to introduce hydrogen into samples, melt extraction to measure hydrogen content, and digital image correlation to analyze localized plastic strains during in situ tensile tests in a scanning electron microscope. Cracks initiate both in regions with and without nearby localized slip. Moreover, the fraction of cracks initiating with no nearby slip is greater at higher hydrogen content. Slip-assisted crack initiation generally occurs at locations where intergranular slip is arrested, especially at intersections of slipping coherent twin boundaries with thin twin lamellae. Cracks that initiate without nearby slip occur at a wider variety of microstructural features, including inclusions, triple junctions, and surface flaws.

| S-EPMC466962 | biostudies-literature

Internal crack characteristics in very-high-cycle fatigue of a gradient structured titanium alloy.

Project description:Gradient structure (GS) is commonly designed and processed in engineering materials to improve mechanical properties especially fatigue performance by taking advantage of the strengthened surface. However, whether the very-high-cycle fatigue (VHCF) property can be improved by GS is questioning due to the different crack initiation mechanisms between low-, high-cycle and VHCF. In this paper, GS of a Ti-6Al-4V alloy is generated by pre-torsion and characterized by electron backscatter diffraction. Then the VHCF behavior of the GS specimen is studied. The fractography and synchrotron radiation X-ray microtomography presented detailed characteristics of the internal crack initiation region in VHCF of the titanium alloy with GS. The results indicated that, in contrast to the low- and high-cycle regimes, the VHCF strength is reduced for the specimens with GS. Thus, the GS induced by pre-torsion cannot enhance the VHCF strength of the titanium alloy. This implies that VHCF test (property) is an important consideration for the microstructural designed materials. The graphical abstract is available in Supplementary information.

| S-EPMC7075889 | biostudies-literature

The Influence of Porosity on Fatigue Crack Initiation in Additively Manufactured Titanium Components.

Project description:Without post-manufacture HIPing the fatigue life of electron beam melting (EBM) additively manufactured parts is currently dominated by the presence of porosity, exhibiting large amounts of scatter. Here we have shown that the size and location of these defects is crucial in determining the fatigue life of EBM Ti-6Al-4V samples. X-ray computed tomography has been used to characterise all the pores in fatigue samples prior to testing and to follow the initiation and growth of fatigue cracks. This shows that the initiation stage comprises a large fraction of life (>70%). In these samples the initiating defect was often some way from being the largest (merely within the top 35% of large defects). Using various ranking strategies including a range of parameters, we found that when the proximity to the surface and the pore aspect ratio were included the actual initiating defect was within the top 3% of defects ranked most harmful. This lays the basis for considering how the deposition parameters can be optimised to ensure that the distribution of pores is tailored to the distribution of applied stresses in additively manufactured parts to maximise the fatigue life for a given loading cycle.

| S-EPMC5544733 | biostudies-literature

Healing of Fatigue Crack in 1045 Steel by Using Eddy Current Treatment.

Project description:In order to investigate the methods to heal fatigue cracks in metals, tubular specimens of 1045 steel with axial and radial fatigue cracks were treated under the eddy current. The optical microscope was employed to examine the change of fatigue cracks of specimens before and after the eddy current treatment. The results show that the fatigue cracks along the axial direction of the specimen could be healed effectively in the fatigue crack initiation zone and the crack tip zone under the eddy current treatment, and the healing could occur within a very short time. The voltage breakdown and the transient thermal compressive stress caused by the detouring of eddy current around the fatigue crack were the main factors contributing to the healing in the fatigue crack initiation zone and the crack tip zone, respectively. Eddy current treatment may be a novel and effective method for crack healing.

| S-EPMC5509091 | biostudies-other

Influence of Residual Stress Field on the Fatigue Crack Propagation in Prestressing Steel Wires.

Project description:This paper deals with the effect of several residual stress profiles on the fatigue crack propagation in prestressing steel wires subjected to tension loading or bending moment. To this end, a computer program was developed to evaluate the crack front evolution on the basis of the Walker law. Results demonstrate that the absence of residual stresses makes the crack propagate towards a preferential crack path. When surface residual stresses are tensile and, correspondingly, core residual stresses are compressive, the fatigue crack fronts rapidly converge towards a quasi-straightshape. When surface residual stresses are compressive, with their corresponding tensile stresses in the core area, a preferential crack path also appears.

| S-EPMC5458905 | biostudies-other

Fatigue Life Prediction Based on Crack Closure and Equivalent Initial Flaw Size.

Project description:Failure analysis and fatigue life prediction are necessary and critical for engineering structural materials. In this paper, a general methodology is proposed to predict fatigue life of smooth and circular-hole specimens, in which the crack closure model and equivalent initial flaw size (EIFS) concept are employed. Different effects of crack closure on small crack growth region and long crack growth region are considered in the proposed method. The EIFS is determined by the fatigue limit and fatigue threshold stress intensity factor △Kth. Fatigue limit is directly obtained from experimental data, and △Kth is calculated by using a back-extrapolation method. Experimental data for smooth and circular-hole specimens in three different alloys (Al2024-T3, Al7075-T6 and Ti-6Al-4V) under multiple stress ratios are used to validate the method. In the validation section, Semi-circular surface crack and quarter-circular corner crack are assumed to be the initial crack shapes for the smooth and circular-hole specimens, respectively. A good agreement is observed between model predictions and experimental data. The detailed analysis and discussion are performed on the proposed model. Some conclusions and future work are given.

| S-EPMC5455393 | biostudies-other

Prediction of 316 stainless steel low-cycle fatigue life based on machine learning

Project description:The low-cycle fatigue life of 316 stainless steel is a significant basis for safety assessment. Usually, many factors affect the low-cycle fatigue life of stainless steel, and the relationship between the influencing factors and fatigue life is complicated and nonlinear. Therefore, it is hard to predict fatigue life using the traditional empirical formula. Based on this, a machine learning algorithm is proposed. In this paper, based on the large amount of existing experimental data, machine learning methods are used to predict the low circumferential fatigue life of 316 stainless steel. The results show that the prediction accuracy of nu-SVR and ELM models is high and can meet engineering needs.

| S-EPMC10130168 | biostudies-literature

Bending Fatigue Behaviour and Fatigue Endurance Limit Prediction of 20Cr2Ni4A Gear Steel after the Ultrasonic Surface Rolling Process.

Project description:To study the effect of the surface properties on the bending fatigue performance of heavy-duty gear steel, the authors of this paper used the ultrasonic surface rolling process (USRP) to strengthen 20Cr2Ni4A carburized gear steel. USRP is a novel technique in which the ultrasonic technology is incorporated into the concept of conventional deep rolling. In this study, we illustrated how the surface properties and cross-section mechanical property influence the three-point bending fatigue life of the samples before and after USRP treatment. At the same time, the predicted failure probability-stress-number of cycles (P-S-N) curve was drawn, and the fatigue fracture was analysed. The results show that the fatigue limit increased from 651.36 MPa to 918.88 MPa after USRP treatment. The fatigue source is mainly from the sample interior or surface scratches, and the fatigue performance is positively correlated with the results of the material surface roughness, surface residual stress and surface hardness. At the same time, combined with the change in the phase structure, dislocation structure, residual stress and hardness of the cross section of the material, it is found that the USRP process turns the steel into a gradient material with five layers. Finally, the coupling mechanism between the ultrasonic surface strengthening deformation layer and the carburized layer of 20Cr2Ni4A carburized gear steel is presented, and the grain structure distribution diagram of the section of the 20Cr2Ni4A model after surface strengthening treatment was simulated. The mechanism that influenced the fatigue performance after USRP treatment is explained from the perspectives of the surface and cross section of the samples.

| S-EPMC8152014 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data