Large-Scale Surfactant-Free Synthesis of p-Type SnTe Nanoparticles for Thermoelectric Applications.
Ontology highlight
ABSTRACT:
SUBMITTER: Han G
PROVIDER: S-EPMC5503326 | biostudies-other | 2017 Feb
REPOSITORIES: biostudies-other
Similar Datasets
Project description:A surfactant-free solution methodology, simply using water as a solvent, has been developed for the straightforward synthesis of single-phase orthorhombic SnSe nanoplates in gram quantities. Individual nanoplates are composed of {100} surfaces with {011} edge facets. Hot-pressed nanostructured compacts (Eg ≈0.85 eV) exhibit excellent electrical conductivity and thermoelectric power factors (S(2) σ) at 550 K. S(2) σ values are 8-fold higher than equivalent materials prepared using citric acid as a structure-directing agent, and electrical properties are comparable to the best-performing, extrinsically doped p-type polycrystalline tin selenides. The method offers an energy-efficient, rapid route to p-type SnSe nanostructures.
| S-EPMC5074331 | biostudies-literature
Project description:The room-temperature controlled crystallization of monodispersed ZnS nanoparticles (average size of 5 nm) doped with luminescent ions (such as Mn2+, Eu3+, Sm3+, Nd3+, and Yb3+) was achieved via a microfluidic approach. The preparation did not require any stabilizing ligands or surfactants, minimizing potential sources of impurities. The synthesized nanomaterials were characterized from a structural (XRD and XAS at lanthanide L3 edges), morphological (TEM), and compositional (XPS, ICP-MS) perspective, giving complementary information on the materials' features. In view of potential applications in the field of optical bioimaging, the optical emission properties of the doped nanoparticles were assessed, and samples showed strong luminescent properties while being less affected by self-quenching mechanisms. Furthermore, in vitro cytotoxicity experiments were conducted, showing no negative effects and evidencing the appeal of the synthesized materials for potential applications in the field of optical bioimaging.
| S-EPMC8011799 | biostudies-literature
Project description:There is scarce information on cationic surfactants' biocidal and corrosion inhbibition effects on Slime-Forming Bacteria (SFB) isolated from oil field formation water. Therefore, this work focused on the the synthesis of a cationic surfactant (CS) to increase its features by capping different metal nanoparticles (zinc, ZnNPs-C-CS; manganese, MnNPs-C-CS and tin, SnNPs-C-CS) and used them as biocides and corrosion inhibitors. The cationic surfactant was synthesized and characterized by Fourier-Transform Infrared (FTIR) and Nuclear Magnetic Resonance (NMR) spectroscopy. Afterwards, different nanoparticles were synthesized, characterized, and exploited to cap by the CS. The CS and the different nanoparticles capped by the CS were tested for their antimicrobial susceptibility against standard bacterial and yeast strains. The synthesized compounds were further evaluated as anti-biofilms agents against positively-developed bacterial biofilms. Moreover, the CS and the ZnNPs-C-CS, MnNPs-C-CS, and SnNPs-C-CS were assessed as potential biocides against SFB, particularly Pseudomonas sp. (isolated from contaminated formation water), and as corrosion inhibitors against cultivated salinity. The results revealed the great effect of the different CS-capped NPs as broad-spectrum antimicrobial and anti-biofilm agents at lower Minimum Inhibitory Concentrations (MICs), Minimum Bactericidal Concentrations (MBCs), Minimum Fungicidal Concentrations (MFCs) and Minimum Biofilm Inhibitory Concentrations (MBICs), and the activities were reported in order of SnNPs-C-CS > MnNPs-C-CS > ZnNPs-C-CS > CS. Furthermore, the ZnNPs-C-CS, MnNPs-C-CS, and SnNPs-C-CS demonstrated biocidal and corrosion inhibition effects against Pseudomonas sp. at a salinity of 3.5% NaCl, with metal corrosion inhibition efficiencies of 88.6, 94.0 and 96.9%, in comparison to a CS efficiency of 85.7%. In conclusion, the present work provides a newly synthesized cationic surfactant and has enhanced its antimicrobial and its metal corrosion inhibition effects by capping different nanoparticles, and it has been successfully applied against slime-forming bacteria at a salinity of 3.5% NaCl.
| S-EPMC7249094 | biostudies-literature
Project description:Copper nanoparticles (Cu-NPs) represent a viable low-cost alternative to replace bulk copper or other more expensive NPs (e.g. gold or silver) in various applications such as electronics for electrical contact materials or high conductivity materials. This study deals with the synthesis of well dispersed Cu-NPs by using an Ar + H2 microplasma using a solid copper precursor. The morphological analysis is carried out by electron microscopy showing particles with a mean diameter of 8 nm. Crystallinity and chemical analyses were also carried out by X-ray diffraction and X-ray photoelectron spectroscopy, respectively. In the second step, the Cu-NPs were successfully deposited onto porous carbon nanotube ribbons; surface coverage and the penetration depth of the Cu-NPs inside the CNT ribbon structure were investigated as these can be beneficial for a number of applications. The oxidation state of the Cu-NPs was also studied in detail under different conditions.
| S-EPMC9419625 | biostudies-literature
Project description:Gold nanoparticles have unique properties that are highly dependent on their shape and size. Synthetic methods that enable precise control over nanoparticle morphology currently require shape-directing agents such as surfactants or polymers that force growth in a particular direction by adsorbing to specific crystal facets. These auxiliary reagents passivate the nanoparticles' surface, and thus decrease their performance in applications like catalysis and surface-enhanced Raman scattering. Here, a surfactant- and polymer-free approach to achieving high-performance gold nanoparticles is reported. A theoretical framework to elucidate the growth mechanism of nanoparticles in surfactant-free media is developed and it is applied to identify strategies for shape-controlled syntheses. Using the results of the analyses, a simple, green-chemistry synthesis of the four most commonly used morphologies: nanostars, nanospheres, nanorods, and nanoplates is designed. The nanoparticles synthesized by this method outperform analogous particles with surfactant and polymer coatings in both catalysis and surface-enhanced Raman scattering.
| S-EPMC5502103 | biostudies-literature
Project description:In this study, we report the synthesis of PbS particles having dimensions in the quantum-dot regime (13.17 to 26.91 nm) using a cyclohexane:isopropanol:dimethyl-sulfoxide surfactant-free microemulsion (CID-SFME) scheme without a capping agent. We found that with an increase in the microemulsion concentration and particle size, there was a simultaneous reduction in band gap due to the quantum confinement effect. Furthermore, a microemulsion concentration of 0.0125 M was the optimum microemulsion concentration for the growth of uniformly distributed, small particle-sized, ordered PbS nanoparticles using CID-SFME at a constant temperature and other effective parameters. From the results obtained in the present study, we believe that during the reaction, it was not the low values of viscosity and dielectric constant that were responsible for keeping PbS stabilized inside the core of the micelle of the CID microemulsion, but rather the van der Waals forces that also controlled the growth of spherical PbS. We fabricated a highly stable FTO/TiO2/PbS/PANI/NiS/C photodetector at an optimized microemulsion solution concentration. The fabricated photodetector showed a rise time of ∼0.39 s and a decay time of ∼0.22 s, with a photoresponsivity of ∼5.466 μA W-1, external quantum efficiency of ∼0.116 × 10-4%, and detectivity of 6.83 × 107 Jones. Therefore, the CID-SFME scheme is an easy, low-cost route to fabricate efficient, precise, stable, and fast-switching photodetector devices.
| S-EPMC10828937 | biostudies-literature
Project description:Direct assembling of N-graphene, i.e. nitrogen doped graphene, in a controllable manner was achieved using microwave plasmas at atmospheric pressure conditions. The synthesis is accomplished via a single step using ethanol and ammonia as carbon and nitrogen precursors. Tailoring of the high-energy density plasma environment results in a selective synthesis of N-graphene (~0.4% doping level) in a narrow range of externally controlled operational conditions, i.e. precursor and background gas fluxes, plasma reactor design and microwave power. Applying infrared (IR) and ultraviolet (UV) irradiation to the flow of free-standing sheets in the post-plasma zone carries out changes in the percentage of sp2, the N doping type and the oxygen functionalities. X-ray photoelectron spectroscopy (XPS) revealed the relative extension of the graphene sheets ?-system and the type of nitrogen chemical functions present in the lattice structure. Scanning Electron microscopy (SEM), Transmission Electron microscopy (TEM) and Raman spectroscopy were applied to determine morphological and structural characteristics of the sheets. Optical emission and FT-IR spectroscopy were applied for characterization of the high-energy density plasma environment and outlet gas stream. Electrochemical measurements were also performed to elucidate the electrochemical behavior of NG for supercapacitor applications.
| S-EPMC6105711 | biostudies-literature
Project description:Thermoelectric materials exhibit a voltage under an applied thermal gradient and are the heart of radioisotope thermoelectric generators (RTGs), which are the main power system for space missions such as Voyager I, Voyager II, and the Mars Curiosity rover. However, materials currently in use enable only modest thermal-to-electrical conversion efficiencies near 6.5% at the system level, warranting the development of material systems with improved thermoelectric performance. Previous work has demonstrated large thermoelectric figures of merit for lanthanum telluride (La3-x Te4), a high-temperature n-type material, achieving a peak zT value of 1.1 at 1275 K at an optimum cation vacancy concentration. Here we present an investigation of the thermoelectric properties of neodymium telluride (Nd3-x Te4), another rare-earth telluride with a similar structure to La3-x Te4. Density functional theory (DFT) calculations predicted a significant increase in the Seebeck coefficient over La3-x Te4 at equivalent vacancy concentrations due to an increased density of states (DOS) near the Fermi level from the 4f electrons of Nd. The high temperature electrical resistivity, Seebeck coefficient, and thermal conductivity were measured for Nd3-x Te4 at various carrier concentrations. These measurements were compared to La3-x Te4 in order to elucidate the impact of the four 4f electrons of Nd on the transport properties of Nd3-x Te4. A zT of 1.2 was achieved at 1273 K for Nd2.78Te4, which is a 10% improvement over that of La2.74Te4.
| S-EPMC6961965 | biostudies-literature
Project description:Although numerous reports on nonprecious metal catalysts for replacing expensive Pt-based catalysts have been published, few of these studies have demonstrated their practical application in fuel cells. In this work, we report graphitic carbon nitride and carbon nanofiber hybrid materials synthesized by a facile and gram-scale method via liquid-based reactions, without the use of toxic materials or a high pressure-high temperature reactor, for use as fuel cell cathodes. The resulting materials exhibited remarkable methanol tolerance, selectivity, and stability even without a metal dopant. Furthermore, these completely metal-free catalysts exhibited outstanding performance as cathode materials in an actual fuel cell device: a membrane electrode assembly with both acidic and alkaline polymer electrolytes. The fabrication method and remarkable performance of the single cell produced in this study represent progressive steps toward the realistic application of metal-free cathode electrocatalysts in fuel cells.
| S-EPMC4345340 | biostudies-literature
Project description:In this work, we measure the thermal and thermoelectric properties of large-area Si0.8Ge0.2 nano-meshed films fabricated by DC sputtering of Si0.8Ge0.2 on highly ordered porous alumina matrices. The Si0.8Ge0.2 film replicated the porous alumina structure resulting in nano-meshed films. Very good control of the nanomesh geometrical features (pore diameter, pitch, neck) was achieved through the alumina template, with pore diameters ranging from 294 ± 5nm down to 31 ± 4 nm. The method we developed is able to provide large areas of nano-meshes in a simple and reproducible way, being easily scalable for industrial applications. Most importantly, the thermal conductivity of the films was reduced as the diameter of the porous became smaller to values that varied from κ = 1.54 ± 0.27 W K(-1)m(-1), down to the ultra-low κ = 0.55 ± 0.10 W K(-1)m(-1) value. The latter is well below the amorphous limit, while the Seebeck coefficient and electrical conductivity of the material were retained. These properties, together with our large area fabrication approach, can provide an important route towards achieving high conversion efficiency, large area, and high scalable thermoelectric materials.
| S-EPMC5030677 | biostudies-literature