Influence of Ultrafine 2CaO·SiO₂ Powder on Hydration Properties of Reactive Powder Concrete.

ABSTRACT: In this research, we assessed the influence of an ultrafine 2CaO·SiO₂ powder on the hydration properties of a reactive powder concrete system. The ultrafine powder was manufactured through chemical combustion method. The morphology of ultrafine powder and the development of hydration products in the cement paste prepared with ultrafine powder were investigated by scanning electron microscopy (SEM), mineralogical composition were determined by X-ray diffraction, while the heat release characteristics up to the age of 3 days were investigated by calorimetry. Moreover, the properties of cementitious system in fresh and hardened state (setting time, drying shrinkage, and compressive strength) with 5% ordinary Portland cement replaced by ultrafine powder were evaluated. From SEM micrographs, the particle size of ultrafine powder was found to be up to several hundred nanometers. The hydration product started formulating at the age of 3 days due to slow reacting nature of belitic 2CaO·SiO₂. The initial and final setting times were prolonged and no significant difference in drying shrinkage was observed when 5% ordinary Portland cement was replaced by ultrafine powder. Moreover, in comparison to control reactive powder concrete, the reactive powder concrete containing ultrafine powder showed improvement in compressive strength at and above 7 days of testing. Based on above, it can be concluded that the manufactured ultrafine 2CaO·SiO₂ powder has the potential to improve the performance of a reactive powder cementitious system.

SUBMITTER: Sun H

PROVIDER: S-EPMC5512907 | biostudies-other | 2015 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Elevated Temperature Performance of Reactive Powder Concrete Containing Recycled Fine Aggregates.

Project description:This study examines the effect of elevated temperature on various properties of reactive powder concrete (RPC) containing varying percentages of recycled fine aggregates as sand replacement. Recycled fine aggregates were collected from two sources, i.e., demolished normal strength concrete and demolished RPC. The specimens were prepared using 25%, 50%, and 75% replacement of natural sand with recycled fine aggregates, exposed to two different curing conditions and were subjected to four temperatures, i.e., 25, 200, 400, and 600 °C. Later, the specimens were tested for mass loss, compressive strength test, split-tensile strength test, flexural strength test, and water absorption test at all temperature ranges. Results determined that although the mechanical properties degraded with the temperature rise, the recycled aggregates can be employed as a partial replacement of natural sand in RPC without causing a significant decrease in the performance of RPC, and can help to produce more sustainable RPC by using recycled aggregates.

| S-EPMC7504074 | biostudies-literature

Mechanical Testing of Composite Steel and Reactive Powder Concrete Structural Element.

Project description:Reactive powder concrete (RPC), typically with higher compressive strength, is particularly attractive to structural engineers to apply them in infrastructures for enhancing their resistance under severe environments and loads. The main objective of the initial study presented in the paper was to investigate the behavior of two types of these new cementitious materials differing in the nature of microfibers. The RPC mixes were reinforced with steel and then with basalt microfibers. To evaluate the structural performance of developed unconventional materials, properties were investigated experimentally and compared with the control normal concrete mix. Mechanical tests indicated that dispersing fine fibers for making RPC, a mean compressive strength of 198.3 MPa and flexural strength 52.6 MPa or 23.2 MPa, respectively, were developed after 28 days of standard curing at ambient temperatures. In composite structures consisting of steel girders and a concrete slab, it is necessary to prevent the relative slip at the steel and concrete interface using shear connectors. The very high RPC strength enabled a material saving, weight-reduced application of precast construction, and particularly effective joint to steel beams. The investigation of such shear connection efficiency, in the case of the higher strength concrete deck, using standard push-out test specimens was executed. Finite element numerical models were developed. The outputs of the studies are presented in the paper.

| S-EPMC7558303 | biostudies-literature

Experimental Research on Concrete Beams Reinforced with High Ductility Steel Bars and Strengthened with a Reactive Powder Concrete Layer in the Compression Zone.

Project description:The article describes four-point bending tests of three reinforced concrete beams with identical cross-sections, spans, and high-ductility steel reinforcement systems. Two beams were strengthened in the compressed section with a thin layer of reactive powder concrete (RPC) bonded with evenly spaced stirrups. Their remaining sections, and the third reference beam, were made of ordinary concrete. Measurements of their deflections, strains and axis curvature; ultrasonic tests; and a photogrammetric analysis of the beams are the main results of the study. For one of the beams with the RPC, the load was increased in one stage. For the two remaining beams, the load was applied in four stages, increasing the maximum load from stage to stage in order to allow the analysis of the damage evolution before reaching the bending resistance. The most important effect observed was the stable behaviour of the strengthened beams in the post-critical state, as opposed to the reference beam, which had about two to three times less energy-absorbing capacity in this range. Moreover, thanks to the use of the RPC layer, the process of concrete cover delamination in the compression zone was significantly reduced, the high ductility of the rebars was fully utilized during the formation of plastic hinges, and the bending capacity was increased by approximately 12%.

| S-EPMC7560432 | biostudies-literature

Influence of Powder Deposition on Powder Bed and Specimen Properties.

Project description:Three-dimensional printing used to be a rapid prototyping process, but nowadays it is establishing as an additive manufacturing (AM) process. One of these AM techniques is selective laser sintering (SLS), which most often involves partial melting of the particles and therefore belongs to the category of powder bed fusion processes. Much progress has been made in this field by research on process parameters like laser power, hatch distance, and scanning speed while still lacking a fundamental understanding of the powder deposition and its influence on parts. A critical issue for economic manufacturing is the building time of parts with good mechanical properties, which can be reduced by lower surface roughness due to less or missing post processing. Therefore, the influence of three blade shapes on powder bed surface roughness has been evaluated for PA12 powder with three different grain size distributions by using advanced X-ray micro computed tomography (XMT) and a confocal laser scanning microscope (LSM). Along with those methods, new techniques for powder characterization were tested and compared. Lowest roughness has been achieved with a flat blade, based on a higher compression due to a larger contact zone between blade and powder bed. Furthermore, an anisotropic effect of the mechanical properties resulting from different building directions has been detected which can be explained by varying amounts of solid contact paths through the powder bed depending on powder application direction. In addition, an optimal combination of process parameters with an even compression of the powder bed leads to low surface roughness, complementing the advantages of additive manufacturing.

| S-EPMC6357138 | biostudies-other

The Effect of High Protein Powder Structure on Hydration, Glass Transition, Water Sorption, and Thermomechanical Properties.

Project description:Poor solubility of high protein milk powders can be an issue during the production of nutritional formulations, as well as for end-users. One possible way to improve powder solubility is through the creation of vacuoles and pores in the particle structure using high pressure gas injection during spray drying. The aim of this study was to determine whether changes in particle morphology effect physical properties, such as hydration, water sorption, structural strength, glass transition temperature, and α-relaxation temperatures. Four milk protein concentrate powders (MPC, 80%, w/w, protein) were produced, i.e., regular (R) and agglomerated (A) without nitrogen injection and regular (RN) and agglomerated (AN) with nitrogen injection. Electron microscopy confirmed that nitrogen injection increased powder particles' sphericity and created fractured structures with pores in both regular and agglomerated systems. Environmental scanning electron microscopy (ESEM) showed that nitrogen injection enhanced the moisture uptake and solubility properties of RN and AN as compared with non-nitrogen-injected powders (R and A). In particular, at the final swelling at over 100% relative humidity (RH), R, A, AN, and RN powders showed an increase in particle size of 25, 20, 40, and 97% respectively. The injection of nitrogen gas (NI) did not influence calorimetric glass transition temperature (Tg), which could be expected as there was no change to the powder composition, however, the agglomeration of powders did effect Tg. Interestingly, the creation of porous powder particles by NI did alter the α-relaxation temperatures (up to ~16 °C difference between R and AN powders at 44% RH) and the structural strength (up to ~11 °C difference between R and AN powders at 44% RH). The results of this study provide an in-depth understanding of the changes in the morphology and physical-mechanical properties of nitrogen gas-injected MPC powders.

| S-EPMC8834494 | biostudies-literature

Influence of Fly Ash Additive on the Properties of Concrete with Slag Cement.

Project description:This paper presents research on the impact of fly ash addition on selected physical and mechanical parameters of concrete made with slag cement. Experimental tests were carried out to measure the migration of chloride ions in concrete, the tightness of concrete exposed to water under pressure, and the compressive strength and tensile strength of concrete during splitting. Six series of concrete mixes made with CEM IIIA 42.5 and 32.5 cement were tested. The base concrete mix was modified by adding fly ash as a partial cement substitute in the amounts of 25% and 33%. A comparative analysis of the obtained results indicates a significant improvement in tightness, especially in concrete based on CEM IIIA 32.5 cement and resistance to chloride ion penetration for the concretes containing fly ash additive. In the concretes containing fly ash additive, a slower rate of initial strength increase and high strength over a long period of maturation are shown. In accordance with the presented research results, it is suggested that changes to the European standardization system be considered, to allow the use of fly ash additive in concrete made with CEM IIIA 42.5 or 32.5 cement classes. Such a solution is not currently acceptable in standards in some European Countries.

| S-EPMC7435652 | biostudies-literature

Freeze-Dissolving Method: A Fast Green Technology for Producing Nanoparticles and Ultrafine Powder.

Project description:A new technology, a freeze-dissolving method, has been developed to isolate nanoparticles or ultrafine powder and is a more efficient and sustainable method than the traditional freeze-drying method. In this work, frozen spherical ice particles were produced with an aqueous solution of sodium bicarbonate or ammonium dihydrogen phosphate at various concentrations to generate nanoparticles of NaHCO3 or (NH4)(H2PO4). The freeze-drying method sublimates ice, and nanoparticles of NaHCO3 or (NH4)(H2PO4) in the ice templates remain. The freeze-dissolving method dissolves ice particles in a low freezing point solvent at temperatures below 0 °C, and then, nanoparticles of NaHCO3 or (NH4)(H2PO4) can be isolated after filtration. The freeze-dissolving method is 100 times faster with about 100 times less energy consumption than the freeze-drying method as demonstrated in this work with a much smaller facility footprint and produces the same quantity of nanoparticles with a more uniform size distribution.

| S-EPMC9214760 | biostudies-literature

Preparation of Ultrafine Fly Ash-Based Superhydrophobic Composite Coating and Its Application to Foam Concrete.

Project description:The waterproof and thermal insulation property of foamed concrete is very important. In this study, the ultrafine fly ash (UFA)-based superhydrophobic composite coating was applied onto foam concrete. The UFA-based base coating that closely adhered to the concrete initially improved the waterproofness of the test block, and the silane coupling agent-modified UFA-based surface coating further achieved superhydrophobicity. The UFA on the coating surface and the asperities on the surface jointly formed a lotus leaf-like rough micro-nanostructure. The 154.34° water drop contact angle and 2.41° sliding angle on No. 5 coating were reached, indicating that it was a superhydrophobic surface. The water absorption ratios of the composite coating block were 1.87% and 16.6% at 4 h and 7 days, which were reduced by 97% and 75% in comparison with the original foam concrete. The compressive strength and heat conductivity coefficient after soaking for 4 h of the composite coating block were higher than 4.0 MPa and 0.225 W·m-1·K-1, respectively. The UFA-based superhydrophobic composite coating proposed in this study and applied onto foam concrete is simple and cheap, requires no precise instrument, and can be applied in a large area.

| S-EPMC7650569 | biostudies-literature

Influence of Crimped Steel Fibre on Properties of Concrete Based on an Aggregate Mix of Waste and Natural Aggregates.

Project description:This research was inspired by the growing global shortage of natural aggregates. Different types of waste ceramics (apart from recycled concrete) are the most popular materials for the production of waste aggregates as possible substitutes for natural ones. The aim of this research was to analyse the efficiency of different aggregate mixes composed of waste and natural materials focusing on two waste ceramic aggregates, which were prepared concrete mixes based on specifically composed aggregates (blend of natural aggregate, porous and iron oxide-rich (red) waste ceramic aggregate, and dense, kaolin-based (white) waste ceramic aggregate). All aggregates were thoroughly tested before utilisation for concrete mix creation. Altogether, four blends of aggregates were prepared in order to prepare concrete mixes using a simplex experiment design. The mixes were then modified by adding various amounts of crimped steel fibre. Such properties of hardened steel fibre-reinforced concrete (SFRC) such as density, compressive strength, shear strength, ultrasound propagation velocity, dynamic modulus of elasticity, and limit of proportionality during flexural testing were of special interest. Tests were conducted according to European and Japanese standards. The achieved fibre-reinforced concretes were characterised by satisfactory strength characteristics, thereby enabling the substitution of traditional reinforcement. Strength classes according to the fib Model Code 2010 were assigned.

| S-EPMC7216236 | biostudies-literature

Influence of Glass Silica Waste Nano Powder on the Mechanical and Microstructure Properties of Alkali-Activated Mortars.

Project description:The recycling of millions of tons of glass bottle waste produced each year is far from optimal. In the present work, ground blast furnace slag (GBFS) was substituted in fly ash-based alkali-activated mortars (AAMs) for the purpose of preparing glass bottle waste nano-powder (BGWNP). The AAMs mixed with BGWNP were subsequently subjected to assessment in terms of their energy consumption, economic viability, and mechanical and chemical qualities. Besides affording AAMs better mechanical qualities and making them more durable, waste recycling was also observed to diminish the emissions of carbon dioxide. A more than 6% decrease in carbon dioxide emissions, an over 16% increase in compressive strength, better durability and lower water absorption were demonstrated by AAM consisting of 5% BGWNP as a GBFS substitute. By contrast, lower strength was exhibited by AAM comprising 10% BGWNP. The conclusion reached was that the AAMs produced with BGWNP attenuated the effects of global warming and thus were environmentally advantageous. This could mean that glass waste, inadequate for reuse in glass manufacturing, could be given a second life rather than being disposed of in landfills, which is significant as concrete remains the most commonplace synthetic material throughout the world.

| S-EPMC7075184 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data