Fabricating Superior NiAl Bronze Components through Wire Arc Additive Manufacturing.

ABSTRACT: Cast nickel aluminum bronze (NAB) alloy is widely used for large engineering components in marine applications due to its excellent mechanical properties and corrosion resistance. Casting porosity, as well as coarse microstructure, however, are accompanied by a decrease in mechanical properties of cast NAB components. Although heat treatment, friction stir processing, and fusion welding were implemented to eliminate porosity, improve mechanical properties, and refine the microstructure of as-cast metal, their applications are limited to either surface modification or component repair. Instead of traditional casting techniques, this study focuses on developing NAB components using recently expanded wire arc additive manufacturing (WAAM). Consumable welding wire is melted and deposited layer-by-layer on substrates producing near-net shaped NAB components. Additively-manufactured NAB components without post-processing are fully dense, and exhibit fine microstructure, as well as comparable mechanical properties, to as-cast NAB alloy. The effects of heat input from the welding process and post-weld-heat-treatment (PWHT) are shown to give uniform NAB alloys with superior mechanical properties revealing potential marine applications of the WAAM technique in NAB production.

SUBMITTER: Ding D

PROVIDER: S-EPMC5509263 | biostudies-other | 2016 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Vat photopolymerization additive manufacturing (Vat AM) technologies have found niche industrial use being able to produce personalized parts in moderate quantity. However, Vat AM lacks in its ability to produce parts of satisfactory thermal and mechanical properties for structural applications. The purpose of this investigation was to develop high-performance resins with glass transition temperatures (Tg) above 200 °C for Vat AM, evaluate the properties of the produced thermosets and establish a structure-property relationship of the thermosets produced. Herein, we have developed SLA-type resins that feature bio-derived monomer hesperetin trimethacrylate (HTM) synthesized from the flavonone hesperetin. Diluents 4-acryloyl morpholine, styrene, 4-methyl styrene and 4-tert butylstyrene (tbutylsty) were photocured with HTM as the monomer and all produced thermosets with Tg values above 200 °C. Investigations of suitable crosslinkers urethane dimethacrylate, the vinyl ester CN 151 and Ebecryl 4859 (Eb4859) showed that each crosslinker displayed different benefits when formulated with HTM as the monomer and tbutylSty as the diluent (HTM:crosslinker:tbutylSty with mass ratio 2:1:2). The crosslinker CN 151 produced the thermoset of greatest onset of thermal decomposition temperature (T0) of 352 °C. Eb4859 produced the thermoset of highest tensile strength, 19 ± 7 MPa, amongst the set of varied crosslinkers. The formulation featuring UDM (HTM:UDM:tbutysty) offered ease of processing and was seemingly the easiest to print. Investigations of reactive diluent showed that styrene produced the thermoset of the highest extent of cure and the overall highest tensile strength, 25 ± 5 MPa, while tbutylSty produced the thermoset with the greatest Tan-δ Tg, 231 °C. HTM was synthesized, formulated with diluents, crosslinkers and initiators. The HTM resins were then 3D printed to produce thermosets of Tg values greater than 200 °C. The polymer properties were evaluated and a structure-reactivity relationship was discussed.

Dataset Information

Fabricating Superior NiAl Bronze Components through Wire Arc Additive Manufacturing.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets