Process Design of Aluminum Tailor Heat Treated Blanks.

ABSTRACT: In many industrials field, especially in the automotive sector, there is a trend toward lightweight constructions in order to reduce the weight and thereby the CO₂ and NOx emissions of the products. An auspicious approach within this context is the substitution of conventional deep drawing steel by precipitation hardenable aluminum alloys. However, based on the low formability, the application for complex stamping parts is challenging. Therefore, at the Institute of Manufacturing Technology, an innovative technology to enhance the forming limit of these lightweight materials was invented. The key idea of the so-called Tailor Heat Treated Blanks (THTB) is optimization of the mechanical properties by local heat treatment before the forming operation. An accurate description of material properties is crucial to predict the forming behavior of tailor heat treated blanks by simulation. Therefore, within in this research project, a holistic approach for the design of the THTB process in dependency of the main influencing parameters is presented and discussed in detail. The capability of the approach for the process development of complex forming operations is demonstrated by a comparison of local blank thickness of a tailgate with the corresponding results from simulation.

SUBMITTER: Kahrimanidis A

PROVIDER: S-EPMC5458868 | biostudies-other | 2015 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Metal-organic frameworks tailor the properties of aluminum nanocrystals.

Project description:Metal-organic frameworks (MOFs) and metal nanoparticles are two classes of materials that have received considerable recent attention, each for controlling chemical reactivities, albeit in very different ways. Here, we report the growth of MOF shell layers surrounding aluminum nanocrystals (Al NCs), an Earth-abundant metal with energetic, plasmonic, and photocatalytic properties. The MOF shell growth proceeds by means of dissolution-and-growth chemistry that uses the intrinsic surface oxide of the NC to obtain the Al3+ ions accommodated into the MOF nodes. Changes in the Al NC plasmon resonance provide an intrinsic optical probe of its dissolution and growth kinetics. This same chemistry enables a highly controlled oxidation of the Al NCs, providing a precise method for reducing NC size in a shape-preserving manner. The MOF shell encapsulation of the Al NCs results in increased efficiencies for plasmon-enhanced photocatalysis, which is observed for the hydrogen-deuterium exchange and reverse water-gas shift reactions.

| S-EPMC6368424 | biostudies-literature

Tetris-Style Stacking Process to Tailor the Orientation of Carbon Fiber Scaffolds for Efficient Heat Dissipation.

Project description:As the miniaturization of electronic devices and complication of electronic packaging, there are growing demands for thermal interfacial materials with enhanced thermal conductivity and the capability to direct the heat toward heat sink for highly efficient heat dissipation. Pitch-based carbon fiber (CF) with ultrahigh axial thermal conductivity and aspect ratios exhibits great potential for developing thermally conductive composites as TIMs. However, it is still hard to fabricate composites with aligned carbon fiber in a general approach to fully utilize its excellent axial thermal conductivity in specific direction. Here, three types of CF scaffolds with different oriented structure were developed via magnetic field-assisted Tetris-style stacking and carbonization process. By regulating the magnetic field direction and initial stacking density, the self-supporting CF scaffolds with horizontally aligned (HCS), diagonally aligned and vertically aligned (VCS) fibers were constructed. After embedding the polydimethylsiloxane (PDMS), the three composites exhibited unique heat transfer properties, and the HCS/PDMS and VCS/PDMS composites presented a high thermal conductivity of 42.18 and 45.01 W m-1 K-1 in fiber alignment direction, respectively, which were about 209 and 224 times higher than that of PDMS. The excellent thermal conductivity is mainly ascribed that the oriented CF scaffolds construct effective phonon transport pathway in the matrix. In addition, fishbone-shaped CF scaffold was also produced by multiple stacking and carbonization process, and the prepared composites exhibited a controlled heat transfer path, which can allow more versatility in the design of thermal management system.

| S-EPMC10247643 | biostudies-literature

Rational design of a robust aluminum metal-organic framework for multi-purpose water-sorption-driven heat allocations.

Project description:Adsorption-driven heat transfer technology using water as working fluid is a promising eco-friendly strategy to address the exponential increase of global energy demands for cooling and heating purposes. Here we present the water sorption properties of a porous aluminum carboxylate metal-organic framework, [Al(OH)(C6H3NO4)]·nH2O, KMF-1, discovered by a joint computational predictive and experimental approaches, which exhibits step-like sorption isotherms, record volumetric working capacity (0.36 mL mL-1) and specific energy capacity (263 kWh m-3) under cooling working conditions, very high coefficient of performances of 0.75 (cooling) and 1.74 (heating) together with low driving temperature below 70 °C which allows the exploitation of solar heat, high cycling stability and remarkable heat storage capacity (348 kWh m-3). This level of performances makes this porous material as a unique and ideal multi-purpose water adsorbent to tackle the challenges of thermal energy storage and its further efficient exploitation for both cooling and heating applications.

| S-EPMC7547100 | biostudies-literature

D-Tailor: automated analysis and design of DNA sequences.

Project description:Current advances in DNA synthesis, cloning and sequencing technologies afford high-throughput implementation of artificial sequences into living cells. However, flexible computational tools for multi-objective sequence design are lacking, limiting the potential of these technologies.We developed DNA-Tailor (D-Tailor), a fully extendable software framework, for property-based design of synthetic DNA sequences. D-Tailor permits the seamless integration of multiple sequence analysis tools into a generic Monte Carlo simulation that evolves sequences toward any combination of rationally defined properties. As proof of principle, we show that D-Tailor is capable of designing sequence libraries comprising all possible combinations among three different sequence properties influencing translation efficiency in Escherichia coli The capacity to design artificial sequences that systematically sample any given parameter space should support the implementation of more rigorous experimental designs.Source code is available for download at https://sourceforge.net/projects/dtailor/ CONTACT: aparkin@lbl.gov or cambray.guillaume@gmail.com Supplementary information: Supplementary data are available at Bioinformatics online (D-Tailor Tutorial).

| S-EPMC3982154 | biostudies-literature

Optimization of Printing Process Variables and the Effect of Post-Heat Treatments on the Mechanical Properties of Extruded Polylactic Acid-Aluminum Composites.

Project description:Polymer extrusions are employed in the fabrication of crucial parts for automotive, aerospace, and other mechanical applications. The use of fillers and microfibers is contributing to the advancement of material extrusion polymers. In order to enhance their mechanical characteristics, printed materials undergo a post-heating process utilizing microwaves. Specimens were fabricated using polylactic acid filaments containing 2 wt% aluminum. Two sets of specimens were fabricated and subjected to testing in order to evaluate the features of extruded specimens and specimens that underwent post-heating. In terms of mechanical performance, specimens subjected to post-heating exhibited superior results compared to specimens merely subjected to extrusion. The tensile, flexural, and Shore D hardness properties of the specimens exhibited improvements of 5.07, 6.16, and 1.32%, respectively, after being subjected to heating. Furthermore, the wear rate decreased by 13.58 percent. The results of the regression analysis indicate that the print angle and the air gap exhibit the greatest influence on the observed responses. The validation test outcomes exhibit a high level of concordance with the predicted findings. The mechanical and surface properties of components extruded with filler-added material are enhanced by subsequent heating.

| S-EPMC10747175 | biostudies-literature

Multipronged heat-exchanger based on femtosecond laser-nano/microstructured Aluminum for thermoelectric heat scavengers.

Project description:Femtosecond (fs) laser processing can significantly alter the optical, thermal, mechanical, and electrical properties of materials. Here, we show that fs-laser processing transforms aluminum (Al) to a highly efficient and multipronged heat exchanger. By optimizing the formed surface nano- and microstructures, we increase the Al emissivity and surface area by 700% and 300%, respectively. Accordingly, we show that fs-laser treated Al (fs-Al) increases the radiative and convective cooling power of fs-Al by 2100% and 300%, respectively, at 200 °C. As a direct application, we use fs-Al as a heat sink for a thermoelectric generator (TEG) and demonstrate a 280% increase in the TEG output power compared to a TEG with an untreated Al heat exchanger at 200 °C. The multipronged enhancement in fs-Al heat exchange properties lead to an increase in the TEG output power over a wide temperature ( T ) range ( T>50°C ). Conversely, a simple radiative cooling heat exchanger increases the TEG output power within a limited temperature range (T>150°C) . We investigate the laser processing parameters necessary to maximize the spectral emissivity and surface area of fs-Al. Fs-Al promises to be a widely used and compact heat exchanger for passive cooling of computers and data centers as well as to increase the efficiency of TEGs incorporated in sensors and handheld electronics.

| S-EPMC7453914 | biostudies-literature

Aluminum Matrix Composites Manufactured using Nitridation-Induced Self-Forming Process.

Project description:Conventional manufacturing processes for aluminum matrix composites (AMCs) involve complex procedures that require unique equipment and skills at each stage. This increases the process costs and limits the scope of potential applications. In this study, a simple and facile route for AMC manufacturing is developed, a mixture of Al powder and the ceramic reinforcement is simply heated under nitrogen atmosphere to produce the composite. During heating under nitrogen atmosphere, the surface modification of both Al and the reinforcement is induced by nitridation. When the oxide layer covering Al powder surface is transformed to nitrides, temperature in the local region increases rapidly, resulting in a partial melt of Al powder. The molten Al infiltrates into the empty space among Al powder and reinforcement, thereby enabling consolidation of powders without external forces. It is possible to fabricate AMCs with various types, sizes, volume fractions, and morphologies of the reinforcement. Furthermore, the manufacturing temperature can be lowered below the melting point of Al (or the solidus temperature for alloys) because of the exothermic nature of the nitridation, which prevents formation of un-wanted reactants. The relative simplicity of this process will not only provide sufficient price competitiveness for the final products but also contribute to the expansion of the application scope of AMCs.

| S-EPMC6938477 | biostudies-literature

Microstructural deformation process of shock-compressed polycrystalline aluminum.

Project description:Plastic deformation of polycrystalline materials under shock wave loading is a critical characteristic in material science and engineering. However, owing to the nanosecond time scale of the shock-induced deformation process, we currently have a poor mechanistic understanding of the structural changes from atomic scale to mesoscale. Here, we observed the dynamic grain refinement of polycrystalline aluminum foil under laser-driven shock wave loading using time-resolved X-ray diffraction. Diffraction spots on the Debye-Scherrer ring from micrometer-sized aluminum grains appeared and disappeared irregularly, and were shifted and broadened as a result of laser-induced shock wave loading. Behind the front of shock wave, large grains in aluminum foil were deformed, and subsequently exhibited grain rotation and a reduction in size. The width distribution of the diffraction spots broadened because of shock-induced grain refinement and microstrain in each grain. We performed quantitative analysis of the inhomogeneous lattice strain and grain size in the shocked polycrysalline aluminum using the Williamson-Hall method and determined the dislocation density under shock wave loading.

| S-EPMC6527857 | biostudies-other

Silicate Removal in Aluminum Hydroxide Co-Precipitation Process.

Project description:The removal mechanisms of silicate using an aluminum hydroxide co-precipitation process was investigated and compared with an adsorption process, in order to establish an effective and validated method for silicate removal from wastewater. Adsorption isotherms, XRD and FT-IR analyses showed that silicate uptake occurred by adsorption to boehmite for initial Si/Al molar ratios smaller than two, but by precipitation of poorly crystalline kaolinite for the ratios larger than two, in both co-precipitation and adsorption processes. Silicate was removed by two steps: (i) an initial rapid uptake in a few seconds; and (ii) a slow uptake over several hours in both processes. The uptake rate in the first step was higher in the co-precipitation process than in adsorption process, presumably due to increased silicate adsorption to boehmite and rapid precipitation of kaolinite. These results suggest that silicate removal using aluminum salts could be effectively achieved if the pH adjustment and aluminum concentration are strictly controlled.

| S-EPMC5453091 | biostudies-other

The simplified tailor-made workflows for a 3D slicer-based craniofacial implant design.

Project description:A specific design of craniofacial implant model is vital and urgent for patients with traumatic head injury. The mirror technique is commonly used for modeling these implants, but it requires the presence of a healthy skull region opposite to the defect. To address this limitation, we propose three processing workflows for modeling craniofacial implants: the mirror method, the baffle planner, and the baffle-based mirror guideline. These workflows are based on extension modules on the 3D Slicer platform and were developed to simplify the modeling process for a variety of craniofacial scenarios. To evaluate the effectiveness of these proposed workflows, we investigated craniofacial CT datasets collected from four accidental cases. The designed implant models were created using the three proposed workflows and compared to reference models created by an experienced neurosurgeon. The spatial properties of the models were evaluated using performance metrics. Our results show that the mirror method is suitable for cases where a healthy skull region can be completely reflected to the defect region. The baffle planner module offers a flexible prototype model that can be fit independently to any defect location, but it requires customized refinement of contour and thickness to fill the missing region seamlessly and relies on the user's experience and expertise. The proposed baffle-based mirror guideline method strengthens the baffle planner method by tracing the mirrored surface. Overall, our study suggests that the three proposed workflows for craniofacial implant modeling simplify the process and can be practically applied to a variety of craniofacial scenarios. These findings have the potential to improve the care of patients with traumatic head injuries and could be used by neurosurgeons and other medical professionals.

| S-EPMC9938178 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data