Challenges in Additive Manufacturing of Space Parts: Powder Feedstock Cross-Contamination and Its Impact on End Products.

ABSTRACT: This work studies the tensile properties of Ti-6Al-4V samples produced by laser powder bed based Additive Manufacturing (AM), for different build orientations. The results showed high scattering of the yield and tensile strength and low fracture elongation. The subsequent fractographic investigation revealed the presence of tungsten particles on the fracture surface. Hence, its detection and impact on tensile properties of AM Ti-6Al-4V were investigated. X-ray Computed Tomography (X-ray CT) scanning indicated that these inclusions were evenly distributed throughout the samples, however the inclusions area was shown to be larger in the load-bearing plane for the vertical specimens. A microstructural study proved that the mostly spherical tungsten particles were embedded in the fully martensitic Ti-6Al-4V AM material. The particle size distribution, the flowability and the morphology of the powder feedstock were investigated and appeared to be in line with observations from other studies. X-ray CT scanning of the powder however made the high density particles visible, where various techniques, commonly used in the certification of powder feedstock, failed to detect the contaminant. As the detection of cross contamination in the powder feedstock proves to be challenging, the use of only one type of powder per AM equipment is recommended for critical applications such as Space parts.

SUBMITTER: Brandao AD

PROVIDER: S-EPMC5459071 | biostudies-other | 2017 May

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:This paper presents lightweight tooling concepts based on additive manufacturing, with the aim of developing advanced tooling systems as well as installing sensors for real-time monitoring and control during the anchoring and manufacturing of aeronautical parts. Leveraging additive manufacturing techniques in the production of tooling yields benefits in manufacturing flexibility and material usage. These concepts transform traditional tooling systems into active, intelligent tools, improving the manufacturing process and part quality. Integrated sensors measure variables such as displacement, humidity and temperature allowing data analysis and correlation with process quality variables such as accuracy errors, tolerances achieved and surface finish. In addition to sensor integration, additive manufacturing by directed energy arc and wire deposition (DED-arc) has been selected for part manufacturing. The research includes the mechanical characterisation of the material and the microstructure of the material once manufactured by DED-arc. Design for additive manufacturing" principles guide the design process to effectively exploit the capabilities of DED-arc. These turrets, equipped with sensors, allow real-time monitoring and control of turret deformation during clamping and manufacturing of aeronautical parts. As a first step, deformation monitoring is carried out within the defined tolerance of ± 0.15, which allows a control point to be established in the turret. Future analysis of the sensor data will allow correlations with process quality variables to be established. Remarkably, the optimised version of the turret after applying DED technology weighed only 2.2 kg, significantly lighter than the original 6 kg version. Additive manufacturing and the use of lightweight structures for fixture fabrication, followed by the addition of sensors, provide valuable information and control, improving process efficiency and part quality. This research contributes to the development of intelligent and efficient tool systems for aeronautical applications.

Project description:Vat photopolymerization additive manufacturing (Vat AM) technologies have found niche industrial use being able to produce personalized parts in moderate quantity. However, Vat AM lacks in its ability to produce parts of satisfactory thermal and mechanical properties for structural applications. The purpose of this investigation was to develop high-performance resins with glass transition temperatures (Tg) above 200 °C for Vat AM, evaluate the properties of the produced thermosets and establish a structure-property relationship of the thermosets produced. Herein, we have developed SLA-type resins that feature bio-derived monomer hesperetin trimethacrylate (HTM) synthesized from the flavonone hesperetin. Diluents 4-acryloyl morpholine, styrene, 4-methyl styrene and 4-tert butylstyrene (tbutylsty) were photocured with HTM as the monomer and all produced thermosets with Tg values above 200 °C. Investigations of suitable crosslinkers urethane dimethacrylate, the vinyl ester CN 151 and Ebecryl 4859 (Eb4859) showed that each crosslinker displayed different benefits when formulated with HTM as the monomer and tbutylSty as the diluent (HTM:crosslinker:tbutylSty with mass ratio 2:1:2). The crosslinker CN 151 produced the thermoset of greatest onset of thermal decomposition temperature (T0) of 352 °C. Eb4859 produced the thermoset of highest tensile strength, 19 ± 7 MPa, amongst the set of varied crosslinkers. The formulation featuring UDM (HTM:UDM:tbutysty) offered ease of processing and was seemingly the easiest to print. Investigations of reactive diluent showed that styrene produced the thermoset of the highest extent of cure and the overall highest tensile strength, 25 ± 5 MPa, while tbutylSty produced the thermoset with the greatest Tan-δ Tg, 231 °C. HTM was synthesized, formulated with diluents, crosslinkers and initiators. The HTM resins were then 3D printed to produce thermosets of Tg values greater than 200 °C. The polymer properties were evaluated and a structure-reactivity relationship was discussed.

Dataset Information

Challenges in Additive Manufacturing of Space Parts: Powder Feedstock Cross-Contamination and Its Impact on End Products.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets