Acceleration of Intended Pozzolanic Reaction under Initial Thermal Treatment for Developing Cementless Fly Ash Based Mortar.

ABSTRACT: Without using strong alkaline solution or ordinary Portland cement, a new structural binder consisting of fly ash and hydrated lime was hardened through an intensified pozzolanic reaction. The main experimental variables are the addition of silica fume and initial thermal treatment (60 °C for 3 days). A series of experiments consisting of mechanical testing (compressive and flexural strength, modulus of elasticity), X-ray diffraction, and measurements of the heat of hydration, pore structure, and shrinkage were conducted. These tests show that this new fly ash-based mortar has a compressive strength of 15 MPa at 91 days without any silica fume addition or initial thermal treatment. The strength increased to over 50 MPa based on the acceleration of the intensified pozzolanic reaction from the silica fume addition and initial thermal treatment. This is explained by a significant synergistic effect induced by the silica fume. It intensifies the pozzolanic reaction under thermal treatment and provides a space filling effect. This improved material performance can open a new pathway to utilize the industrial by-product of fly ash in cementless construction materials.

SUBMITTER: Kwon YH

PROVIDER: S-EPMC5503319 | biostudies-other | 2017 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

---Mechanical behavior of textile reinforced alkali-activated mortar based on fly ash, metakaolin and ladle furnace slag.

Project description:The need for repair and maintenance has become dominant in the European construction sector. This, combined with the urge to decrease CO 2 emissions, has resulted in the development of lower carbon footprint repair solutions such as textile reinforced mortars (TRM) based on alkali-activated materials (AAM). Life cycle studies indicate that AAM CO 2 savings, when compared to Portland cement, range from 80% to 30%. Furthermore, in this study, recycled aggregates were considered with the aim to promote a circular economy mindset. AAM mortars formulation based on fly ash, ladle furnace slag and metakaolin were tested for compressive and flexural strength. Three out of all formulations were chosen for an analysis on the potential of these mortars to be used for TRM applications. Tensile and shear bond tests, combined with a concrete substrate, were executed as indicators of the TRM effectiveness. Scanning electron microscopy and chemical analysis based on energy dispersive X-ray spectroscopy were used to interpret the results and reveal the reasons behind the different level of performance of these composites. Results indicated that TRM based on high calcium fly ash are unsuitable for structural strengthening applications due to low bond between matrix and/or substrate and fibers. Metakaolin-based TRM showed good performance both in terms of tensile strength and bond capacity, which suggests potential as a repair mortar.

| S-EPMC10445836 | biostudies-literature

Mechanical Properties and Microstructure of Class C Fly Ash-Based Geopolymer Paste and Mortar.

Project description:This paper presents workability, compressive strength and microstructure for geopolymer pastes and mortars made of class C fly ash at mass ratios of water-to-fly ash from 0.30 to 0.35. Fluidity was in the range of 145-173 mm for pastes and 131-136 mm for mortars. The highest strengths of paste and mortar were 58 MPa and 85 MPa when they were cured at 70 °C for 24 h. In XRD patterns, unreacted quartz and some reacted product were observed. SEM examination indicated that reacted product has formed and covered the unreacted particles in the paste and mortar that were consistent with their high strength.

| S-EPMC5452326 | biostudies-other

Combined Effects of Non-Conforming Fly Ash and Recycled Masonry Aggregates on Mortar Properties.

Project description:This work evaluates the effects of using non-conforming fly ash (Nc-FA) generated in a thermoelectric power plant as filler material for mortars made with natural sand (NA) and recycled sand from masonry waste (FRMA). The incorporation of powdered recycled masonry filler (R-MF) is also tested as an alternative to siliceous filler (Si-F). Three families of mortars were designed to study: the effect of replacing Si-F with Nc-FA on mortars made with NA; the effect of replacing Si-F with Nc-FA on mortars made with 50% of NA and 50% of FRMA; and the effect of replacing Si-F with R-MF on mortars made with NA and FRMA. Replacing Si-F with Nc-FA is a viable alternative that increases the mechanical strength, the workability and durability properties and decreases the shrinkage. The use of FRMA and Nc-FA improved the mechanical strength of mortars, and it slightly increased the shrinkage. The replacement of Si-F with R-MF on mortars made with FRMA is not a good alternative, because it has a negative impact on all of the properties tested. This work can help both to reduce cement and natural resources' consumption and to increase the recycling rate of Nc-FA and FRMA.

| S-EPMC5457083 | biostudies-other

Sustainability, Eco-Point and Engineering Performance of Different Workability OPC Fly-Ash Mortar Mixes.

Project description:This study investigates the engineering performance and CO₂ footprint of mortar mixers by replacing Portland cement with 10%, 20%, 40% and 60% fly ash, a common industrial waste material. Samples of self-compacting mortar (SCM) were prepared with four different water/binder ratios and varying dosages of superplasticizer to give three ranges of workability, i.e., normal, high and self-compacting mortar mix. The engineering performance was assessed in term of compressive strength after designated curing periods for all mixes. CO₂ footprint was the environmental impact indicator of each production stage. The optimum mix obtained was at 10% replacement rate for all mixes. Total production emission reduced by 56% when the fly ash replacement rate increased from 0% to 60% (maximum). This is translated to a reduction of 80% in eco-points (assuming that the energy consumption rate of production with 0% fly ash is at 100%). Such re-utilization is encouraged since it is able to reduce possible soil toxicity due to sulfur leaching by 5% to 27% and landfill area by 15% to 91% on average.

| S-EPMC5503092 | biostudies-other

Thermal Behaviour of Metakaolin/Fly Ash Geopolymers with Chamotte Aggregate.

Project description:Geopolymers are generally appreciated for their good resistance against high temperatures. This paper compares the influence of thermal treatment with temperatures ranging from 200 to 1200 °C on the mechanical properties and microstructure of geopolymers based on two different aluminosilicate precursors, metakaolin and fly ash. Moreover, the paper is also aimed at characterizing the effect of chamotte aggregate on the performance of geopolymers subjected to high temperatures. Thermal treatment leads to a deterioration in the strength of metakaolin geopolymer, whereas fly ash geopolymer gains strength upon heating. The formation of albite above 900 °C is responsible for the fusion of geopolymer matrix during exposure to 1200 °C, which leads to the deformation of the geopolymer samples. Chamotte aggregate improves the performance of geopolymer material by increasing the thermal stability of geopolymers via sintering of the aggregate particles with the geopolymer matrix in the contact zone.

| S-EPMC5456915 | biostudies-other

Heat-Induced Acceleration of Pozzolanic Reaction Under Restrained Conditions and Consequent Structural Modification.

Project description:This study investigated the heat-induced acceleration of cement hydration and pozzolanic reaction focusing on mechanical performance and structural modification at the meso- and micro-scale. The pozzolanic reaction was implemented by substituting 20 wt.% of cement with silica fume, considered the typical dosage of silica fume in ultra-high performance concrete. By actively consuming a limited amount of water and outer-formed portlandite on the unreacted cement grains, it was confirmed that high-temperature curing greatly enhances the pozzolanic reaction when compared with cement hydration under the same environment. The rate of strength development from the dual reactions of cement hydration and pozzolanic reaction was increased. After the high-temperature curing, further strength development was negligible because of the limited space availability and preconsumption of water under a low water-to-cement environment. Since the pozzolanic reaction does not directly require the anhydrous cement, the reaction can be more easily accelerated under restrained conditions because it does not heavily rely on the diffusion of the limited amount of water. Therefore, it significantly increases the mean chain length of the C-S-H, the size of C-S-H globules with a higher surface fractal dimension. This finding will be helpful in understanding the complicated hydration mechanism of high-strength concrete or ultra-high performance concrete, which has a very low water-to-cement ratio.

| S-EPMC7372358 | biostudies-literature

Data on the pozzolanic activity in coconut shell ash (CSA) for use in sustainable construction.

Project description:The data presented herein are results of the research summary of the investigation for pozzolanic activity in coconut shell ash (CSA) towards a sustainable construction. The data article provides information on the properties of Coconut Shell Ash that are indicative of pozzolanic activity as stated in ASTM C618-15 (2015) [1], BS EN 197-1 (2011) [2] and Joshua et al. (2018) [3]. The data are the physical property of the sand used in determining the binder strengths and the chemical and physical properties (oxide composition and Strength Activity Indices respectively) of the pulverized, calcined and sieved Coconut Shell Ash.

| S-EPMC5996609 | biostudies-literature

Fly Ash from Lignite Combustion as a Filler for Rubber Mixes. Part I: Physical Valorization of Fly Ash.

Project description:The potential use of fly ash (FA) originating from lignite combustion at the Belchatow Power Plant (Poland) as filler for rubber mixes was evaluated. Samples of fly ash collected from heaps created in different years were compared according to their chemical and phase composition, particle size distribution, and morphology. The sieve fractionation of fly ash results in size fractions of different chemical structures, phase compositions, and morphologies, reflected in changes to their specific surface area, surface energy, and activity in rubber mixes. Fractionation turned out to be more effective than grinding from the point of view of using ash as a filler for rubber mixes, because it results in higher specific surface area (SSA) and chemical composition differentiation. Carbon black can be replaced by up to 40% by weight with the fly ash fraction (FFA) of dimensions below 125 µm, without any significant deterioration in the mechanical properties of styrene butadiene rubber (SBR) vulcanizates filled with 50 phr of active carbon black (N 220). Despite the larger fly ash fraction of grain dimensions in the range between 125 and 250 µm presenting the highest specific surface area, the particle size adversely affects its strengthening effect in rubber. Taking into account all the tests performed, ranging from morphology, Payne effect and bound rubber, to mechanical and abrasion tests, the highest potential effectivity is presented by a sample containing 30 phr of N 220 and 20 phr of FFA of grain sizes from 63 to 125 µm. The obtained results indicate that fractionation seems to be an effective physical method of fly ash valorization.

| S-EPMC9324915 | biostudies-literature

Coal fly ash soil

Project description:Coal fly ash soil Raw sequence reads

| PRJNA572189 | ENA

Effect of copolymer latexes on physicomechanical properties of mortar containing high volume fly ash as a replacement material of cement.

Project description:This paper investigates the physicomechanical properties of mortar containing high volume of fly ash (FA) as partial replacement of cement in presence of copolymer latexes. Portland cement (PC) was partially replaced with 0, 10, 20, 30 50, and 60% FA. Copolymer latexes were used based on 2-hydroxyethyl acrylate (2-HEA) and 2-hydroxymethylacrylate (2-HEMA). Testing included workability, setting time, absorption, chemically combined water content, compressive strength, and scanning electron microscopy (SEM). The addition of FA to mortar as replacement of PC affected the physicomechanical properties of mortar. As the content of FA in the concrete increased, the setting times (initial and final) were elongated. The results obtained at 28 days of curing indicate that the maximum properties of mortar occur at around 30% FA. Beyond 30% FA the properties of mortar reduce and at 60% FA the properties of mortar are lower than those of the reference mortar without FA. However, the addition of polymer latexes into mortar containing FA improved most of the physicomechanical properties of mortar at all curing times. Compressive strength, combined water, and workability of mortar containing FA premixed with latexes are higher than those of mortar containing FA without latexes.

| S-EPMC4165383 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data