Improved Formula for the Stress Intensity Factor of Semi-Elliptical Surface Cracks in Welded Joints under Bending Stress.

ABSTRACT: Welded joints are prone to fatigue cracking with the existence of welding defects and bending stress. Fracture mechanics is a useful approach in which the fatigue life of the welded joint can be predicted. The key challenge of such predictions using fracture mechanics is how to accurately calculate the stress intensity factor (SIF). An empirical formula for calculating the SIF of welded joints under bending stress was developed by Baik, Yamada and Ishikawa based on the hybrid method. However, when calculating the SIF of a semi-elliptical crack, this study found that the accuracy of the Baik-Yamada formula was poor when comparing the benchmark results, experimental data and numerical results. The reasons for the reduced accuracy of the Baik-Yamada formula were identified and discussed in this paper. Furthermore, a new correction factor was developed and added to the Baik-Yamada formula by using theoretical analysis and numerical regression. Finally, the predictions using the modified Baik-Yamada formula were compared with the benchmark results, experimental data and numerical results. It was found that the accuracy of the modified Baik-Yamada formula was greatly improved. Therefore, it is proposed that this modified formula is used to conveniently and accurately calculate the SIF of semi-elliptical cracks in welded joints under bending stress.

SUBMITTER: Peng Y

PROVIDER: S-EPMC5459108 | biostudies-other | 2017 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Weight Function Method for Stress Intensity Factors of Semi-Elliptical Surface Cracks on Functionally Graded Plates Subjected to Non-Uniform Stresses.

Project description:In this paper, a weight function method based on the first four terms of a Taylor's series expansion is proposed to determine the stress intensity factors of functionally graded plates with semi-elliptical surface cracks. Cracked surfaces that are subjected to constant, linear, parabolic and cubic stress fields are considered. The weight functions for the surface, deepest and general points on the crack faces of long and deep cracked functionally graded plates are derived, which has never been done before in the literature. The accuracy of the method in this study is then validated by comparing the results with those of finite element modeling. The numerical results indicate that the derived weight functions are highly accurate and robust enough to predict the stress intensity factors for cracked functionally graded plates subjected to non-uniform stress distributions. The weight function method is therefore a time-saving technique and suitable for handling non-uniform stress fields.

| S-EPMC7411839 | biostudies-literature

Analysis of Selected Properties of Welded Joints of the HSLA Steels.

Project description:This paper presents research of the impact toughness and hardness distribution in specific zones of a 'single V'butt multiple-pass welded joints of the high-strength low-alloyed steels. Obtained values of the impact toughness are analyzed in correlation with a microstructure in specific zones of the welded joint, together with the micro hardness distribution found in the related zones. Based on the carried out analysis and results obtained in experiments, the applied technology of welding was evaluated. The original conclusions on influence of the selected welding procedure manual metal arc (MMA) for the root passes and metal active gas (MAG) for the filling and covering passes) on impact toughness of the high-strength low-alloyed steels are drawn. The paper also presents discussion on the valid standards and recommendations related to welding of those steels, from the aspect of applications in design of steel welded constructions.

| S-EPMC7143795 | biostudies-literature

Locally-curved geometry generates bending cracks in the African elephant skin.

Project description:An intricate network of crevices adorns the skin surface of the African bush elephant, Loxodonta africana. These micrometre-wide channels enhance the effectiveness of thermal regulation (by water retention) as well as protection against parasites and intense solar radiation (by mud adherence). While the adaptive value of these structures is well established, their morphological characterisation and generative mechanism are unknown. Using microscopy, computed tomography and a custom physics-based lattice model, we show that African elephant skin channels are fractures of the animal brittle and desquamation-deficient skin outermost layer. We suggest that the progressive thickening of the hyperkeratinised stratum corneum causes its fracture due to local bending mechanical stress in the troughs of a lattice of skin millimetric elevations. The African elephant skin channels are therefore generated by thickening of a brittle material on a locally-curved substrate rather than by a canonical tensile cracking process caused by frustrated shrinkage.

| S-EPMC6168576 | biostudies-literature

Computational modeling of fatigue crack propagation in butt welded joints subjected to axial load.

Project description:This article addresses the study of crack behavior elicited on axial fatigue in specimens joined by butt weld made of steel ASTM A36 by using fracture mechanics and simulation software of finite elements (Ansys APDL, Franc3D). The computational model was initially to define the geometry model by using CAD software. Specimens with Weld Reinforcement of 2 mm and 3mm were simulated. Subsequently, the type of element for the mesh, the information inclusion concerning material mechanical properties and load conditions were selected. By using Franc3D software, the crack propagation phenomenon is analyzed, and its growth parameters have been established. In this way, it is possible to calculate the magnitude of stress intensity factor (SIF) along the crack front. It is concluded that the stress located in the weld toe is maximized proportionately to the size of the weld reinforcement due to the concentration effect of geometric stress. In addition, it is observed that the propagation rate obtained from Paris law has a similar behavior for the studied weld reinforcements; the latter as there were short cracks.

| S-EPMC6597091 | biostudies-literature

EBSD Characterization of the Microstructure of 7A52 Aluminum Alloy Joints Welded by Friction Stir Welding.

Project description:The microstructure and texture of materials significantly influence the mechanical properties and fracture behavior; the effect of microstructure in different zones of friction stir-welded joints of 7A52 aluminum alloy on fracture behavior was investigated in this paper. The microstructural characteristics of sections of the welded joints were tested using the electron backscattered diffraction (EBSD) technique. The results indicate that the fracture is located at the advancing side of the thermomechanically affected zone (AS-TMAZ) and the stir zone (SZ) interface. The AS-TMAZ microstructure is vastly different from the microstructure and texture of other areas. The grain orientation is disordered, and the grain shape is seriously deformed under the action of stirring force. The grain size grows unevenly under the input of friction heat, resulting in a large amount of recrystallization, and there is a significant difference in the Taylor factor between adjacent grains and the AS-TMAZ-SZ interface. On the contrary, there are fine and uniform equiaxed grains in the nugget zone, the microstructure is uniform, and the Taylor factor is small at adjacent grains. Therefore, the uneven transition of microstructure and texture in the AS-TMAZ and the SZ provide conditions for crack initiation, which become the weak point of mechanical properties.

| S-EPMC8585471 | biostudies-literature

Data on microhardness and structural analysis of friction stir spot welded lap joints of AA5083-H116.

Project description:Friction stir spot welding (FSSW) was established to compete reasonably with the reverting, bolting, adhesive bonding as well as resistance spot welding (RSW) which have been used in the past for lap joining in automobile, aerospace, marine, railways, defence and shipbuilding industries. The use of these ancient and conventional joining techniques had led to increasing material cost, installation labour, and additional weight in the aircraft, shipbuilding, and other areas of applications. All these are disadvantages that can be overcome using FSSW. This research work carried out friction stir spot welding on 5058-H116 aluminium alloy by employing rotational speed in the step of 300 rpm ranges from 600 rpm to 1200 rpm with a no travel speed. It was noted that the dwell times were in the step of 5 s varying from 5 s to 15 s while the tool plunge rate was maintained at 30 mm/min. In this dataset, a cylindrical tapered rotating H13 Hot-working steel tool was used with a probe length of 5 mm and probe diameter of 6 mm, it has a shoulder diameter of 18 mm. The tool penetration depth (plunge) was maintained at 0.2 mm and the tool tilt angle at 2°. Structural integrity was carried out using Rigaku ultima IV multifunctional X-ray diffractometer (XRD) with a scan voltage of 40 kV and scan current of 30 mA. This was used to determine crystallite sizes, peak intensity, d-spacing, full width at half maximum intensity (FWHM) of the diffraction peak. TH713 digital microhardness equipment with diamond indenter was used for microhardness data acquisition following ASTM E92-82 standard test. The average Vickers hardness data values at different zones of the spot-welds were captured and presented.

| S-EPMC8129645 | biostudies-literature

Heating and Strain Sensing Elements Based on Segregated Polyethylene/Carbon Black Composites in Polymer Welded Joints.

Project description:The development of easy and direct real-time monitoring of welded joint quality instead of surface damage analysis is crucial to improve the quality of industrial products. This work presents the results of high-density polyethylene (HDPE)-based composites with various carbon black (CB) content (from 20 to 30 vol.%) for use as a heating element and strain sensor in electrofusion-welded polymer joints. The pyroresistive heating process was used to determine the effect of generated Joule heat during welding on the structure and sensor properties of polymer-carbon composites. It is shown that the generation of Joule heat depends on the nanocarbon content and affects the crystallinity of the polymer matrix. The partial disruption of the conductive path of carbon black particles was observed and, as a result, a decrease in electrical conductivity for composites with lower CB content after welding was found. For the highest CB amount, conductivity increased, which is caused by smaller particle-to-particle distance for filler paths. Therefore, the best balance between pyroresistive and sensor properties was found.

| S-EPMC11312915 | biostudies-literature

Detection of Multiple Cracks in Four-Point Bending Tests Using the Coda Wave Interferometry Method.

Project description:The enlargement of the cracks outside the permitted dimension is one of the main causes for the reduction of service life of Reinforced Concrete (RC) structures. Cracks can develop due to many causes such as dynamic or static load. When tensile stress exceeds the tensile strength of RC, cracks appear. Traditional techniques have limitations in early stage damage detection and localisation, especially on large-scale structures. The ultrasonic Coda Wave Interferometry (CWI) method using diffuse waves is one of the most promising methods to detect subtle changes in heterogeneous materials, such as concrete. In this paper, the assessment of the CWI method applied for multiple cracks opening detection on two specimens based on four-point bending test is presented. Both beams were monitored using a limited number of embedded Ultrasonic (US) transducers as well as other transducers and techniques (e.g., Digital Image Correlation (DIC), LVDT sensors, strain gauges, and Fiber Optics Sensor (FOS)). Results show that strain change and crack formation are successfully and efficiently detected by CWI method even earlier than by the other techniques. The CWI technique using embedded US transducers is undoubtedly a feasible, efficient, and promising method for long-term monitoring on real infrastructure.

| S-EPMC7180998 | biostudies-literature

Microstructure and Mechanical Properties of Welded Joints of 1.4462 Duplex Steel Made by the K-TIG Method.

Project description:K-TIG (Keyhole Tungsten Inert Gas) method is a new, emerging welding technology that offers a significant acceleration of the joining process, even for very thick plates. However, its potential for welding of certain materials is still unknown. Particularly challenging are duplex steels as this technology does not allow the use of a filler material, which is crucial for these steels and for weld joint microstructure adjustment. In order to demonstrate the suitability of this technology for single-pass welding of 1.4462 duplex steel detailed studies of the microstructure of the weld joints obtained for different linear energies were carried out and discussed with respect to their mechanical properties. According to the results obtained, the heat-affected zone (HAZ) shows a microstructure similar to the HAZ of duplex steel welded with the traditional TIG multi-pass methods. However, the weld, due to the lack of filler material, had a microstructure different to that typical for duplex steel welded joints and was also characterized by an increased content of ferrite. However, all joints, both in terms of microstructure and mechanical properties, met the requirements of the relevant standards. Moreover, the K-TIG process can be carried out in the linear energy range typical of duplex steel welding, although further optimization is needed.

| S-EPMC8708518 | biostudies-literature

The Effect of Ultrasonic Peening Treatment on Fatigue Performance of Welded Joints.

Project description:Ultrasonic peening treatment (UPT) as a method of severe plastic deformation was used to treat cruciform welded joints of Q345 steel. The application of UPT achieves material surface nanocrystallization of the peening zone, reduces stress concentration, and produces residual compressive stresses at the welded toe. Micro-structure, hardness, stress relief, S-N curve, and the fatigue fracture mechanism of cruciform welded joint of Q345 steel, both before and after UPT, were analyzed in detail. The main results show that: stress concentration and residual tensile stress are the main reasons to reduce fatigue strength of cruciform welded joints. The fatigue life of cruciform welded joints is improved for surface hardening, compressive stress, and grain refinement by UPT. Residual compressive stress caused by UPT is released with the increase of fatigue life. A very significant fatigue strength improvement happens when UPT is replenished repeatedly after a certain number of cycles.

| S-EPMC5456831 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data