Enhancement of the Mechanical Properties of Basalt Fiber-Wood-Plastic Composites via Maleic Anhydride Grafted High-Density Polyethylene (MAPE) Addition.

ABSTRACT: This study investigated the mechanisms, using microscopy and strength testing approaches, by which the addition of maleic anhydride grafted high-density polyethylene (MAPE) enhances the mechanical properties of basalt fiber-wood-plastic composites (BF-WPCs). The maximum values of the specific tensile and flexural strengths are achieved at a MAPE content of 5%-8%. The elongation increases rapidly at first and then continues slowly. The nearly complete integration of the wood fiber with the high-density polyethylene upon MAPE addition to WPC is examined, and two models of interfacial behavior are proposed. We examined the physical significance of both interfacial models and their ability to accurately describe the effects of MAPE addition. The mechanism of formation of the Model I interface and the integrated matrix is outlined based on the chemical reactions that may occur between the various components as a result of hydrogen bond formation or based on the principle of compatibility, resulting from similar polarity. The Model I fracture occurred on the outer surface of the interfacial layer, visually demonstrating the compatibilization effect of MAPE addition.

SUBMITTER: Chen J

PROVIDER: S-EPMC5458936 | biostudies-other | 2013 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effects of wood fiber impulse-cyclone drying process on the UV-accelerated aging properties of wood-plastic composites.

Project description:The impulse-cyclone drying and the silane coupling agent (A187) modification are applied to treat wood fibers under the following conditions: 180°C, 180°C+A187, 200°C+A187, 220°C+A187 and 240°C+ A187. Then, HDPE/wood fiber composites are fabricated with a two-stage plastic extruder, and the effects of impulse-cyclone drying technique on the UV-accelerated aging properties of composites are investigated. Fourier-transform infrared spectroscopy (FTIR) reveals that the silane coupling agent chemically reacts with the hydroxyl groups on the wood fiber surfaces, the anti-UV aging properties of composites is enhanced. Mechanical test shows that during the 0-3000 h of UV aging process, the mechanical properties of samples tend to increase initially and then decrease within a period of time. After 3000 h of UV aging, the specimen 4 exhibits the least loss of mechanical properties, with flexural modulus, flexural modulus and impact strength of 65.40 Mpa, 2082.08 Mpa and 12.85 Mpa, respectively. The effects of impulse-cyclone drying technique on the UV-accelerated aging properties of composites are investigated through Spectrophotometry and Surface microstructure observation. indicates that the ΔL* and ΔE* values increase greatly at the stage of 0-1000 h aging, which though tend to stabilize after 1000 h. The degree of discoloration changes little for specimen 4,and the number of surface cracks is relatively small, which exhibits the optimal aging resistance. In conclusion, the addition of wood fibers treated by impulse-cyclone drying (220°C) and A187 modification is effective in enhancing the anti-UV aging properties of HDPE/wood fiber composites. Nevertheless, such enhancing effect turns to decline when the temperature of impulse-cyclone drying treatment is excessively high.

| S-EPMC9612545 | biostudies-literature

Preparation of High Density Polyethylene/Waste Polyurethane Blends Compatibilized with Polyethylene-Graft-Maleic Anhydride by Radiation.

Project description:Polyurethane (PU) is a very popular polymer that is used in a variety of applications due to its good mechanical, thermal, and chemical properties. However, PU recycling has received significant attention due to environmental issues. In this study, we developed a recycling method for waste PU that utilizes the radiation grafting technique. Grafting of waste PU was carried out using a radiation technique with polyethylene-graft-maleic anhydride (PE-g-MA). The PE-g-MA-grafted PU/high density polyethylene (HDPE) composite was prepared by melt-blending at various concentrations (0-10 phr) of PE-g-MA-grafted PU. The composites were characterized using fourier transform infrared spectroscopy (FT-IR), and their surface morphology and thermal/mechanical properties are reported. For 1 phr PU, the PU could be easily introduced to the HDPE during the melt processing in the blender after the radiation-induced grafting of PU with PE-g-MA. PE-g-MA was easily reacted with PU according to the increasing radiation dose and was located at the interface between the PU and the HDPE during the melt processing in the blender, which improved the interfacial interactions and the mechanical properties of the resultant composites. However, the elongation at break for a PU content >2 phr was drastically decreased.

| S-EPMC5507029 | biostudies-other

Thermal Stability of Polycaprolactone Grafted Densely with Maleic Anhydride Analysed Using the Coats-Redfern Equation.

Project description:The plastic waste problem has recently attracted unprecedented attention globally. To reduce the adverse eff ects on environments, biodegradable polymers have been studied to solve the problems. Poly(ε-caprolactone) (PCL) is one of the common biodegradable plastics used on its own or blended with natural polymers because of its excellent properties after blending. However, PCL and natural polymers are difficult to blend due to the polymers' properties. Grafted polymerization of maleic anhydride and dibenzoyl peroxide (DBPO) with PCL is one of the improvements used for blending immiscible polymers. In this study, we first focused on the effects of three factors (stirring time, maleic anhydride (MA) amount and benzoyl peroxide amount) on the grafting ratio with a maximum value of 4.16% when applying 3.000 g MA and 1.120 g DBPO to 3.375 g PCL with a stirring time of 18 h. After that, the grafting condition was studied based on the kinetic thermal decomposition and activation energy by the Coats-Redfern method. The optimal fitting model was confirmed by the determination coefficient of nearly 1 to explain the contracting volume mechanism of synthesized PCL-g-MA. Consequently, grafted MA hydrophilically augmented PCL as the reduced contact angle of water suggests, facilitating the creation of a plastic-biomaterial composite.

| S-EPMC9571202 | biostudies-literature

Effects of SiO2 Filler in the Shell and Wood Fiber in the Core on the Thermal Expansion of Core-Shell Wood/Polyethylene Composites.

Project description:The influence of nano-silica (nSiO2) and micro-silica (mSiO2) in the shell and wood fiber filler in the core on the thermal expansion behavior of co-extruded wood/polyethylene composites (Co-WPCs) was investigated to optimize the thermal expansion resistance. The cut Co-WPCs samples showed anisotropic thermal expansion, and the thermal expansion strain and linear coefficient of thermal expansion (LCTE) decreased by filling the shell layer with rigid silica, especially nSiO2. Finite element analysis indicated that the polymer-filled shell was mainly responsible for the thermal expansion. The entire Co-WPCs samples exhibited a lower thermal expansion strain than the cut Co-WPCs samples due to protection by the shell. Increasing the wood fiber content in the core significantly decreased the thermal expansion strain and LCTE of the Co-WPCs. The Co-WPCs whose core layer was filled with 70% wood fiber exhibited the greatest anisotropic thermal expansion.

| S-EPMC7692157 | biostudies-literature

Effect of Modified Red Pottery Clay on the Moisture Absorption Behavior and Weatherability of Polyethylene-Based Wood-Plastic Composites.

Project description:Red pottery clay (RPC) was modified using a silane coupling agent, and the modified RPC (mRPC) was then used to enhance the performance of high-density polyethylene-based wood-plastic composites. The effect of the mRPC content on the performances of the composites was investigated through Fourier transform infrared spectrometry, differential mechanical analysis (DMA) and ultraviolet (UV)-accelerated aging tests. After adding the mRPC, a moisture adsorption hysteresis was observed. The DMA results indicated that the mRPC effectively enhanced the rigidity and elasticity of the composites. The mRPC affected the thermal gravimetric, leading to a reduction of the thermal degradation rate and a right-shift of the thermal degradation peak; the initial thermal degradation temperature was increased. After 3000 h of UV-accelerated aging, the flexural strength and impact strength both declined. For aging time between 0 and 1000 h, the increase in amplitude of ΔL* (luminescence) and ΔE* (color) reached a maximum; the surface fading did not became obvious. ΔL* and ΔE* increased more significantly between 1000 and 2000 h. These characterization results indicate that the chromophores of the mRPC became briefly active. However, when the aging times were higher than 2000 h, the photo-degradation reaction was effectively prevented by adding the mRPC. The best overall enhancement was observed for an mRPC mass percentage of 5%, with a storage modulus of 3264 MPa and an increase in loss modulus by 16.8%, the best anti-aging performance and the lowest degree of color fading.

| S-EPMC5459118 | biostudies-other

Weathering Characteristics of Wood Plastic Composites Reinforced with Extracted or Delignified Wood Flour.

Project description:This study investigated weathering performance of an HDPE wood plastic composite reinforced with extracted or delignified wood flour (WF). The wood flour was pre-extracted with three different solvents, toluene/ethanol (TE), acetone/water (AW), and hot water (HW), or sodium chlorite/acetic acid. The spectral properties of the composites before and after artificial weathering under accelerated conditions were characterized by Fourier transform infrared (FTIR) spectroscopy, the surface color parameters were analyzed using colorimetry, and the mechanical properties were determined by a flexural test. Weathering of WPC resulted in a surface lightening and a decrease in wood index (wood/HDPE) and flexural strength. WPCs that were reinforced with delignified wood flour showed higher ΔL* and ΔE* values, together with lower MOE and MOR retention ratios upon weathering when compared to those with non-extracted control and extracted WF.

| S-EPMC5508992 | biostudies-other

The Effect of Recycling on Wood-Fiber Thermoplastic Composites.

Project description:The aim of this study was to investigate the effect of recycling on polypropylene (PP) and wood-fiber thermoplastic composites (WPCs) using a co-rotating twin-screw extruder. After nine extrusion passes microscopy studies confirmed that the fiber length decreased with the increased number of recycling passes but the increased processing time also resulted in excellent dispersion and interfacial adhesion of the wood fibers in the PP matrix. Thermal, rheological, and mechanical properties were studied. The repeated extrusion passes had minimal effect on thermal behavior and the viscosity decreased with an increased number of passes, indicating slight degradation. The recycling processes had an effect on the tensile strength of WPCs while the effect was minor on the PP. However, even after the nine recycling passes the strength of WPC was considerably better (37 MPa) compared to PP (28 MPa). The good degree of property retention after recycling makes this recycling strategy a viable alternative to discarding the materials. Thus, it has been demonstrated that, by following the most commonly used extrusion process, WPCs can be recycled several times and this methodology can be industrially adapted for the manufacturing of recycled products.

| S-EPMC7463641 | biostudies-literature

Sustainable Cellulose-Aluminum-Plastic Composites from Beverage Cartons Scraps and Recycled Polyethylene.

Project description:The sustainable management of multilayer paper/plastic waste is a technological challenge due to its composite nature. In this paper, a mechanical recycling approach for multilayer cartons (MC) is reported, illustrating the realization of thermoplastic composites based on recycled polyethylene and an amount of milled MC ranging from 20 to 90 wt%. The effect of composition of the composites on the morphology and on thermal, mechanical, and water absorption behavior was investigated and rationalized, demonstrating that above 80 wt% of MC, the fibrous nature of the filler dominates the overall properties of the materials. A maleated polyethylene was also used as a coupling agent and its effectiveness in improving mechanical parameters of composites up to 60 wt% of MC was highlighted.

| S-EPMC8963112 | biostudies-literature

Multiscale Polymer Dynamics in Hierarchical Carbon Nanotube Grafted Glass Fiber Reinforced Composites.

Project description:Carbon nanotube (CNT) grafted glass fiber reinforced epoxy nanocomposites (GFRP) present a range of stiffnesses (MPa to GPa) and length scales (μm to nm) at the fiber-matrix interface. The contribution of functionalized CNT networks to the local and bulk polymer dynamics is studied here by using a combination of torsion dynamical mechanical thermal analysis (DMTA), positron annihilation lifetime spectroscopy (PALS), and neutron scattering (NS) measurements. DMTA measurements highlight a reduction in the storage modulus (G') in the rubbery region and an asymmetric broadening of the loss modulus (G″) peak in the α-transition region. NS measurements show a suppressed hydrogen mean-square displacement (MSD) in the presence of glass fibers but a higher hydrogen MSD after grafting functionalized CNTs onto fiber surfaces. PALS measurements show greater free volume characteristics in the presence of the functionalized CNT modified composites, supporting the view that these interface layers increase polymer mobility. While NS and DMTA are sensitive to different modes of chain dynamics, the localization of functionalized nanotubes at the fiber interface is found to affect the distribution of polymer relaxation modes without significantly altering the thermally activated relaxation processes.

| S-EPMC7067277 | biostudies-literature

Preparation and Characterization of Extruded Composites Based on Polypropylene and Chitosan Compatibilized with Polypropylene-Graft-Maleic Anhydride.

Project description:The preparation of composites of synthetic and natural polymers represent an interesting option to combine properties; in this manner, polypropylene and chitosan extruded films using a different proportion of components and polypropylene-graft-maleic anhydride (PPgMA) as compatibilizer were prepared. The effect of the content of the biopolymer in the polypropylene (PP) matrix, the addition of compatibilizer, and the particle size on the properties of the composites was analyzed using characterization by fourier transform-infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), tensile strength, and contact angle, finding that in general, the addition of the compatibilizer and reducing the particle size of the chitosan, favored the physicochemical and morphological properties of the films.

| S-EPMC5459115 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data