Effective Degradation of Aqueous Tetracycline Using a Nano-TiO₂/Carbon Electrocatalytic Membrane.

ABSTRACT: In this work, an electrocatalytic membrane was prepared to degrade aqueous tetracycline (TC) using a carbon membrane coated with nano-TiO₂ via a sol-gel process. SEM, XRD, EDS, and XPS were used to characterize the composition and structure of the electrocatalytic membrane. The effect of operating conditions on the removal rate of tetracycline was investigated systematically. The results show that the chemical oxygen demand (COD) removal rate increased with increasing residence time while it decreased with increasing the initial concentration of tetracycline. Moreover, pH had little effect on the removal of tetracycline, and the electrocatalytic membrane could effectively remove tetracycline with initial concentration of 50 mg·L-1 (pH, 3.8-9.6). The 100% tetracycline and 87.8% COD removal rate could be achieved under the following operating conditions: tetracycline concentration of 50 mg·L-1, current density of 1 mA·cm-2, temperature of 25 °C, and residence time of 4.4 min. This study provides a new and feasible method for removing antibiotics in water with the synergistic effect of electrocatalytic oxidation and membrane separation. It is evident that there will be a broad market for the application of electrocatalytic membrane in the field of antibiotic wastewater treatment.

SUBMITTER: Liu Z

PROVIDER: S-EPMC5503005 | biostudies-other | 2016 May

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:The morphology-controlled synthesis of nanostructured photocatalysts by an environmentally friendly and low-cost method provides a feasible way to realize practical applications of photocatalysts. Herein, Bi2WO6 (BWO) nanophotocatalysts with mulberry shape, sheet-like, and round-cake morphologies have been successfully synthesized through a highly facile solvothermal process by simply adjusting the solvothermal temperature or utilizing selective addition of ethylene glycol as an orientation agent without using strong acids and bases and/or hazardous chemicals. The ratio of ethylene glycol and glacial acetic acid can affect the morphology and oxygen vacancy content of BWO, thereby influencing the photocatalytic performance. The photocatalytic activity of the as-prepared samples was evaluated by degradation of rhodamine B (RhB) and tetracycline under visible-light irradiation. The results indicated that all the BWO samples exhibited morphology-associated photocatalytic activity, and the sheet-like structure of BWO obtained via solvothermal treatment at 120 °C with ethylene glycol and glacial acetic acid ratio of 1:3 achieved the maximum specific surface area and possessed abundant oxygen vacancies, exhibiting outstanding photocatalytic activity for degradation of RhB and tetracycline. The degradation rate of RhB reached 100% within 20 min. To the best of our knowledge, this value is one of the most remarkable values for pristine BWO photocatalysts. Radical capture experiments demonstrated that hydroxyl radicals (·OH) play major roles compared with electrons (e−) and holes (h+) in the photocatalytic degradation process. A possible mechanism for the photocatalytic degradation of pollutants was proposed to better understand the reaction process. We believe that the more economical, efficient and greener methodology can provide guidance to develop highly efficient photocatalysts with favourable morphology and structure. Supplementary Information The online version contains supplementary material available at 10.1007/s10854-022-09654-z.

Dataset Information

Effective Degradation of Aqueous Tetracycline Using a Nano-TiO₂/Carbon Electrocatalytic Membrane.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets