A Study of Polycrystalline Silicon Damage Features Based on Nanosecond Pulse Laser Irradiation with Different Wavelength Effects.

ABSTRACT: Based on PVDF (piezoelectric sensing techniques), this paper attempts to study the propagation law of shock waves in brittle materials during the process of three-wavelength laser irradiation of polysilicon, and discusses the formation mechanism of thermal shock failure. The experimental results show that the vapor pressure effect and the plasma pressure effect in the process of pulsed laser irradiation lead to the splashing of high temperature and high density melt. With the decrease of the laser wavelength, the laser breakdown threshold decreases and the shock wave is weakened. Because of the pressure effect of the laser shock, the brittle fracture zone is at the edge of the irradiated area. The surface tension gradient and surface shear wave caused by the surface wave are the result of coherent coupling between optical and thermodynamics. The average propagation velocity of laser shock wave in polysilicon is 8.47 × 103 m/s, and the experiment has reached the conclusion that the laser shock wave pressure peak exponentially distributes attenuation in the polysilicon.

SUBMITTER: Xu J

PROVIDER: S-EPMC5503343 | biostudies-other | 2017 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Multi-wavelength growth of nanosecond laser-induced surface damage on fused silica gratings.

Project description:The nanosecond laser-induced damage growth phenomenon on the exit surface of fused silica grating is investigated at 1064?nm and 355?nm separately and also simultaneously. Experiments are first carried out on damage sites on a plane fused silica sample showing two different morphologies, and a damage type is selected for ensuring the repeatability of the subsequent tests. Comparing the mono-wavelength growth results on a grating and a plane fused silica sample, the periodic surface structure is found to be an aggravating factor for damage growth. This is highly supported by calculations of the enhancement of the optical electric field intensity thanks to Finite-Difference Time-Domain simulations. Finally, the mono-wavelength results enable us to quantify a coupling occurring in the multi-wavelength configuration, which could originate from the heating of the plasma (more likely produced in the ultraviolet) preferentially by the infrared pulse. This study provides interesting results about the involvement of the surface topography in damage growth, and paves the way towards the comprehension of this phenomenon at high-energy nanosecond laser facilities where fused silica gratings are simultaneously irradiated at several wavelengths.

| S-EPMC5772444 | biostudies-literature

Tunable-wavelength nanosecond laser tailoring of plasmon resonance spectra of gold nanoparticle colloids.

Project description:Metal nanoparticles have applications across a range of fields of science and industry. While there are numerous existing methods to facilitate their large-scale production, most face limitations, particularly in achieving reproducible processes and minimizing undesirable impurities. Common issues are varying particle sizes and aggregates with unfavorable spectral properties. Researchers are currently developing methods to separate or modify nanoparticle sizes and shapes post-synthesis and to eliminate impurities. One promising approach involves laser light irradiation and enables the changing of nanoparticle sizes and shapes while controlling crucial spectral parameters. In this work, we present a novel extension of this method by irradiating nanoparticle colloids with variable-wavelength nanosecond laser pulses on both sides of the extinction band. Our results demonstrate the use of gradual laser wavelength tuning to optimize the photothermal reshaping of gold nanorods and achieve precise control over the plasmon resonance band. By irradiating both sides of the plasmon resonance band, we execute a multistep tuning process, controlling the band's width and spectral position. A statistical analysis of SEM images reveals differences in the nanorod morphology when irradiated on the long- or short-wavelength side of the plasmon resonance band. The fine-tuning of plasmonic spectral properties is desirable for various applications, including the development of sensors and filters and the exploitation of the photothermal effect. The findings of this study can be extended to other plasmonic nanostructures.

| S-EPMC10334372 | biostudies-literature

Straightforward Patterning of Functional Polymers by Sequential Nanosecond Pulsed Laser Irradiation.

Project description:Laser-based methods have demonstrated to be effective in the fabrication of surface micro- and nanostructures, which have a wide range of applications, such as cell culture, sensors or controlled wettability. One laser-based technique used for micro- and nanostructuring of surfaces is the formation of laser-induced periodic surface structures (LIPSS). LIPSS are formed upon repetitive irradiation at fluences well below the ablation threshold and in particular, linear structures are formed in the case of irradiation with linearly polarized laser beams. In this work, we report on the simple fabrication of a library of ordered nanostructures in a polymer surface by repeated irradiation using a nanosecond pulsed laser operating in the UV and visible region in order to obtain nanoscale-controlled functionality. By using a combination of pulses at different wavelengths and sequential irradiation with different polarization orientations, it is possible to obtain different geometries of nanostructures, in particular linear gratings, grids and arrays of nanodots. We use this experimental approach to nanostructure the semiconductor polymer poly(3-hexylthiophene) (P3HT) and the ferroelectric copolymer poly[(vinylidenefluoride-co-trifluoroethylene] (P(VDF-TrFE)) since nanogratings in semiconductor polymers, such as P3HT and nanodots, in ferroelectric systems are viewed as systems with potential applications in organic photovoltaics or non-volatile memories.

| S-EPMC8146350 | biostudies-literature

Controllable Plasmonic Nanostructures induced by Dual-wavelength Femtosecond Laser Irradiation.

Project description:We demonstrated an abnormal double-peak (annular shaped) energy deposition through dual-wavelength synthesis of the fundamental frequency (ω) and the second-harmonic frequency (2ω) of a femtosecond (fs) Ti:sapphire laser. The annular shaped distribution of the dual-wavelength fs laser was confirmed through real beam shape detection. This uniquely simple and flexible technique enables the formation of functional plasmonic nanostructures. We applied this double-peak fs-laser-induced dewetting effect to the controlled fabrication and precise deposition of Au nanostructures, by using a simple, lithography-free, and single-step process. In this process, the double-peak energy-shaped fs laser pulse induces surface patterning of a thin film followed by nanoscale hydrodynamic instability, which is highly controllable under specific irradiation conditions. Nanostructure morphology (shape, size, and distribution) modulation can be achieved by adjusting the laser irradiation parameters, and the subsequent ion-beam polishing enables further dimensional reduction and removal of the surrounding film. The unique optical properties of the resulting nanostructure are highly sensitive to the shape and size of the nanostructure. In contrast to a nanoparticle, the resonance-scattering spectrum of an Au nanobump exhibites two resonance peaks. These suggest that the dual-wavelength fs laser-based dewetting of thin films can be an effective means for the scalable manufacturing of patterned-functional nanostructures.

| S-EPMC5725531 | biostudies-literature

Sub-wavelength patterned pulse laser lithography for efficient fabrication of large-area metasurfaces

Project description:Rigorously designed sub-micrometer structure arrays are widely used in metasurfaces for light modulation. One of the glaring restrictions is the unavailability of easily accessible fabrication methods to efficiently produce large-area and freely designed structure arrays with nanoscale resolution. We develop a patterned pulse laser lithography (PPLL) approach to create structure arrays with sub-wavelength feature resolution and periods from less than 1 μm to over 15 μm on large-area thin films with substrates under ambient conditions. Separated ultrafast laser pulses with patterned wavefront by quasi-binary phase masks rapidly create periodic ablated/modified structures by high-speed scanning. The gradient intensity boundary and circular polarization of the wavefront weaken diffraction and polarization-dependent asymmetricity effects during light propagation for high uniformity. Structural units of metasurfaces are obtained on metal and inorganic photoresist films, such as antennas, catenaries, and nanogratings. We demonstrate a large-area metasurface (10 × 10 mm2) revealing excellent infrared absorption (3–7 μm), which comprises 250,000 concentric rings and takes only 5 minutes to produce. Fabrication of metasurfaces with nanoscale structures is inefficient for large areas. Here, the authors introduce patterned pulse laser lithography for creating structured arrays with sub-wavelength feature on large-area thin films under ambient conditions.

| S-EPMC9530239 | biostudies-literature

Transparent polycrystalline cubic silicon nitride.

Project description:Glasses and single crystals have traditionally been used as optical windows. Recently, there has been a high demand for harder and tougher optical windows that are able to endure severe conditions. Transparent polycrystalline ceramics can fulfill this demand because of their superior mechanical properties. It is known that polycrystalline ceramics with a spinel structure in compositions of MgAl2O4 and aluminum oxynitride (γ-AlON) show high optical transparency. Here we report the synthesis of the hardest transparent spinel ceramic, i.e. polycrystalline cubic silicon nitride (c-Si3N4). This material shows an intrinsic optical transparency over a wide range of wavelengths below its band-gap energy (258 nm) and is categorized as one of the third hardest materials next to diamond and cubic boron nitride (cBN). Since the high temperature metastability of c-Si3N4 in air is superior to those of diamond and cBN, the transparent c-Si3N4 ceramic can potentially be used as a window under extremely severe conditions.

| S-EPMC5355983 | biostudies-literature

Enhanced cavity coupling to silicon vacancies in 4H silicon carbide using laser irradiation and thermal annealing.

Project description:The negatively charged silicon monovacancy [Formula: see text] in 4H silicon carbide (SiC) is a spin-active point defect that has the potential to act as a qubit in solid-state quantum information applications. Photonic crystal cavities (PCCs) can augment the optical emission of the [Formula: see text], yet fine-tuning the defect-cavity interaction remains challenging. We report on two postfabrication processes that result in enhancement of the [Formula: see text] optical emission from our PCCs, an indication of improved coupling between the cavity and ensemble of silicon vacancies. Below-bandgap irradiation at 785-nm and 532-nm wavelengths carried out at times ranging from a few minutes to several hours results in stable enhancement of emission, believed to result from changing the relative ratio of [Formula: see text] ("dark state") to [Formula: see text] ("bright state"). The much faster change effected by 532-nm irradiation may result from cooperative charge-state conversion due to proximal defects. Thermal annealing at 100 °C, carried out over 20 min, also results in emission enhancements and may be explained by the relatively low-activation energy diffusion of carbon interstitials [Formula: see text], subsequently recombining with other defects to create additional [Formula: see text]s. These PCC-enabled experiments reveal insights into defect modifications and interactions within a controlled, designated volume and indicate pathways to improved defect-cavity interactions.

| S-EPMC8000350 | biostudies-literature

Nucleation and growth of gold nanoparticles initiated by nanosecond and femtosecond laser irradiation of aqueous [AuCl4].

Project description:Irradiation of aqueous [AuCl4]- with 532 nm nanosecond (ns) laser pulses produces monodisperse (PDI = 0.04) 5 nm Au nanoparticles (AuNPs) without any additives or capping agents via a plasmon-enhanced photothermal autocatalytic mechanism. Compared with 800 nm femtosecond (fs) laser pulses, the AuNP growth kinetics under ns laser irradiation follow the same autocatalytic rate law, but with a significantly lower sensitivity to laser pulse energy. The results are explained using a simple model for simulating heat transfer in liquid water and at the interface with AuNPs. While the extent of water superheating with the ns laser is smaller compared to the fs laser, its significantly longer duration can provide sufficient energy to dissociate a small fraction of the [AuCl4]- present, resulting in the formation of AuNPs by coalescence of the resulting Au atoms. Irradiation of initially formed AuNPs at 532 nm results in plasmon-enhanced superheating of water, which greatly accelerates the rate of thermal dissociation of [AuCl4]- and accounts for the observed autocatalytic kinetics. The plasmon-enhanced heating under ns laser irradiation fragments the AuNPs and results in nearly uniform 5 nm particles, while the lack of particles' heating under fs laser irradiation results in the growth of the particles as large as 40 nm.

| S-EPMC6310131 | biostudies-literature

Generating Silicon Nanofiber Clusters from Grinding Sludge by Millisecond Pulsed Laser Irradiation.

Project description:Silicon nanofiber clusters were successfully generated by the irradiation of millisecond pulsed laser light on silicon sludge disposed from wafer back-grinding processes. It was found that the size, intensity, and growing speed of the laser-induced plume varied with the gas pressure, while the size and morphology of the nanofibers were dependent on the laser pulse duration. The generated nanofibers were mainly amorphous with crystalline nanoparticles on their tips. The crystallinity and oxidation degree of the nanofibers depended on the preheating conditions of the silicon sludge. This study demonstrated the possibility of changing silicon waste into functional nanomaterials, which are possibly useful for fabricating high-performance lithium-ion battery electrodes.

| S-EPMC7221718 | biostudies-literature

Crystallization of Ge2Sb2Te5 thin films by nano- and femtosecond single laser pulse irradiation.

Project description:The amorphous to crystalline phase transformation of Ge2Sb2Te5 (GST) films by UV nanosecond (ns) and femtosecond (fs) single laser pulse irradiation at the same wavelength is compared. Detailed structural information about the phase transformation is collected by x-ray diffraction and high resolution transmission electron microscopy (TEM). The threshold fluences to induce crystallization are determined for both pulse lengths. A large difference between ns and fs pulse irradiation was found regarding the grain size distribution and morphology of the crystallized films. For fs single pulse irradiated GST thin films, columnar grains with a diameter of 20 to 60?nm were obtained as evidenced by cross-sectional TEM analysis. The local atomic arrangement was investigated by high-resolution Cs-corrected scanning TEM. Neither tetrahedral nor off-octahedral positions of Ge-atoms could be observed in the largely defect-free grains. A high optical reflectivity contrast (~25%) between amorphous and completely crystallized GST films was achieved by fs laser irradiation induced at fluences between 13 and 16?mJ/cm(2) and by ns laser irradiation induced at fluences between 67 and 130?mJ/cm(2). Finally, the fluence dependent increase of the reflectivity is discussed in terms of each photon involved into the crystallization process for ns and fs pulses, respectively.

| S-EPMC4904278 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data