Compressive Properties of Open-Cell Al Hybrid Foams at Different Temperatures.

ABSTRACT: Hybrid Ni/Al foams were fabricated by depositing electroless Ni-P (EN) coatings on open-cell Al foam substrate to obtain enhanced mechanical properties. The microstructure, chemical components and phases of the hybrid foams were observed and analyzed by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD), respectively. The mechanical properties of the foams were studied by compressive tests at different temperatures. The experiment results show that the coating is mainly composed of Ni and P elements. There was neither defect at the interface nor crack in the coatings, indicating that the EN coatings had fine adhesion to the Al substrate. The compressive strengths and energy absorption capacities of the as-received foam and hybrid foams decrease with the increasing testing temperatures, but the hybrid foams exhibit a lower decrement rate than the as-received foam. This might be attributed to the different failure mechanisms at different testing temperatures, which is conformed by fractography observation.

SUBMITTER: Liu J

PROVIDER: S-EPMC5459119 | biostudies-other | 2017 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Compressive Behavior of Al-TiB2 Composite Foams Fabricated under Increased Pressure.

Project description:The application of increased pressure was used as a strategy to investigate the effect of different cell structures on the mechanical properties of Al-TiB2 composite foams. In situ Al-xTiB2 (x = 5, 10 wt.%) composites were foamed under three different pressures (0.1 MPa, 0.24 MPa, 0.4 MPa) through the liquid melt route. The macro-structure of the composite foams was analyzed in terms of cell size distribution measured by X-ray microcomputed tomography (micro-CT). It was found that the mean cell size decreases, and the cell size distribution range narrows with increasing pressure. Uniaxial compression tests revealed that the stress fluctuation (Rsd) of 10TiB2 foams is larger than that of 5TiB2 foams under the same pressure. Moreover, cell size refinement causes the simultaneous deformation of multi-layer cells, which leads to an enhancement in the energy absorption efficiency and specific energy absorption. The comparison of experimental data with theoretical predictions (G&A model) is discussed.

| S-EPMC8434092 | biostudies-literature

Synthesis and Quasi-Static Compressive Properties of Mg-AZ91D-Al₂O₃ Syntactic Foams.

Project description:Magnesium alloys have considerably lower density than the aluminum alloy matrices that are typically used in syntactic foams, allowing for greater specific energy absorption. Despite the potential advantages, few studies have reported the properties of magnesium alloy matrix syntactic foams. In this work, Al₂O₃ hollow particles of three different size ranges, 0.106-0.212 mm, 0.212-0.425 mm, and 0.425-0.500 mm were encapsulated in Mg-AZ91D by a sub-atmospheric pressure infiltration technique. It is shown that the peak strength, plateau strength and toughness of the foam increases with increasing hollow sphere wall thickness to diameter (t/D) ratio. Since t/D was found to increase with decreasing hollow sphere diameter, the foams produced with smaller spheres showed improved performance-specifically, higher energy absorption per unit weight. These foams show better performance than other metallic foams on a specific property basis.

| S-EPMC5512899 | biostudies-other

Influences of Increased Pressure Foaming on the Cellular Structure and Compressive Properties of In Situ Al-4.5%Cu-xTiB2 Composite Foams with Different Particle Fraction.

Project description:Metallic foams have drawn increasing attention in applications ranging from lightweight structures to energy absorption devices. Mechanical properties of metallic foams depend on both their microstructure and cellular structure. In situ Al-4.5%Cu-xTiB2 composites were used as start materials for fabrication of closed-cell foams through liquid route under atmosphere pressure and increased pressure, aiming at simultaneously strengthening the cell wall material and optimizing the cellular structure. Macro-structural features of the foams were determined by micro X-ray computed tomography (µCT); results exhibit that increasing weight ratio of in situ TiB2 particles leads to coarsened cell structure for foams made under atmosphere pressure, due to the increase in critical thickness of cell wall rupture. Significant reduction of cell size and increase in cell circularity were observed for foams fabricated under increased pressure. Quasi static compression test results indicate that yield strength of foam samples increases with increasing particle fraction and refinement of cell structure. Microstructure observation shows that the continuous network at interdendritic regions consists of in situ TiB2 particles and intermetallic compounds are responsible for the reduced ductility of cell wall materials and the reduction in energy absorption efficiency of foams with high particle fraction. The influences of cell structure on the normalized strength and specific energy absorption were also discussed, and it was found that the improvement of yield strength and energy absorption of composite foams attributes to both the reinforcement of in situ TiB2 particles and the refinement of cellular structure.

| S-EPMC8157061 | biostudies-literature

Structure and Compressive Properties of Invar-Cenosphere Syntactic Foams.

Project description:The present study investigates the mechanical performance of syntactic foams produced by means of the metal powder injection molding process having an Invar (FeNi36) matrix and including cenospheres as hollow particles at weight fractions (wt.%) of 5 and 10, respectively, corresponding to approximately 41.6 and 60.0 vol.% in relation to the metal content and at 0.6 g/cm³ hollow particle density. The synthesis process results in survival of cenospheres and provides low density syntactic foams. The microstructure of the materials is investigated as well as the mechanical performance under quasi-static and high strain rate compressive loads. The compressive stress-strain curves of syntactic foams reveal a continuous strain hardening behavior in the plastic region, followed by a densification region. The results reveal a strain rate sensitivity in cenosphere-based Invar matrix syntactic foams. Differences in properties between cenosphere- and glass microsphere-based materials are discussed in relation to the findings of microstructural investigations. Cenospheres present a viable choice as filler material in iron-based syntactic foams due to their higher thermal stability compared to glass microspheres.

| S-EPMC5456466 | biostudies-other

Data characterizing compressive properties of Al/Al2O3 syntactic foam core metal matrix sandwich.

Project description:Microstructural observations and compressive property datasets of metal matrix syntactic foam core sandwich composite at quasi-static and high strain rate (HSR) conditions (525-845 s(-1)) are provided. The data supplied in this article includes sample preparation procedure prior to scanning electron and optical microscopy as well as the micrographs. The data used to construct the stress-strain curves and the derived compressive properties of all specimens in both quasi-static and HSR regions are included. Videos of quasi-static compressive failure and that obtained by a high speed image acquisition system during deformation and failure of HSR specimen are also included.

| S-EPMC4624990 | biostudies-literature

Assessing CO2 Adsorption on Amino-Functionalized Mesocellular Foams Synthesized at Different Aging Temperatures.

Project description:A wide variety of solid sorbents has recently been synthesized for application in CO2 adsorption. Among them, mesoporous silicas deserve attention because of their ability to accommodate large concentrations of different chemicals as a consequence of their surface chemistry and tunable pore structure. Functionalized materials exhibit promising features for CO2 adsorption at high temperatures and low CO2 concentrations. This work aimed to assess the influence of the textural properties on the performance of CO2 adsorption on functionalized mesoporous silica. With this goal, several mesoporous silica foams were synthesized by varying the aging temperature, obtaining materials with larger pore diameter. Thus, the synthesized materials were functionalized by grafting or impregnation with 3-aminopropyltriethoxysilane, polyethylenimine, and tetraethylenepentamine as amine sources. Finally, the amino functionalized materials were assessed for CO2 capture by means of equilibrium adsorption isotherms at 25, 45, and 65°C. Among the most outstanding results, high aging temperatures favor the performance of impregnated materials by exposing greater pore diameters. Low or intermediate temperatures favor grafting by preserving an appropriate density of silanol groups.

| S-EPMC7702615 | biostudies-literature

Adsorption and Aggregation Properties of Some Polysorbates at Different Temperatures.

Project description:Measurements of the surface tension of aqueous solutions of polysorbates (Tween 20, Tween 60 and Tween 80) at 293, 303 and 313 K were made. On the basis of the obtained results the Gibbs surface excess concentration of the Tweens at the water-air interface and critical micelle concentrations were determined. Knowing the Gibbs surface excess concentration and taking into account the difference between the limiting area occupied by water and Tween molecules at the water-air interface, the fraction occupied by Tween molecules was established. The limiting area occupied by the Tween molecule was calculated by applying the Joos equation. The area determined in such a way was confirmed by the calculations of cross section of Tween molecules based on the bond lengths and the angles between them as well as the average distance between the molecules, taking into account their different conformations. This area was used for calculation of the standard Gibbs energy of adsorption using the Langmuir equation. The standard Gibbs energy of Tweens adsorption at the water-air interface was also calculated from the hydrophobic part of Tween molecule-water interface tension and that of hydrophobic part. Using the determined values of standard Gibbs energy of adsorption at different temperatures, the standard enthalpy and entropy values were deduced. The standard thermodynamic functions of micellization were also determined and compared to the Gibbs energy of Tween molecules interactions through the water phase.

| S-EPMC6244871 | biostudies-literature

Impact of anionic polyacrylamide on stability and surface properties of the Al2O3-polymer solution system at different temperatures.

Project description:The stability mechanism and thermal properties of the system alumina-anionic polyacrylamide (PAM) was studied. The polymer's adsorption properties in dependence on the following parameters solution pH (in the range 3-9), temperature (in the range 15-35 °C), and carboxyl groups' content in the PAM chains (in the range 5-30 %) were examined. The turbidimetry method was applied for determination of the suspension stability of alumina in the presence of PAM. The obtained results indicate that the polymer addition improves significantly Al2O3 suspension stability at pH 6 and 9 (in the whole examined temperature range). PAM containing a larger number of carboxyl groups stabilizes solid particles more effectively (due to greater contribution of electrosteric interactions). Moreover, the polymer adsorption on the alumina surface causes changes in the thermal stability of the examined systems. In dependence on temperature, the higher the content of carboxyl groups in the PAM molecules, the greater the total mass loss. This is due to increased adsorption of polyacrylamide whose chains contain numerous -COOH groups.

| S-EPMC4978783 | biostudies-literature

Preparation and Properties of High-Temperature-Resistant, Lightweight, Flexible Polyimide Foams with Different Diamine Structures.

Project description:Polyimide foam (PIF) is a rising star in high-end applications such as aerospace thermal insulation and military sound absorption. However, the basic rule on molecular backbone design and uniform pore formation of PIF still need to be explored. In this work, polyester ammonium salt (PEAS) precursor powders are synthesized between alcoholysis ester of 3, 3', 4, 4'-benzophenone tetracarboxylic dianhydride (BTDE) and aromatic diamines with different chain flexibility and conformation symmetry. Then, a standard "stepwise heating" thermo-foaming approach is used to prepare PIF with comprehensive properties. A rational thermo-foaming program is designed based on in situ observation of pore formation during heating. The fabricated PIFs have uniform pore structure, and PIFBTDA-PDA shows the smallest size (147 μm) and narrow distribution. Interestingly, PIFBTDA-PDA also presents a balanced strain recovery rate (SR = 91%) and mechanical robustness (0.051 MPa at 25% strain) and its pore structure maintains regularity after 10 compression-recovery cycles, mainly due to high rigidity of the chains. Furthermore, all the PIFs possess lightweight feature (15-20 kg∙m-3), good heat resistance (Tg at 270-340 °C), thermal stability (T5% at 480-530 °C), thermal insulation properties (λ = 0.046-0.053 W∙m-1K-1 at 20 °C, λ = 0.078-0.089 W∙m-1K-1 at 200 °C), and excellent flame retardancy (LOI > 40%). The reported monomer-mediated pore-structure control strategy can provide guidelines for the preparation of high-performance PIF and its industrial applications.

| S-EPMC10304918 | biostudies-literature

Data on mechanical properties of open-cell AlSi10Mg materials and open-cell AlSi10Mg-SiC composites with different pore sizes and strain rates.

Project description:This data article describes the stress-strain curves, energy absorption and energy absorption efficiency of open-cell AlSi10Mg materials and open-cell AlSi10Mg-SiC composites with different pore sizes and strain rates. The data were obtained by quasi-static compression loading up to 60% strain at strain rates of 0.01 and 0.001 s-1 according to ISO 13,314:2011 standard. The data can be used to compare the effects of pore size and strain rate on the compressive properties of the materials. The data are related to the research article entitled "Fabrication, Experimental Investigation and Prediction of Wear Behavior of Open-Cell AlSi10Mg-SiC Composite Materials" (Kolev, M., Drenchev, L., & Petkov, V. (2023). Fabrication, Experimental Investigation and Prediction of Wear Behavior of Open-Cell AlSi10Mg-SiC Composite Materials. Metals, 13(4), 814. MDPI AG. Retrieved from http://dx.doi.org/10.3390/met13040814).

| S-EPMC10412759 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data