Small Strain Stiffness of Unsaturated Sands Containing a Polyacrylamide Solution.

ABSTRACT: Sand improvements using organic agents have shown promising results. Polyacrylamide is one possible organic agent, which has been shown to influence the shear strength, stiffness, soil remediation, and erosion resistance of geomaterials. In this study, we explored the shear wave velocity (S-wave) and water retention curves of unsaturated sands containing polyacrylamide solutions. The shear wave velocity was measured during the water retention curve measurement tests according to the variation of the degree of saturation. The experimental setup was verified through comparison of the measured water retention curves with the published data. The results show that (1) the S-wave velocity of saturated sands increases with polyacrylamide concentration; (2) as the degree of saturation decreases, the S-wave velocity increases; (3) near the residual water (or polyacrylamide solution) saturation, the S-wave velocity increases dramatically; (4) as the degree of saturation decreases, the S-wave velocity at unsaturated conditions increases with any given water (or polyacrylamide solution) saturation, like the water retention curves; (5) the S-wave velocity increases with the increase in capillary pressure; and (6) the predicted S-wave velocity at a given degree of saturation is slightly overestimated, and the modification of the equation is required.

SUBMITTER: Jung J

PROVIDER: S-EPMC5507007 | biostudies-other | 2017 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:The present research reports on in-water, site-specific photodeposition of glyphosate (GLP)-containing polyacrylamide (PAA-GLP) nanometer-thick films (nanofilms) on an inner surface of fused silica (fused quartz) microcapillaries presilanized with trimethoxy(octen-7-yl)silane (TMOS). TMOS was chosen because of the vinyl group presence in its structure, enabling its participation in the (UV light)-activated free-radical polymerization (UV-FRP) after its immobilization on a fused silica surface. The photodeposition was conducted in an aqueous (H2O/ACN; 3:1, v/v) solution, using UV-FRP (λ = 365 nm) of the acrylamide (AA) functional monomer, the N,N'-methylenebis(acrylamide) (BAA) cross-linking monomer, GLP, and the azobisisobutyronitrile (AIBN) UV-FRP initiator. Acetonitrile (ACN) was used as the porogen and the solvent to dissolve monomers and GLP. Because of the micrometric diameters of microcapillaries, the silanization and photodeposition procedures were first optimized on fused silica slides. The introduction of TMOS, as well as the formation of PAA and PAA-GLP nanofilms, was determined using atomic force microscopy (AFM), scanning electron microscopy with energy-dispersive X-ray (SEM-EDX) spectroscopy, and confocal micro-Raman spectroscopy. Particularly, AFM and SEM-EDX measurements determined nanofilms' thickness and GLP content, respectively, whereas in-depth confocal (micro-Raman spectroscopy)-assisted imaging of PAA- and PAA-GLP-coated microcapillary inner surfaces confirmed the successful photodeposition. Moreover, we examined the GLP impact on polymer gelation by monitoring hydration in a hydrogel and a dried powder PAA-GLP. Our study demonstrated the usefulness of the in-capillary micro-Raman spectroscopy imaging and in-depth profiling of GLP-encapsulated PAA nanofilms. In the future, our simple and inexpensive procedure will enable the fabrication of polymer-based microfluidic chemosensors or adsorptive-separating devices for GLP detection, determination, and degradation.

Dataset Information

Small Strain Stiffness of Unsaturated Sands Containing a Polyacrylamide Solution.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets