Flame Retardancy of Carbon Fibre Reinforced Sorbitol Based Bioepoxy Composites with Phosphorus-Containing Additives.

ABSTRACT: Carbon fibre reinforced flame-retarded bioepoxy composites were prepared from commercially available sorbitol polyglycidyl ether (SPE) cured with cycloaliphatic amine hardener. Samples containing 1, 2, and 3% phosphorus (P) were prepared using additive type flame retardants (FRs) resorcinol bis(diphenyl phosphate) (RDP), ammonium polyphosphate (APP), and their combinations. The fire performance of the composites was investigated by limiting oxygen index (LOI), UL-94 tests, and mass loss calorimetry. The effect of FRs on the glass transition temperature, and storage modulus was evaluated by dynamic mechanical analysis (DMA), while the mechanical performance was investigated by tensile, bending, and interlaminar shear measurements, as well as by Charpy impact test. In formulations containing both FRs, the presence of RDP, acting mainly in gas phase, ensured balanced gas and solid-phase mechanism leading to best overall fire performance. APP advantageously compensated the plasticizing (storage modulus and glass transition temperature decreasing) effect of RDP in combined formulations; furthermore, it led to increased tensile strength and Charpy impact energy.

SUBMITTER: Toldy A

PROVIDER: S-EPMC5458979 | biostudies-other | 2017 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Nanoscopic origin of cracks in carbon fibre-reinforced plastic composites.

Project description:Voids and cracks can fatally degrade structural materials such as metals and ceramics but are tolerated in carbon fibre-reinforced plastic (CFRP) composites if monitored to prevent their growth to a critical size. Thus, the use of CFRPs as aeronautical structural materials requires an understanding of microscopic crack formation. However, this crack-formation mechanism remains unclear because experimental difficulties have hindered studies of relevant phenomena that occur before crack formation. Herein, we report high-resolution (~50?nm) and non-destructive three-dimensional observations of crack initiation and propagation under applied stress. This evaluation reveals that voids and cracks do not simply result from local stresses but instead occur largely through two competing nanoscale mechanisms, namely, fibre/plastic interface debonding and in-plastic crack initiation. Therefore, nanoscopic insights into these heterogeneities are essential for controlling crack initiation and determining reasonable safety margins for CFRP composite use.

| S-EPMC6917772 | biostudies-literature

Multiply fully recyclable carbon fibre reinforced heat-resistant covalent thermosetting advanced composites.

Project description:Nondestructive retrieval of expensive carbon fibres (CFs) from CF-reinforced thermosetting advanced composites widely applied in high-tech fields has remained inaccessible as the harsh conditions required to recycle high-performance resin matrices unavoidably damage the structure and properties of CFs. Degradable thermosetting resins with stable covalent structures offer a potential solution to this conflict. Here we design a new synthesis scheme and prepare a recyclable CF-reinforced poly(hexahydrotriazine) resin matrix advanced composite. The multiple recycling experiments and characterization data establish that this composite demonstrates performance comparable to those of its commercial counterparts, and more importantly, it realizes multiple intact recoveries of CFs and near-total recycling of the principal raw materials through gentle depolymerization in certain dilute acid solution. To our best knowledge, this study demonstrates for the first time a feasible and environment-friendly preparation-recycle-regeneration strategy for multiple CF-recycling from CF-reinforced advanced composites.

| S-EPMC5337986 | biostudies-literature

Phosphorus-Containing Flame-Retardant Benzocyclobutylene Composites with High Thermal Stability and Low CTE.

Project description:As a component of printed circuit substrate, copper clad laminate (CCL) needs to meet the performance requirements of heat resistance, flame retardancy, and low coefficient of thermal expansion (CTE), which, respectively, affects the stability, safety, and processability of terminal electronic products. In this paper, benzocyclobutylene (BCB)-functionalized phosphorus-oxygen flame retardant composites were prepared through introducing the BCB groups, and the performance was researched by thermogravimetric analysis, microcombustion calorimetry, and thermomechanical analysis. The research results show that these phosphorus oxide compounds containing BCB groups show good thermal stability and low total heat release (THR) after thermal curing, and the more BCB groups on the phosphorus oxide monomers, the better the thermal stability and flame retardancy of cured resins. The Td5 and THR of the composite (M3) are as high as 443 °C and 23.1 kJ/g, respectively. In addition, the CTE of M3 is as low as 16.71 ppm/°C. Introduction of BCB groups which can be crosslinked through heat to improve the thermal stability, flame retardancy, and reduced CTE of traditional organophosphorus flame retardant materials. These materials are expected to be good candidates for CCL substrates for electronic circuits.

| S-EPMC10018689 | biostudies-literature

Electrically and Thermally Conductive Carbon Fibre Fabric Reinforced Polymer Composites Based on Nanocarbons and an In-situ Polymerizable Cyclic Oligoester.

Project description:There is growing interest in carbon fibre fabric reinforced polymer (CFRP) composites based on a thermoplastic matrix, which is easy to rapidly produce, repair or recycle. To expand the applications of thermoplastic CFRP composites, we propose a process for fabricating conductive CFRP composites with improved electrical and thermal conductivities using an in-situ polymerizable and thermoplastic cyclic butylene terephthalate oligomer matrix, which can induce good impregnation of carbon fibres and a high dispersion of nanocarbon fillers. Under optimal processing conditions, the surface resistivity below the order of 10+10 Ω/sq, which can enable electrostatic powder painting application for automotive outer panels, can be induced with a low nanofiller content of 1 wt%. Furthermore, CFRP composites containing 20 wt% graphene nanoplatelets (GNPs) were found to exhibit an excellent thermal conductivity of 13.7 W/m·K. Incorporating multi-walled carbon nanotubes into CFRP composites is more advantageous for improving electrical conductivity, whereas incorporating GNPs is more beneficial for enhancing thermal conductivity. It is possible to fabricate the developed thermoplastic CFRP composites within 2 min. The proposed composites have sufficient potential for use in automotive outer panels, engine blocks and other mechanical components that require conductive characteristics.

| S-EPMC5955969 | biostudies-literature

Three Dimensional Printing of Multiscale Carbon Fiber-Reinforced Polymer Composites Containing Graphene or Carbon Nanotubes.

Project description:Three-dimensional printing offers a promising, challenging opportunity to manufacture component parts with ad hoc designed composite materials. In this study, the novelty of the research is the production of multiscale composites by means of a solvent-free process based on melt compounding of acrylonitrile-butadiene-styrene (ABS), with various amounts of microfillers, i.e., milled (M) carbon fibers (CFs) and nanofillers, i.e., carbon nanotubes (CNTs) or graphene nanoplatelets (GNPs). The compounded materials were processed into compression molded sheets and into extruded filaments. The latter were then used to print fused filament fabrication (FFF) specimens. The multiscale addition of the microfillers inside the ABS matrix caused a notable increase in rigidity and a slight increase in strength. However, it also brought about a significant reduction of the strain at break. Importantly, GNPs addition had a good impact on the rigidity of the materials, whereas CNTs favored/improved the composites' electrical conductivity. In particular, the addition of this nanofiller was very effective in improving the electrical conductivity compared to pure ABS and micro composites, even with the lowest CNT content. However, the filament extrusion and FFF process led to the creation of voids within the structure, causing a significant loss of mechanical properties and a slight improvement of the electrical conductivity of the printed multiscale composites. Selective parameters have been presented for the comparison and selection of compositions of multiscale nanocomposites.

| S-EPMC9227618 | biostudies-literature

Scanning electron microscopy datasets for local fibre volume fraction determination in non-crimp glass-fibre reinforced composites.

Project description:The fatigue damage evolution depends on the local fibre volume fraction as observed in the co-submitted publication [1]. Conventionally, fibre volume fractions are determined as an averaged overall fibre volume fraction determined from small cuts of the laminate. Alternatively, automatically stitching of scanning electron microscopy (SEM) images can make high-resolution scans of large cross-section area with large contrast between the polymer and glass-fibre phase. Therefore, local distribution of the fibre volume fraction can be characterised automatically using such scan-data. The two datasets presented here cover two large Field of Views scanning electron microscopy (SEM) images. The two images is generated from between 1200 and 1800 high-resolution scan pictures which have been stitched into two high-resolution tif-files. The resolution corresponds to between 700 and 5000 pixels covering each fibre. The datasets are coming from two different non-crimp fabric glass fibre reinforced epoxy composites typically used in the wind turbine industry. Depending on the regions analysed, fibre volume fraction in the range of 50-85% is found. The maximum local fibre volume fraction is found averaging the local fibre volume fraction over 5?×?5 fibre diameter (80?×?80 µm2) areas. The local fibre volume fraction has been used in the analysis performed in [1].

| S-EPMC7905358 | biostudies-literature

Nanomechanical properties of bird feather rachises: exploring naturally occurring fibre reinforced laminar composites.

Project description:Flight feathers have evolved under selective pressures to be sufficiently light and strong enough to cope with the stresses of flight. The feather shaft (rachis) must resist these stresses and is fundamental to this mode of locomotion. Relatively little work has been done on rachis morphology, especially from a mechanical perspective and never at the nanoscale. Nano-indentation is a cornerstone technique in materials testing. Here we use this technique to make use of differentially oriented fibres and their resulting mechanical anisotropy. The rachis is established as a multi-layered fibrous composite material with varying laminar properties in three feathers of birds with markedly different flight styles; the Mute Swan (Cygnus olor), the Bald Eagle (Haliaeetus leucocephalus) and the partridge (Perdix perdix). These birds were chosen not just because they are from different clades and have different flight styles, but because they have feathers large enough to gain meaningful results from nano-indentation. Results from our initial datasets indicate that the proportions and orientation of the laminae are not fixed and may vary either in order to cope with the stresses of flight particular to the bird or with phylogenetic lineage.

| S-EPMC4223922 | biostudies-literature

Flame-retardant polyvinyl alcohol membrane with high transparency based on a reactive phosphorus-containing compound.

Project description:Flame-retardant polyvinyl alcohol (PVA) membranes with high transparency and flexibility were prepared by mixing an aqueous solution of a phosphorus-containing acrylic acid (AOPA) with PVA. The reaction between AOPA and PVA, the transparency, the crystallinity and the flexibility of the membrane were investigated with Fourier transform infrared spectrometry (FTIR), UV-vis light transmittance, X-ray diffraction and tensile tests, respectively. The limited oxygen index (LOI) and vertical flame (UL 94 VTM), microscale combustion calorimetry, thermogravimetric analysis (TGA) and TGA-FTIR were employed to evaluate the flame retardancy as well as to reveal the corresponding mechanisms. Results showed that PVA containing 30 wt% of AOPA can reach the UL 94 VTM V0 rating with an LOI of 27.3% and retain 95% of the original transparency of pure PVA. Adding AOPA reduces crystallinity of PVA, while the flexibility is increased. AOPA depresses the thermal degradation of PVA and promotes char formation during combustion. The proposed decomposition mechanism indicates that AOPA acts mainly in the condensed phase.

| S-EPMC5579114 | biostudies-literature

Multi-Functional Carbon Fibre Composites using Carbon Nanotubes as an Alternative to Polymer Sizing.

Project description:Carbon fibre reinforced polymers (CFRP) were introduced to the aerospace, automobile and civil engineering industries for their high strength and low weight. A key feature of CFRP is the polymer sizing - a coating applied to the surface of the carbon fibres to assist handling, improve the interfacial adhesion between fibre and polymer matrix and allow this matrix to wet-out the carbon fibres. In this paper, we introduce an alternative material to the polymer sizing, namely carbon nanotubes (CNTs) on the carbon fibres, which in addition imparts electrical and thermal functionality. High quality CNTs are grown at a high density as a result of a 35?nm aluminium interlayer which has previously been shown to minimise diffusion of the catalyst in the carbon fibre substrate. A CNT modified-CFRP show 300%, 450% and 230% improvements in the electrical conductivity on the 'surface', 'through-thickness' and 'volume' directions, respectively. Furthermore, through-thickness thermal conductivity calculations reveal a 107% increase. These improvements suggest the potential of a direct replacement for lightning strike solutions and to enhance the efficiency of current de-icing solutions employed in the aerospace industry.

| S-EPMC5120359 | biostudies-literature

Thermal Stability, Flammability and Mechanical Performances of Unsaturated Polyester-Melamine Resin Blends and of Glass Fibre-Reinforced Composites Based on Them.

Project description:A novel blend of unsaturated polyester (UP) resin with an inherently flame-retardant and char-forming melamine formaldehyde (MF) resin has been prepared with the aim of reducing the flammability of the former. MF resin, sourced as a spray-dried resin, was dissolved in diethyleneglycol solvent; the dissolved resin and the UP-MF blend were autocured by heating under conditions normally used for curing UP, i.e., room temperature for 24 h and post-curing at 80 °C for 12-24 h. The cured UP-MF blends, although heterogeneous in nature, were rigid materials having fire performances superior to those of the cured UP alone. The blends also burned, but with a much reduced smoke output compared with that from UP. Although the heterogeneity of the blends helped in improving the fire performances of the blends in terms of the MF domains forming a semi-protective char, acting as thermal barriers for the adjoining UP domains, and hence reducing their thermal degradation, the mechanical properties of composites based on them were impaired. Nevertheless, whilst UP/MF blends may not be suitable for use as matrices in glass-reinforced composites in load-bearing applications, they may lend themselves to applications as fire-retardant gel coats, especially in view of their low-smoke, char-forming attributes.

| S-EPMC9693295 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data