Effects of Laser Shock Processing on Morphologies and Mechanical Properties of ANSI 304 Stainless Steel Weldments Subjected to Cavitation Erosion.

ABSTRACT: Effects of laser shock processing (LSP) on the cavitation erosion resistance of laser weldments were investigated by optical microscope (OM), scanning electron microscope (SEM) observations, roughness tester, micro hardness tester, and X-ray diffraction (XRD) technology. The morphological microstructures were characterized. Cumulative mass loss, incubation period, erosion rate, and damaged surface areas were monitored during cavitation erosion. Surface roughness, micro-hardness, and residual stress were measured in different zones. Results showed that LSP could improve the damage of morphological microstructures and mechanical properties after cavitation erosion. The compressive residual stresses were generated during the process of LSP, which was an effective guarantee for the improvement of the above mentioned properties.

SUBMITTER: Zhang L

PROVIDER: S-EPMC5503387 | biostudies-other | 2017 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Compressibility of 304 Stainless Steel Powder Metallurgy Materials Reinforced with 304 Short Stainless Steel Fibers.

Project description:Powder metallurgy (P/M) technique is usually used for manufacturing porous metal materials. However, some P/M materials are limitedly used in engineering for their performance deficiency. A novel 304 stainless steel P/M material was produced by a solid-state sintering of 304 stainless steel powders and 304 short stainless steel fibers, which were alternately laid in layers according to mass ratio. In this paper, the compressive properties of the P/M materials were characterized by a series of uniaxial compression tests. The effects of fiber content, compaction pressure and high temperature nitriding on compressive properties were investigated. The results indicated that, without nitriding, the samples changed from cuboid to cydariform without damage in the process of compression. The compressive stress was enhanced with increasing fiber content ranging from 0 to 8 wt.%. For compaction pressure from 55 to 75 MPa, greater compaction pressure improved compressive stress. Moreover, high temperature nitriding was able to significantly improve the yield stress, but collapse failure eventually occurred.

| S-EPMC5456726 | biostudies-other

Electrolytic plasma processing-an innovative treatment for surface modification of 304 stainless steel.

Project description:There is widespread attention to surface profile and modification of 304 stainless steel for research development and application. Here, a successful electrolytic plasma processing (EPP) technique has been developed for both surface pretreatment and coating deposition of 304 stainless steel. Representative images confirm that the number of the pits increases and the ravines gradually disappear on the steel pretreated by EPP with the increase of processing time and applied voltage. Moreover, there is an obvious enhancement in surface roughness of 304 stainless steel after EPP pretreatment. In the case of coating deposition, the further EPP modification conducted on the pretreated sample offers a simple and effective technique for the production of zinc coatings having the features of full coverage and homogeneous distribution. The results show that a zinc coating with a thickness of approximately 0.5 μm can be obtained on the 304 stainless steel by means of EPP for only 60 s.

| S-EPMC5428051 | biostudies-literature

Nanosecond laser coloration on stainless steel surface.

Project description:In this work, we present laser coloration on 304 stainless steel using nanosecond laser. Surface modifications are tuned by adjusting laser parameters of scanning speed, repetition rate, and pulse width. A comprehensive study of the physical mechanism leading to the appearance is presented. Microscopic patterns are measured and employed as input to simulate light-matter interferences, while chemical states and crystal structures of composites to figure out intrinsic colors. Quantitative analysis clarifies the final colors and RGB values are the combinations of structural colors and intrinsic colors from the oxidized pigments, with the latter dominating. Therefore, the engineering and scientific insights of nanosecond laser coloration highlight large-scale utilization of the present route for colorful and resistant steels.

| S-EPMC5541041 | biostudies-literature

Multiscale correlative tomography: an investigation of creep cavitation in 316 stainless steel.

Project description:Creep cavitation in an ex-service nuclear steam header Type 316 stainless steel sample is investigated through a multiscale tomography workflow spanning eight orders of magnitude, combining X-ray computed tomography (CT), plasma focused ion beam (FIB) scanning electron microscope (SEM) imaging and scanning transmission electron microscope (STEM) tomography. Guided by microscale X-ray CT, nanoscale X-ray CT is used to investigate the size and morphology of cavities at a triple point of grain boundaries. In order to understand the factors affecting the extent of cavitation, the orientation and crystallographic misorientation of each boundary is characterised using electron backscatter diffraction (EBSD). Additionally, in order to better understand boundary phase growth, the chemistry of a single boundary and its associated secondary phase precipitates is probed through STEM energy dispersive X-ray (EDX) tomography. The difference in cavitation of the three grain boundaries investigated suggests that the orientation of grain boundaries with respect to the direction of principal stress is important in the promotion of cavity formation.

| S-EPMC5544716 | biostudies-literature

Coupling mechanism between wear and oxidation processes of 304 stainless steel in hydrogen peroxide environments.

Project description:Stainless steel is widely used in strongly oxidizing hydrogen peroxide (H2O2) environments. It is crucial to study its wear behaviour and failure mode. The tribological properties and oxidation of 304 stainless steel were investigated using a MMW-1 tribo-tester with a three-electrode setup in H2O2 solutions with different concentrations. Corrosion current densities (CCDs), coefficients of frictions (COFs), wear mass losses, wear surface topographies, and metal oxide films were analysed and compared. The results show that the wear process and oxidation process interacted significantly with each other. Increasing the concentration of H2O2 or the oxidation time was useful to form a layer of integrated, homogeneous, compact and thick metal oxide film. The dense metal oxide films with higher mechanical strengths improved the wear process and also reduced the oxidation reaction. The wear process removed the metal oxide films to increase the oxidation reaction. Theoretical data is provided for the rational design and application of friction pairs in oxidation corrosion conditions.

| S-EPMC5443796 | biostudies-literature

Parameters Influencing Cavitation Within Vials Subjected to Drop Shock.

Project description:The pharmaceutical industry has made improvements to mitigate protein degradation during the drug manufacturing process, storage, and transportation. However, there is less quality control after the manufacturer releases the drug. Previous research has shown that drop shock due to mishandling and accidental dropping of therapeutic vials may cause cavitation, aggregation, and particle formation. In this study, the cavitation behavior of Deionized (DI) water and 10mM L-Histidine buffer solution which were subjected to drop shock by hand dropping were investigated to study the effects of vial materials, solutions, fill volumes, drop heights, and internal vial geometries. A Phantom v7 high-speed camera was used to record images at a rate of 66,700 frames per second of the vials as they underwent drop shock. These videos were then reviewed to find the angle of impact, and to determine if there was cavitation. The results indicate that decreasing fill height by using a smaller fill volume or larger diameter vials were found to mitigate cavitation across drop heights. Secondly, results indicate there is a significant difference between the cavitation behavior of glass and plastic vials, and plastic had more cavitation cases. Lastly, there was not a significant difference in the occurrence of cavitation between DI water and L-Histidine buffer solution.

| S-EPMC6915723 | biostudies-literature

Corrosion Behavior of AISI 304 Stainless Steel Reinforcements in SCBA-SF Ternary Ecological Concrete Exposed to MgSO4.

Project description:In this study, ternary ecological concrete (TEC) mixtures were produced with partial substitution of the ordinary Portland cement (OPC) by 10%, 20%, and 30% of sugar cane bagasse ash (SCBA) and silica fume (SF); a control mixture (100% OPC) was prepared according to ACI 211.1 standard. The studied TEC specimens were reinforced with AISI 304 stainless steel and AISI 1018 carbon steel rebars. TEC reinforced specimens were immersed in two different electrolytes, a control (DI-water) and 3.5 wt.% MgSO4 solution, for 180 days. The electrochemical corrosion was monitored by corrosion potential (Ecorr) according to ASTM C-876-15 standard, and the linear polarization resistance (LPR) technique using ASTM G59 standard. The Ecorr and current density icorr results show that AISI 304 stainless steel rebars have a high corrosion resistance, with icorr values below 0.1 µA/cm2, which is interpreted as a level of negligible corrosion. The best corrosion performance was found for the TEC mixture made with a 20% addition of blend of sugar cane bagasse ash-silica fume (SCBA-SF) to the OPC.

| S-EPMC7288276 | biostudies-literature

Corrosion Inhibition of Mild Steel and 304 Stainless Steel in 1 M Hydrochloric Acid Solution by Tea Tree Extract and Its Main Constituents.

Project description:Tea tree extract, containing antioxidant constituents α-terpineol, terpinen-4-ol, and α-terpinene, has a wide range of applications in the cosmetic, food, and pharmaceutical industries. In this study, tea tree extract showed an anticorrosive effect under 1 M HCl solution on mild steel (MS) and 304 stainless steel (STS). Uniform corrosion for MS and pitting corrosion for STS at 298 K were retarded, with inhibition efficiencies of 77% and 86%, respectively. The inhibition of uniform and pitting corrosion was confirmed by scanning electron microscopy and laser scanning confocal microscopy in terms of surface roughness and pitting morphologies. The most effective constituent contributing to the inhibitory performance of tea tree extract was revealed to be α-terpineol, with an inhibition efficiency of 83%. The adsorption of tea tree extract was confirmed by surface characterization analysis using Fourier transform infrared spectroscopy, Raman spectroscopy, and Electrochemical impedance spectroscopy. Interestingly, G- and D-peaks of Raman spectra were detected from the inhibited steels, and this finding is the first example in the corrosion inhibition field. The anticorrosion mechanism can be explained by the formation of organic-Fe complexes on the corroded steel surface via electron donor and acceptor interactions in the presence of an oxygen atom of the hydroxyl group or ether of organic inhibitors.

| S-EPMC8433979 | biostudies-literature

Novel porphyrin derivatives as corrosion inhibitors for stainless steel 304 in acidic environment: synthesis, electrochemical and quantum calculation studies.

Project description:A Novel 5,10,15,20-tetra (thiophen-2-yl) porphyrin (P1) and 5,10,15,20-tetrakis (5-Bromothiophen-2-yl) porphyrin (P2) were successfully synthesized, and their chemical structures were proved based on its correct elemental analysis and spectral data (IR and 1H-NMR). These compounds were examined as corrosion inhibitors for stainless steel 304 (SS304) in 2 M HCl utilizing mass reduction (MR) and electrochemical tests at inhibitor concentration (1 × 10-6-21 × 10-6 M). The protection efficiency (IE %) was effectively enhanced with improving the concentration of investigated compounds and reached 92.5%, 88.5% at 21 × 10-6 M for P1 & P2, respectively and decreases with raising the temperature. Langmuir's isotherm was constrained as the best fitted isotherm depicts the physical-chemical adsorption capabilities of P1 & P2 on SS304 surface with change in ΔGoads = 22.5 kJ mol-1. According to the PDP data reported, P1 and P2 work as mixed find inhibitors to suppress both cathodic and anodic processes. Porphyrin derivatives (P1 & P2) are included on the surface of SS304, according to surface morphology techniques SEM/EDX and AFM. Quantum calculations (DFT) and Monte Carlo simulation (MC) showed the impact of the chemical structure of porphyrin derivatives on their IE %.

| S-EPMC10579412 | biostudies-literature

Mouse Lung Response to Stainless Steel and Mild Steel Welding Fume

Project description:A/J mice are genetically predisposed to spontaneous and/or chemically-induced lung tumors while C57BL/6J (B6) mice are resistant. This genetic disparity provides a unique scenario to identify molecular mechanisms associated with the lung response to welding fume at the transcriptome level.

2010-04-30 | GSE20174 | GEO

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data