Effect of Hybrid Talc-Basalt Fillers in the Shell Layer on Thermal and Mechanical Performance of Co-Extruded Wood Plastic Composites.

ABSTRACT: Hybrid basalt fiber (BF) and Talc filled high density polyethylene (HDPE) and co-extruded wood-plastic composites (WPCs) with different BF/Talc/HDPE composition levels in the shell were prepared and their mechanical, morphological and thermal properties were characterized. Incorporating BFs into the HDPE-Talc composite substantially enhanced the thermal expansion property, flexural, tensile and dynamic modulus without causing a significant decrease in the tensile and impact strength of the composites. Strain energy estimation suggested positive and better interfacial interactions of HDPE with BFs than that with talc. The co-extruded structure design improved the mechanical properties of WPC due to the protective shell layer. The composite flexural and impact strength properties increased, and the thermal expansion decreased as BF content increased in the hybrid BF/Talc filled shells. The cone calorimetry data demonstrated that flame resistance of co-extruded WPCs was improved with the use of combined fillers in the shell layer, especially with increased loading of BFs. The combined shell filler system with BFs and Talc could offer a balance between cost and performance for co-extruded WPCs.

SUBMITTER: Huang R

PROVIDER: S-EPMC5458851 | biostudies-other | 2015 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:This paper presents the synthesis and physicochemical characterization of a new hybrid composite. Its main goals are evaluating the structure and studying the thermal and mechanical properties of the crosslinked polymeric materials based on varying chemical properties of the compounds. As an organic crosslinking monomer, bisphenol A glycerolate diacrylate (BPA.GDA) was used. Trimethoxyvinylsilane (TMVS) and N-vinyl-2-pyrrolidone (NVP) were used as comonomers and active diluents. The inorganic fraction was the silica in the form of nanoparticles (NANOSiO2). The hybrid composites were obtained by the bulk polymerization method using the UV initiator Irqacure 651 with a constant weight ratio of the tetrafunctional monomer BPA.GDA to TMVS or NVP (7:3 wt.%) and different wt.% of silica nanoparticles (0, 1, 3%). The proper course of polymerization was confirmed by the ATR/FTIR spectroscopy and SEM EDAX analysis. In the composites spectra the signals correspond to the C=O groups from NVP at 1672-1675 cm-1, and the vibrations of Si-O-C and Si-O-Si groups at 1053-1100 cm-1 from TMVS and NANOSiO2 are visible. Thermal stabilities of the obtained composites were studied by a differential scanning calorimetry DSC. Compared to NVP the samples with TMVS degraded in one stage (422.6-425.3 °C). The NVP-derived materials decomposed in three stages (three endothermic effects on the DSC curves). The addition of NANOSiO2 increases the temperature of composites maximum degradation insignificantly. Additionally, the Shore D hardness test was carried out with original metrological measurements of changes in diameter after indentation in relation to the type of material. The accuracy analysis of the obtained test results was based on a comparative analysis of graphical curves obtained from experimental tests. The values of the changes course of similarity in the examined factors, represented by those of characteristic coefficients were determined based on the Fréchet's theory.

Dataset Information

Effect of Hybrid Talc-Basalt Fillers in the Shell Layer on Thermal and Mechanical Performance of Co-Extruded Wood Plastic Composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets