Synergistic Effects of Sm and C Co-Doped Mixed Phase Crystalline TiO₂ for Visible Light Photocatalytic Activity.

ABSTRACT: Mixed phase TiO₂ nanoparticles with element doping by Sm and C were prepared via a facile sol-gel procedure. The UV-Vis light-diffuse reflectance spectroscopy analysis showed that the absorption region of co-doped TiO₂ was shifted to the visible-light region, which was attributed to incorporation of samarium and carbon into the TiO₂ lattice during high-temperature reaction. Samarium effectively decreased the anatase-rutile phase transformation. The grain size can be controlled by Sm doping to achieve a large specific surface area useful for the enhancement of photocatalytic activity. The photocatalytic activities under visible light irradiation were evaluated by photocatalytic degradation of methylene blue (MB). The degradation rate of MB over the Sm-C co-doped TiO₂ sample was the best. Additionally, first-order apparent rate constants increased by about 4.3 times compared to that of commercial Degusssa P25 under the same experimental conditions. Using different types of scavengers, the results indicated that the electrons, holes, and •OH radicals are the main active species for the MB degradation. The high visible-light photocatalytic activity was attributed to low recombination of the photo-generated electrons and holes which originated from the synergistic effect of the co-doped ions and the heterostructure.

SUBMITTER: Peng F

PROVIDER: S-EPMC5459127 | biostudies-other | 2017 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Graphitic carbon nitride (g-C₃N₄) and titanium dioxide (TiO₂) were chosen as a model system to investigate photocatalytic abilities of heterojunction system under UV and visible light conditions. The use of g-C₃N₄ has been shown to be effective in the reduction in recombination through the interaction between the two interfaces of TiO₂ and g-C₃N₄. A simple method of preparing g-C₃N₄ through the pyrolysis of melamine was employed, which was then added to undoped TiO₂ material to form the g-C₃N₄-TiO₂ system. These materials were then fully characterized by X-ray diffraction (XRD), Brunauer Emmett Teller (BET), and various spectroscopic techniques including Raman, X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), diffuse absorbance, and photoluminescence analysis. Photocatalysis studies were conducted using the model dye, rhodamine 6G utilizing visible and UV light irradiation. Raman spectroscopy confirmed that a composite of the materials was formed as opposed to a mixture of the two. Using XPS analysis, a shift in the nitrogen peak to that indicative of substitutional nitrogen was detected for all doped samples. This is then mirrored in the diffuse absorbance results, which show a clear decrease in band gap values for these samples, showing the effective band gap alteration achieved through this preparation process. When g-C₃N₄-TiO₂ samples were analyzed under visible light irradiation, no significant improvement was observed compared that of pure TiO₂. However, under UV light irradiation conditions, the photocatalytic ability of the doped samples exhibited an increased reactivity when compared to the undoped TiO₂ (0.130 min-1), with 4% g-C₃N₄-TiO₂ (0.187 min-1), showing a 43.9% increase in reactivity. Further doping to 8% g-C₃N₄-TiO₂ lead to a decrease in reactivity against rhodamine 6G. BET analysis determined that the surface area of the 4% and 8% g-C₃N₄-TiO₂ samples were very similar, with values of 29.4 and 28.5 m²/g, respectively, suggesting that the actual surface area is not a contributing factor. This could be due to an overloading of the system with covering of the active sites resulting in a lower reaction rate. XPS analysis showed that surface hydroxyl radicals and oxygen vacancies are not being formed throughout this preparation. Therefore, it can be suggested that the increased photocatalytic reaction rates are due to successful interfacial interactions with the g-C₃N₄-doped TiO₂ systems.

Dataset Information

Synergistic Effects of Sm and C Co-Doped Mixed Phase Crystalline TiO₂ for Visible Light Photocatalytic Activity.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets