Investigation on Polylactide (PLA)/Poly(butylene adipate-co-terephthalate) (PBAT)/Bark Flour of Plane Tree (PF) Eco-Composites.

ABSTRACT: Polylactide (PLA)/poly(butylene adipate-co-terephthalate) (PBAT)/bark flour of plane tree (PF) eco-composites were prepared via melt blending. The morphologies, mechanical properties, crystal structures and melting and crystallization behaviors of the eco-composites were investigated by means of scanning electron microscopy (SEM), mechanical tests, polarized light microscopy (PLM), wide angle X-ray diffraction (WAXD) and differential scanning calorimetry (DSC), respectively. It is shown that the interfacial adhesion between PLA matrix and PF is weak and the mechanical properties of PLA/PF eco-composites are poor. The titanate treatment improves the adhesion between the matrix and the filler and enhances the stiffness of the eco-composites. The toughness is improved by PBAT and ductile fractured surfaces can be found. The spherulitic size of PLA is decreased by the addition of PF. The α crystalline form of PLA remains in the composites. Compared with PF, T-PF (PF treated by a titanate coupling agent) and PBAT have negative effects on the crystallization of PLA.

SUBMITTER: Dou Q

PROVIDER: S-EPMC5503033 | biostudies-other | 2016 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Biodegradation Behavior of Poly(Butylene Adipate-Co-Terephthalate) (PBAT), Poly(Lactic Acid) (PLA), and Their Blend in Freshwater with Sediment.

Project description:Poly(butylene adipate-co-terephthalate) (PBAT) and poly(lactic acid) (PLA) are well-known biodegadable polyesters due to their outstanding performance. The biodegradation behavior of PLA/PBAT blends in freshwater with sediment is investigated in this study by analyzing the appearance, chemical structure and aggregation structure of their degraded residues via SEM, TG, DSC, gel permeation chromatography (GPC) and XPS. The effect of aggregation structure, hydrophilia and biodegradation mechanisms of PBAT and PLA on the biodegradability of PLA/PBAT blends is illuminated in this work. After biodegradation, the butylene terephthalate unit in the molecular structure of the components and the molecular weight of PLA/PBAT blends decreased, while the content of C-O bond in the composites increased, indicating that the samples indeed degraded. After 24 months of degradation, the increase in the relative peak area proportion of C-O to C=O in PLA/PBAT-25, PLA/PBAT-50 and PLA/PBAT-75 was 62%, 46% and 68%, respectively. The biodegradation rates of PBAT and PLA in the PLA/PBAT blend were lower than those for the respective single polymers.

| S-EPMC7504808 | biostudies-literature

Introduction of stereocomplex crystallites of PLA for the solid and microcellular poly(lactide)/poly(butylene adipate-<i>co</i>-terephthalate) blends.

Project description:Solid and microcellular poly(l-lactide)/poly(butylene adipate-co-terephthalate) (PLLA/PBAT) blends with or without poly(d-lactide) (PDLA) were prepared via melt blending and batch foaming process with supercritical carbon dioxide, respectively. The introduction of PDLA on the rheological properties, crystallization behavior and dynamic mechanical properties of the PLLA matrix were investigated. The formed PLA stereocomplex between PLLA and PDLA enhanced the storage modulus and complex viscosity of PLLA/PBAT blends efficiently. Interestingly, the addition of 5 wt% or 10 wt% PDLA in the PLLA/PBAT blends was unfavorable for the PLLA crystallization behavior. The potential reason can be sc-PLA crystallites acting as the physical crosslinking points, which constrained the molecular mobility of the PLLA matrix and even blocked the nucleating effect of PBAT domains. Both the enhanced melt strength and decreased crystallinity of the PLLA matrix are favorable for the cell nucleation and growth and the gas adsorption, respectively. The designed partially foaming of PLLA/PBAT with or without PDLA was carried out to investigate the foaming mechanism. The final cell morphology of PLLA/PBAT foams exhibited typical open-cell structure mainly attributed to the soft immiscible PBAT phase as separated domains. With further addition of PDLA in the PLLA/PBAT blends, the microcellular morphology exhibited decreased average cell size and increased cell density. The sc-PLA crystallites networks in the PLLA matrix acted as cell nucleating agents, which meanwhile resisted the force of cell growth and then prevented the cell collapse.

| S-EPMC9079314 | biostudies-literature

Homocomposites of Polylactide (PLA) with Induced Interfacial Stereocomplex Crystallites.

Project description:The demand for "green" degradable composite materials increases with growing environmental awareness. The key challenge is achieving the preferred physical properties and maintaining their eco-attributes in terms of the degradability of the matrix and the filler. Herein, we have designed a series of "green" homocomposites materials based purely on polylactide (PLA) polymers with different structures. Film-extruded homocomposites were prepared by melt-blending PLA matrixes (which had different degrees of crystallinity) with PLLA and PLA stereocomplex (SC) particles. The PLLA and SC particles were spherical and with 300-500 nm size. Interfacial crystalline structures in the form of stereocomplexes were obtained for certain particulate-homocomposite formulations. These SC crystallites were found at the particle/matrix interface when adding PLLA particles to a PLA matrix with d-lactide units, as confirmed by XRD and DSC data analyses. For all homocomposites, the PLLA and SC particles acted as nucleating agents and enhanced the crystallization of the PLA matrixes. The SC particles were more rigid and had a higher Young's modulus compared with the PLLA particles. The mechanical properties of the homocomposites varied with particle size, rigidity, and the interfacial adhesion between the particles and the matrix. An improved tensile strength in the homocomposites was achieved from the interfacial stereocomplex formation. Hereafter, homocomposites with tunable crystalline arrangements and subsequently physical properties, are promising alternatives in strive for eco-composites and by this, creating materials that are completely degradable and sustainable.

| S-EPMC4613739 | biostudies-literature

Tree bark metagenome

Project description:Fungal diversity driven by bark features affects phorophyte preference in epiphytic orchids from southern China.

| PRJNA702612 | ENA

Nano-stereocomplexation of polylactide (PLA) spheres by spray droplet atomization.

Project description:A direct, efficient, and scalable method to prepare stereocomplexed polylactide (PLA)-based nanoparticles (NPs) is achieved. By an appropriate combination of fabrication parameters, NPs with controlled shape and crystalline morphology are obtained and even pure PLA stereocomplexes (PLASC) are successfully prepared using the spray-drying technology. The formed particles of varying D- and L-LA content have an average size of ?400 nm, where the smallest size is obtained for PLA50, which has an equimolar composition of PLLA and PDLA in solution. Raman spectra of the particles show the typical shifts for PLASC in PLA50, and thermal analysis indicates the presence of pure stereocomplexation, with only one melting peak at 226 °C. Topographic images of the particles exhibit a single phase with different surface roughness in correlation with the thermal analysis. A high yield of spherically shaped particles is obtained. The results clearly provide a proficient method for achieving PLASC NPs that are expected to function as renewable materials in PLA-based nanocomposites and potentially as more stable drug delivery carriers.

| S-EPMC4283727 | biostudies-literature

Augmentation of a Microbial Consortium for Enhanced Polylactide (PLA) Degradation.

Project description:Bioplastics are eco-friendly and derived from renewable biomass sources. Innovation in recycling methods will tackle some of the critical issues facing the acceptance of bioplastics. Polylactic acid (PLA) is the commonly used and well-studied bioplastic that is presumed to be biodegradable. Considering their demand and use in near future, exploration for microbes capable of bioplastic degradation has high potential. Four PLA degrading strains were isolated and identified as Penicillium chrysogenum, Cladosporium sphaerospermum, Serratia marcescens and Rhodotorula mucilaginosa. A consortium of above strains degraded 44 % (w/w) PLA in 30 days time in laboratory conditions. Subsequently, the microbial consortium employed effectively for PLA composting.

| S-EPMC4729741 | biostudies-literature

Properties of Biodegradable Films Based on Poly(butylene Succinate) (PBS) and Poly(butylene Adipate-co-Terephthalate) (PBAT) Blends †,‡.

Project description:Compression molded biodegradable films based on poly(butylene succinate) (PBS) and poly(butylene adipate-co-terephthalate) (PBAT) at varying weights were prepared, and their relevant properties for packaging applications are here reported. The melt rheology of the blends was first studied, and the binary PBS/PBAT blends exhibited marked shear thinning and complex thermoreological behavior, due to the formation of a co-continuous morphology in the 50 wt% blend. The films were characterized by infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), mechanical tensile tests, scanning electron microscopy (SEM), and oxygen and water vapor permeability. PBS crystallization was inhibited in the blends with higher contents of PBAT, and FTIR and SEM analysis suggested that limited interactions occur between the two polymer phases. The films showed increasing stiffness as the PBS percentage increased; further, a sharp decrease in elongation at break was noticed for the films containing percentages of PBS greater than 25 wt%. Gas permeability decreased with increasing PBS content, indicating that the barrier properties of PBS can be tuned by blending with PBAT. The results obtained point out that the blend containing 25 wt% PBS is a good compromise between elastic modulus (135 MPa) and deformation at break (390%) values. Overall, PBS/PBAT blends represent an alternative for packaging films, as they combine biodegradability, good barrier properties and reasonable mechanical behavior.

| S-EPMC7600530 | biostudies-literature

Electrical and Optical Properties of Silicon OxideLignin Polylactide (SiO2-L-PLA).

Project description:This paper presents a study on the electrical properties of new polylactide-basednanocomposites with the addition of silicon-dioxide-lignin nanoparticles and glycerine as a plasticizer.Four samples were prepared with nanoparticle mass fractions ranging between 0.01 to 0.15(0.01, 0.05, 0.10, and 0.15), and three samples were prepared without nanoparticle filler-unfilledand unprocessed polylactide, unfilled and processed polylactide, and polylactide with Fusabondand glycerine. All samples were manufactured using the melt mixing extrusion techniqueand injection molding. Only the unfilled and unprocessed PLA sample was directly preparedby injection molding. Dielectric properties were studied with broadband spectroscopy in a frequencyrange from 0.1 Hz to 1 MHz in 55 steps designed on a logarithmic scale and a temperature rangefrom 293.15 to 333.15 K with a 5 K step. Optical properties of nanocomposites were measuredwith UV-VIS spectroscopy at wavelengths from 190 to 1100 nm. The experimental data show thatthe addition of silicon-dioxide-lignin and glycerine significantly affected the electrical propertiesof the studied nanocomposites based on polylactide. Permittivity and electrical conductivity showa significant increase with an increasing concentration of nanoparticle filler. The optical properties arealso affected by nanofiller and cause an increase in absorbance as the number of silicon-dioxide-ligninnanoparticles increase.

| S-EPMC7144936 | biostudies-literature

Quantifying carbon in tree bark: The importance of bark morphology and tree size.

Project description:Bark contributes approximately 20% to the total above-ground biomass of trees, yet bark is not properly accounted for when estimating carbon sequestered by trees. Current allometric functions estimate tree volume from diameter measured over the bark, and derive bark density and carbon content from estimates for wood. As the bark density of hardwood species is 40%-50% lower than the wood density, but nearly equivalent in conifers, bark carbon is overestimated for most species. The latter is further exacerbated by variation in bark volume with bark surface morphology.Fissured bark volume is overestimated by diameter over bark measurements by up to 40%. The vacant space in fissures can be accounted for by a bark fissure index (BFI). We calculate bark carbon for Australian species from a non-destructive and effective BFI using bark thickness measured in the field.Bark volume, and in turn bark carbon, scaled inversely with tree size (diameter) so that bark volume comprised 42% of small trees (10 cm diameter at breast height, DBH) but 23% of large trees (50 cm DBH). Our BFI method using a bark thickness gauge (BGM) yielded similar results than using the less time-efficient contour gauge method (CM) to estimate BFI (bias BGM-CM -1.3%, non-significant at p = 0.72). Both BGM and CM had an error of <4% compared to digitized BFI from destructive sampled stem disks. An average of 15 bark gauge measurements per tree estimated bark thickness (and inconsequence BFI) for both fissured and unfissured bark with <20% error relative to the exact value.Using the bark gauge method, BFI can be rapidly measured from large numbers of trees needed for estimating bark carbon at the community level and modelling carbon uptake, storage and cycling in woody biomes.

| S-EPMC8048897 | biostudies-literature

Polylactide (PLA) as a Cell Carrier in Mesophilic Anaerobic Digestion-A New Strategy in the Management of PLA.

Project description:The management of waste polylactide (PLA) in various solutions of thermophilic anaerobic digestion (AD) is problematic and often uneconomical. This paper proposes a different approach to the use of PLA in mesophilic AD, used more commonly on the industrial scale, which consists of assigning the function of a microbial carrier to the biopolymer. The study involved the testing of waste wafers and waste wafers and cheese in a co-substrate system, combined with digested sewage sludge. The experiment was conducted on a laboratory scale, in a batch bioreactor mode. They were used as test samples and as samples with the addition of a carrier: WF-control and WFC-control; WF + PLA and WFC + PLA. The main objective of the study was to verify the impact of PLA in the granular (PLAG) and powder (PLAP) forms on the stability and efficiency of the process. The results of the analysis of physicochemical properties of the carriers, including the critical thermal analysis by differential scanning calorimetry (DSC), as well as the amount of cellular biomass of Bacillus amyloliquefaciens obtained in a culture with the addition of the tested PLAG and PLAP, confirmed that PLA can be an effective cell carrier in mesophilic AD. The addition of PLAG produced better results for bacterial proliferation than the addition of powdered PLA. The highest level of dehydrogenase activity was maintained in the WFC + PLAG system. An increase in the volume of the methane produced for the samples digested with the PLA granules carrier was registered in the study. It went up by c.a. 26% for WF, from 356.11 m3 Mg-1 VS (WF-control) to 448.84 m3 Mg-1 VS (WF + PLAG), and for WFC, from 413.46 m3 Mg-1 VS, (WFC-control) to 519.98 m3 Mg-1 VS (WFC + PLAG).

| S-EPMC9697477 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data