Synthesis of Poly(norbornene-methylamine), a Biomimetic of Chitosan, by Ring-Opening Metathesis Polymerization (ROMP).

ABSTRACT: ROMP is an effective method for preparing functional polymers due to its having characteristics of "living" polymerization and rapid development of catalysts. In the present work, poly(norbornene-methylamine), a mimic of chitosan, was synthesized via ROMP reaction. The amino-protected product, 5-norbornene-2-(N-methyl)-phthalimide, was prepared by a reaction of 5-norbornene-2-methylamine with phthalic anhydride, which was then subjected to the ROMP reaction in the presence of Hoveyda-Grubbs 2nd catalyst to afford poly(norbornene-(N-methyl)-phthalimide). The target product, poly(norbornene-methylamine), was obtained by deprotection reaction of poly(norbornene-(N-methyl)-phthalimide). The products in each step were characterized by FTIR and ¹H-NMR, and their thermal stabilities were determined by TG analysis. The effects of molar ratio between monomer ([M]/[I]) and catalyst on the average relative molecular weight ( M n ¯ ) and molecular weight distribution of the produced polymer products were determined by gel permeation chromatography (GPC). It was found that the M n ¯ of poly(norbornene-(N-methyl)-phthalimide) was controllable and exhibited a narrow polydispersity index (PDI) (~1.10). The synthesis condition of 5-norbornene-2-(N-methyl)-phthalimide was optimized by determining the yields at different reaction temperatures and reaction times. The highest yield was obtained at a reaction temperature of 130 °C and a reaction time of 20 min. Our work provides a new strategy to synthesize polymers with controllable structures and free -NH₂ groups via ROMP.

SUBMITTER: Li N

PROVIDER: S-EPMC5532665 | biostudies-other | 2017 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:We report the synthesis and characterization of synthetic polymer aerogels based on dendritic-type urethane-norbornene monomers. The core of those monomers is based either on an aromatic/rigid (TIPM/Desmodur RE), or an aliphatic/flexible (Desmodur N3300) triisocyanate. The terminal norbornene groups (three at the tip of each of the three branches) were polymerized via ROMP using the inexpensive 1st generation Grubbs catalyst. The polymerization/gelation conditions were optimized by varying the amount of the catalyst. The resulting wet-gels were dried either from pentane under ambient pressure at 50 °C, or from t-butanol via freeze-drying, or by using supercritical fluid (SCF) CO?. Monomers were characterized with high resolution mass spectrometry (HRMS), ¹H- and solid-state 13C-NMR. Aerogels were characterized with ATR-FTIR and solid-state 13C-NMR. The porous network was probed with N?-sorption and SEM. The thermal stability of monomers and aerogels was studied with TGA, which also provides evidence for the number of norbornene groups that reacted via ROMP. At low densities (<0.1 g cm?3) all aerogels were highly porous (porosity > 90%), mostly macroporous materials; aerogels based on the aliphatic/flexible core were fragile, whereas aerogels containing the aromatic/rigid core were plastic, and at even lower densities (0.03 g cm?3) foamy. At higher densities (0.2?0.7 g cm?3) all materials were stiff, strong, and hard. At low monomer concentrations all aerogels consisted of discrete primary particles that formed spherical secondary aggregates. At higher monomer concentrations the structure consisted of fused particles with the size of the previous secondary aggregates, due to the low solubility of the developing polymer, which phase-separated and formed a primary particle network. Same-size fused aggregates were observed for both aliphatic and aromatic triisocyanate-derived aerogels, leading to the conclusion that it is not the aliphatic or aromatic core that determines phase separation, but rather the solubility of the polymeric backbone (polynorbornene) that is in both cases the same. The material properties were compared to those of analogous aerogels bearing only one norbornene moiety at the tip of each branch deriving from the same cores.

Dataset Information

Synthesis of Poly(norbornene-methylamine), a Biomimetic of Chitosan, by Ring-Opening Metathesis Polymerization (ROMP).

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure