Rapid Fabrication of High-Aspect-Ratio Platinum Microprobes by Electrochemical Discharge Etching.

ABSTRACT: Using a graphite crucible as the counter-electrode, platinum microprobes with an aspect ratio of 30 and a tip apex radius less than 100 nm were fabricated by an electrochemical discharge etching process. The "neck-in" structure on the platinum wire induced by the electrical discharge at the liquid-air interface plays a key role in the probe shape and the voltage of the following pure electrochemical etching determines the final probe aspect ratio and tip dimensions. Moreover, the shape and diameter of the graphite counter-electrode also exhibit a significant effect on the realization of high-aspect-ratio probes. The method presented here provides a simple and rapid approach to the fabrication of micro-tools for micromachining, micromanipulation, as well as biomedical applications.

SUBMITTER: Zhang M

PROVIDER: S-EPMC5502880 | biostudies-other | 2016 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Polydimethyl siloxane wet etching for three dimensional fabrication of microneedle array and high-aspect-ratio micropillars.

Project description:Among various transdermal drug delivery (TDD) approaches, utilizing the microneedles (MNs) not only can penetrate the skin but also deliver the drug with reduced tissue damage, reduced pain, and no bleeding. However, the MNs with larger height are required to overcome the skin barrier for effective TDD. Unlike 2D patterning, etching polydimethyl siloxane (PDMS) micropillars for fabrication of 3D microstructures is presented. The PDMS micropillars were first constructed by casting PDMS on the computer numerical control-machined cylindrical microwells, which then went through etching process to obtain the MNs for subsequent fabrication of polymer MNs or high aspect ratio micropillars.

| S-EPMC4000402 | biostudies-other

Fabrication of high-aspect-ratio metallic nanostructures using nanoskiving.

Project description:This communication describes the fabrication of gold structures (for example, rings) with wall thickness of 40 nm, and with high aspect ratios up to 25. This technique combines thin-film deposition of metal on a topographically patterned epoxy substrate, with nanometer-scale sectioning using a microtome in a plane parallel to the patterned substrate. The dimensions of the metal structures are determined by the thickness of the metal film and the thickness of the epoxy sections. The shape of the resulting nanostructure is defined by the cross section of the original template.

| S-EPMC2558673 | biostudies-other

Wafer-scale 3D shaping of high aspect ratio structures by multistep plasma etching and corner lithography.

Project description:The current progress of system miniaturization relies extensively on the development of 3D machining techniques to increase the areal structure density. In this work, a wafer-scale out-of-plane 3D silicon (Si) shaping technology is reported, which combines a multistep plasma etching process with corner lithography. The multistep plasma etching procedure results in high aspect ratio structures with stacked semicircles etched deep into the sidewall and thereby introduces corners with a proper geometry for the subsequent corner lithography. Due to the geometrical contrast between the gaps and sidewall, residues are left only inside the gaps and form an inversion mask inside the semicircles. Using this mask, octahedra and donuts can be etched in a repeated manner into Si over the full wafer area, which demonstrates the potential of this technology for constructing high-density 3D structures with good dimensional control in the bulk of Si wafers.

| S-EPMC8433478 | biostudies-literature

Wafer-scale fabrication of high-aspect ratio nanochannels based on edge-lithography technique.

Project description:This paper introduced a wafer-scale fabrication approach for the preparation of nanochannels with high-aspect ratio (the ratio of the channel depth to its width). Edge lithography was used to pattern nanogaps in an aluminum film, which was functioned as deep reactive ion etching mask thereafter to form the nanochannel. Nanochannels with aspect ratio up to 172 and width down to 44 nm were successfully fabricated on a 4-inch Si wafer with width nonuniformity less than 13.6%. A microfluidic chip integrated with nanometer-sized filters was successfully fabricated by utilizing the present method for geometric-controllable nanoparticle packing.

| S-EPMC3293387 | biostudies-other

High Anodic-Voltage Focusing of Charge Carriers in Silicon Enables the Etching of Regularly-Arranged Submicrometer Pores at High Density and High Aspect-Ratio.

Project description:The anodic dissolution of silicon in acidic electrolytes is a well-known technology enabling the silicon machining to be accurately controlled down to the micrometer scale in low-doped n-type silicon electrodes. Attempts to scale down this technology to the submicrometer scale has shown to be challenging, though it premises to enable the fabrication of meso and nano structures/systems that would greatly impact the fields of biosensors and nanomedicine. In this work, we report on the electrochemical etching at high anodic voltages (up to 40 V) of two-dimensional regular arrays of millions pores per square centimeter (up to 30 × 106 cm-2) with sub-micrometric diameter (down to ~860 nm), high depth (up to ~40 ?m), and high aspect-ratio (up to ~45) using low-doped n-type silicon electrodes (resistivity 3-8 ? cm). The use of high anodic voltages, which are over one order of magnitude higher than that commonly used in electrochemical etching of silicon, tremendously improves hole focusing at the pore tips during the etching and enables, in turn, the control of electrochemical etching of submicrometer-sized pores when spatial period reduces below 2 ?m. A theoretical model allows experimental results to be interpreted in terms of an electric-field-enhanced focusing of holes at the tip apex of the pores at high anodic voltages, with respect to the pore base, which leads to a smaller curvature radius of the tip apex and enables, in turn, the etching of pore tips to be preferentially sustained over time and space.

| S-EPMC6287200 | biostudies-literature

Simple and customizable method for fabrication of high-aspect ratio microneedle molds using low-cost 3D printing.

Project description:We present a simple and customizable microneedle mold fabrication technique using a low-cost desktop SLA 3D printer. As opposed to conventional microneedle fabrication methods, this technique neither requires complex and expensive manufacturing facilities nor expertise in microfabrication. While most low-cost 3D-printed microneedles to date display low aspect ratios and poor tip sharpness, we show that by introducing a two-step "Print & Fill" mold fabrication method, it is possible to obtain high-aspect ratio sharp needles that are capable of penetrating tissue. Studying first the effect of varying design input parameters and print settings, it is shown that printed needles are always shorter than specified. With decreasing input height, needles also begin displaying an increasingly greater than specified needle base diameter. Both factors contribute to low aspect ratio needles when attempting to print sub-millimeter height needles. By setting input height tall enough, it is possible to print needles with high-aspect ratios and tip radii of 20-40 µm. This tip sharpness is smaller than the specified printer resolution. Consequently, high-aspect ratio sharp needle arrays are printed in basins which are backfilled and cured in a second step, leaving sub-millimeter microneedles exposed resulting microneedle arrays which can be used as male masters. Silicone female master molds are then formed from the fabricated microneedle arrays. Using the molds, both carboxymethyl cellulose loaded with rhodamine B as well as polylactic acid microneedle arrays are produced and their quality examined. A skin insertion study is performed to demonstrate the functional capabilities of arrays made from the fabricated molds. This method can be easily adopted by the microneedle research community for in-house master mold fabrication and parametric optimization of microneedle arrays.

| S-EPMC6799892 | biostudies-literature

Reduced Etch Lag and High Aspect Ratios by Deep Reactive Ion Etching (DRIE).

Project description:Deep reactive ion etching (DRIE) with the Bosch process is one of the key procedures used to manufacture micron-sized structures for MEMS and microfluidic applications in silicon and, hence, of increasing importance for miniaturisation in biomedical research. While guaranteeing high aspect ratio structures and providing high design flexibility, the etching procedure suffers from reactive ion etching lag and often relies on complex oxide masks to enable deep etching. The reactive ion etching lag, leading to reduced etch depths for features exceeding an aspect ratio of 1:1, typically causes a height difference of above 10% for structures with aspect ratios ranging from 2.5:1 to 10:1, and, therefore, can significantly influence subsequent device functionality. In this work, we introduce an optimised two-step Bosch process that reduces the etch lag to below 1.5%. Furthermore, we demonstrate an improved three-step Bosch process, allowing the fabrication of structures with 6 μm width at depths up to 180 μm while maintaining their stability.

| S-EPMC8150727 | biostudies-literature

Carcinogenic Potential of High Aspect Ratio Carbon Nanomaterials.

Project description:Engineered nanomaterials, including high aspect ratio carbon nanomaterials, are often commercialized without a complete human risk assessment and safety evaluation. A health concern has been raised that high aspect ratio nanomaterials such as carbon nanotubes may cause unintended health consequences, such as asbestos-like lung cancer and mesothelioma, when chronically inhaled. Considering the widespread industrial and clinical applications and the increasing incidence of human exposure to nanomaterials, it is important to address the issue of nanomaterial carcinogenicity in a timely manner. This review summarizes recent advances in nanomaterial genotoxicity and carcinogenicity with a focus on high aspect ratio carbon nanotubes, and discusses current knowledge gaps and future research directions.

| S-EPMC4996468 | biostudies-literature

From Chip Size to Wafer-Scale Nanoporous Gold Reliable Fabrication Using Low Currents Electrochemical Etching.

Project description:We report a simple, scalable route to wafer-size processing for fabrication of tunable nanoporous gold (NPG) by the anodization process at low constant current in a solution of hydrofluoric acid and dimethylformamide. Microstructural, optical, and electrochemical investigations were employed for a systematic analysis of the sample porosity evolution while increasing the anodization duration, namely the small angle X-ray scattering (SAXS) technique and electrochemical impedance spectroscopy (EIS). Whereas the SAXS analysis practically completes the scanning electronic microscopy (SEM) investigations and provides data about the impact of the etching time on the nanoporous gold layers in terms of fractal dimension and average pore surface area, the EIS analysis was used to estimate the electroactive area, the associated roughness factor, as well as the heterogeneous electron transfer rate constant. The bridge between the analyses is made by the scanning electrochemical microscopy (SECM) survey, which practically correlates the surface morphology with the electrochemical activity. The results were correlated to endorse the control over the gold film nanostructuration process deposited directly on the substrate that can be further subjected to different technological processes, retaining its properties. The results show that the anodization duration influences the surface area, which subsequently modifies the properties of NPG, thus enabling tuning the samples for specific applications, either optical or chemical.

| S-EPMC7700230 | biostudies-literature

High aspect ratio nanotubes assembled from macrocyclic iminium salts.

Project description:One-dimensional nanostructures such as carbon nanotubes and actin filaments rely on strong and directional interactions to stabilize their high aspect ratio shapes. This requirement has precluded making isolated, long, thin organic nanotubes by stacking molecular macrocycles, as their noncovalent stacking interactions are generally too weak. Here we report high aspect ratio (>103), lyotropic nanotubes of stacked, macrocyclic, iminium salts, which are formed by protonation of the corresponding imine-linked macrocycles. Iminium ion formation establishes cohesive interactions that, in organic solvent (tetrahydrofuran), are two orders of magnitude stronger than the neutral macrocycles, as explained by physical arguments and demonstrated by molecular dynamics simulations. Nanotube formation stabilizes the iminium ions, which otherwise rapidly hydrolyze, and is reversed and restored upon addition of bases and acids. Acids generated by irradiating a photoacid generator or sonicating chlorinated solvents also induced nanotube assembly, allowing these nanostructures to be coupled to diverse stimuli, and, once assembled, they can be fixed permanently by cross-linking their pendant alkenes. As large macrocyclic chromonic liquid crystals, these iminium salts are easily accessible through a modular design and provide a means to rationally synthesize structures that mimic the morphology and rheology of carbon nanotubes and biological tubules.

| S-EPMC6130376 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data