Effect of Storage in Distilled Water for Three Months on the Antimicrobial Properties of Poly(methyl methacrylate) Denture Base Material Doped with Inorganic Filler.

ABSTRACT: The colonization of poly(methyl methacrylate) (PMMA) denture base materials by pathogenic microorganisms is a major problem associated with the use of prostheses, and the incorporation of antimicrobial fillers is a method of improving the antimicrobial properties of these materials. Numerous studies have demonstrated the initial in vitro antimicrobial effectiveness of this type of material; however, reports demonstrating the stability of these fillers over longer periods are not available. In this study, silver sodium hydrogen zirconium phosphate was introduced into the powder component of a PMMA denture base material at concentrations of 0.25%, 0.5%, 1%, 2%, 4%, and 8% (w/w). The survival rates of the gram-positive bacterium Staphylococcus aureus, gram-negative bacterium Escherichia coli and yeast-type fungus Candida albicans were established after fungal or bacterial suspensions were incubated with samples that had been previously stored in distilled water. Storage over a three-month period led to the progressive reduction of the initial antimicrobial properties. The results of this study suggest that additional microbiological tests should be conducted for materials that are treated with antimicrobial fillers and intended for long-term use. Future long-term studies of the migration of silver ions from the polymer matrix and the influence of different media on this ion emission are required.

SUBMITTER: Chladek G

PROVIDER: S-EPMC5503091 | biostudies-other | 2016 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:This study aimed to investigate the cleansing effects of grapefruit seed extract (GSE) on biofilms of Candida albicans (C. albicans) formed on denture-base resin and the influence of GSE on the mechanical and surface characteristics of the resin. GSE solution diluted with distilled water to 0.1% (0.1% GSE) and 1% (1% GSE) and solutions with Polident® denture cleansing tablet dissolved in distilled water (Polident) or in 0.1% GSE solution (0.1% G+P) were prepared as cleansing solutions. Discs of acrylic resin were prepared, and the biofilm of C. albicans was formed on the discs. The discs with the biofilm were treated with each solution for 5 min at 25°C. After the treatment, the biofilm on the discs was analyzed using a colony forming unit (CFU) assay, fluorescence microscopy, and scanning electron microscopy (SEM). In order to assess the persistent cleansing effect, the discs treated with each solution for 5 min were aerobically incubated in Yeast Nitrogen Base medium for another 24 h. After incubation, the persistent effect was assessed by CFU assay. Some specimens of acrylic resin were immersed in each solution for 7 days, and changes in surface roughness (Ra), Vickers hardness (VH), flexural strength (FS), and flexural modulus (FM) were evaluated. As a result, the treatment with 1% GSE for 5 min almost completely eliminated the biofilm formed on the resin; whereas, the treatment with 0.1% GSE, Polident, and 0.1% G+P for 5 min showed a statistically significant inhibitory effect on biofilms. In addition, 0.1% GSE and 0.1% G+P exerted a persistent inhibitory effect on biofilms. Fluorescence microscopy indicated that Polident mainly induced the death of yeast, while the cleansing solutions containing at least 0.1% GSE induced the death of hyphae as well as yeast. SEM also revealed that Polident caused wrinkles, shrinkage, and some deep craters predominantly on the cell surfaces of yeast, while the solutions containing at least 0.1% GSE induced wrinkles, shrinkage, and some damage on cell surfaces of not only yeasts but also hyphae. No significant changes in Ra, VH, FS, or FM were observed after immersion in any of the solutions. Taken together, GSE solution is capable of cleansing C. albicans biofilms on denture-base resin and has a persistent inhibitory effect on biofilm development, without any deteriorations of resin surface.

Project description:Flexural strength (FS) of denture base resins (DBRs) had been improved by reinforcing it with different glass fibers. However, a limited data are available on the effect of glass fiber reinforcement with conventional heat-cured resin after prolonged water storage.This study aimed to evaluate the reinforcing effect of novel S-glass and nylon fibers on the FS of acrylic DBRs. It also aimed to evaluate the effect of glass fiber reinforcement on the FS of acrylic DBRs after a prolonged storage in water.One hundred and sixty identical specimens were fabricated in specially designed molds according to the manufacturer's instructions. The three experimental groups were prepared consisting of conventional (unreinforced) acrylic resin, novel S-glass fiber-reinforced and nylon fiber-reinforced acrylic resin. The specimens were fabricated in a standardized fashion for each experimental group. Each group was further subdivided into two groups on the basis of storage conditions (dry and wet). FS was tested using a three-point universal testing machine at a crosshead speed of 5 mm/min. Glass fiber-reinforced group was further tested after prolonged storage in distilled water. Entered data were statistically analyzed with one-way ANOVA and least significant difference post hoc test.In this study, statistically significant differences were noted in the FS of all the groups. S-glass fiber-reinforced group had highest FS compared to the other two groups (P < 0.001). Nylon fiber-reinforced group had lowest FS. All the groups stored in distilled water revealed a decrease in strength compared to those stored in dry atmosphere. Among wet specimens, those stored for 3 weeks had a significantly higher FS than those stored at one and 2 weeks (P < 0.01).Within the limitations of this investigation, the FS of heat-cured acrylic DBR was improved after reinforcement with glass fibers. It can be recommended to strengthen distal extension partial and complete denture bases. Nylon fibers may not be desirable for strengthening acrylic denture bases.

Dataset Information

Effect of Storage in Distilled Water for Three Months on the Antimicrobial Properties of Poly(methyl methacrylate) Denture Base Material Doped with Inorganic Filler.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets