Characterization of Platinum Nanoparticles Deposited on Functionalized Graphene Sheets.

ABSTRACT: Due to its special electronic and ballistic transport properties, graphene has attracted much interest from researchers. In this study, platinum (Pt) nanoparticles were deposited on oxidized graphene sheets (cG). The graphene sheets were applied to overcome the corrosion problems of carbon black at operating conditions of proton exchange membrane fuel cells. To enhance the interfacial interactions between the graphene sheets and the Pt nanoparticles, the oxygen-containing functional groups were introduced onto the surface of graphene sheets. The results showed the Pt nanoparticles were uniformly dispersed on the surface of graphene sheets with a mean Pt particle size of 2.08 nm. The Pt nanoparticles deposited on graphene sheets exhibited better crystallinity and higher oxygen resistance. The metal Pt was the predominant Pt chemical state on Pt/cG (60.4%). The results from the cyclic voltammetry analysis showed the value of the electrochemical surface area (ECSA) was 88 m²/g (Pt/cG), much higher than that of Pt/C (46 m²/g). The long-term test illustrated the degradation in ECSA exhibited the order of Pt/C (33%) > Pt/cG (7%). The values of the utilization efficiency were calculated to be 64% for Pt/cG and 32% for Pt/C.

SUBMITTER: Chiang YC

PROVIDER: S-EPMC5512925 | biostudies-other | 2015 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Super-tough MXene-functionalized graphene sheets.

Project description:Flexible reduced graphene oxide (rGO) sheets are being considered for applications in portable electrical devices and flexible energy storage systems. However, the poor mechanical properties and electrical conductivities of rGO sheets are limiting factors for the development of such devices. Here we use MXene (M) nanosheets to functionalize graphene oxide platelets through Ti-O-C covalent bonding to obtain MrGO sheets. A MrGO sheet was crosslinked by a conjugated molecule (1-aminopyrene-disuccinimidyl suberate, AD). The incorporation of MXene nanosheets and AD molecules reduces the voids within the graphene sheet and improves the alignment of graphene platelets, resulting in much higher compactness and high toughness. In situ Raman spectroscopy and molecular dynamics simulations reveal the synergistic interfacial interaction mechanisms of Ti-O-C covalent bonding, sliding of MXene nanosheets, and ?-? bridging. Furthermore, a supercapacitor based on our super-tough MXene-functionalized graphene sheets provides a combination of energy and power densities that are high for flexible supercapacitors.

| S-EPMC7190721 | biostudies-literature

Tissue distribution and urinary excretion of intravenously administered chemically functionalized graphene oxide sheets.

Project description:The design of graphene-based materials for biomedical purposes is of great interest. Graphene oxide (GO) sheets represent the most widespread type of graphene materials in biological investigations. In this work, thin GO sheets were synthesized and further chemically functionalized with DOTA (1,4,7,10-tetraazacyclododecane-1,4,7,10-tetraacetic acid), a stable radiometal chelating agent, by an epoxide opening reaction. We report the tissue distribution of the functionalized GO sheets labeled with radioactive indium (111In) after intravenous administration in mice. Whole body single photon emission computed tomography (SPECT/CT) imaging, gamma counting studies, Raman microscopy and histological investigations indicated extensive urinary excretion and predominantly spleen accumulation. Intact GO sheets were detected in the urine of injected mice by Raman spectroscopy, high resolution transmission electron microscopy (HR-TEM) and electron diffraction. These results offer a previously unavailable pharmacological understanding on how chemically functionalized GO sheets transport in the blood stream and interact with physiological barriers that will determine their body excretion and tissue accumulation.

| S-EPMC5497267 | biostudies-literature

Enhanced Antibacterial Activity through Silver Nanoparticles Deposited onto Carboxylated Graphene Oxide Surface.

Project description:The strong bactericidal action of silver nanoparticles (AgNPs) is usually limited by their degree of aggregation. Deposition of AgNPs onto a graphene oxide (GO) surface to generate GO-Ag hybrids has been shown to be an effective method of controlling these aggregation problems. In this sense, a novel carboxylated graphene oxide-silver nanoparticle (GOCOOH-Ag) material has been synthesized, and their antibacterial and biofilm formation inhibitions have been studied. AgNPs decorating the GOCOOH surface achieved an average size of 6.74 ± 0.25 nm, which was smaller than that of AgNPs deposited onto the GO surface. In addition, better distribution of AgNPs was achieved using carboxylated material. It is important to highlight the main role of the carboxylic groups in the nucleation and growth of the AgNPs that decorate the GO-based material surface. In vitro antibacterial activity and antibiofilm-forming action were tested against Gram-positive (Staphylococcus aureus and Staphylococcus epidermidis) and Gram-negative bacteria (Pseudomonas aeruginosa and Escherichia coli). Both GO-Ag and GOCOOH-Ag reduced bacterial growth, analyzed by time-kill curves. However, the minimum inhibitory concentration and the minimum bactericidal concentration of GOCOOH-Ag were lower than those of GO-Ag for all strains studied, indicating that GOCOOH-Ag has better antibacterial activity. In addition, both nanomaterials prevent biofilm formation, with a higher reduction of biofilm mass and cell viability in the presence of GOCOOH-Ag. The carboxylation functionalization in GO-based materials can be applied to improve the bactericidal and antibiofilm-forming action of the AgNPs.

| S-EPMC9228250 | biostudies-literature

In-situ electrochemically deposited polypyrrole nanoparticles incorporated reduced graphene oxide as an efficient counter electrode for platinum-free dye-sensitized solar cells.

Project description:This paper reports a rapid and in-situ electrochemical polymerization method for the fabrication of polypyrrole nanoparticles incorporated reduced graphene oxide (rGO@PPy) nanocomposites on a ITO conducting glass and its application as a counter electrode for platinum-free dye-sensitized solar cell (DSSC). The scanning electron microscopic images show the uniform distribution of PPy nanoparticles with diameter ranges between 20 and 30 nm on the rGO sheets. The electrochemical studies reveal that the rGO@PPy has smaller charge transfer resistance and similar electrocatalytic activity as that of the standard Pt counter electrode for the I?(-)/I(-) redox reaction. The overall solar to electrical energy conversion efficiency of the DSSC with the rGO@PPy counter electrode is 2.21%, which is merely equal to the efficiency of DSSC with sputtered Pt counter electrode (2.19%). The excellent photovoltaic performance, rapid and simple fabrication method and low-cost of the rGO@PPy can be potentially exploited as a alternative counter electrode to the expensive Pt in DSSCs.

| S-EPMC4058879 | biostudies-other

Prismatic Silver Nanoparticles Decorated on Graphene Oxide Sheets for Superior Antibacterial Activity.

Project description:Spherical silver nanoparticles (Ag NPs) and silver nanoprisms (Ag NPrsms) were synthesized and decorated on graphene oxide (GO) nanosheets. The Ag contents were 29% and 23% in the GO-Ag NPs and GO-Ag NPrsms, respectively. The Ag NPrsms exhibited stronger (111) crystal signal than Ag NPs. The GO-Ag NPrsms exhibited higher Ag (I) content (75.6%) than GO-Ag NPs (69.9%). Increasing the nanomaterial concentration from 25 to 100 µg mL-1 improved the bactericidal efficiency, and the antibacterial potency was in the order: GO-Ag NPrsms > GO-Ag NPs > Ag NPrsms > Ag NPs > GO. Gram-positive Staphylococcus aureus (S. aureus) was more vulnerable than Gram-negative Escherichia coli (E. coli) upon exposure to these nanomaterials. The GO-Ag NPrsms demonstrated a complete (100%) bactericidal effect against S. aureus at a concentration of 100 µg mL-1. The GO-Ag composites outperformed those of Ag or GO due to the synergistic effect of bacteriostatic Ag particles and GO affinity toward bacteria. The levels of reactive oxygen species produced in the bacteria-nanomaterial mixtures were highly correlated to the antibacterial efficacy values. The GO-Ag NPrsms are promising as bactericidal agents to suppress biofilm formation and inhibit bacterial infection.

| S-EPMC9147939 | biostudies-literature

Improved Biocompatibility of Amino-functionalized Graphene Oxide in Caenorhabditis elegans

Project description:Graphene oxide (GO) holds high promise for diagnostic and therapeutic applications in nanomedicine but reportedly displays immunotoxicity, underlining the need for developing functionalized GO with improved biocompatibility. Here, we study the adverse effects of GO and amino-functionalized GO (GONH2) during Caenorhabditis elegans development and ageing upon acute or chronic exposure. Chronic GO treatment throughout the C. elegans development causes decreased fecundity and a reduction of animal size, while acute treatment does not lead to any measurable physiological decline. However, RNA-Seq data reveal that acute GO exposure induces innate immune gene expression. The p38 MAP kinase, PMK-1, which is a well-established master regulator of innate immunity, protects C. elegans from chronic GO toxicity, as pmk-1 mutants show reduced tissue-functionality and facultative vivipary. In a direct comparison, GONH2 exposure does not cause detrimental effects in the wild type or in pmk-1 mutants, and the innate immune response is considerably less pronounced. Our work establishes the enhanced biocompatibility of amino-functionalized GO in a whole-organism, emphasizing its potential as biomedical nanomaterial.

2022-05-10 | GSE131070 | GEO

Immobilization of ?-galactosidase onto functionalized graphene nano-sheets using response surface methodology and its analytical applications.

Project description:?-Galactosidase is a vital enzyme with diverse application in molecular biology and industries. It was covalently attached onto functionalized graphene nano-sheets for various analytical applications based on lactose reduction.Response surface methodology based on Box-Behnken design of experiment was used for determination of optimal immobilization conditions, which resulted in 84.2% immobilization efficiency. Native and immobilized functionalized graphene was characterized with the help of transmission and scanning electron microscopy, followed by Fourier transform infrared (FTIR) spectroscopy. Functionalized graphene sheets decorated with islands of immobilized enzyme were evidently visualized under both transmission and scanning electron microscopy after immobilization. FTIR spectra provided insight on various chemical interactions and bonding, involved during and after immobilization. Optimum temperature and energy of activation (E(a)) remains unchanged whereas optimum pH and K(m) were changed after immobilization. Increased thermal stability of enzyme was observed after conjugating the enzyme with functionalized graphene.Immobilized ?-galactosidase showed excellent reusability with a retention of more than 92% enzymatic activity after 10 reuses and an ideal performance at broad ranges of industrial environment.

| S-EPMC3399898 | biostudies-literature

Adsorption of 1,4-phenylene diisothiocyanate onto the graphene oxide sheets functionalized with polydiphenylamine in doped state.

Project description:Adsorption processes of 1,4-phenylene diisothiocyanate (PDITC) on two new platforms of the type graphene oxide (GO) sheets and GO layers functionalization with polydiphenylamine (PDPA) are studied by Raman scattering and photoluminescence (PL). An interaction in solid state phase of the two constituents, i.e. PDITC and GO sheets, and a deposition of PDITC onto the PDPA functionalized GO layers, respectively, by the drop casting method, were performed. In the first case, it is shown that interaction in solid state phase of GO with PDITC leads to an intercalation of the organic compound between GO sheets simultaneously with the appearance of the o-thiocarbamate groups, that induces: (i) an enhancement of the PDITC Raman lines situated in the 400-800 and 1000-1300 cm-1 spectral ranges, (ii) a change in the ratio between the relative intensities of the two Raman lines peaked at 1585 and 1602 cm-1 accompanied by an up-shift in the case of the second line and (iii) a down-shift of the PDTIC PL band from 502 to 491 nm. Using cyclic voltammetry, an electrochemical functionalization of the GO layers with PDPA doped with H3PMo12O40 heteropolyanions takes place, as demonstrated by Raman scattering and FTIR spectroscopy. The presence of the amine groups in the molecular structure of the doped PDPA functionalized GO layers induces a chemical adsorption of PDITC on this platform, when the thiourea groups appear simultaneously with o-thiocarbamate groups. A chemical mechanism is proposed to take place at the interface of the GO sheets and the doped PDPA functionalized GO layers, respectively, with PDITC.

| S-EPMC6700158 | biostudies-literature

Universal Transfer Printing of Micelle-Templated Nanoparticles Using Plasma-Functionalized Graphene.

Project description:Nanostructure incorporation into devices plays a key role in improving performance, yet processes for preparing two-dimensional (2D) arrays of colloidal nanoparticles tend not to be universally applicable, particularly for soft and oxygen-sensitive substrates for organic and perovskite-based electronics. Here, we show a method of transferring reverse micelle-deposited (RMD) nanoparticles (perovskite and metal oxide) on top of an organic layer, using a functionalized graphene carrier layer for transfer printing. As the technique can be applied universally to RMD nanoparticles, we used magnetic (γ-Fe2O3) and luminescent (methylammonium lead bromide (MAPbBr3)) nanoparticles to validate the transfer-printing methodology. The strong photoluminescence from the MAPbBr3 under UV illumination and high intrinsic field of the γ-Fe2O3 as measured by magnetic force microscopy (MFM), coupled with Raman measurements of the graphene layer, confirm that all components survive the transfer-printing process with little loss of properties. Such an approach to introducing uniform 2D arrays of nanoparticles onto sensitive substrates opens up new avenues to tune the device interfacial properties.

| S-EPMC7564086 | biostudies-literature

Improved Mechanical and Electrochemical Properties of XNBR Dielectric Elastomer Actuator by Poly(dopamine) Functionalized Graphene Nano-Sheets.

Project description:In this work, graphene nano-sheets (GNS) functionalized with poly(dopamine) (PDA) (denoted as GNS-PDA) were dispersed in a carboxylated nitrile butadiene rubber (XNBR) matrix to obtain excellent dielectric composites via latex mixing. Because hydrogen bonds were formed between ?COOH groups of XNBR and phenolic hydroxyl groups of PDA, the encapsulation of GNS-PDA around XNBR latex particles was achieved, and led to a segregated network structure of filler formed in the GNS-PDA/XNBR composite. Thus, the XNBR composite filled with GNS-PDA showed improved filler dispersion, enhanced dielectric constant and dielectric strength, and decreased conductivity compared with the XNBR composite filled with pristine GNS. Finally, the GNS-PDA/XNBR composite displayed an actuated strain of 2.4% at 18 kV/mm, and this actuated strain was much larger than that of pure XNBR (1.3%) at the same electric field. This simple, environmentally friendly, low-cost, and effective method provides a promising route for obtaining a high-performance dielectric elastomer with improved mechanical and electrochemical properties.

| S-EPMC6419049 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data