Assessment of Pozzolanic Activity Using Methods Based on the Measurement of Electrical Conductivity of Suspensions of Portland Cement and Pozzolan.

ABSTRACT: The use of methods based on measuring electrical conductivity to assess pozzolanic activity has recently been used primarily in aqueous suspensions of pozzolan: calcium hydroxide. However, the use of similar methods in suspensions of cement with pozzolans has not been widely studied. This paper proposes a new method for rapid assessment of the pozzolanic activity of mineral admixtures in aqueous cement suspensions. In this study, the conditions for the application of the method were optimized, such as time, temperature, w/c ratio and dosage procedure. Finally, results are presented from the application of this method for characterizing the pozzolanic activity of the spent catalytic cracking catalyst. These results corroborate as previously reported, namely the high reactivity of this pozzolan obtained by other methods, such as thermogravimetry or evolution of the mechanical strength. In addition, the pozzolanic activity of the catalyst was compared with other pozzolans such as metakaolin and silica fume.

SUBMITTER: Velazquez S

PROVIDER: S-EPMC5512672 | biostudies-other | 2014 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Assessment of the Pozzolanic Activity of a Spent Catalyst by Conductivity Measurement of Aqueous Suspensions with Calcium Hydroxide.

Project description:The pozzolanic activity of the spent catalyst produced by fluid catalytic cracking (FCC) has been studied by various methods in recent years. However, no quick and easy method has been reported for this activity based on the associated studies. In this work, the pozzolanic activity of a spent catalyst was investigated by measuring its electrical conductivity in aqueous suspensions of pozzolan/calcium hydroxide. The behavior of the FCC catalyst residue was compared to that of reactive and inert materials of similar chemical compositions. Further, the influence of temperature on the suspension was studied, and also, a new method was proposed in which the pozzolan/calcium hydroxide ratio was varied (with the initial presence of solid Ca(OH)₂ in the system). It was concluded that the method is effective, fast and simple for evaluating the high reactivity of the catalyst. Therefore, this method is an alternative for the evaluation of the reactivity of pozzolanic materials.

| S-EPMC5453365 | biostudies-other

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation.

Project description:Electrical measurements are promising for evaluation of frost damage of concrete, but the index is still controversial. In this paper, to propose an efficient index, various electrical characteristics were examined to correlate them with the mechanical property degradation of meso-scale mortar samples due to combined effects of sodium chloride and freeze-thaw cycles (FTCs). While the electrical responses of specimens were measured during FTCs, the mechanical properties were obtained from three-point bending tests after FTCs. Typical microstructural change after the damage was also analyzed by using a water absorption test. The results showed that no clear degradation tendency was observed for electrical resistivity at the lowest temperature, the activation energy or the freezing/thawing point change with the FTCs. The reduction in electrical resistivity at reference temperature has a consistent tendency with that of elastic modulus and flexural strength, thus can be an efficient index for quantitative frost damage evaluation. The change due to salt-frost damage is mainly due to the increase of connectivity rather than porosity.

| S-EPMC7085024 | biostudies-literature

Near-infrared photoluminescence of Portland cement.

Project description:Portland cement emits bright near-infrared photoluminescence that can be excited by light wavelengths ranging from at least 500-1000 nm. The emission has a peak wavelength near 1140 nm and a width of approximately 30 nm. Its source is suggested to be small particles of silicon associated with calcium silicate phases. The luminescence peak wavelength appears independent of the cement hydration state, aggregates, and mechanical strain but increases weakly with increasing temperature. It varies slightly with the type of cement, suggesting a new non-contact method for identifying cement formulations. After a thin opaque coating is applied to a cement or concrete surface, subsequent formation of microcracks exposes the substrate's near-infrared emission, revealing the fracture locations, pattern, and progression. This damage would escape detection in normal imaging inspections. Near-infrared luminescence imaging may therefore provide a new tool for non-destructive testing of cement-based structures.

| S-EPMC8786940 | biostudies-literature

Strength and Microstructure Assessment of Partially Replaced Ordinary Portland Cement and Calcium Sulfoaluminate Cement with Pozzolans and Spent Coffee Grounds.

Project description:Supplementary cementitious materials are considered a viable and affordable way to reduce CO2 emissions from the cement industry's perspective since they can partially or nearly entirely replace ordinary Portland cement (OPC). This study compared the impact of adding spent coffee grounds (SCGs), fly ash (FA), and volcanic ash (VA) to two types of cement: OPC and calcium sulfoaluminate cement (CSA). Cement samples were characterized using compressive strength measurements (up to 210 days of curing), scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS), X-ray diffraction (XRD), attenuated total reflection infrared spectroscopy, and hydration temperature measurements. In all the studied systems, the presence of SCGs reduced compressive strength and delayed the hydration process. CSA composite cement containing 3.5% SCGs, 30% FA, and 30% VA showed compressive strength values of 20.4 MPa and 20.3 MPa, respectively, meeting the minimum requirement for non-structural applications. Additionally, the results indicate a formation of cementitious gel, calcium silicate hydrate (C-S-H) in the OPC-based composite cements, and calcium alumino-silicate hydrate (C-A-S-H) as well as ettringite in the CSA-based composite cements.

| S-EPMC10384487 | biostudies-literature

Chitosan-Based Accelerated Portland Cement Promotes Dentinogenic/Osteogenic Differentiation and Mineralization Activity of SHED.

Project description:Calcium silicate-based cements (CSCs) are widely used in various endodontic treatments to promote wound healing and hard tissue formation. Chitosan-based accelerated Portland cement (APC-CT) is a promising and affordable material for endodontic use. This study investigated the effect of APC-CT on apoptosis, cell attachment, dentinogenic/osteogenic differentiation and mineralization activity of stem cells from human exfoliated deciduous teeth (SHED). APC-CT was prepared with various concentrations of chitosan (CT) solution (0%, 0.625%, 1.25% and 2.5% (w/v)). Cell attachment was determined by direct contact analysis using field emission scanning electron microscopy (FESEM); while the material extracts were used for the analyses of apoptosis by flow cytometry, dentinogenic/osteogenic marker expression by real-time PCR and mineralization activity by Alizarin Red and Von Kossa staining. The cells effectively attached to the surfaces of APC and APC-CT, acquiring flattened elongated and rounded-shape morphology. Treatment of SHED with APC and APC-CT extracts showed no apoptotic effect. APC-CT induced upregulation of DSPP, MEPE, DMP-1, OPN, OCN, OPG and RANKL expression levels in SHED after 14 days, whereas RUNX2, ALP and COL1A1 expression levels were downregulated. Mineralization assays showed a progressive increase in the formation of calcium deposits in cells with material containing higher CT concentration and with incubation time. In conclusion, APC-CT is nontoxic and promotes dentinogenic/osteogenic differentiation and mineralization activity of SHED, indicating its regenerative potential as a promising substitute for the commercially available CSCs to induce dentin/bone regeneration.

| S-EPMC8512062 | biostudies-literature

Radiological Characteristics of Carbonated Portland Cement Mortars Made with GGBFS

Project description:The objective of this study is to assess whether the carbonation process can modify the physicochemical characteristics of the natural radionuclides of the three natural radioactive series, together with 40K. Three mortar specimens with different percentages of ground granulated blast-furnace slag (GGBFS), cured under water for 1, 3, 7, 14, or 28 days, were subjected to a natural carbonation process. Activity concentrations for the solid and ground mortars were determined by gamma spectrometry and by radiochemical separation of isotopic uranium. The novelty of this paper relies principally on the study we have carried out, for the first time, of the radiological characteristics of carbonated Portland cement mortars. It was found that the chemical properties of the 3 mortar specimens were not affected by the carbonation process, with particular attention placed on uranium (238U, 235U, and 234U), the activity concentrations of which were equivalent to the 226Ra results and ranged from 5.5 ± 1.6 Bq kg−1 to 21.4 ± 1.2 Bq kg−1 for the 238U. The average activity concentrations for the 3 types of mortars were lower than 20.1 Bq kg−1, 14.5 Bq kg−1, and 120.2 Bq kg−1 for the 226Ra, 232Th (212Pb), and 40K, respectively. Annual effective dose rates were equivalent to the natural background of 0.024 mSv. In addition, it was observed that the variation rate for the 222Rn emanation was due primarily to the Portland cement hydration and not due to the pore size redistribution as a consequence of the carbonation process. This research will provide new insights into the potential radiological risk from carbonated cement-based materials. Moreover, the assessment that is presented in this study will convey valuable information for future research that will explore the activity concentration of building materials containing NORM materials.

| S-EPMC9100595 | biostudies-literature

Microbial activity influences electrical conductivity of biofilm anode.

Project description:This study assessed the conductivity of a Geobacter-enriched biofilm anode in a microbial electrochemical cell (MxC) equipped with two gold anodes (25?mM acetate medium), as different proton gradients were built throughout the biofilm. There was no pH gradient across the biofilm anode at 100?mM phosphate buffer (current density 2.38 A/m2) and biofilm conductivity (Kbio) was as high as 0.87?mS/cm. In comparison, an inner biofilm became acidic at 2.5?mM phosphate buffer in which dead cells were accumulated at ?80??m of the inner biofilm anode. At this low phosphate buffer, Kbio significantly decreased by 0.27?mS/cm, together with declined current density of 0.64 A/m2. This work demonstrates that biofilm conductivity depends on the composition of live and dead cells in the conductive biofilm anode.

| S-EPMC7321815 | biostudies-literature

Synthesis and Characterization of a Hybrid Cement Based on Fly Ash, Metakaolin and Portland Cement Clinker.

Project description:Hybrid cement has become one of the most viable options in the reduction of CO2 emissions to the environment that are generated by the cement industry. This could be explained by the reduction of the content of clinker in the final mixture and substitution of the remaining percentage with supplementary cementitious materials with the help of an alkaline activation. Following that, properties that are provided by an Ordinary Portland Cement and of a geopolymer are mixed in this type of hybrid material and could be achieved at room temperature. Thereafter, the main objective of this research was to synthesize hybrid cements reducing the clinker content of Portland Cement up to 20% and use metakaolin and fly ash as supplementary cementitious materials in different proportions. The mixtures were alkaline activated with a mixture of sodium silicate and sodium hydroxide, calculating the amounts according to the percentage of Na2O that is present in each of the activators. The samples were then characterized using Compressive strength, X-ray diffraction, Fourier Transform Infrared Spectroscopy, and Scanning Electron Microscopy with energy-dispersive X-ray spectroscopy. The results indicated that the hybrid cements have similar mechanical properties than an Ordinary Portland Cement, and they resulted in a dense matrix of hydration products similar to those that are generated by cements and geopolymers.

| S-EPMC7084432 | biostudies-literature

Effect of Nano-SiO? on the Hydration and Microstructure of Portland Cement.

Project description:This paper systematically studied the modification of cement-based materials by nano-SiO? particles with an average diameter of about 20 nm. In order to obtain the effect of nano-SiO? particles on the mechanical properties, hydration, and pore structure of cement-based materials, adding 1%, 3%, and 5% content of nano-SiO? in cement paste, respectively. The results showed that the reaction of nano-SiO? particles with Ca(OH)? (crystal powder) started within 1 h, and formed C-S-H gel. The reaction speed was faster after aging for three days. The mechanical properties of cement-based materials were improved with the addition of 3% nano-SiO?, and the early strength enhancement of test pieces was obvious. Three-day compressive strength increased 33.2%, and 28-day compressive strength increased 18.5%. The exothermic peak of hydration heat of cement increased significantly after the addition of nano-SiO?. Appearance time of the exothermic peak was advanced and the total heat release increased. Thermogravimetric-differential scanning calorimetry (TG-DSC) analysis showed that nano-SiO? promoted the formation of C-S-H gel. The results of mercury intrusion porosimetry (MIP) showed that the total porosity of cement paste with 3% nano-SiO? was reduced by 5.51% and 5.4% at three days and 28 days, respectively, compared with the pure cement paste. At the same time, the pore structure of cement paste was optimized, and much-detrimental pores and detrimental pores decreased, while less harmful pores and innocuous pores increased.

| S-EPMC5302711 | biostudies-literature

Effects of Alkali on Water Soluble Hexavalent Chromium in Ordinary Portland Cement.

Project description:Due to the toxicity and mobility of chromium, the disposal of chromium-containing waste is a pressing issue. Co-processing of chromium-containing waste in a cement kiln is currently one of the most effective methods. However, the presence of water-soluble hexavalent chromium (Cr(VI)) in cement limits the use of this method. In this study, Na2CO3 was used to simulate alkali in industrial raw materials to investigate the pattern of influence of alkali content on water-soluble hexavalent chromium. The mechanisms associated with the oxidation and dissolution of chromium were investigated using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and inductively coupled plasma emission spectrometry (ICP-OES). The proportion of Cr(VI) in the clinker detected by XPS increased rapidly with increasing alkali content. In the cement slurry system, alkali promotes more hexavalent chromium leaching by influencing pH and other ion concentrations (Ca2+, SO42-). Therefore, the addition of alkali to either the raw meal or to the cement slurry system will favour an increase in the water-soluble Cr(VI) content. This study may provide theoretical guidance for the preparation and use of clinkers containing chromium.

| S-EPMC9025607 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data