Dynamic Behavior of Nanocomposites Reinforced with Multi-Walled Carbon Nanotubes (MWCNTs).
Ontology highlight
ABSTRACT:
SUBMITTER: Her SC
PROVIDER: S-EPMC5458950 | biostudies-other | 2013 Jun
REPOSITORIES: biostudies-other
Similar Datasets
Project description:The nanomechanical properties of carbon nanotubes particulate-reinforced aluminum matrix nanocomposites (Al-CNTs) have been characterized using nanoindentation. Bulk nanocomposite specimens containing 2 wt % multiwalled CNTs (MWCNTs) were synthesized by a combination of ball milling and powder metallurgy route. It has been tried to understand the correlation between microstructural evolution particularly carbon nanotubes (CNTs) dispersion during milling and mechanical properties of Al-2 wt % nanocomposites. Maximum enhancement of +23% and +44% has been found in Young's modulus and hardness respectively, owing to well homogenous dispersion of CNTs within the aluminum matrix at longer milling time.
| S-EPMC5456694 | biostudies-other
Project description:The influence of carbon multi-walled nanotubes (MWCNTs) and halloysite nanotubes (HNTs) on the physical, thermal, mechanical, and electrical properties of EVA (ethylene vinyl acetate) copolymer was investigated. EVA-based nanocomposites containing MWCNTs or HNTs, as well as hybrid nanocomposites containing both nanofillers were prepared by melt blending. Scanning electron microcopy (SEM) images revealed the presence of good dispersion of both kinds of nanotubes throughout the EVA matrix. The incorporation of nanotubes into the EVA copolymer matrix did not significantly affect the crystallization behavior of the polymer. The tensile strength of EVA-based nanocomposites increased along with the increasing CNTs (carbon nanotubes) content (increased up to approximately 40% at the loading of 8 wt.%). In turn, HNTs increased to a great extent the strain at break. Mechanical cyclic tensile tests demonstrated that nanocomposites with hybrid reinforcement exhibit interesting strengthening behavior. The synergistic effect of hybrid nanofillers on the modulus at 100% and 200% elongation was visible. Moreover, along with the increase of MWCNTs content in EVA/CNTs nanocomposites, an enhancement in electrical conductivity was observed.
| S-EPMC7504041 | biostudies-literature
Project description:Metamaterial behavior of polymer nanocomposites (NCs) based on isotactic polypropylene (iPP) and multi-walled carbon nanotubes (MWCNTs) was investigated based on the observation of a negative dielectric constant (ε'). It is demonstrated that as the dielectric constant switches from negative to positive, the plasma frequency (ωp) depends strongly on the ultrasound-assisted fabrication method, as well as on the melt flow index of the iPP. NCs were fabricated using ultrasound-assisted extrusion methods with 10 wt % loadings of MWCNTs in iPPs with different melt flow indices (MFI). AC electrical conductivity (σ(AC)) as a function of frequency was determined to complement the electrical classification of the NCs, which were previously designated as insulating (I), static-dissipative (SD), and conductive (C) materials. It was found that the SD and C materials can also be classified as metamaterials (M). This type of behavior emerges from the negative dielectric constant observed at low frequencies although, at certain frequencies, the dielectric constant becomes positive. Our method of fabrication allows for the preparation of metamaterials with tunable ωp. iPP pure samples show only positive dielectric constants. Electrical conductivity increases in all cases with the addition of MWCNTs with the largest increases observed for samples with the highest MFI. A relationship between MFI and the fabrication method, with respect to electrical properties, is reported.
| S-EPMC5457228 | biostudies-literature
Project description:Nano-objects have been investigated for drug delivery, oil detection, contaminant removal, and tribology applications. In some applications, they are subjected to friction and deformation during contact with each other and their surfaces on which they slide. Experimental studies directly comparing local and global deformation are lacking. This research performs nanoindentation (local deformation) and compression tests (global deformation) with a nanoindenter (sharp tip and flat punch, respectively) on molybdenum disulfide (MoS2) multi-walled nanotubes (MWNTs), ~500 nm in diameter. Hardness of the MoS2 nanotube was similar to bulk and does not follow the "smaller is stronger" phenomenon as previously reported for other nano-objects. Tungsten disulfide (WS2) MWNTs, ~300 nm in diameter and carbon nanohorns (CNHs) 80-100 nm in diameter were of interest and also selected for compression studies. These studies aid in understanding the mechanisms involved during global deformation when nano-objects are introduced to reduce friction and wear. For compression, highest loads were required for WS2 nanotubes, then MoS2 nanotubes and CNHs to achieve the same displacement. This was due to the greater number of defects with the MoS2 nanotubes and the flexibility of the CNHs. Repeat compression tests of nano-objects were performed showing a hardening effect for all three nano-objects.
| S-EPMC4336937 | biostudies-other
Project description:This article is devoted to the investigation of the sensing behavior of chemically treated multi-walled carbon nanotubes (MWNTs) at room temperature. Chemical treatment of MWNTs was carried out with a solution of either sulfuric or chromic acids. The materials obtained were investigated by transmission electron microscopy, scanning electron microscopy, Raman-spectroscopy, X-ray diffraction, and Fourier transform infrared spectroscopy. The active layer of chemiresistive gas sensors was obtained by cold pressing (compaction) at 11 MPa of powders of bare and treated multi-walled carbon nanotubes. The sensing properties of pellets were investigated using a custom dynamic type of station at room temperature (25 ± 2 °C). Detection of NO2 was performed in synthetic air (79 vol% N2, 21 vol% O2). It was found that the chemical treatment significantly affects the sensing properties of multi-walled carbon nanotubes, which is indicated by increasing the response of the sensors toward 100-500 ppm NO2 and lower concentrations.
| S-EPMC9503782 | biostudies-literature
Project description:Carbon nanotubes could accumulate in organism and have a negative impact on the structure and function of the ecosystem when they were discharged into environment. Furthermore, it will affect the migration and fate of pollutants in the water body. The study is mainly to explore the adsorption behavior and mechanism of beta-blocker on multi-walled carbon nanotubes (MWCNTs). Propranolol (PRO) was selected as the representative of beta-blocker. The effects of different environmental factors such as pH, ionic strength and humic acid (HA) on the adsorption process were investigated. The adsorption results were characterized by Zeta potential. At the same time, the effects of different types of drugs on the adsorption process were explored and the possible adsorption mechanisms were analyzed. The experimental results showed that the adsorption behavior was significantly different under different pH conditions. ?-? EDA interaction, hydrophobic interaction and hydrogen bonding were speculated to be the main adsorption mechanisms for PRO adsorption on MWCNTs.
| S-EPMC7314780 | biostudies-literature
Project description:Long carbon nanotubes (CNTs) resemble asbestos fibers due to their high length to diameter ratio and they thus have genotoxic effects. Another parameter that might explain their genotoxic effects is contamination with heavy metal ions. On the other hand, short (1-2 µm) CNTs do not resemble asbestos fibers, and, once purified from contaminations, they might be suitable for medical applications. To identify the role of fiber thickness and surface properties on genotoxicity, well-characterized short pristine and carboxylated single-walled (SCNTs) and multi-walled (MCNTs) CNTs of different diameters were studied for cytotoxicity, the cell's response to oxidative stress (immunoreactivity against hemoxygenase 1 and glutathione levels), and in a hypoxanthine guanine phosphoribosyltransferase (HPRT) assay using V79 chinese hamster fibroblasts and human lung adenocarcinoma A549 cells. DNA repair was demonstrated by measuring immunoreactivity against activated histone H2AX protein. The number of micronuclei as well as the number of multinucleated cells was determined. CNTs acted more cytotoxic in V79 than in A549 cells. Plain and carboxylated thin (<8 nm) SCNTs and MCNTs showed greater cytotoxic potential and carboxylated CNTs showed indication for generating oxidative stress. Multi-walled CNTs did not cause HPRT mutation, micronucleus formation, DNA damage, interference with cell division, and oxidative stress. Carboxylated, but not plain, SCNTs showed indication for in vitro DNA damage according to increase of H2AX-immunoreactive cells and HPRT mutation. Although short CNTs presented a low in vitro genotoxicity, functionalization of short SCNTs can render these particles genotoxic.
| S-EPMC4434219 | biostudies-literature
Project description:There have been a number of theoretical and experimental studies on tensile properties of carbon nanotubes (CNT), reporting the Young's modulus of the individual CNT up to 1 TPa. Although CNT shows the promise to be used as reinforcement in a high modulus/strength composite material, it exhibits quite disappointing in terms of modulus or strength. Along with recent advance in CNT growth technique, we will be able to directly measure tensile properties of millimeter-long MWCNTs. This study firstly tackles the direct measurement of the tensile properties of millimeter-long MWCNTs that can be used as reinforcement in a composite system. A carefully designed tensile testing technique for the MWCNTs is developed, which allows us to obtain more accurate and reliable measured values. The average tensile strength and Young's modulus of the CNTs investigated in this study are measured to be 0.85?GPa and 34.65?GPa, respectively. Also, this work statistically investigates the effect of the CNT dimensions including length, diameter and volume on the tensile properties. To the best of our knowledge, this is the very first report on the tensile properties of macroscopically long and continuous CNTs.
| S-EPMC5573399 | biostudies-literature
Project description:The studies focusing on magnesium oxychloride cement (MOC) composites have recently become fairly widespread because of MOC's excellent mechanical properties and environmental sustainability. Numerous fillers, admixtures and nano-dopants were studied in order to improve the overall performance of MOC-based derivatives. Some of them exhibited specific flaws, such as a tendency to aggregate, increase in porosity, aeration of the composite matrix, depreciation in water resistance and mechanical strength, etc. In this manuscript, MOC-based composites doped by multi-walled carbon nanotubes (MWCNTs) are designed and tested. In order to modify the final properties of composites, diatomite was admixed as partial substitution of MgO, which was used in the composition of the researched material in excess, i.e., the majority of MgO constituted part of MOC and the rest served as fine filler. The composites were subjected to the broad experimental campaign that covered SEM (scanning electron microscopy), EDS (energy dispersive spectroscopy), HR-TEM (high-resolution transmission electron microscopy), XRD (X-ray diffraction), OM (optical microscopy) and STA-MS (simultaneous thermal analysis with mass spectroscopy). For 28 days hardened samples, macrostructural and microstructural parameters, mechanical properties, hygric and thermal characteristics were experimentally assessed. The incorporation of MWCNTs and diatomite resulted in the significant enhancement of composites' compactness, mechanical strength and stiffness and reduction in water absorption and rate of water imbibition. The thermal properties of the enriched MOC composites yielded interesting values and provided information for future modification of thermal performance of MOC composites with respect to their specific use in practice, e.g., in passive moderation of indoor climate. The combination of MWCNTs and diatomite represents a valuable modification of the MOC matrix and can be further exploited in the design and development of advanced building materials and components.
| S-EPMC8399920 | biostudies-literature
Project description:This study intends to develop protocols for sampling and characterizing multi-walled carbon nanotube (MWCNT) aerosols in workplaces or during inhalation studies. Manufactured dry powder containing MWCNT's, combined with soot and metal catalysts, form complex morphologies and diverse shapes. The aerosols, examined in this study, were produced using an acoustical generator. Representative samples were collected from an exposure chamber using filters and a cascade impactor for microscopic and gravimetric analyses. Results from filters showed that a density of 0.008-0.10 particles per µm² filter surface provided adequate samples for particle counting and sizing. Microscopic counting indicated that MWCNT's, resuspended at a concentration of 10 mg/m³, contained 2.7 × 10⁴ particles/cm³. Each particle structure contained an average of 18 nanotubes, resulting in a total of 4.9 × 10⁵ nanotubes/cm³. In addition, fibrous particles within the aerosol had a count median length of 3.04 µm and a width of 100.3 nm, while the isometric particles had a count median diameter of 0.90 µm. A combination of impactor and microscopic measurements established that the mass median aerodynamic diameter of the mixture was 1.5 µm. It was also determined that the mean effective density of well-defined isometric particles was between 0.71 and 0.88 g/cm³, and the mean shape factor of individual nanotubes was between 1.94 and 2.71. The information obtained from this study can be used for designing animal inhalation exposure studies and adopted as guidance for sampling and characterizing MWCNT aerosols in workplaces. The measurement scheme should be relevant for any carbon nanotube aerosol.
| S-EPMC4664058 | biostudies-literature