Electrical Properties of CZO Films Prepared by Ultrasonic Spray Pyrolysis.

ABSTRACT: CuZnO (CZO) films have attracted increasing amounts of attention due to their promising potential applications in semiconductor devices. ZnO shows n-type conductivity, and attempts have been made to dope several elements in ZnO to improve the electrical properties. This study investigated the electrical property transitions of CZO films and determined the copper concentration at which the conductivity of CZO films will change from n-type to p-type. In this study, CZO films were fabricated by ultrasonic spray pyrolysis with copper acetate, zinc acetate, and ammonium acetate precursor solution. The concentrations of Cu ions in the CZO films were controlled by the concentration ratios of copper acetate to zinc acetate in the precursor solutions. In addition, these samples were analyzed by Hall effect measurements, X-ray diffraction, transmittance measurements, and photoluminescence measurements. The results show that the conductivity of the CZO film changes from n-type to p-type when the copper ion concentration in the film is 5%.

SUBMITTER: Chen LC

PROVIDER: S-EPMC5512636 | biostudies-other | 2014 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

TiO2 thin films by ultrasonic spray pyrolysis as photocatalytic material for air purification.

Project description:In this study, we showed that the TiO2 thin films deposited onto window glass are practicable for air purification and self-cleaning applications. TiO2 films were deposited onto window glass by ultrasonic spray pyrolysis method. Different deposition temperatures were used in the range of 250-450°C. The structural, morphological, optical properties and surface chemical composition were investigated to understand probable factors affecting photocatalytic performance and wettability of the TiO2 thin films. The TiO2 thin films were smooth, compacted and adhered adequately on the substrate with a thickness in the range of 100-240 nm. X-ray diffraction patterns revealed that all the TiO2 thin films consisted of anatase phase structure with the mean crystallite size in the range of 13-35 nm. The optical measurements showed that the deposited films were highly transparent (approx. 85%). The wettability test results showed that the TiO2 thin films sprayed at 350°C and 450°C and annealed at 500°C for 1 h were superhydrophilic. The photocatalytic activity of the films was tested for the degradation of methyl tert-butyl ether (MTBE) in multi-section plug-flow reactor. The TiO2 film deposited at 350°C exhibited the highest amount of conversion of MTBE, approximately 80%.

| S-EPMC6408371 | biostudies-literature

Electrochemical properties of tungsten sulfide-carbon composite microspheres prepared by spray pyrolysis.

Project description:Tungsten sulfide (WS2)-carbon composite powders with superior electrochemical properties are prepared by a two-step process. WO3-carbon composite powders were first prepared by conventional spray pyrolysis, and they were then sulfidated to form WS2-carbon powders. Bare WS2 powders are also prepared by sulfidation of bare WO3 powders obtained by spray pyrolysis. Stacked graphitic layers could not be found in the bare WS2 and WS2-carbon composite powders. The amorphous bare WS2 and WS2-carbon composite powders have Brunauer-Emmett-Teller (BET) surface areas of 2.8 and 4 m(2) g(-1), respectively. The initial discharge and charge capacities of the WS2-carbon composite powders at a current density of 100 mA g(-1) are 1055 and 714 mA h g(-1), respectively, and the corresponding initial Coulombic efficiency is 68%. On the other hand, the initial discharge and charge capacities of the bare WS2 powders are 514 and 346 mA h g(-1), respectively. The discharge capacities of the WS2-carbon composite powders for the 2(nd) and 50(th) cycles are 716 and 555 mA h g(-1), respectively, and the corresponding capacity retention measured after first cycle is 78%.

| S-EPMC4148672 | biostudies-literature

Synthesis of Li₂Ti₃O₇ Anode Materials by Ultrasonic Spray Pyrolysis and Their Electrochemical Properties.

Project description:Ramsdellite-type lithium titanate (Li₂Ti₃O₇) powders were synthesized by performing ultrasonic spray pyrolysis, and their chemical and physical properties were characterized by performing Scanning Electron Microscope (SEM), powder X-ray Diffraction (XRD), and Inductively Coupled Plasma (ICP) analyses. The as-prepared Li₂Ti₃O₇ precursor powders had spherical morphologies with hollow microstructures, but an irregularly shaped morphology was obtained after calcination above 900 °C. The ramsdellite Li₂Ti₃O₇ crystal phase was obtained after the calcination at 1100 °C under an argon/hydrogen atmosphere. The first rechargeable capacity of the Li₂Ti₃O₇ anode material was 168 mAh/g at 0.1 C and 82 mAh/g at 20 C, and the discharge capacity retention ratio was 99% at 1 C after the 500th cycle. The cycle performance of the Li₂Ti₃O₇ anode was also highly stable at 50 °C, demonstrating the superiority of Li₂Ti₃O₇ anode materials reported previously.

| S-EPMC5458944 | biostudies-other

Formation of Indium-Doped Zinc Oxide Thin Films Using Ultrasonic Spray Pyrolysis: The Importance of the Water Content in the Aerosol Solution and the Substrate Temperature for Enhancing Electrical Transport.

Project description:Indium doped zinc oxide [ZnO:In] thin films have been deposited at 430°C on soda-lime glass substrates by the chemical spray technique, starting from zinc acetate and indium acetate. Pulverization of the solution was done by ultrasonic excitation. The variations in the electrical, structural, optical, and morphological characteristics of ZnO:In thin films, as a function of both the water content in the starting solution and the substrate temperature, were studied. The electrical resistivity of ZnO:In thin films is not significantly affected with the increase in the water content, up to 200 mL/L; further increase in water content causes an increase in the resistivity of the films. All films show a polycrystalline character, fitting well with the hexagonal ZnO wurtzite-type structure. No preferential growth in samples deposited with the lowest water content was observed, whereas an increase in water content gave rise to a (002) growth. The surface morphology of the films shows a consistency with structure results, as non-geometrical shaped round grains were observed in the case of films deposited with the lowest water content, whereas hexagonal slices, with a wide size distribution were observed in the other cases. In addition, films deposited with the highest water content show a narrow size distribution.

| S-EPMC5448918 | biostudies-other

Semitransparent Sb2S3 thin film solar cells by ultrasonic spray pyrolysis for use in solar windows.

Project description:The integration of photovoltaic (PV) solar energy in zero-energy buildings requires durable and efficient solar windows composed of lightweight and semitransparent thin film solar cells. Inorganic materials with a high optical absorption coefficient, such as Sb2S3 (>105 cm-1 at 450 nm), offer semitransparency, appreciable efficiency, and long-term durability at low cost. Oxide-free throughout the Sb2S3 layer thickness, as confirmed by combined studies of energy dispersive X-ray spectroscopy and synchrotron soft X-ray emission spectroscopy, semitransparent Sb2S3 thin films can be rapidly grown in air by the area-scalable ultrasonic spray pyrolysis method. Integrated into a ITO/TiO2/Sb2S3/P3HT/Au solar cell, a power conversion efficiency (PCE) of 5.5% at air mass 1.5 global (AM1.5G) is achieved, which is a record among spray-deposited Sb2S3 solar cells. An average visible transparency (AVT) of 26% of the back-contact-less ITO/TiO2/Sb2S3 solar cell stack in the wavelength range of 380-740 nm is attained by tuning the Sb2S3 absorber thickness to 100 nm. In scale-up from mm2 to cm2 areas, the Sb2S3 hybrid solar cells show a decrease in efficiency of only 3.2% for an 88 mm2 Sb2S3 solar cell, which retains 70% relative efficiency after one year of non-encapsulated storage. A cell with a PCE of 3.9% at 1 sun shows a PCE of 7.4% at 0.1 sun, attesting to the applicability of these solar cells for light harvesting under cloud cover.

| S-EPMC6902894 | biostudies-literature

Controlling the Wettability of ZnO Thin Films by Spray Pyrolysis for Photocatalytic Applications.

Project description:Herein, we synthesized the zinc oxide (ZnO) thin films (TFs) deposited on glass substrates via spray pyrolysis (SP) to prepare self-cleaning glass. Various process parameters were used to optimize photocatalytic performance. Substrates were coated at room temperature (RT) and 250 °C with a 1 mL or 2 mL ZnO solution while maintaining a distance from the spray gun to the substrate of 20 cm or 30 cm. Several characterization techniques, i.e., XRD, SEM, AFM, and UV-Vis were used to determine the structural, morphological, and optical characteristics of the prepared samples. The wettability of the samples was evaluated using contact angle measurements. As ZnO is hydrophilic in nature, the RT deposited samples showed a hydrophilic character, whereas the ZnO TFs deposited at 250 °C demonstrated a hydrophobic character. The XRD results showed a higher degree of crystallinity for samples deposited on heated substrates. Because of this higher crystallinity, the surface energy decreased, and the contact angle increased. Moreover, by using 2 mL solution, better surface coverage and roughness were obtained for the ZnO TFs. However, by exploiting the distance of the spray to the samples size distribution and surface coverage can be controlled, the samples deposited at 30 mL showed a uniform particle size distribution from 30-40 nm. In addition, the photoactivity of the samples was tested by the degradation of rhodamine B dye. Substrates prepared with a 2 mL solution sprayed at 20 cm showed higher dye degradation than other samples, which can play a vital role in self-cleaning. Hence, by changing the said parameters, the ZnO thin film properties on glass substrates were optimized for self-cleaning diversity.

| S-EPMC9105918 | biostudies-literature

A simple method to set the spray properties for flame spray pyrolysis production of nanoparticles.

Project description:The most critical part of the flame spray pyrolysis (FSP) process is the nozzle, since it plays a key role in setting the spray properties. In this study, we developed an approach to adjust the nozzle throat gap size for a desired dispersion gas flow rate and upstream pressure, based on the external size and shape of a two phase external mixing nozzle. An equation was derived and validated by comparing the predicted gas flow rates with the data provided in a commercial nozzle supplier chart. Experiments were also conducted in our lab-scale FSP reactor to test the validity of the predictions. The approach developed here was found to closely predict the gap size necessary to pass the required dispersion gas flow at a desired pressure drop. Error in predictions was found to be less than 3% at an upstream pressure range of 3-10 bars. The isentropic flow assumption for perfect gases across the convergent-divergent nozzle was found to fail below 2 bars, consistent with the theory applied. By using the method here, the nozzle setting for a desired operation in an FSP process can be easily done, minimizing the time-consuming trial and error steps needed otherwise.

| S-EPMC7509832 | biostudies-literature

Influence of Antimony Species on Electrical Properties of Sb-Doped Zinc Oxide Thin Films Prepared by Pulsed Laser Deposition.

Project description:This study systematically investigates the influence of antimony (Sb) species on the electrical properties of Sb-doped zinc oxide (SZO) thin films prepared by pulsed laser deposition in an oxygen-rich environment. The Sb species-related defects were controlled through a qualitative change in energy per atom by increasing the Sb content in the Sb2O3:ZnO-ablating target. By increasing the content of Sb2O3 (wt.%) in the target, Sb3+ became the dominant Sb ablation species in the plasma plume. Consequently, n-type conductivity was converted to p-type conductivity in the SZO thin films prepared using the ablating target containing 2 wt.% Sb2O3. The substituted Sb species in the Zn site (SbZn3+ and SbZn+) were responsible for forming n-type conductivity at low-level Sb doping. On the other hand, the Sb-Zn complex defects (SbZn-2VZn) contributed to the formation of p-type conductivity at high-level doping. The increase in Sb2O3 content in the ablating target, leading to a qualitative change in energy per Sb ion, offers a new pathway to achieve high-performing optoelectronics using ZnO-based p-n junctions.

| S-EPMC10255333 | biostudies-literature

Theophylline cocrystals prepared by spray drying: physicochemical properties and aerosolization performance.

Project description:The purpose of this work was to characterize theophylline (THF) cocrystals prepared by spray drying in terms of the physicochemical properties and inhalation performance when aerosolized from a dry powder inhaler. Cocrystals of theophylline with urea (THF-URE), saccharin (THF-SAC) and nicotinamide (THF-NIC) were prepared by spray drying. Milled THF and THF-SAC cocrystals were also used for comparison. The physical purity, particle size, particle morphology and surface energy of the materials were determined. The in vitro aerosol performance of the spray-dried cocrystals, drug-alone and a drug-carrier aerosol, was assessed. The spray-dried particles had different size distributions, morphologies and surface energies. The milled samples had higher surface energy than those prepared by spray drying. Good agreement was observed between multi-stage liquid impinger and next-generation impactor in terms of assessing spray-dried THF particles. The fine particle fractions of both formulations were similar for THF, but drug-alone formulations outperformed drug-carrier formulations for the THF cocrystals. The aerosolization performance of different THF cocrystals was within the following rank order as obtained from both drug-alone and drug-carrier formulations: THF-NIC>THF-URE>THF-SAC. It was proposed that micromeritic properties dominate over particle surface energy in terms of determining the aerosol performance of THF cocrystals. Spray drying could be a potential technique for preparing cocrystals with modified physical properties.

| S-EPMC3581642 | biostudies-literature

Measurements of Microstructural, Chemical, Optical, and Electrical Properties of Silicon-Oxygen-Nitrogen Films Prepared by Plasma-Enhanced Atomic Layer Deposition.

Project description:In this study, silicon nitride (SiNx) thin films with different oxygen concentration (i.e., SiON film) were precisely deposited by plasma enhanced atomic layer deposition on Si (100) substrates. Thus, the effect of oxygen concentration on film properties is able to be comparatively studied and various valuable results are obtained. In detail, x-ray reflectivity, x-ray photoelectron spectroscopy, atomic force microscopy, and spectroscopic ellipsometry are used to systematically characterize the microstructural, optical, and electrical properties of SiON film. The experimental results indicate that the surface roughness increases from 0.13 to 0.2 nm as the oxygen concentration decreases. The refractive index of the SiON film reveals an increase from 1.55 to 1.86 with decreasing oxygen concentration. Accordingly, the band-gap energy of these films determined by oxygen 1s-peak analysis decreases from 6.2 to 4.8 eV. Moreover, the I-V tests demonstrate that the film exhibits lower leakage current and better insulation for higher oxygen concentration in film. These results indicate that oxygen affects microstructural, optical, and electrical properties of the prepared SiNx film.

| S-EPMC6316811 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data